CN106634481A - Heat insulation glass paint for sightseeing elevators and preparation method of heat insulation glass paint - Google Patents
Heat insulation glass paint for sightseeing elevators and preparation method of heat insulation glass paint Download PDFInfo
- Publication number
- CN106634481A CN106634481A CN201611078167.5A CN201611078167A CN106634481A CN 106634481 A CN106634481 A CN 106634481A CN 201611078167 A CN201611078167 A CN 201611078167A CN 106634481 A CN106634481 A CN 106634481A
- Authority
- CN
- China
- Prior art keywords
- parts
- plated film
- glass coating
- insulating glass
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides coated heat insulation glass paint for sightseeing elevators and a preparation method of the coated heat insulation glass paint. The coated heat insulation glass paint is prepared from 10-30 parts of inorganic nano ceramic resin, 10-20 parts of organic modified polyester acrylate, 5-10 parts of nano powder, 2-4 parts of photoinitiators, 1-4 parts of dispersion liquid, 2-3 parts of a flatting agent, 0.5-1 part of a base material wetting agent, 1-2 parts of auxiliary agents and 2-8 parts of organic solvents, wherein the photoinitiators refer to one or more of 1-hydroxyl-cyclohexyl-phenyl ketone, (2,4,6-trimethylbenzoyl)diphenylphosphine oxide and 2-hydroxy-2-methyl-1-phenyl-1-acetone. The heat insulation glass paint prepared from the raw materials is great in heat insulation performance, capable of isolating heat inside and outside the elevators to the great extent and high in weather resistance and acid-alkali corrosion resistance. In addition, the heat insulation glass paint is high in hardness and safety and is suitable for high-rise sightseeing elevators.
Description
Technical field
The invention belongs to sightseeing elevator field of material technology, and in particular to a kind of sightseeing elevator insulating glass coating and its system
Preparation Method.
Background technology
Sightseeing elevator is widely used in view of travelling as a kind of body-sensing sightseeing elevator, and builds in general high level
Build during sight spot is gone sightseeing and be also applied;In the case where the safety of passenger is ensured, for ease of going sightseeing, typically by sightseeing elevator 360
Degree adopts clear glass, guest is more perfectly experienced under vision without dead angle beautiful scenery;However, due to sightseeing elevator glass it is general
Expose, it is easy to by ambient temperature, rainwater and other ambient influnences, cause life-span, hydraulic performance decline;Existing glass heat-proof effect
Really poor, thermoplastic property is not high, it is impossible to which the high-quality sightseeing elevator glass of Manchu is required.
Based on technical problem present in above-mentioned sightseeing elevator glass, not yet there is the solution of correlation;Therefore compel to be essential
Seek effective scheme to solve the above problems.
The content of the invention
The purpose of the present invention is, for weak point present in above-mentioned technology, to propose a kind of heat-insulated glass of sightseeing elevator plated film
Glass coating, it is intended to solve the problems, such as existing sightseeing elevator glass short life, poor performance.
The present invention provides a kind of sightseeing elevator plated film insulating glass coating, including:10 parts to 30 of electrodeless nano ceramics resin
Part, 10 parts to 20 parts of organosilicon modified polyester acrylate, 5 parts to 10 parts of nano-powder, 2 parts to 4 parts of light trigger, dispersion liquid
2 parts to 8 of 1 part to 4 parts, 2 parts to 3 parts of levelling agent, 0.5 part to 1 part of substrate wetting agents, 1 part to 2 parts of auxiliary agent and organic solvent
Part;Wherein, light trigger be 1- hydroxy-cyclohexyl-phenyl ketones,(2,4,6-trimethylbenzoyl)Dipheny oxide
Change one or more in phosphine, 2- hydroxy-2-methyl -1- phenyl -1- acetone.
Further, substrate wetting agents are organic silicon modified by polyether compound.
Further, surfactant is also included;Surfactant is cetyl benzenesulfonic acid sodium.
Further, dispersion liquid includes that near-infrared long wave intercepts nano material dispersion liquid, near-infrared shortwave and intercepts nanometer material
At least one in material dispersion liquid or UV-preventing nano material dispersion liquid.
Further, nano-powder by tin oxide, organotin, tin-antiomony oxide, zinc oxide, zinc oxide aluminum, tin indium oxide, four
At least one composition in Fe 3 O, silica or titanium oxide.
Further, also including inorganic salts;Inorganic salts are that sodium chloride and potassium chloride structure press 1:1 ratio composition.
