CN106634595B - A kind of online curing agent of self-purified environment-friendly type communication equipment and preparation method thereof - Google Patents
A kind of online curing agent of self-purified environment-friendly type communication equipment and preparation method thereof Download PDFInfo
- Publication number
- CN106634595B CN106634595B CN201610946648.7A CN201610946648A CN106634595B CN 106634595 B CN106634595 B CN 106634595B CN 201610946648 A CN201610946648 A CN 201610946648A CN 106634595 B CN106634595 B CN 106634595B
- Authority
- CN
- China
- Prior art keywords
- curing agent
- self
- communication equipment
- type communication
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
This patent discloses a kind of online curing agent of self-purified environment-friendly type communication equipment and preparation method thereof, wherein, the raw material that curing agent includes following weight percent is prepared：0.05 5% aerosil, 0.01 2% nano-titanium dioxide, 15 50% waxes, 45 80% solvent type organic washing agent.The present invention has surface contaminant removal effect good the online maintenance of communication equipment, and equipment surface has self-purification function after maintenance, has anti-pollution effect, compatibility is strong, does not corrode, safe to use, environmentally friendly, the advantages that being harmful to human health.
Description
Technical field
The present invention relates to a kind of curing agent more particularly to a kind of online curing agent of self-purified environment-friendly type communication equipment and its preparations
Method.
Background technology
Communication equipment, including exchange system, mobile base station etc., in its During Process of Long-term Operation, due to its various circuit from
The suction-operated of the generations such as the electromagnetic field, the electrostatic field that are so formed, accumulate over a long period deposited in equipment a large amount of dust, greasy dirt,
Moisture, salinity, metal dirt and other charged particles.These " pollutants " not only influence the performances such as the heat dissipation of equipment, but also
Conductive ion in " pollutant " easily forms the microcircuit of conductivity type, causes to equipment " slowly corrosion ", different degrees of causes
The loose contacts of sophisticated electronics, reactance reduction, electric leakage, short circuit, error code, bad plate etc. cause circuit energy loss, transmission letter
Number weaken, transmission rate and quality it is unstable the problems such as.Therefore, communication equipment is carried out comprehensively, depth keep a public place clean maintenance, have
Important meaning.
Be presently used for communication equipment keep a public place clean maintenance product more for electrified cleaning agent, only cleaning function lacks comprehensively
The maintenance of depth.Although these cleaning agent cleaning performances are good, insulation values are high, but cleaning is charged, but equipment does not have certainly after cleaning
Net work energy, also without creepage protection function.The apparatus insulated protective agent of some electric apparatus has creepage protection function, but does not have
Standby cleaning and self-purification function.
Invention content
The present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment and preparation method thereof, to overcome the prior art
The defects of.
To achieve the above object, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, including following heavy
The raw material of amount percentage is prepared：0.05-5% aerosils, 0.01-2% nano-titanium dioxides, 15-50% waxes,
45-80% solvent type organic washing agent.
Further, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, can also have such spy
Sign：Wherein, wax be microwax, paraffin, polyethylene wax, polypropylene wax, in petroleum jelly any one or it is two or more.
Further, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, can also have such spy
Sign：Wherein, wax is microwax.
Further, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, can also have such spy
Sign：Wherein, cleaning agent be a fluorine dichloroethanes, trifluorobichloroethane, in five fluorine dichloroethanes any one or it is two or more.
Further, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, can also have such spy
Sign：Wherein, cleaning agent is five fluorine dichloroethanes (HCFC-225).
Further, the present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment, can also have such spy
Sign：It is prepared by the raw material of following weight percent：1% aerosil, 0.05% nano-titanium dioxide, 35% crystallite
Wax, 63.95% 5 fluorine dichloroethanes.
The present invention also provides a kind of preparation methods of the online curing agent of self-purified environment-friendly type communication equipment, organic clear in solvent type
Wax is added in lotion, stirring dissolves wax, then adds in aerosil and nano-titanium dioxide, stirring to obtain curing agent.
Further, the present invention provides a kind of preparation method of the online curing agent of self-purified environment-friendly type communication equipment, can also have
There is such feature：The specific steps are：Step 1: adding in wax in solvent type organic washing agent, 30-60min is stirred, makes wax molten
Solution.In this step, speed of agitator is arbitrarily set, and dissolves wax.
Step 2: adding in aerosil, using rotating speed as 100-300 revs/min, 60-90min is stirred.Preferably, with turn
Speed is 200 revs/min, stirs 60min.
Step 3: adding in nano-titanium dioxide, using rotating speed as 100-300 revs/min, 60-90min is stirred.Preferably, with turn
Speed is 200 revs/min, stirs 60min.
