CN106673486A - Wet-mixed mortar admixture - Google Patents
Wet-mixed mortar admixture Download PDFInfo
- Publication number
- CN106673486A CN106673486A CN201610548109.8A CN201610548109A CN106673486A CN 106673486 A CN106673486 A CN 106673486A CN 201610548109 A CN201610548109 A CN 201610548109A CN 106673486 A CN106673486 A CN 106673486A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- mortar
- remaining
- wet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wet-mixed mortar admixture. The wet-mixed mortar admixture comprises a plastic regulating agent and a coagulation regulating agent, wherein the plastic regulating agent is prepared from components as follows: 5%-15% of a water reducer, 0.5%-2% of a water retaining agent, 0.5%-1.5% of an additive, 0.1%-0.6% of a shrinkage reducing agent, 0.5%-3% of a thixotropic lubricant, 0.2%-0.4% of a cosolvent and the balance of water; the coagulation regulating agent is prepared from components as follows: 5%-15% of a retarder, 0.2%-2% of a plastic retaining agent, 1%-3% of a stabilizer and the balance of water. The wet-mixed mortar admixture comprises the plastic regulating agent and the coagulation regulating agent, mortar has good plastic retaining property and workability due to mixing of the double components, the opening time is greatly prolonged, and the compressive strength and the adhesion stress of the mortar are improved.
Description
Technical field
The present invention relates to mortar additive technical field, more particularly to a kind of wet mixing mortar additive, the present invention's is subtracting
Plasticizing component, thixotroping lubrication component, slow setting component are introduced on the basis of water preparation, are strengthened component, are reduced component and stable component,
Make mortar have good plasticity and the time delay of time, also solve on mortar hollowing, problem of Cracking after wall.
Background technology
Because country advocates " energy-saving and emission-reduction ", build a conservation-minded society, realize the strategic requirement of sustainable development, popularization and application
Premixing mortar, especially wet mixing mortar have particularly significant meaning.The key problem in technology of premixing mortar is exactly outside high performance mortar
Plus agent, and the use of traditional mortar water reducer, within a certain period of time denseness loss is too big to make mortar, and mortar is difficult to wall,
Or the phenomenons such as sagging are produced after upper wall, the construction requirement of premixing mortar can not be met.
The content of the invention
It is an object of the invention to provide a kind of wet mixing mortar additive, the present invention's introduces on the basis of water reducer
Plasticizing component, thixotroping lubrication component, slow setting component, strengthen component, reduce component and stable component, having mortar good plastic
Property and the time delay of time, also solve on mortar hollowing, problem of Cracking after wall.
In order to solve the problems, such as above-mentioned technology, the technical solution used in the present invention is：A kind of wet mixing mortar additive, it is described
Mortar additive includes adjusting modeling agent and adjustable solidification agent, wherein, it is described to adjust modeling agent to be made up of following component：Water reducer 5~15%, water conservation
Agent 0.5~2%, dose 0.5~1.5%, economization agent 0.1~0.6%, thixotropic lubricant 0.5~3%, cosolvent 0.2~
0.4%, remaining is water；The adjustable solidification agent is constituted with following component：Retarder 5~15%, plasticity-maintaining agent 0.2~2%, stabilizer 1
~3%, remaining is water.
Preferably, it is described to adjust modeling agent to be made up of following component：Polycarboxylate water-reducer 5%, starch ether 0.5%, diethanol list
Isopropanolamine 0.5%, Polyethylene Glycol 0.1%, thixotropic lubricant 0.5%, cosolvent 0.2%, remaining is water；The adjustable solidification agent by
Following component is constituted：Sodium gluconate 5%, plasticity-maintaining agent 0.2%, stabilizer 1%, remaining is water.
Preferably, the volume of the tune modeling agent is the 2%~5% of cement amount, and the volume of the adjustable solidification agent is glue material use
The 0~1% of amount.
Therefore, using the technical scheme of the embodiment of the present invention, have the advantages that：Outside the wet mixing mortar of the present invention
Plus agent, by adjusting modeling agent to constitute with adjustable solidification agent, the incorporation of double-component makes mortar have good guarantor's plasticity and workability, wherein, adjust
Diminishing component and water conservation component in modeling agent is the evaporation for reducing being reduced while the mortar ratio of mud moisture content, and thixotropic lubricant is
The lubricity of mortar is maintained, economization agent is the reduction of the shrinkage cracking of mortar；Slow setting component and plasticizing component in adjustable solidification agent
Combination be in order to adjust the completion of the open hour of mortar and mortar after setting time, and stabilizer is primarily to aqueous solution is produced
The stability of product；So as to substantially prolongs the open hour, the comprcssive strength and cohesive force of mortar is improve.