Further, also including curing agent;Curing agent is selected from gamma-aminopropyl-triethoxy-silane, aliphatic isocyanates
And butylamine presses 2:2:1 ratio composition.
Further, also including thickener;Thickener is selected from hydroxy aqueous acid.
Further, also including coalescents;Coalescents press 2 by dipropylene and ethylene glycol only son:1 ratio
Composition.
The present invention also provides a kind of preparation method of sightseeing elevator plated film insulating glass coating, comprises the following steps, including:
S1:First, by 10 parts to 30 parts of electrodeless nano ceramics resin, 10 parts to 20 parts of organosilicon modified polyester acrylate, receive
1 part to 4 parts of 5 parts to 10 parts of ground rice body, 2 parts to 4 parts of light trigger and dispersion liquid, in closed reaction vessel, temperature is 45 °
Mix in C to 90 °C, uniform stirring obtains mixed liquor in 6 minutes to 15 minutes;
S2:Then by 2 parts to 3 parts of levelling agent, 0.5 part to 1 part of substrate wetting agents, 1 part to 2 parts of auxiliary agent and organic solvent 2
Part to 8 parts add uniform stirring in above-mentioned mixed liquor, ultrasonication 10 minutes to 20 minutes;
S3:Finally it is filled with nitrogen constant pressure and is incubated 10 minutes to 15 minutes, that is, obtains the coating.
By the way that there is good heat-proof quality using insulating glass coating made by above-mentioned raw materials, can largely every
Temperature between insulation ladder is inside and outside, being not easily susceptible to extraneous factor when elevator is in high level affects, so as to improve sightseeing
Experience effect;Simultaneously using the insulating glass coating of offer of the invention, weather-resistant property is high, antiacid caustic corrosion preferable,
And the insulating glass coating hardness is high, security is good, for high-rise sightseeing elevator is more suitable for.
Description of the drawings
With reference to the accompanying drawings and detailed description the present invention is further detailed explanation.
Below with reference to accompanying drawing, the invention will be further described:
Fig. 1 is a kind of flow chart of sightseeing elevator plated film insulating glass coating preparation method of the invention.
Specific embodiment
It should be noted that in the case where not conflicting, the feature in embodiment and embodiment in the application can phase
Mutually combination.Below with reference to the accompanying drawings and in conjunction with the embodiments describing the present invention in detail.
The present invention provides a kind of sightseeing elevator plated film insulating glass coating, and it mainly includes raw material:Including:Electrodeless nanometer pottery
Porcelain resin 10kg to 30kg, organosilicon modified polyester acrylate 10kg to 20kg, nano-powder 5kg to 10kg, light trigger
2kg to 4kg, dispersion liquid 1kg to 4kg, levelling agent 2kg to 3kg, substrate wetting agents 0.5kg to 1 part of kg, auxiliary agent 1kg to 2kg with
And organic solvent 2kg to 8kg;Wherein, light trigger be 2- hydroxy-2-methyl -1- phenyl -1- acetone, 1- hydroxy-cyciohexyls -
Phenyl ketone,(2,4,6-trimethylbenzoyl)One or more in diphenyl phosphine oxide;It is organic-silicon-modified poly-
Ester acrylate is the bifunctionality polyester acrylate of model DR-E750;Organic solvent is butyl acetate, butanone, second
One or more composition in acetoacetic ester;Substrate wetting agents are organic silicon modified by polyether compound;By using above-mentioned raw materials system
Into insulating glass coating can be that heat-protecting glass has good heat-proof quality, can largely completely cut off elevator interior and
Temperature between outside, being not easily susceptible to extraneous factor when elevator is in high level affects, so as to improve the experience effect of sightseeing.
Preferably, with reference to such scheme, in the present embodiment, be improve heat barriering effect, plated film insulating glass coating
In nano-powder by titanium dioxide, tin indium oxide, zinc oxide, γ crystal formation ferric oxides, silica and tin-antiomony oxide
Combine for any two or three;Ordinary circumstance can press 2 using titanium dioxide, tin indium oxide, zinc oxide:1:1 material
Ratio mixes;Or with tin indium oxide, zinc oxide, γ crystal formations ferric oxide as material in proportion 2:2:1 is matched, by upper
Stating producing for nano-powder material can improve plated film insulating glass coating heat barriering effect.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes surfactant;Table
Face activating agent is cetyl benzenesulfonic acid sodium;The use of surfactant can improve plated film insulating glass coating Surface heat-treatent
Effect, increases resistance to water.