Step 4: using rotating speed as 500-700 revs/min, 30-60min is emulsified.Preferably, using rotating speed as 600 revs/min, stirring
30min。
Further, the present invention provides a kind of preparation method of the online curing agent of self-purified environment-friendly type communication equipment, can also have
There is such feature：Wherein, step 2 and step 3 can be with exchange sequences.
The advantageous effect of this patent is：The present invention provides a kind of online curing agent of self-purified environment-friendly type communication equipment and its system
Preparation Method, the aerosil included in curing agent are spherical shape, and the aerosil after dispersion is arranged in equipment surface
" small small hill " shape is formed, air is filled in the recess of " small small hill ", that is, forms one layer of very thin nanometer air layer, dust
Wait pollutants be difficult intrusion, make equipment after maintenance, surface formed film have self-purification function, can prevent pernicious gas,
The erosion of the pollutants such as dust.Meanwhile also make the film that there is insulation protection, even if the accidents such as water logging occur, can also protect
Demonstrate,prove equipment normal operation 30 minutes.
In addition, the Photosynthetic Energy that the titanium dioxide included in curing agent generates, has powerful oxidability, can make mould
Pollutants is waited to resolve into carbon dioxide and water, so as to make equipment after maintenance, the film that surface is formed has sterilizing function.
It is green environment friendly curing agent, and to human body in addition, without ozone-layer depleting substance (ODS) in curing agent
Health is harmless.
Description of the drawings
Fig. 1 is sprinkling curing agent rear surface microgram.
Specific embodiment
Embodiment one
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 1% |
| Nano-titanium dioxide | 0.05% |
| Microwax | 35% |
| Five fluorine dichloroethanes (HCFC-225) | 63.95%. |
Wherein, microwax is the dispersible carrier of aerosil and nano-titanium dioxide, and one layer is formed in body surface
Film, to its protective effect of charging equipment.
In the present embodiment, microwax may be any one wax such as paraffin, polyethylene wax, polypropylene wax or petroleum jelly.
Wherein, five fluorine dichloroethanes (HCFC-225) can uniformly disperse aerosil and nano-titanium dioxide, simultaneously
Microwax can be dissolved again, and also there is cleaning and osmosis.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax that percentage weighs stirs 30min, dissolves microwax, transparent.Wherein, container can be closed container, can prevent
Liquid splashes out when only stirring, while the impurity such as dust is avoided to fall into, naturally it is also possible to use other kinds of container.Agitating mode
It can select the modes such as magnetic agitation or mechanical agitation.
Step 2: weighing aerosil by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 3: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 4: using rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Embodiment two
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
In the present embodiment, microwax may be any one wax such as paraffin, polyethylene wax, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax that percentage weighs stirs 30min, dissolves microwax, transparent.
Step 2: weighing aerosil by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 3: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 4: using rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Embodiment three
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 1.5% |
| Nano-titanium dioxide | 0.5% |
| Microwax | 30% |
| Five fluorine dichloroethanes (HCFC-225) | 68%. |
In the present embodiment, microwax may be any one wax such as paraffin, polyethylene wax, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax that percentage weighs stirs 30min, dissolves microwax, transparent.
Step 2: weighing aerosil by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 3: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 4: using rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Example IV
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 2% |
| Nano-titanium dioxide | 0.1% |
| Microwax | 40% |
| Five fluorine dichloroethanes (HCFC-225) | 57.9%. |
In the present embodiment, microwax may be any one wax such as paraffin, polyethylene wax, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax that percentage weighs stirs 30min, dissolves microwax, transparent.
Step 2: weighing aerosil by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 3: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 200 revs/min, stirring
60min。
Step 4: using rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Embodiment five
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 3% |
| Nano-titanium dioxide | 2% |
| Microwax | 15% |
| Five fluorine dichloroethanes (HCFC-225) | 80%. |
In the present embodiment, microwax may be any one wax such as paraffin, polyethylene wax, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax that percentage weighs stirs 60min, dissolves microwax, transparent.
Step 2: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 100 revs/min, stirring
90min。
Step 3: weighing aerosil by weight percentage, add in container, using rotating speed as 100 revs/min, stirring
90min。
Step 4: using rotating speed as 500 revs/min, stirring and emulsifying 60min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Embodiment six
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 5% |
| Nano-titanium dioxide | 1% |
| Microwax | 40% |
| Paraffin | 9% |
| Five fluorine dichloroethanes (HCFC-225) | 80%. |
In the present embodiment, microwax and paraffin may be microwax, paraffin, polyethylene wax, polypropylene wax or petroleum jelly
Etc. arbitrary two kinds of wax, weight ratio 40:9.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) or a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent type organic washing agent.
