CN106700274A - Rubber for sealing strip of automobile and preparation method of rubber - Google Patents

Rubber for sealing strip of automobile and preparation method of rubber Download PDF

Info

Publication number
CN106700274A
CN106700274A CN201510471063.XA CN201510471063A CN106700274A CN 106700274 A CN106700274 A CN 106700274A CN 201510471063 A CN201510471063 A CN 201510471063A CN 106700274 A CN106700274 A CN 106700274A
Authority
CN
China
Prior art keywords
weather strip
agent
rubber
automobile
accelerator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510471063.XA
Other languages
Chinese (zh)
Inventor
赵宏超
苏怀生
井垒
高建国
詹才福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAICANG GUANLIAN POLYMERIC MATERIAL CO Ltd
Original Assignee
TAICANG GUANLIAN POLYMERIC MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAICANG GUANLIAN POLYMERIC MATERIAL CO Ltd filed Critical TAICANG GUANLIAN POLYMERIC MATERIAL CO Ltd
Priority to CN201510471063.XA priority Critical patent/CN106700274A/en
Publication of CN106700274A publication Critical patent/CN106700274A/en
Pending legal-status Critical Current

Abstract

The invention discloses rubber for a sealing strip of an automobile. The rubber is prepared from the following components in percentage by weight: 20%-25% of ethylene propylene diene monomer, 31%-36% of carbon black, 12%-16% of a filling agent, 20-25% of a softening plastifier, 2.6-2.8% of an active agent, 3-5% of a moisture absorbent, and 1.3-2% of the total of a vulcanizing agent and an accelerant. The rubber disclosed by the invention has the characteristics of being resistant to heat, resistant to ozone, high in compression deformation properties, high in sealing properties, free from pollution, free from flavor, long in service life, free from production of bubbles, and low in defect rate.

Description

Weather strip for automobile rubber and preparation method thereof
Technical field
The present invention relates to a kind of rubber, more particularly to it is a kind of adapt to weather strip for automobile rubber and its Preparation method.
Background technology
Sealing is an important indicator of vehicle complete vehicle quality, and weather strip for automobile product is exactly One of good and bad important spare part of this index is determined, it is widely used in wind before and after automobile The vehicle body positions such as gear, car door, vehicle window, initiation cabin, boot, fill up between car body component Gap, with functions such as damping, waterproof and dustproof, sound insulation, decorations, to driver and conductor and Vehicle plays maintenance effect.
With the progressively development of automobile industry, the demand for exports amount of weather strip for automobile increases year by year, Requirement to its quality is also stepped up.In addition to common product performance is met, also more fill Weight environmental protection, low stain, tasteless grade requires, more to adapt to the development of Hyundai Motor industry.
The content of the invention
The purpose of the present invention is aiming above mentioned problem, there is provided a kind of combination property is good, low dirt Dye, it is tasteless, bubble is avoided the occurrence of when production, the automobile sealed EPDM of rate of reducing the number of rejects and seconds Rubber, while additionally providing a kind of method for preparing the rubber.
To achieve these goals, the invention provides following technical scheme:Weather strip for automobile is used Rubber, it is made up of following components in percentage by weight:
Ethylene propylene diene rubber 20%-25%;
Carbon black 31%-36%;
Filler 12%-16%;
Soften plasticizer 20-25%;
Activating agent 2.6-2.8%;
Vulcanizing agent+accelerator 1.3-2%;
Hygroscopic agent 3-5%.
Preferably, the ethylene propylene diene rubber trade mark is EP525.
Preferably, the carbon black trade mark is HS-22.
Preferably, above-mentioned softening plasticizer can select P2280.
Preferably, the filler is CaCO3
Preferably, the softening plasticizer is P2280.
Preferably, the activating agent is the one kind or many in stearic acid, polyethylene glycol, zinc oxide Kind.
Preferably, the vulcanizing agent is sulphur, and the accelerator is accelerator TT, accelerator One or more in M, altax, accelerator TBZTD.
Preferably, the hygroscopic agent is calcium oxide CaO.
The present invention a kind of preparation method of weather strip for automobile rubber is also provided, its successively include with Lower step:
(1) get the raw materials ready:Proportioning according to claim 1, by ethylene propylene diene rubber, carbon black + filler, softening plasticizer, hygroscopic agent, activating agent are placed after weighing respectively, separately by vulcanizing agent + accelerator is matched somebody with somebody together after weighing;
(2) first mixing:By ethylene propylene diene rubber and activating agent and part carbon black+filler With soften plasticizer input mixer mixing 30-60 second, then proceed to input remaining carbon black+fill out Material and softening plasticizer are kneaded 60-120 seconds, are unloaded after then continuing to knead 60-90 seconds after cleaning Expect slice on cutting machine, be made elastomeric compound A;
(3) second mixing:Elastomeric compound A, hygroscopic agent and vulcanizing agent+accelerator input is close Mill is kneaded 60-90 seconds, and cutting machine is dumped into after then continuing to knead 30-60 seconds after cleaning Upper slice, completes to prepare.
From the ethylene propylene diene rubber of trade mark EP525, viscosity is low, ethylene contents 60 or so, Can further help rubber product to obtain outstanding extrusion effect, improve extrusion efficiency.
Hygroscopic agent can play a part of to absorb moisture in sealing strip, prevent product bubble.
The present invention is used as body of rubber material by from suitable ethylene propylene diene rubber, by closing The formulation ratio of reason, makes the physical and mechanical properties of product good.Original of reduced contamination is selected simultaneously Material, it is to avoid from variable color substance so that the appearance that product has had.Vulcanizing system is selected Product is tasteless after vulcanization or material of substantially tasteless.Therefore, product combination property of the invention is good It is good, low stain, free from extraneous odour.In preparation method, by optimizing calendering process, mixing is reached Glue is uniformly dispersed, and reduces the defects such as product bubble, reduces percent defective, improve production efficiency.
Specific embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, shown So, described embodiment is only a part of embodiment of the invention, rather than whole implementation Example.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creativeness The every other embodiment obtained under the premise of work, belongs to the scope of protection of the invention.
Embodiment 1-6
Weather strip for automobile rubber involved in the present invention is manufactured according to following steps:(1) it is standby Material:Ethylene propylene diene rubber, carbon black+filler are softened plasticising by the proportioning in table 1 below Agent, hygroscopic agent, activating agent are placed after weighing respectively, are matched somebody with somebody after separately vulcanizing agent+accelerator is weighed Together;
(2) first mixing:By ethylene propylene diene rubber and activating agent, part carbon black+filler and Soften plasticizer input mixer mixing 30-60 seconds, then proceed to put into remaining carbon black+filler Kneaded 60-120 seconds with plasticizer is softened, unloaded after then continuing to knead 60-90 seconds after cleaning Expect slice on cutting machine, be made elastomeric compound A;
(3) second mixing:Elastomeric compound A, hygroscopic agent and vulcanizing agent+accelerator input is close Mill is kneaded 60-90 seconds, and cutting machine is dumped into after then continuing to knead 30-60 seconds after cleaning Upper slice, completes to prepare.
Each raw materials used composition of embodiment and content are shown in Table 1.
The composition and consumption of the embodiment 1-6 raw materials of table 1
In preparation process, the mixing time of each embodiment is shown in Table 2.
The mixing time of the embodiment 1-6 of table 2
Time in calendering process is very crucial, and time length is related to the uniform of mixing, material point Whether dissipate.Time is too short, and material is not completely dispersed, and the defect such as product surface particle is more.When Between it is long, increase cost, it is also possible to cause sizing material Mooney low, easy bubble of product etc.. The present invention uses appropriate mixing time so that material dispersion is uniform, and surface is without particle, product Bubble-free.
Table 3 is the performance parameter of embodiment 1-6 products.
The performance parameter of the embodiment 1-6 products of table 3
As can be seen from Table 3, the rubber of embodiment 1-6 is well adapted for window sealing strip Vulcanization production technology, does not produce bubble, extrusion flowability to be obtained for raising.Meanwhile, stretching Intensity can reach more than 8.6MPa through experiment, and highest can reach close to 9.4MPa, extend Rate can reach 297-340%, be suitably applied automobile sealed slat gum.
Above-described is only the preferred embodiment of the present invention, it is noted that for this area Those of ordinary skill for, without departing from the concept of the premise of the invention, can also do Go out some deformations and improvement, these belong to protection scope of the present invention.

