CN106638151B - Grey cigarette paper and preparation method thereof is wrapped in a kind of improvement - Google Patents
Grey cigarette paper and preparation method thereof is wrapped in a kind of improvement Download PDFInfo
- Publication number
- CN106638151B CN106638151B CN201610957799.2A CN201610957799A CN106638151B CN 106638151 B CN106638151 B CN 106638151B CN 201610957799 A CN201610957799 A CN 201610957799A CN 106638151 B CN106638151 B CN 106638151B
- Authority
- CN
- China
- Prior art keywords
- cigarette
- grey
- cigarette paper
- paper
- improvement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the improvement packet ash cigarette paper fields in tobacco business, and in particular to grey cigarette paper and preparation method thereof is wrapped in a kind of improvement.A kind of grey cigarette paper of improvement packet, is mainly prepared by slurry, filler and combustion adjuvant；In terms of the quality of product volume cigarette paper, the mass percent of the filler is 40%~65%；Quantification of 35 ~ 50g/m of the cigarette paper2；The mass percent of the combustion adjuvant is 0.5% ~ 10%, and wherein the ratio between sylvite/sodium salt amount of substance is 1:0.2~50.The burning velocity Proper Match of grey cigarette paper and pipe tobacco is wrapped in improvement of the invention, guarantees that cigarette packet ash is good, and greyish white to hold grey ability strong.Grey whiteness is high after grey cigarette paper burning is wrapped in the improvement, and breach number is few, does not fall ash and gray columns is straight and upright.It is applicable to the cigarette of the plurality of specifications such as all tobacco leaf formulations and ramuscule cigarette, middle ramuscule cigarette and conventional cigarette.
Description
Technical field
The invention belongs to the cigarette paper fields in tobacco business, and in particular to grey cigarette paper and its preparation side are wrapped in a kind of improvement
Method.
Background technique
With stepping up for people's living standard and cigarette smoking class, cigarette ash wrappage is increasingly by people's
Pay attention to.The packet ash performance of cigarette is good, then the column of smoke is beautiful；If it is poor to wrap grey performance, ash piece cannot be wrapped in cigarette well when suction
On silk, cigarette ash is fallen seriously.
Recent domestic is more to the research of cigarette ash wrappage, and the functional cigarette paper for wrapping grey performance can be improved by concentrating on exploitation
Aspect.Cigarette paper and pipe tobacco directly participate in the burning of cigarette as cigarette main body, rise to the grey performance of the packet of cigarette the most key
It influences.
There is presently no a cigarette paper to be applicable to all tobacco leaf formulations, at the same solve ramuscule cigarette, middle ramuscule cigarette and often
The packet ash poor appearance for advising cigarette, the ash that floats fall the problems such as grey, gray columns breach number is more.Therefore, one kind is needed to can be applied in the market
Existing cigarette producing process, and it is obviously improved cigarette ash wrappage appearance, while there is the improvement packet ash cigarette paper of broad applicability.
Summary of the invention
The technical problem to be solved in the present invention is that overcome the deficiencies of existing technologies, grey whiteness is high after providing a kind of burning,
Breach number is few, does not fall ash, the straight and upright improvement packet ash cigarette paper of gray columns.
The invention is realized by the following technical scheme:
A kind of grey cigarette paper of improvement packet, is mainly prepared by slurry, filler and combustion adjuvant；With the quality of product volume cigarette paper
Meter, the mass percent of the filler are 40%~65%；Quantification of 35~50g/m of the cigarette paper2；The combustion adjuvant
Mass percent is 0.5%~10%, and wherein the ratio between sylvite/sodium salt amount of substance is 1:0.2~50.
Inventor has been surprisingly found that cigarette paper under specific quantitative and filer content, cooperate combustion adjuvant controlling and
The matched Reasonable Combustion speed of pipe tobacco, it is ensured that cigarette packet ash is good, greyish white, and it is strong to hold grey ability.
Preferably, heretofore described to improve the mistake that conventional kind and dosage are also used in the preparation process for wrapping grey cigarette paper
Journey auxiliary agent, such as retention and drainage aid agent, flocculant, defoaming agent, wet strength agent etc..
Preferably, the mass percent of the filler is 46%~57%；Quantification of 37~47g/m of the cigarette paper2。
The filler is the one or more of calcium carbonate, magnesium hydroxide.