Preferably, with reference to such scheme, in the present embodiment, dispersion liquid includes that near-infrared long wave intercepts nano material dispersion
Liquid, near-infrared shortwave intercept nano material dispersion liquid or at least one in UV-preventing nano material dispersion liquid;Using upper
Stating dispersion liquid can effectively facilitate the scattered property of light of coating surface, increase transparency, and grow dim while can reduce viscosity and reduce flocculation.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes C1- C5 Lower aliphatic
Alcohol;Wherein, lower aliphatic alcohols can press 1 by ethanol and isopropanol:1 ratio composition;Plated film heat-protecting glass can so be improved
Paint stability.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes inorganic salts;Inorganic salts are
The halide salt of alkaline-earth metal is constituted;And also microemulsified resin can be added, can so improve plated film heat-protecting glass coating
Hardness, is easy to clean and be difficult scratch.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes curing agent;Curing agent is selected
Can be by 2 from gamma-aminopropyl-triethoxy-silane, aliphatic isocyanates and butylamine:2:1 ratio composition;Using solidification
It is more preferable that agent can improve plated film heat-protecting glass coating heat resistance, resistance to water;While the mechanical property of plated film heat-protecting glass is more preferably.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes thickener;Thickener is selected
From hydroxy aqueous acid, the viscosity between plated film heat-protecting glass material can be so improved, and painting can be effectively improved
The acid resistance of layer.
Preferably, with reference to such scheme, in the present embodiment, plated film insulating glass coating also includes coalescents;Film forming is helped
Agent presses 2 by dipropylene and ethylene glycol only son:1 ratio composition;Plated film heat-protecting glass can be improved using coalescents
Coating surface forms film, optimizes the translucent effect of plated film insulating glass coating.
With reference to such scheme, correspondingly, as shown in figure 1, the present invention also provides a kind of sightseeing elevator plated film heat-protecting glass applying
The preparation method of material, comprises the following steps:
S1:First, by 10 parts to 30 parts of electrodeless nano ceramics resin, 10 parts to 20 parts of organosilicon modified polyester acrylate, receive
1 part to 4 parts of 5 parts to 10 parts of ground rice body, 2 parts to 4 parts of light trigger and dispersion liquid, in closed reaction vessel, temperature is 45 °
Mix in C to 90 °C, uniform stirring obtains mixed liquor in 6 minutes to 15 minutes;
S2:Then by 2 parts to 3 parts of levelling agent, 0.5 part to 1 part of substrate wetting agents, 1 part to 2 parts of auxiliary agent and organic solvent 2
Part to 8 parts add uniform stirring in above-mentioned mixed liquor, ultrasonication 10 minutes to 20 minutes;
S3:Finally it is filled with nitrogen constant pressure and is incubated 10 minutes to 15 minutes, that is, obtains the coating.
Preferably, it is further comprising the steps of in S1 steps with reference to such scheme:
S11:Addition surfactant, surfactant is cetyl benzenesulfonic acid sodium, increases the heat-insulated glass of plated film under molten condition
The reactivity of glass coating;Meanwhile, the use of surfactant can improve plated film insulating glass coating Surface heat-treatent effect,
Increase resistance to water.
S12:Addition dispersion liquid, dispersion liquid includes that near-infrared long wave intercepts nano material dispersion liquid, near-infrared shortwave and intercepts
At least one in nano material dispersion liquid or UV-preventing nano material dispersion liquid;Can effectively be promoted using above-mentioned dispersion liquid
The light for entering coating surface dissipates property, increases transparency, and grows dim while can reduce viscosity and reduce flocculation.
Preferably, it is further comprising the steps of in S2 steps with reference to such scheme:
S11:Addition C1- C5 Lower aliphatic alcohols and inorganic salts;Lower aliphatic alcohols press 1 by ethanol and isopropanol:1 composition, it is inorganic
Salt is constituted for the halide salt of alkaline-earth metal;And also microemulsified resin can be added, can so improve the painting of plated film heat-protecting glass
The hardness of material figure layer, is easy to clean and be difficult scratch.
S22:Addition includes curing agent;Curing agent is selected from gamma-aminopropyl-triethoxy-silane, aliphatic isocyanates and fourth
Amine presses 2:2:1 ratio composition;Plated film heat-protecting glass coating heat resistance, resistance to water can be improved using curing agent more preferable;Simultaneously
The mechanical property of plated film heat-protecting glass is more preferably.
