CN106638150A - Glassine coating material - Google Patents

Glassine coating material Download PDF

Info

Publication number
CN106638150A
CN106638150A CN201610955801.2A CN201610955801A CN106638150A CN 106638150 A CN106638150 A CN 106638150A CN 201610955801 A CN201610955801 A CN 201610955801A CN 106638150 A CN106638150 A CN 106638150A
Authority
CN
China
Prior art keywords
weight
coating
latex
relative
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610955801.2A
Other languages
Chinese (zh)
Other versions
CN106638150B (en
Inventor
朱蕾
周明华
李秀梅
韩继友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINFENG SPECIAL PAPER CO Ltd
Original Assignee
MINFENG SPECIAL PAPER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MINFENG SPECIAL PAPER CO Ltd filed Critical MINFENG SPECIAL PAPER CO Ltd
Priority to CN201610955801.2A priority Critical patent/CN106638150B/en
Publication of CN106638150A publication Critical patent/CN106638150A/en
Application granted granted Critical
Publication of CN106638150B publication Critical patent/CN106638150B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A glassine coating material is prepared from, by total coating formulation weight, 3-5% of at least one or two pigments different in molecular weight, 1-2% of at least one type of acrylic resin, 2-4% of at least one type of polyvinyl alcohol, 1-3% of at least one type of latex, 0.1-0.3% of at least one functional additive, 0.01-0.03% of at least one viscosity modifier and the balance water. After addition of the viscosity modifier, coating viscosity is controlled within a range of 500-600mPa.S. Glassine which adopts the glassine coating material has advantages of freeness of repellence to silicon oil coating, uniformity in silicon oil coating, low consumption and the like.

