CN106675104A - Environment-friendly active calcium carbonate - Google Patents
Environment-friendly active calcium carbonate Download PDFInfo
- Publication number
- CN106675104A CN106675104A CN201510752687.9A CN201510752687A CN106675104A CN 106675104 A CN106675104 A CN 106675104A CN 201510752687 A CN201510752687 A CN 201510752687A CN 106675104 A CN106675104 A CN 106675104A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- environment
- active calcium
- friendly active
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly active calcium carbonate, which is prepared from the following raw materials (by weight): 90-110 parts of calcium carbonate, 3-4 parts of polyethylene wax, 1-2 parts of glycerin, 4-5 parts of potash feldspar powder, 0.2-0.4 part of high density polyethylene, 2-4 parts of sodium hyaluronate, 3.3-4.5 parts of anilmomethyl triethoxy, 3-5 parts of copper stearate, 1-2 parts of tea polyphenol, 1.5-2.5 parts of styrene and a proper amount of deionized water. According to the formula, environment-friendly nontoxic raw materials are used, and safe and nontoxic ingredients are added. By the use of high-molecular polymer, strength, toughness and high temperature and low temperature resistance of the product are greatly enhanced.
Description
Technical field
The present invention relates to calcium carbonate field, more particularly to a kind of environment-friendly active calcium carbonate.
Background technology
Calcium carbonate is a kind of highly important functional inorganic filling, be widely used in plastics, rubber,
The industrial circle such as coating and papermaking.In the application of calcium carbonate, most products belong to the category of polymer,
Such as plastics, rubber, adhesive, coating etc., and occupy the important market share..However, dispersant
With the addition of surface modifier so that nano-calcium carbonate temperature is diminished significantly using window, reason is conventional
Dispersant and coupling agent are easily decomposes at high temperature, cause bubble, cracking, defect, deformation etc., and not
Beneficial to environmental protection；Activated Calcium carbonate is with calcium carbonate as base-material, using polyfunctional surfactant and compound height
Effect processing aid, is modified activation process and forms to inorganic powder surface.Calcium carbonate after modified process
Powder, surface forms a kind of special cladding structure, can significantly improve in the polymer matrixs such as polyolefin
Dispersiveness and compatibility, and interface interaction can be produced and between polymer matrix, so as to improve the anti-impact of product
Hit intensity, is a kind of incremental filling additive of function admirable.
A kind of environment-friendly active calcium carbonate disclosed by the invention, it is obtained by the raw material of following weight parts：Carbonic acid
Calcium 90-110, Tissuemat E 3-4, glycerine 1-2, feldspar in powder 4-5, high density polyethylene (HDPE) 0.2-0.4,
Sodium Hyaluronate 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, Tea Polyphenols 1-2, benzene
Ethene 1.5-2.5, appropriate deionized water.Inventive formulation adopt environment-protecting asepsis raw material, addition safety non-toxic into
Point, make product cold can all improve a lot enhancing, toughness reinforcing, high temperature resistant are low with high molecular polymer.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of environment-friendly active calcium carbonate, it is
It is obtained by the raw material of following weight parts：Calcium carbonate 90-110, Tissuemat E 3-4, glycerine 1-2, potassium are long
Stone flour 4-5, high density polyethylene (HDPE) 0.2-0.4, Sodium Hyaluronate 2-4, anilinomethyl triethoxy 3.3-4.5,
Copper stearate 3-5, Tea Polyphenols 1-2, styrene 1.5-2.5, appropriate deionized water.
A kind of preparation method of environment-friendly active calcium carbonate of the present invention is comprised the following steps：
(1) calcium carbonate is added after homogenizer, adds Tissuemat E, glycerine, feldspar in powder, highly dense
Degree polyethylene, Sodium Hyaluronate, anilinomethyl triethoxy, copper stearate, Tea Polyphenols, are warming up to 70-80 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.
The invention has the beneficial effects as follows：Formula adopts environment-protecting asepsis raw material, adds safety non-toxic composition, with height
Molecularly Imprinted Polymer makes product cold can all improve a lot enhancing, toughness reinforcing, high temperature resistant are low.
Specific embodiment
Specific embodiment：A kind of environment-friendly active calcium carbonate, it is obtained by the raw material of following weight parts：Calcium carbonate
90-110, Tissuemat E 3-4, glycerine 1-2, feldspar in powder 4-5, high density polyethylene (HDPE) 0.2-0.4, thoroughly
Bright matter acid sodium 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, Tea Polyphenols 1-2, benzene second
Alkene 1.5-2.5, appropriate deionized water.
A kind of preparation method of environment-friendly active calcium carbonate of the present invention is comprised the following steps：
(1) calcium carbonate is added after homogenizer, adds Tissuemat E, glycerine, feldspar in powder, highly dense
Degree polyethylene, Sodium Hyaluronate, anilinomethyl triethoxy, copper stearate, Tea Polyphenols, are warming up to 70-80 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.
Inventive formulation adopts environment-protecting asepsis raw material, adds safety non-toxic composition, and with high molecular polymer product is made
Product cold can all improve a lot enhancing, toughness reinforcing, high temperature resistant are low.
Obviously, above-described embodiment is only intended to clearly illustrate example, and not to embodiment
Limit.For those of ordinary skill in the field, it can also be made on the basis of the above description
The change or variation of its multi-form.There is no need to be exhaustive to all of embodiment.And by
Among this obvious change extended out or variation are still in the protection domain of the invention.
Claims (2)
1. a kind of environment-friendly active calcium carbonate, it is characterised in that：It is obtained by the raw material of following weight parts：Carbonic acid
Calcium 90-110, Tissuemat E 3-4, glycerine 1-2, feldspar in powder 4-5, high density polyethylene (HDPE) 0.2-0.4,
Sodium Hyaluronate 2-4, anilinomethyl triethoxy 3.3-4.5, copper stearate 3-5, Tea Polyphenols 1-2, benzene
Ethene 1.5-2.5, appropriate deionized water.
2. a kind of environment-friendly active calcium carbonate according to claim 1, it is characterised in that：Preparation method include with
Lower step：
(1) calcium carbonate is added after homogenizer, adds Tissuemat E, glycerine, feldspar in powder, high density
Polyethylene, Sodium Hyaluronate, anilinomethyl triethoxy, copper stearate, Tea Polyphenols, are warming up to 70-80 DEG C
Between stir, insulation 20-30 minutes after pour out.
(2) appropriate deionized water, stirring is added to form suspension and pour out the material poured out while hot；
(3) suspension is mixed with styrene, is stirred 20 minutes, dried, be ground into fine powder.