CN106634595A - Self-cleaning environmental communication equipment online curing agent and preparation method thereof - Google Patents
Self-cleaning environmental communication equipment online curing agent and preparation method thereof Download PDFInfo
- Publication number
- CN106634595A CN106634595A CN201610946648.7A CN201610946648A CN106634595A CN 106634595 A CN106634595 A CN 106634595A CN 201610946648 A CN201610946648 A CN 201610946648A CN 106634595 A CN106634595 A CN 106634595A
- Authority
- CN
- China
- Prior art keywords
- communication equipment
- self
- sealing compound
- wax
- type communication
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a self-cleaning environmental communication equipment online curing agent and a preparation method thereof. The self-cleaning environmental communication equipment online curing agent is prepared from the raw materials of, by weight percentage, 0.05-5% of fumed silica, 0.01-2% of nano titanium dioxide, 15-50% of wax and 45-80% of solvent type organic cleaning agent. The self-cleaning environmental communication equipment online curing agent has the advantages of being good in effects on removing surface pollutant of communication equipment during online maintenance, capable of providing a surface self-cleaning function for maintained communication equipment and achieving antifouling effects, good in compatibility, corrosion-proof, safe in application, environmentally friendly, free from hazard to body health and the like.
Description
Technical field
The present invention relates to a kind of sealing compound, more particularly to a kind of online sealing compound of self-purified environment-friendly type communication equipment and its preparation
Method.
Background technology
Communication equipment, including exchange system, mobile base station etc., in its During Process of Long-term Operation, due to its various circuit certainly
The suction-operated of the generations such as electromagnetic field, the electrostatic field for so being formed, accumulate over a long period deposited on equipment substantial amounts of dust, greasy dirt,
Moisture, salinity, metal dirt and other charged particles.These " pollutants " not only affect the performances such as the radiating of equipment, and
Conductive ion in " pollutant " easily forms the microcircuit of conductivity type, causes to equipment " slow corrosion ", and different degrees of causes
Loose contact, reactance reduction, electric leakage, short circuit, error code, bad plate of sophisticated electronics etc., cause circuit energy loss, transmission letter
Number weaken, transfer rate and quality it is unstable the problems such as.Therefore, communication equipment is carried out comprehensively, depth keep a public place clean maintenance, have
Important meaning.
Be presently used for communication equipment keep a public place clean maintenance product it is more for electrified cleaning agent, only cleaning function lacks comprehensively
The maintenance of depth.Although these cleaning agent cleaning performances are good, insulation values are high, can powered clean, but equipment does not possess certainly after cleaning
Net work energy, also without creepage protection function.The apparatus insulated protective agent of some electric apparatus, with creepage protection function, but does not have
Standby cleaning and self-purification function.
The content of the invention
The present invention provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, to overcome prior art
Defect.
For achieving the above object, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, including following heavy
The raw material of amount percentage is prepared from：0.05-5% aerosils, 0.01-2% nano titanium oxides, 15-50% waxes,
45-80% solvent-borne type organic washing agent.
Further, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, can also have such spy
Levy：Wherein, wax is any one in microwax, paraffin, Tissuemat E, polypropylene wax, petroleum jelly or two or more.
Further, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, can also have such spy
Levy：Wherein, wax is microwax.
Further, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, can also have such spy
Levy：Wherein, cleaning agent be in a fluorine dichloroethanes, trifluorobichloroethane, five fluorine dichloroethanes any one or it is two or more.
Further, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, can also have such spy
Levy：Wherein, cleaning agent is five fluorine dichloroethanes (HCFC-225).
Further, the present invention provides a kind of self-purified environment-friendly type communication equipment online sealing compound, can also have such spy
Levy：It is prepared from by the raw material of following percentage by weight：1% aerosil, 0.05% nano titanium oxide, 35% crystallite
Wax, 63.95% 5 fluorine dichloroethanes.
The present invention also provides a kind of preparation method of the online sealing compound of self-purified environment-friendly type communication equipment, organic clear in solvent-borne type
Add wax, stirring to dissolve wax in lotion, be subsequently adding aerosil and nano titanium oxide, stirring obtains sealing compound.
Further, the present invention provides a kind of preparation method of the online sealing compound of self-purified environment-friendly type communication equipment, can also have
There is such feature：Concretely comprise the following steps：Step one, wax is added in solvent-borne type organic washing agent, stir 30-60min, make wax molten
Solution.In this step, speed of agitator is arbitrarily arranged, and dissolves wax.
Step 2, addition aerosil, with rotating speed as 100-300 rev/min, stir 60-90min.Preferably, with turn
Speed is 200 revs/min, stirs 60min.
