CN106675266A - Waterborne colored steel paint - Google Patents
Waterborne colored steel paint Download PDFInfo
- Publication number
- CN106675266A CN106675266A CN201611232253.7A CN201611232253A CN106675266A CN 106675266 A CN106675266 A CN 106675266A CN 201611232253 A CN201611232253 A CN 201611232253A CN 106675266 A CN106675266 A CN 106675266A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- waterborne
- paint
- aqueouss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterborne colored steel paint. The waterborne colored steel paint comprises waterborne acrylic emulsion, silica sol, titanium dioxide, sericite powder, waterborne color paste, an amine salt dispersant, a nonionic wetting agent PE-100, a silicone oil defoaming agent, a flatting agent, an anti-sag agent and water. Through research and development, the waterborne colored steel paint, a one-coat paint, is prepared from waterborne resins by being supplemented by waterborne functional additives and environment-friendly pigment and filler through a conventional application technology and has the advantages of waterborne performance, energy conservation, environmental protection, non-flammability, non-explosive performance and no need for special treatment of base material surfaces and primer coating.
Description
Technical field
The present invention relates to build, the water-repellent paint of building materials, and in particular to a kind of aqueouss coloured silk steel paint.
Background technology
With economic fast development, environmental protection is also increasingly put on process.After the improvement of physical conditions for life, people are more
Focus on the healthy nuisanceless of the quality of life and living environment.But water-repellent paint in the market still adopts organic reagent mostly
Benzene, toluene etc. are as solvent and add some poisonous additives, water-repellent paint made by these raw materials and additive to contain easily
The toxic gas of volatilization, directly endanger health.
The content of the invention
It is an object of the invention to provide a kind of water paint, it have aqueouss, energy-saving and environmental protection, do not fire, the characteristic such as not quick-fried.
For achieving the above object, the technical solution used in the present invention is as follows：A kind of aqueouss coloured silk steel paint, by following weight portion
Raw material is constituted：
Aqueous acrylic emulsion 40-60 parts, Ludox 10-30 parts, titanium dioxide 10-20 parts, sericite in powder 5-15 parts, aqueouss
Mill base 1.5-3.5 parts, ammonium salt dispersant 0.1-0.3 parts, non-ionic wetting agent PE-100 0.2-0.4 parts, silicon oil foam killer 0.1-
0.4 part, levelling agent 0.3-0.8 parts, anti-sagging agent 0.5-1.0 parts, water 5-10 parts.
The Ludox is organosilicon.
The titanium dioxide model Rutile type titanium dioxide ZR-940.
The ammonium salt dispersant model 5040.
Silicon oil foam killer model NXZ.
The levelling agent is polyurethane levelling agent R2020.
The anti-sagging agent is anti-sagging agent BYK333.
Above-mentioned aqueouss coloured silk steel paint is developed using conventional technique for applying, is concretely comprised the following steps：
Slurrying：First by water, ammonium salt dispersant, non-ionic wetting agent PE-100, silicon oil foam killer, levelling agent and resist sagging
In agent input dispersion tank, stir, successively put into titanium dioxide, sericite in powder under stirring, dispersed with stirring 30-
40min is to substantially uniformity；The rate of dispersion of blender is 1000-1200rpm/min；
Grinding：The slurry of step one gained is transferred in sand mill and is ground, sand milling acc power is 20-22KW, is ground
Consume time as 50-60min；
Paint：Ground slurry obtained by step 2 is transferred in rustless steel paint mixing tank, aqueous acrylamide yogurt is added
Liquid and Ludox, stirring 20-30min to substantially uniformity, the speed of blender is 800rpm/min；
Toning：Mixing color is carried out according to product needed, aqueous color paste is added in the paint obtained by step 3, stirring is mixed
Close uniform；
Filter, pack：The water colour paint mixed colours is carried out filtering and metering packing.
Beneficial effects of the present invention：The aqueouss coloured silk steel paint of the present invention adopts water-base resin, is equipped with aqueous functional auxiliary agent, environmental protection
Type color stuffing combines conventional technique for applying and develops.Product is without harmful substances such as formaldehyde, benzene homologues, TDI；With aqueouss,
Energy-saving and environmental protection, do not fire, it is not quick-fried the advantages of；And paint film is smooth, adhesive force is good；Simultaneously substrate surface does not need special handling, is not required to
Apply priming；The present invention is paint for priming paint and top lacquer.
Specific embodiment
The specific embodiment of the present invention is described in detail below.It should be appreciated that described herein concrete
Embodiment is merely to illustrate and explains the present invention, it is not limited to these embodiments.In embodiment, aqueous acrylic emulsion is
Ahmedabad richness Industrial Co., Ltd. product, organosilicon is Jiangyin Guobang Chemical Co., Ltd.'s product, and titanium dioxide is Zhenjiang titanium dioxide stock
Part company limited product, sericite in powder is Chuzhou Grea Minerals Co., Ltd.'s product, and aqueous color paste is Suzhou generation name science and technology
Limited company's product, ammonium salt dispersant 5040, non-ionic wetting agent PE-100, silicon oil foam killer NXZ, polyurethane levelling agent
R2020 is Shenzhen Haichuan Chemical Technology Co., Ltd's product, and anti-sagging agent BYK333 is German Bick chemical company product.