It is further preferred that the mass percent of the filler is 49%~54%；Quantification of the 41 of the cigarette paper~
44g/m2。
Preferably, the particle size range of the filler is 0.1 μm~4.5 μm.It is further preferred that the partial size model of the filler
Enclose is 0.8 μm~2.5 μm.Packing material size influences cigarette ash wrappage by the distributing homogeneity influenced in page.
Preferably, the mass percent of the combustion adjuvant is 4%~8%, and wherein the ratio between sylvite/sodium salt amount of substance is
1:1~10.
Preferably, the mass percent of the combustion adjuvant is 6%~7%, and wherein the ratio between sylvite/sodium salt amount of substance is
1:2~5.
Preferably, the combustion adjuvant is mixed in the ratio that sylvite/sodium salt mass ratio is 1:0.2-50, is then mixed with water
It is even, it is coated on body paper surface, cigarette paper is dried, controlling mass percent of the combustion adjuvant in cigarette paper is 0.5%-10%.
Preferably, the combustion adjuvant is potassium citrate, sodium citrate, potassium malate, natrium malicum, potassium succinate, fourth
One or more of diacid sodium, potassium lactate, sodium lactate, potassium phosphate, sodium phosphate.
Preferably, the slurry is the mixing of one or more of soft wood pulp, hard wood pulp and jute pulp.By soft wood pulp, firmly
Wood pulp, jute pulp are spare after mashing is handled respectively, and slurry can be one such or several mixing, mix in proportion with water
It is even.
Soft wood pulp in the slurry: hard wood pulp: jute pulp=(10~40): (10~40): (20~80), the slurry are beaten
The degree of beating is 40~70 ° of SR.
Preferably, soft wood pulp in the slurry: hard wood pulp: jute pulp=(20~30): (20~30): (40~60), it is described
The beating degree of slurry is 50~60 ° of SR.
Preferably, the rib-loop mode for improving the grey cigarette paper of packet is no rib-loop, horizontal rib-loop, erects rib-loop, oblique rib-loop.
Compared with prior art, the invention has the following advantages:
The burning velocity Proper Match of grey cigarette paper and pipe tobacco is wrapped in improvement of the invention, guarantees that cigarette packet ash is good, greyish white to hold
Grey ability is strong.Grey whiteness is high after grey cigarette paper burning is wrapped in the improvement, and breach number is few, does not fall ash and gray columns is straight and upright.It is applicable to
The cigarette of the plurality of specifications such as all tobacco leaf formulations and ramuscule cigarette, middle ramuscule cigarette and conventional cigarette.
Detailed description of the invention
Fig. 1 is to improve the comparison diagram for wrapping grey cigarette paper burning front and back prepared by embodiment 1；
Fig. 2 is to improve the comparison diagram for wrapping grey cigarette paper burning front and back prepared by embodiment 2；
Fig. 3 is the figure improved after wrapping grey cigarette paper burning prepared by comparative example 1.
Specific embodiment
The present invention is further illustrated combined with specific embodiments below.Unless stated otherwise, it is used in the embodiment of the present invention
Raw material, device and method are the raw material of this field regular market purchase, conventional use of device and method.
Embodiment 1
It is a kind of to improve the preparation method for wrapping grey cigarette paper, paper pulp is taken by formula, it is spare after mashing processing respectively, partial size is added
The filler etc. that range is 0.1 μm~4.5 μm, sizes mixing, manufactures paper with pulp；It takes combustion adjuvant and water after mixing, is coated on body paper surface, it will
Cigarette paper drying, batches, obtains product volume cigarette paper.
Table 1 improves the grey cigarette paper of packet by rib-loop and forms
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 10:10:80 | 50 |
| Filler (CaCO3:Mg(OH)2) | 1:1 | 44 |
| Potassium citrate: sodium citrate | 1:50 | 5 |
| Process assistant | - | 1 |
Improve the quantification of 45g/m for wrapping grey cigarette paper after preparation2, improvement packet ash cigarette paper prepared by embodiment 1, at certain
Cigarette on one trade mark cigarette, the appearance after cigarette burning.As shown in Figure 1, appearance is good after the cigarette burning of the present embodiment, it is greyish white,
It is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 2
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 2.
Table 2 improves without rib-loop wraps grey cigarette paper composition
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 10:40:50 | 55 |
| Filler (CaCO3) | - | 40 |
| Potassium malate: natrium malicum | 1:0.2 | 4 |
| Process assistant | - | 1 |
The quantification of 50g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 2,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning.Greyish white as shown in Fig. 2, cigarette appearance is good, it is strong to hold grey power, does not fall
Ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 3
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 3.