Step 3, addition nano titanium oxide, with rotating speed as 100-300 rev/min, stir 60-90min.Preferably, with turn
Speed is 200 revs/min, stirs 60min.
Step 4, with rotating speed as 500-700 rev/min, emulsify 30-60min.Preferably, with rotating speed as 600 revs/min, stirring
30min。
Further, the present invention provides a kind of preparation method of the online sealing compound of self-purified environment-friendly type communication equipment, can also have
There is such feature：Wherein, step 2 and step 3 can be with exchange sequences.
The beneficial effect of this patent is：The present invention provides a kind of online sealing compound of self-purified environment-friendly type communication equipment and its system
Preparation Method, the aerosil included in sealing compound is spherical shape, and the aerosil after dispersion is arranged in equipment surface
" little small hill " shape is formed, in the recess of " little small hill " air is filled with, that is, form one layer of very thin nanometer air layer, dust
Be difficult to invade Deng pollutant, make equipment after maintenance, the film that its surface is formed has self-purification function, can prevent pernicious gas,
The erosion of the pollutants such as dust.Meanwhile, also make the film that there is insulation protection function, even if there is the accidents such as water logging, also can protect
Card equipment normally runs 30 minutes.
In addition, the Photosynthetic Energy that the titanium dioxide included in sealing compound is produced, with powerful oxidability, can make mould
Carbon dioxide and water are resolved into Deng pollutant, so that equipment is after maintenance, the film that its surface is formed has sterilizing function.
It is green environment friendly sealing compound additionally, not containing ozone-layer depleting substance (ODS) in sealing compound, and to human body
Health is harmless.
Description of the drawings
Fig. 1 is surface microscopic figure after sprinkling sealing compound.
Specific embodiment
Embodiment one
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 1% |
| Nano titanium oxide | 0.05% |
| Microwax | 35% |
| Five fluorine dichloroethanes (HCFC-225) | 63.95%. |
Wherein, microwax is the dispersible carrier of aerosil and nano titanium oxide, and in body surface one layer is formed
Film, to its protective effect of charging equipment.
In the present embodiment, microwax can also be any one wax such as paraffin, Tissuemat E, polypropylene wax or petroleum jelly.
Wherein, five fluorine dichloroethanes (HCFC-225) can dispersed aerosil and nano titanium oxide, while
Microwax can be dissolved again, also with cleaning and osmosis.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
The microwax that percentage is weighed, stirs 30min, dissolves microwax, transparent.Wherein, container can be closed container, can prevent
Liquid spills when only stirring, while avoiding the impurity such as dust from falling into, naturally it is also possible to using other kinds of container.Agitating mode
Can be selecting the mode such as magnetic agitation or mechanical agitation.
Step 2, aerosil is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 3, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 4, with rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Embodiment two
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
In the present embodiment, microwax can also be any one wax such as paraffin, Tissuemat E, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
The microwax that percentage is weighed, stirs 30min, dissolves microwax, transparent.
Step 2, aerosil is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 3, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 4, with rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Embodiment three
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 1.5% |
| Nano titanium oxide | 0.5% |
| Microwax | 30% |
| Five fluorine dichloroethanes (HCFC-225) | 68%. |
In the present embodiment, microwax can also be any one wax such as paraffin, Tissuemat E, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
The microwax that percentage is weighed, stirs 30min, dissolves microwax, transparent.
Step 2, aerosil is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 3, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 4, with rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Example IV
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 2% |
| Nano titanium oxide | 0.1% |
| Microwax | 40% |
| Five fluorine dichloroethanes (HCFC-225) | 57.9%. |
In the present embodiment, microwax can also be any one wax such as paraffin, Tissuemat E, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
The microwax that percentage is weighed, stirs 30min, dissolves microwax, transparent.
Step 2, aerosil is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 3, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 200 revs/min, stir
60min。
Step 4, with rotating speed as 600 revs/min, stirring and emulsifying 30min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Embodiment five
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 3% |
| Nano titanium oxide | 2% |
| Microwax | 15% |
| Five fluorine dichloroethanes (HCFC-225) | 80%. |
In the present embodiment, microwax can also be any one wax such as paraffin, Tissuemat E, polypropylene wax or petroleum jelly.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
The microwax that percentage is weighed, stirs 60min, dissolves microwax, transparent.