Embodiment 1
A kind of aqueouss coloured silk steel paint, is made up of the raw material of following weight portion：
45 parts of aqueous acrylic emulsion, 20 parts of organosilicon, 15 parts of titanium dioxide ZR-940,11 parts of sericite in powder, aqueous color paste
2 parts, 5,040 0.2 parts of ammonium salt dispersant, 0.4 part of non-ionic wetting agent PE-100,0.4 part of silicon oil foam killer, polyurethane levelling
0.5 part of agent R2020,0.5 part of anti-sagging agent BYK333,5 parts of water.
Above-mentioned aqueouss coloured silk steel paint is developed using conventional technique for applying, is concretely comprised the following steps：
Slurrying：First by water, ammonium salt dispersant, non-ionic wetting agent PE-100, silicon oil foam killer, levelling agent and resist sagging
In agent input dispersion tank, stir, successively put into titanium dioxide, sericite in powder under stirring, dispersed with stirring 30-
40min is to substantially uniformity；The rate of dispersion of blender is 1000-1200rpm/min；
Grinding：The slurry of gained in step one is transferred in sand mill and is ground, sand milling acc power is 20-22KW,
Milling time is 50-60min；
Paint：The ground slurry of gained in step 2 is transferred in rustless steel paint mixing tank, water soluble acrylic acid is added
Emulsion and Ludox, stirring 20-30min to substantially uniformity, the speed of blender is 800rpm/min；
Toning：Mixing color is carried out according to product needed, aqueous color paste is added in the paint of gained in step 3, stirred
Mix homogeneously；
Filter, pack：The water colour paint mixed colours is carried out filtering and metering packing.
Embodiment 2
A kind of aqueouss coloured silk steel paint, is made up of the raw material of following weight portion：
40 parts of aqueous acrylic emulsion, 20 parts of organosilicon, 16 parts of titanium dioxide ZR-940,13 parts of sericite in powder, aqueous color paste
2.5 parts, 5,040 0.3 parts of ammonium salt dispersant, 0.3 part of non-ionic wetting agent PE-100,0.4 part of silicon oil foam killer, polyurethane stream
0.7 part of flat agent R2020,0.8 part of anti-sagging agent BYK333,6 parts of water.
Above-mentioned aqueouss coloured silk steel paint is developed using conventional technique for applying, is concretely comprised the following steps：
Slurrying：First by water, ammonium salt dispersant, non-ionic wetting agent PE-100, silicon oil foam killer, levelling agent and resist sagging
In agent input dispersion tank, stir, successively put into titanium dioxide, sericite in powder under stirring, dispersed with stirring 30-
40min is to substantially uniformity；The rate of dispersion of blender is 1000-1200rpm/min；
Grinding：The slurry of gained in step one is transferred in sand mill and is ground, sand milling acc power is 20-22KW,
Milling time is 50-60min；
Paint：The ground slurry of gained in step 2 is transferred in rustless steel paint mixing tank, water soluble acrylic acid is added
Emulsion and Ludox, stirring 20-30min to substantially uniformity, the speed of blender is 800rpm/min；
Toning：Mixing color is carried out according to product needed, aqueous color paste is added in the paint of gained in step 3, stirred
Mix homogeneously；
Filter, pack：The water colour paint mixed colours is carried out filtering and metering packing.
Detection example
Aqueouss of the present invention coloured silk steel paint is sprayed on into 1 meter of width, 10 meters of length surface of thin steel sheet and forms coating, then
Spontaneously dry at ambient temperature；Coating performance is tested.
Aqueouss coloured silk steel paint performance detection data such as following table of the present invention：
Claims (7)
1. a kind of aqueouss coloured silk steel paint, it is characterised in that be made up of the raw material of following weight portion：
Aqueous acrylic emulsion 40-60 parts, Ludox 10-30 parts, titanium dioxide 10-20 parts, sericite in powder 5-15 parts, aqueous color paste
1.5-3.5 parts, ammonium salt dispersant 0.1-0.3 parts, non-ionic wetting agent PE-100 0.2-0.4 parts, silicon oil foam killer 0.1-0.4
Part, levelling agent 0.3-0.8 parts, anti-sagging agent 0.5-1.0 parts, water 5-10 parts.
2. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that：The Ludox is organosilicon.
3. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that：The titanium dioxide model rutile type titanium
White lead ZR-940.
4. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that：The ammonium salt dispersant model 5040.
5. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that：The levelling agent is polyurethane levelling agent
R2020。
6. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that：The anti-sagging agent is anti-sagging agent
BYK333。
7. a kind of aqueouss coloured silk steel paint according to claim 1, it is characterised in that the preparation method is concretely comprised the following steps：
Slurrying：Water, ammonium salt dispersant, non-ionic wetting agent PE-100, silicon oil foam killer, levelling agent and anti-sagging agent are thrown first
In entering dispersion tank, stir, successively put into titanium dioxide, sericite in powder under stirring, dispersed with stirring 30-40min is extremely
Substantially uniformity；The rate of dispersion of blender is 1000-1200rpm/min；
Grinding：The slurry of gained in step one is transferred in sand mill and is ground, sand milling acc power is 20-22KW, is ground
Time is 50-60min；
Paint：The ground slurry of gained in step 2 is transferred in rustless steel paint mixing tank, aqueous acrylic emulsion is added
And Ludox, stirring 20-30min to substantially uniformity, the speed of blender is 800rpm/min；
Toning：Mixing color is carried out according to product needed, aqueous color paste, stirring mixing is added in the paint of gained in step 3
Uniformly；
Filter, pack：The water colour paint mixed colours is carried out filtering and metering packing.