S23:Also include thickener and coalescents;Thickener is selected from hydroxy aqueous acid, can so improve plating
Viscosity between film heat-protecting glass material, and the acid resistance of coating can be effectively improved, and the heat-insulated glass of plated film can be promoted
The smooth performance of glass coating surface, it is to avoid be difficult to clean in dirt adherent glass.
By the way that there is good heat-proof quality using insulating glass coating made by above-mentioned raw materials, can largely every
Temperature between insulation ladder is inside and outside, being not easily susceptible to extraneous factor when elevator is in high level affects, so as to improve sightseeing
Experience effect;Simultaneously using the insulating glass coating of offer of the invention, weather-resistant property is high, antiacid caustic corrosion preferable,
And the insulating glass coating hardness is high, security is good, for high-rise sightseeing elevator is more suitable for.
The above, only presently preferred embodiments of the present invention not does any pro forma restriction to the present invention.It is any ripe
Those skilled in the art is known, under without departing from technical solution of the present invention ambit, all using technology contents described above
Many possible variations and modification, or the Equivalent embodiments for being revised as equivalent variations are made to technical solution of the present invention.Therefore, it is all
It is the content without departing from technical solution of the present invention, any change made for any of the above embodiments is changed according to the technology of the present invention,
Equivalent variations and modification, belong to the protection domain of the technical program.
Claims (10)
1. a kind of sightseeing elevator plated film insulating glass coating, it is characterised in that include:10 parts to 30 of electrodeless nano ceramics resin
Part, 10 parts to 20 parts of organosilicon modified polyester acrylate, 5 parts to 10 parts of nano-powder, 2 parts to 4 parts of light trigger, dispersion liquid
2 parts to 8 of 1 part to 4 parts, 2 parts to 3 parts of levelling agent, 0.5 part to 1 part of substrate wetting agents, 1 part to 2 parts of auxiliary agent and organic solvent
Part, wherein the light trigger be 1- hydroxy-cyclohexyl-phenyl ketones,(2,4,6-trimethylbenzoyl)Hexichol
One or more in base phosphine oxide, 2- hydroxy-2-methyl -1- phenyl -1- acetone.
2. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that the substrate wetting agents are
Organic silicon modified by polyether compound.
3. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that also include surface-active
Agent;The surfactant is cetyl benzenesulfonic acid sodium.
4. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that the dispersion liquid includes near
Infrared long wave intercepts nano material dispersion liquid, near-infrared shortwave and intercepts nano material dispersion liquid or UV-preventing nano material point
At least one in dispersion liquid.
5. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that the nano-powder is by oxygen
Change in tin, organotin, tin-antiomony oxide, zinc oxide, zinc oxide aluminum, tin indium oxide, ferroso-ferric oxide, silica or titanium oxide extremely
A kind of few composition.
6. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that also including inorganic salts;Institute
To state inorganic salts be sodium chloride and potassium chloride structure by 1:1 ratio composition.
7. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that also including curing agent;Institute
Curing agent is stated selected from gamma-aminopropyl-triethoxy-silane, aliphatic isocyanates and butylamine by 2:2:1 ratio composition.
8. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that also including thickener;Institute
Thickener is stated selected from hydroxy aqueous acid.
9. sightseeing elevator plated film insulating glass coating according to claim 1, it is characterised in that also including coalescents;
The coalescents press 2 by dipropylene and ethylene glycol only son:1 ratio composition.
10. a kind of preparation method of sightseeing elevator plated film insulating glass coating, it is characterised in that comprise the following steps:
S1:First, by 10 parts to 30 parts of electrodeless nano ceramics resin, 10 parts to 20 parts of organosilicon modified polyester acrylate, receive
1 part to 4 parts of 5 parts to 10 parts of ground rice body, 2 parts to 4 parts of light trigger and dispersion liquid, in closed reaction vessel, temperature is 45 °
Mix in C to 90 °C, uniform stirring obtains mixed liquor in 6 minutes to 15 minutes;
S2:Then by 2 parts to 3 parts of levelling agent, 0.5 part to 1 part of substrate wetting agents, 1 part to 2 parts of auxiliary agent and organic solvent 2
Part to 8 parts add uniform stirring in above-mentioned mixed liquor, ultrasonication 10 minutes to 20 minutes;
S3:Finally it is filled with nitrogen constant pressure and is incubated 10 minutes to 15 minutes, that is, obtains the coating.