Claims (9)

1. weather strip for automobile rubber, it is characterised in that:It is made up of following components in percentage by weight:
Ethylene propylene diene rubber 20%-25%;
Carbon black 31%-36%;
Filler 12%-16%;
Soften plasticizer 20-25%;
Activating agent 2.6-2.8%;
Vulcanizing agent+accelerator 1.3-2%;
Hygroscopic agent 3-5%.
2. weather strip for automobile rubber according to claim 1, it is characterised in that:The trade mark of the ethylene propylene diene rubber is EP525.
3. weather strip for automobile rubber according to claim 1, it is characterised in that:The carbon black is HS-22.
4. weather strip for automobile rubber according to claim 1, it is characterised in that:The filler is CaCO3
5. weather strip for automobile rubber according to claim 1, it is characterised in that:The softening plasticizer is P2280.
6. weather strip for automobile rubber according to claim 1, it is characterised in that:The activating agent is one or more in stearic acid, polyethylene glycol, zinc oxide.
7. weather strip for automobile rubber according to claim 1, it is characterised in that:The vulcanizing agent is sulphur, and the accelerator is one or more in accelerator TT, captax, altax, accelerator TBZTD.
8. weather strip for automobile rubber according to claim 1, it is characterised in that:The hygroscopic agent is CaO.
9. a kind of preparation method of weather strip for automobile rubber, it is characterised in that:The preparation method is comprised the following steps:
(1) get the raw materials ready:By ethylene propylene diene rubber, carbon black, filler, soften after plasticizer, hygroscopic agent, activating agent are weighed respectively and place, separately by vulcanizing agent+accelerator with together;
(2) first mixing:By ethylene propylene diene rubber and activating agent, and part carbon black+filler and softening plasticizer put into mixer mixing 30-60 seconds, then proceed to put into remaining carbon black+filler and soften plasticizer knead 60-120 seconds, then slice on cutting machine is dumped into after continuing to knead 60-90 seconds after cleaning, elastomeric compound A is made;
(3) second mixing:By elastomeric compound A, hygroscopic agent and vulcanizing agent+accelerator input mixer mixing 60-90 seconds, slice on cutting machine is dumped into after then continuing to knead 30-60 seconds after cleaning, completes to prepare.
CN201510471063.XA 2015-08-04 2015-08-04 Rubber for sealing strip of automobile and preparation method of rubber Pending CN106700274A (en)