Specific embodiment
Embodiment one
A kind of wet mixing mortar additive, the mortar additive includes adjusting modeling agent and adjustable solidification agent, wherein, it is described adjust modeling agent by
Following component is constituted：Polycarboxylate water-reducer 5%, starch ether 0.5%, diethanol monoisopropanolamine 0.5%, Polyethylene Glycol 0.1%,
Thixotropic lubricant 0.5%, cosolvent 0.2%, remaining is water；The adjustable solidification agent is made up of following component：Sodium gluconate 5%,
Plasticity-maintaining agent 0.2%, stabilizer 1%, remaining is water.Modeling agent volume is adjusted to be 3%, adjustable solidification agent volume is 1%.
The preparation of product：Adjust various materials of the modeling agent with adjustable solidification agent by more than to be dissolved in cold water, stir, it is actually used
When the present invention tune modeling agent and adjustable solidification agent be all aqueous products, using two sets of metering systems, separately mix.
Embodiment two
Modeling agent is adjusted to be made up of following component：Polycarboxylate water-reducer 10%, starch ether 1%, diethanol monoisopropanolamine 1%,
Polyethylene Glycol 0.2%, thixotropic lubricant 1.5%, cosolvent 0.3%, remaining is water；Adjustable solidification agent is made up of following components：Fructus Vitis viniferae
Sodium saccharate 10%, plasticity-maintaining agent 0.5%, stabilizer 1%, remaining is water.Adjust modeling agent volume to be the 2% of cement amount when using, adjust
Solidifying agent volume is 0.6%.
Preparation method is same as Example 1.
Embodiment three
Modeling agent is adjusted to be made up of following component：Polycarboxylate water-reducer 15%, starch ether 2%, diethanol monoisopropanolamine 1.
5%, Polyethylene Glycol 0.4%, thixotropic lubricant 2%, cosolvent 0.4%, remaining is water；Adjustable solidification agent is made up of following component：Portugal
Grape sodium saccharate 15%, plasticity-maintaining agent 1%, stabilizer 2%, remaining is water.When using, modeling agent volume is adjusted to be 1.5%, adjustable solidification agent volume
For 0.3%.
Preparation method is same as Example 1.
The technical scheme for being provided the embodiment of the present invention above is described in detail, specific case used herein
The principle and embodiment of the embodiment of the present invention are set forth, the explanation of above example is only applicable to help and understands this
The principle of inventive embodiments；Simultaneously for one of ordinary skill in the art, according to the embodiment of the present invention, in specific embodiment party
Will change in formula and range of application, in sum, this specification content should not be construed as limiting the invention.
Claims (3)
1. a kind of wet mixing mortar additive, it is characterised in that：The mortar additive includes adjusting modeling agent and adjustable solidification agent, wherein, institute
State tune modeling agent to be made up of following component：Water reducer 5~15%, water-retaining agent 0.5~2%, dose 0.5~1.5%, economization agent
0.1~0.6%, thixotropic lubricant 0.5~3%, cosolvent 0.2~0.4%, remaining is water；The adjustable solidification agent is with following component
Constitute：Retarder 5~15%, plasticity-maintaining agent 0.2~2%, stabilizer 1~3%, remaining is water.
2. a kind of wet mixing mortar additive according to claim 1, it is characterised in that：It is described to adjust modeling agent by following component structure
Into：Polycarboxylate water-reducer 5%, starch ether 0.5%, diethanol monoisopropanolamine 0.5%, Polyethylene Glycol 0.1%, thixotropic lubricant
0.5%, cosolvent 0.2%, remaining is water；The adjustable solidification agent is made up of following component：Sodium gluconate 5%, plasticity-maintaining agent
0.2%, stabilizer 1%, remaining is water.
3. a kind of wet mixing mortar additive according to claim 1 and 2, it is characterised in that：It is described adjust modeling agent volume be
The 2%~5% of cement amount, the volume of the adjustable solidification agent is the 0~1% of cement amount.