Step 2, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 100 revs/min, stir
90min。
Step 3, aerosil is weighed by weight percentage, in adding container, with rotating speed as 100 revs/min, stir
90min。
Step 4, with rotating speed as 500 revs/min, stirring and emulsifying 60min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Embodiment six
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 5% |
| Nano titanium oxide | 1% |
| Microwax | 40% |
| Paraffin | 9% |
| Five fluorine dichloroethanes (HCFC-225) | 80%. |
In the present embodiment, microwax and paraffin can also be microwax, paraffin, Tissuemat E, polypropylene wax or petroleum jelly
Etc. any two kinds of wax, weight ratio is 40:9.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) can also be a fluorine dichloroethanes or trifluorobichloroethane etc.
Any one solvent-borne type organic washing agent.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) are weighed by above-mentioned percentage by weight in container, added by weight
Microwax and paraffin that percentage is weighed, stir 40min, dissolve microwax, transparent.
Step 2, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 300 revs/min, stir
70min。
Step 3, aerosil is weighed by weight percentage, in adding container, with rotating speed as 300 revs/min, stir
70min。
Step 4, with rotating speed as 700 revs/min, stirring and emulsifying 40min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
Embodiment seven
The present embodiment provides online sealing compound of a kind of self-purified environment-friendly type communication equipment and preparation method thereof, and sealing compound is by following
The raw material of percentage by weight is prepared from：
| Aerosil | 0.05% |
| Nano titanium oxide | 0.01% |
| Microwax | 50% |
| Five fluorine dichloroethanes (HCFC-225) | 45%. |
| One fluorine dichloroethanes | 4.94% |
In the present embodiment, microwax can also be for microwax, paraffin, Tissuemat E, polypropylene wax or petroleum jelly etc. arbitrarily
A kind of wax.
In the present embodiment, five fluorine dichloroethanes (HCFC-225) and a fluorine dichloroethanes can also for five fluorine dichloroethanes,
Any two kinds of solvent-borne types organic washing agent such as one fluorine dichloroethanes or trifluorobichloroethane.
The preparation method of the sealing compound is concretely comprised the following steps：
Step one, five fluorine dichloroethanes (HCFC-225) and a fluorine dichloroethanes are weighed by above-mentioned percentage by weight in container
It is interior, the microwax for weighing by weight percentage is added, 50min is stirred, microwax is dissolved, it is transparent.
Step 2, nano titanium oxide is weighed by weight percentage, in adding container, with rotating speed as 250 revs/min, stir
80min。
Step 3, aerosil is weighed by weight percentage, in adding container, with rotating speed as 250 revs/min, stir
80min。
Step 4, with rotating speed as 650 revs/min, stirring and emulsifying 50min obtains above-mentioned sealing compound.
Every testing result of sealing compound is shown in Table 1.
The sealing compound testing result of table 1
Claims (9)
1. the online sealing compound of a kind of self-purified environment-friendly type communication equipment, it is characterised in that：
It is prepared from including the raw material of following percentage by weight：
2. the online sealing compound of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the wax is any one in microwax, paraffin, Tissuemat E, polypropylene wax, petroleum jelly or two or more.
3. the online sealing compound of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the wax is microwax.
4. the online sealing compound of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the cleaning agent is any one in a fluorine dichloroethanes, trifluorobichloroethane, five fluorine dichloroethanes or two kinds
More than.
5. the online sealing compound of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
Wherein, the cleaning agent is five fluorine dichloroethanes.
6. the online sealing compound of self-purified environment-friendly type communication equipment according to claim 1, it is characterised in that：
It is prepared from by the raw material of following percentage by weight：
7. the preparation method of the online sealing compound of a kind of self-purified environment-friendly type communication equipment, it is characterised in that：
Wax, stirring is added to dissolve the wax, be subsequently adding aerosil and nanometer two in solvent-borne type organic washing agent
Titanium oxide, stirring obtains the sealing compound.
8. the preparation method of the online sealing compound of self-purified environment-friendly type communication equipment according to claim 7, it is characterised in that：Tool
Body step is：
Step one, the wax is added in the solvent-borne type organic washing agent, stir 30-60min, dissolve the wax；
Step 2, the addition aerosil, with rotating speed as 100-300 rev/min, stir 60-90min；
Preferably, with rotating speed as 200 revs/min, 60min is stirred；
Step 3, the addition nano titanium oxide, with rotating speed as 100-300 rev/min, stir 60-90min；
Preferably, with rotating speed as 200 revs/min, 60min is stirred；
Step 4, with rotating speed as 500-700 rev/min, emulsify 30-60min；
Preferably, with rotating speed as 600 revs/min, 30min is stirred.
9. the preparation method of the online sealing compound of self-purified environment-friendly type communication equipment according to claim 8, it is characterised in that：
Wherein, step 2 and step 3 can be with exchange sequences.