Description

A kind of coating dispensing of Ge Laxin paper
Technical field
The present invention relates to a kind of coating dispensing of Ge Laxin paper, belongs to surface-coating technology field.
Background technology
Lattice Racine paper is extensive in industrial applications such as product packaging, labels.Lattice Racine paper has good internal intensity and thoroughly Lightness characteristic, with the function such as high temperature resistant, protection against the tide, grease proofing, is generally used for the product packaging of the industries such as food, medicine, at a high speed certainly The special adhesive tape of dynamic labeling (particularly suitable high speed label stickup), two-sided tape base material trade mark, laser anti-counterfeit mark is release with other Using etc..The general typicalness purposes of lattice Racine paper is the base stock of sticky label paper, used as one of label substrate, intermediate demand Through multiple tracks processing, finally label paper is processed into together with other auxiliary materials.Surface coating silicone oil is Ge Laxin Zhi Hou roads processing the One step, the grease resistance requirement to silicone oil of printing enterprise's plaid matching Racine paper is higher, it is desirable to which surface uniformly coats very thin one layer Silicone oil, because whether uniformly coating silicone oil will have influence on lower road coating process and last peeling force, but while and expects not disappear Consume excessive silicone oil to reduce processing cost.With rear processing and the progress of printing technology, printing enterprise more and more preference surface The good Ge Laxin paper of grease resistance.The method for strengthening paper oil-resistant characteristic is more, and e.g., surface imposes extraordinary applying glue, surface filming Well to reduce fiber porosity, reduce fat migration and reduce the absorption to grease.An also class is to use film method, in paper Open surface and form closing plastic sheeting, prevent paper from contacting with grease, so as to reach grease proofing effect, but be the use of difficult degradation material Material, can cause environmental problem, not be the development trend of following greaseproof.
At present, with international most advanced level also there is gap in domestic commercially available Ge Laxin paper, and suffer from the drawback that:
A, painting silicone oil operation, silicone oil consumption is more, causes processing cost to remain high;
B, silicone oil coating are uneven, cause release layer to be combined with label layer uneven, cause peeling force unstable, affect certainly Dynamic labeling speed.
The content of the invention
It is an object of the invention to overcome the shortcomings of that prior art is present, and providing one kind can improve lattice draw surface oil resistant Property, there is the Ge Laxin paper through top sizing and do not repel silicone oil coating, and silicone oil coat uniform consumption it is few, without oozing in paper Thoroughly, there are good surface grease resistance and transparency, it is ensured that do not affect the operations such as follow-up gluing, stripping, and other physical indexs to meet The coating dispensing of the Ge Laxin paper of lattice Racine paper standard.
The purpose of the present invention is achieved through the following technical solutions:A kind of coating dispensing of Ge Laxin paper, its feature It is:It includes pigment, at least one acrylic resin, at least one polyethylene of at least one or two different molecular weight Alcohol, at least one latex, at least one functional additive and optional at least one viscosity modifier, remaining is water, wherein:
Relative to coating formulation gross weight, the pigment content is by weight between 3-5%;
Relative to coating formulation gross weight, the acrylic resin content is by weight between 1-2%;
Relative to coating formulation gross weight, the polyvinyl alcohol content is by weight between 2-4%;
Relative to coating formulation gross weight, the latex content is by weight between 1-3%;
Relative to coating formulation gross weight, the functional additive content is by weight between 0.1-0.3%;
Relative to coating formulation gross weight, the viscosity modifier content is by weight between 0.01-0.03%;
The viscosity of coating is controlled in 500~600mPa.S after above-mentioned viscosity modifier addition.
It is further:The pigment of at least one or two different molecular weight, wherein at least one pigment is china clay, Can be a kind of, pigment composition of two kinds of any proportioning therein;
Described acrylic resin be aqua type thermosetting resin, molecular weight > 10000;Described latex is artificial synthesized Latex;Described functional additive has been the modified cellulose of thickening power;
Its degree of polymerization of described polyvinyl alcohol is 1000~3000, and its alcoholysis degree is not less than 50%.
Moreover:Described synthetic latex is one kind of styrene-acrylic latex or styrene-butadiene latex;Described function addition Agent has been the carboxymethylcellulose calcium of thickening power;Described polyvinyl alcohol is PVA1799;Described viscosity modifier is 5% dense The sodium hydrate aqueous solution of degree.
The purpose of present invention addition pigment is to increase coating layer thickness, and formula has certain tack to silicone oil, will not be complete Repel silicone oil.Increase surface smoothness simultaneously, improve glossiness.
The purpose of control viscosity is being smoothed out with coating process is ensured, applying glue is uniform.
The present invention addition polyvinyl alcohol purpose make formula have more superior resistance to water and film forming, not moisture-sensitive and Keep transparency.
The purpose of present invention addition latex is that the formula formed with other components has more excellent grease resistance, it is to avoid silicon Oil permeates into paper.
The invention has the beneficial effects as follows:Through the Ge Laxin paper of this dispensing surface coating, coat with silicone oil is not repelled, together When silicone oil coating consumption is few, coated side uniform, without the good surface grease resistance permeated in paper.Key physical index:Oil Cobb values≤0.15g/ ㎡, transparency >=40%.
Specific embodiment
Below in conjunction with embodiment, the present invention is described further.A kind of coating of Ge Laxin paper of the present invention is matched somebody with somebody Material, it include the pigment of at least one or two different molecular weight, at least one polyvinyl alcohol, at least one acrylic resin, At least one latex and optional at least one functional additive, remaining is water, wherein:
Relative to coating formulation gross weight, the polyvinyl alcohol content is by weight between 3-5%;
Relative to coating formulation gross weight, the enhancing agent content is by weight between 0.3-1%;
Relative to coating formulation gross weight, the tackifier levels are by weight between 0.24-1%;
Relative to coating formulation gross weight, the functional additive content is by weight between 0.1-0.5%;
Relative to coating formulation gross weight, the viscosity modifier content is by weight between 0.01-0.03%;
The viscosity of coating is controlled in 500~600mPa.S after above-mentioned viscosity modifier addition.
It is further:Acrylic resin of the present invention be aqua type thermosetting resin, molecular weight > 10000;Institute The latex stated is a kind of synthetic latex;Described functional additive has been the modified cellulose of thickening power.
Moreover:The hybrid pigment of pigment at least one or two different molecular weight of the present invention, wherein At least one pigment is china clay, and hybrid pigment is preferably chosen from china clay content and is not less than 80%;Described polyvinyl alcohol is preferably From PVA1799;Described latex be preferably chosen from styrene-acrylic latex or styrene-butadiene latex in one kind;Described functional additive is excellent Selection of land is selected from carboxymethylcellulose calcium;Described viscosity modifier is preferably chosen from the sodium hydrate aqueous solution of 5% concentration.
The coating dispensing implementation suggestion of the present invention takes paper machine, and online coating is completed, and can specifically take scraper for coating, meter The coating methods such as length bar.
Below example illustrates the present invention and does not limit the scope of the invention.
Following oily Cobb values are tested according to Cobb unger methods, and transparency, glossiness, smoothness are entered according to relevant criterion Row test.
Embodiment one
Acrylic resin, polyvinyl alcohol, functional additive are sufficiently mixed as sizing material 1 first, by pigment 1,2 and latex It is sufficiently mixed as sizing material 2, is then sufficiently mixed sizing material 1 and sizing material 1 uniformly, viscosity with sodium hydroxide solution adjustment extremely finally 522mPa.S, obtains required sizing agent.
It is as follows according to the paper test effect that embodiment one is obtained:
Project As a result
Oily Cobb values (g/m2) 0.12
Transparency (%) 45
Glossiness (%, 75 degree) 52
Smoothness (positive/negative) 1225/437
Embodiment two
Acrylic resin, polyvinyl alcohol, functional additive are sufficiently mixed as sizing material 1 first, by pigment 1,2 and latex It is sufficiently mixed as sizing material 2, is then sufficiently mixed sizing material 1 and sizing material 1 uniformly, viscosity with sodium hydroxide solution adjustment extremely finally 550mPa.S, obtains required sizing agent.
It is as follows according to the paper test effect that embodiment two is obtained:
Project As a result
Oily Cobb values (g/m2) 0.12
Transparency (%) 45
Glossiness (%, 75 degree) 50
Smoothness (positive/negative) 1200/420
Embodiment three
Acrylic resin, polyvinyl alcohol, functional additive are sufficiently mixed as sizing material 1 first, china clay is filled with latex Divide mixing as sizing material 2, be then sufficiently mixed sizing material 1 and sizing material 1 uniformly, viscosity with sodium hydroxide solution adjustment extremely finally 535mPa.S, obtains required sizing agent.
It is as follows according to the paper test effect that embodiment three is obtained:
Project As a result
Oily Cobb values (g/m2) 0.14
Transparency (%) 45
Glossiness (%, 75 degree) 55
Smoothness (positive/negative) 1350/440