The horizontal rib-loop of table 3, which improves, wraps grey cigarette paper composition
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 40:10:50 | 43 |
| Filler (CaCO3) | - | 46 |
| Potassium succinate: sodium succinate | 1:1 | 10 |
| Process assistant | - | 1 |
The quantification of 37g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 3,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning is good, greyish white, and it is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 4
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 4.
Table 4, which erects rib-loop, improves the grey cigarette paper composition of packet
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 40:40:20 | 23 |
| Filler (CaCO3:Mg(OH)2) | 2:1 | 65 |
| Potassium malate, natrium malicum | 1:30 | 0.5 |
| Process assistant | - | 1.5 |
The quantification of 47g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 4,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning is good, greyish white, and it is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 5
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 5.
The oblique rib-loop of table 5, which improves, wraps grey cigarette paper composition
The quantification of 47g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 5,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning is good, greyish white, and it is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 6
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 6.
Table 6 improves without rib-loop wraps grey cigarette paper composition
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 20:20:60 | 39 |
| Filler (CaCO3:Mg(OH)2) | 1:3 | 54 |
| Potassium phosphate: sodium phosphate | 1:5 | 6 |
| Process assistant | - | 1 |
The quantification of 44g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 6,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning is good, greyish white, and it is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Embodiment 7
The present embodiment and the preparation method of embodiment 1 are essentially identical, and difference is as shown in table 7.
The horizontal rib-loop of table 7, which improves, wraps grey cigarette paper composition
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 25:25:50 | 43 |
| Filler (Mg (OH)2) | - | 49 |
| Potassium citrate: sodium citrate | 1:2 | 7 |
| Process assistant | - | 1 |
The quantification of 41g/m of grey cigarette paper is wrapped in prepared improvement2, improvement packet ash cigarette paper prepared by embodiment 7,
Cigarette on a certain trade mark cigarette, the appearance after cigarette burning is good, greyish white, and it is strong to hold grey power, does not fall ash.
The grey cigarette paper of measurement improvement packet holds grey power, and it is as shown in table 11 to hold grey power result.
Comparative example 1
The preparation method of this comparative example and embodiment 1 is essentially identical, and difference is as shown in table 8.
8 comparative example of table improves the composition for wrapping grey cigarette paper
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 25:25:50 | 65 |
| Filler (CaCO3:Mg(OH)2) | - | 35 |
| Potassium citrate: sodium citrate | 1:2 | 3 |
| Process assistant | - | 1 |
The quantification of 30g/m of grey cigarette paper is wrapped in the improvement of preparation2, by the improvement packet ash cigarette paper of preparation, in a certain trade mark
Cigarette on cigarette.As shown in figure 3, cigarette burning posterior gray column of spinal cord is bent, gray columns breach number is more, and the gray columns whiteness after burning is low.
Measurement cigarette paper holds grey power, and it is as shown in table 11 to hold grey power result.
Comparative example 2
The preparation method of this comparative example and embodiment 2 is essentially identical, and difference is as shown in table 10.
9 comparative example of table improves the composition for wrapping grey cigarette paper
| It is formed at paper | Each component ratio | At mass percent % in paper |
| Soft wood pulp: hard wood pulp: jute pulp | 5:5:90 | 55 |
| Filler (CaCO3) | - | 40 |
| Potassium malate: natrium malicum | 1:0.2 | 4 |
| Process assistant | - | 1 |
The quantification of 50g/m of grey cigarette paper is wrapped in the improvement of preparation2, by the improvement packet ash cigarette paper of preparation, in a certain trade mark
Cigarette on cigarette.The bending of cigarette burning posterior gray column of spinal cord, gray columns breach number is more, and the gray columns whiteness after burning is low.
Measurement cigarette paper holds grey power, and it is as shown in table 11 to hold grey power result.
Comparative example 3
The preparation method of this comparative example and embodiment 2 is essentially identical, and difference is as shown in table 11.
10 comparative example of table improves the composition for wrapping grey cigarette paper
The quantification of 50g/m of grey cigarette paper is wrapped in the improvement of preparation2, by the improvement packet ash cigarette paper of preparation, in a certain trade mark
Cigarette on cigarette.The bending of cigarette burning posterior gray column of spinal cord, gray columns breach number is more, and the gray columns whiteness after burning is low.
Measurement cigarette paper holds grey power, and it is as shown in table 11 to hold grey power result.