The preparation method of the curing agent the specific steps are：
Step 1: weighing five fluorine dichloroethanes (HCFC-225) in container by above-mentioned weight percent, add in by weight
The microwax and paraffin that percentage weighs stir 40min, dissolve microwax, transparent.
Step 2: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 300 revs/min, stirring
70min。
Step 3: weighing aerosil by weight percentage, add in container, using rotating speed as 300 revs/min, stirring
70min。
Step 4: using rotating speed as 700 revs/min, stirring and emulsifying 40min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
Embodiment seven
The present embodiment provides a kind of online curing agents of self-purified environment-friendly type communication equipment and preparation method thereof, and curing agent is by following
The raw material of weight percent is prepared：
| Aerosil | 0.05% |
| Nano-titanium dioxide | 0.01% |
| Microwax | 50% |
| Five fluorine dichloroethanes (HCFC-225) | 45%. |
| One fluorine dichloroethanes | 4.94% |
In the present embodiment, microwax may be that microwax, paraffin, polyethylene wax, polypropylene wax or petroleum jelly etc. are arbitrary
A kind of wax.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) and a fluorine dichloroethanes may be five fluorine dichloroethanes,
Arbitrary two kinds of solvent types organic washing agent such as one fluorine dichloroethanes or trifluorobichloroethane.
The preparation method of the curing agent the specific steps are：
Step 1: five fluorine dichloroethanes (HCFC-225) and a fluorine dichloroethanes are weighed in container by above-mentioned weight percent
It is interior, the microwax weighed by weight percentage is added in, 50min is stirred, dissolves microwax, it is transparent.
Step 2: weighing nano-titanium dioxide by weight percentage, add in container, using rotating speed as 250 revs/min, stirring
80min。
Step 3: weighing aerosil by weight percentage, add in container, using rotating speed as 250 revs/min, stirring
80min。
Step 4: using rotating speed as 650 revs/min, stirring and emulsifying 50min obtains above-mentioned curing agent.
Every testing result of curing agent is shown in Table 1.
1 curing agent testing result of table
Claims (11)
1. a kind of online curing agent of self-purified environment-friendly type communication equipment, it is characterised in that：
Raw material including following weight percent is prepared：
Wherein, the solvent type organic washing agent is arbitrary in a fluorine dichloroethanes, trifluorobichloroethane, five fluorine dichloroethanes
It is one or more kinds of.
2. the online curing agent of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the wax be microwax, paraffin, polyethylene wax, polypropylene wax, in petroleum jelly any one or it is two or more.
3. the online curing agent of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the wax is microwax.
4. the online curing agent of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the cleaning agent is five fluorine dichloroethanes.
5. the online curing agent of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
It is prepared by the raw material of following weight percent：
6. a kind of preparation method of the online curing agent of self-purified environment-friendly type communication equipment as described in claim 1, it is characterised in that：
Wax is added in solvent type organic washing agent, stirring dissolves the wax, then adds in aerosil and nanometer two
Titanium oxide, curing agent described in stirring to obtain.
7. the preparation method of the online curing agent of self-purified environment-friendly type communication equipment according to claim 6, it is characterised in that：Tool
Body step is：
Step 1: adding in the wax in the solvent type organic washing agent, 30-60min is stirred, dissolves the wax；
Step 2: adding in the aerosil, using rotating speed as 100-300 revs/min, 60-90min is stirred；
Step 3: adding in the nano-titanium dioxide, using rotating speed as 100-300 revs/min, 60-90min is stirred；
Step 4: using rotating speed as 500-700 revs/min, 30-60min is emulsified.
8. the preparation method of the online curing agent of self-purified environment-friendly type communication equipment according to claim 7, it is characterised in that：
Wherein, step 2 and step 3 can be with exchange sequences.
9. the preparation method of the online curing agent of self-purified environment-friendly type communication equipment according to claim 7, it is characterised in that：
Step 2 is：The aerosil is added in, using rotating speed as 200 revs/min, stirs 60min.
10. the preparation method of the online curing agent of self-purified environment-friendly type communication equipment according to claim 7, it is characterised in that：
Step 3 is：The nano-titanium dioxide is added in, using rotating speed as 200 revs/min, stirs 60min.
11. the preparation method of the online curing agent of self-purified environment-friendly type communication equipment according to claim 7, it is characterised in that：
Step 4 is：Using rotating speed as 600 revs/min, 30min is emulsified.