Claims (3)

1. a kind of coating dispensing of Ge Laxin paper, it is characterised in that:It include at least one or two different molecular weight pigment, At least one acrylic resin, at least one polyvinyl alcohol, at least one latex, at least one functional additive and it is optional extremely A kind of few viscosity modifier, remaining is water, wherein:
Relative to coating formulation gross weight, the pigment content is by weight between 3-5%;
Relative to coating formulation gross weight, the acrylic resin content is by weight between 1-2%;
Relative to coating formulation gross weight, the polyvinyl alcohol content is by weight between 2-4%;
Relative to coating formulation gross weight, the latex content is by weight between 1-3%;
Relative to coating formulation gross weight, the functional additive content is by weight between 0.1-0.3%;
Relative to coating formulation gross weight, the viscosity modifier content is by weight between 0.01-0.03%;
The viscosity of coating is controlled in 500 ~ 600mPa.S after above-mentioned viscosity modifier addition.
2. the coating dispensing of lattice Racine according to claim 1 paper, it is characterised in that:It is described at least one or two different The pigment of molecular weight, wherein at least one pigment is china clay, can be a kind of pigment mixing of, two kinds of any proportioning therein Thing;
Described acrylic resin be aqua type thermosetting resin, molecular weight > 10000;Described latex is artificial rubber polymer Breast;Described functional additive has been the modified cellulose of thickening power;
Its degree of polymerization of described polyvinyl alcohol is 1000 ~ 3000, and its alcoholysis degree is not less than 50%.
3. the coating dispensing of lattice Racine according to claim 1 and 2 paper, it is characterised in that:Described synthetic latex is benzene One kind of third latex or styrene-butadiene latex;Described functional additive has been the carboxymethylcellulose calcium of thickening power;Described poly- second Enol is PVA1799;Described viscosity modifier is the sodium hydrate aqueous solution of 5% concentration.
CN201610955801.2A 2016-10-27 2016-10-27 A kind of coating dispensing of Ge Laxin paper Active CN106638150B (en)