Comparative example 4
The preparation method of this comparative example and embodiment 2 is essentially identical, the packing material size of this comparative example of difference be greater than
4.5mm。
By the improvement packet ash cigarette paper of preparation, the cigarette on a certain trade mark cigarette.The bending of cigarette burning posterior gray column of spinal cord, gray columns are split
Mouth number is more, and the gray columns whiteness after burning is low.
Measurement cigarette paper holds grey power, and it is as shown in table 11 to hold grey power result.
Hold grey power test result
Cigarette paper hold the measuring method of grey power the following steps are included:
(1) appearance neatly normal cigarette is selected, open defect such as breakage is rejected, deforms, the cigarette of dirt；
(2) cigarette lie against on graduated scale platform and with ruler horizontal alignment, on the cylinder of cigarette mouth building,
5mm draws upper carbon line label with pencil from fire end；
(3) cigarette mouth building is horizontally placed at upward in cigarette ash wrappage detector and carries out static combustion, cigarette need to be in big temperature
Carry out static combustion under 20~24 DEG C of degree, the test atmosphere of relative humidity 55~65%, when experiment should survey atmospheric pressure
Examination, if atmospheric pressure should be illustrated except 86kPa~106kPa range in test report；
(4) for static combustion until cigarette gray columns is broken off, cigarette length L2 has been fired in measurement indicates that cigarette holds grey power.
The calculation method for having fired cigarette length L2 in the step (4) are as follows: measurement carbon line marks it when gray columns is broken off
Remaining cigarette length L1 afterwards subtracts residue length L1 with cigarette raw footage L, can obtain and fire cigarette length L2, and L2 is bigger, indicates
It is stronger that cigarette holds grey power.
In step (1), the cigarette of selection need to 21-23 DEG C of atmospheric temperature, relative humidity 57-63% adjusting atmosphere in
Balance no less than 48 hours；Or the quality of sample 21-23 DEG C of atmospheric temperature, relative humidity 57-63% adjusting atmosphere in 3
Variation is not more than 0.2% in hour.The horizontal positioned balance of cigarette needs four sides need to be in the state contacted with air.
In step (3), using single channel smoking machine lighting cigarette, cigarette is adjusted when the vertical quiet combustion of cigarette is to 5mm
To horizontal direction, the gas hood of cigarette ash wrappage detector is closed in cigarette mouth building horizontal quiet combustion upward.
In step (3), the blower for opening laboratory is needed before test, by the miscellaneous gas in the draught cupboard of cigarette ash wrappage detector
It empties, exhaust no less than 30 minutes.
Experiment takes its arithmetic average as experimental result according to the cigarette sum of test cigarette sample every time.Above-mentioned implementation
Example holds grey power with the grey cigarette paper of comparative example improvement packet, and it is as shown in table 11 to hold grey power result.
Table 11 holds grey power test result
The above only lists the way of realization of present inventive concept, and protection scope of the present invention is not construed as only
Be limited to concrete form described in embodiment, all within the spirits and principles of the present invention, made any modification, equivalent replacement,
Improve etc., it should all be included in the protection scope of the present invention.
Claims (3)
1. grey cigarette paper is wrapped in a kind of improvement, which is characterized in that be mainly prepared by slurry, filler and combustion adjuvant；With product volume
The quality meter of cigarette paper,
The slurry is the mixing of soft wood pulp, hard wood pulp and jute pulp；Soft wood pulp in the slurry: hard wood pulp: jute pulp 40:40:
20, the mass percent of the combustion adjuvant is 0.5%, and the combustion adjuvant is potassium malate and natrium malicum, wherein potassium malate and
The ratio between amount of substance of natrium malicum is 1:30, and the mass percent of the filler is 65%, quantification of 47 g/ of the roll paper
m2；
Or the slurry is the mixing of soft wood pulp, hard wood pulp and jute pulp；Soft wood pulp in the slurry: hard wood pulp: jute pulp 25:
25:50, the mass percent of the combustion adjuvant are 8%, and the combustion adjuvant is potassium lactate and sodium lactate, wherein potassium lactate and lactic acid
The ratio between amount of substance of sodium is 1:6, and the mass percent of the filler is 57%, quantification of 47 g/m of the roll paper2。
2. improving wrap grey cigarette paper according to claim 1, which is characterized in that the particle size range of the filler is 0.1 μm~
4.5 µm。
Grey cigarette paper is wrapped 3. improving according to claim 1, which is characterized in that described to improve the rib-loop mode for wrapping grey cigarette paper
For horizontal rib-loop, perpendicular rib-loop, oblique rib-loop.