CN106633392A - Functional master batch capable of improving antistatic property of polypropylene - Google Patents
Functional master batch capable of improving antistatic property of polypropylene Download PDFInfo
- Publication number
- CN106633392A CN106633392A CN201611097337.4A CN201611097337A CN106633392A CN 106633392 A CN106633392 A CN 106633392A CN 201611097337 A CN201611097337 A CN 201611097337A CN 106633392 A CN106633392 A CN 106633392A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- functional agglomerate
- resin
- screw extruder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of functional master batches, in particular to a functional master batch capable of improving the antistatic property of polypropylene. The functional master batch is prepared from the following ingredients in parts by weight: 80 to 100 parts of carrier resin, 15 to 20 parts of PA resin particles, 10 to 15 parts of active aluminum oxide powder, 10 to 15 parts of clay, 10 to 15 parts of magnesium chloride, 0.5 to 0.7 part of dispersing agents and 0.5 to 0.7 part of coupling agents, wherein the carrier resin is polypropylene resin; the dispersing agent is barium stearate; the coupling agent is a chelating titanate coupling agent. The functional master batch has the advantages that the PA resin particles, the active aluminum oxide powder, the clay and the magnesium chloride are compounded, so that a polypropylene product achieves the effects that the wetness degree of the polypropylene product is improved by combining water through a chemical or physical path, and meanwhile, the excess charge generated in the polypropylene product is timely dispersed, so that the antistatic capability of a polypropylene material is improved.
Description
Technical field
The present invention relates to feature masterbatch field, and in particular to a kind of functional agglomerate of raising polypropylene antistatic ability.
Background technology
Polypropylene(PP)It is a kind of thermoplastic resin by obtained in propylene polymerization, is a kind of nontoxic, odorless, tasteless milky white
Color high crystallinity polymer, with good flexural fatigue resistance, chemical stability.Polypropylene arc resistance is good, dielectric coefficient is high,
Breakdown voltage is high, can be used to make electrical apparatus insulation product or electrical accessorie etc..But as polyacrylic high-insulativity makes polypropylene
Antistatic behaviour it is poor, limit polypropylene further applying in terms of electricity.Chinese patent CN105111582A, patent name
A kind of anlistatig polypropylene material, discloses a kind of being added with using polythiophene or siloxanes as modified poly- the third of antistatic additive
Alkene material.But the polythiophene of powder or siloxanes directly add that dispersion effect is bad and easy conglomeration, so as to affect poly- third
The consistency of performance of alkene material, and the antistatic effect of the antistatic additive is general.
Master batch be by the modified chemical auxiliary agent uniform load of super quantity in vector resin obtained from granular aggregation.With
Directly add modified chemical auxiliary agent in product to compare:The dispersion effect of master batch makes well the performance of product uniform, the carrier of master batch
The compatibility of resin and product resin makes well the performance of the product of addition master batch lift effect more preferably, master batch using safety,
Complete function.
The content of the invention
Cause antistatic behaviour difference for the high-insulativity of polypropylene material and affect polyacrylic application, existing improvement gathers
The problem that the additive effect of the anlistatig powder of propylene is not added with, it is an object of the invention to provide one kind is added to polypropylene material
In functional agglomerate, hence it is evident that improve polypropylene material antistatic effect, while functional agglomerate uniformly divides in polythene material
Dissipate and ensure polypropylene material product propertiess uniformity.
The present invention provides following technical scheme:
A kind of functional agglomerate for improving polypropylene antistatic, is prepared from by the component of following weight portion:Vector resin 80~
100 parts, 15~20 parts of PA resin particles, 10~15 parts of active oxidation aluminium powder, 10~15 parts of clay, magnesium chloride 10~15 part, point
Powder is 0.5~0.7 part, coupling agent is 0.5~0.7 part, and wherein vector resin is acrylic resin.
The functional agglomerate of the present invention is good with the compatibility of polypropylene material as vector resin from acrylic resin, can make
Functional agglomerate is uniformly dispersed in polypropylene material, and contributing to enhanced feature master batch improves the anlistatig ability of polypropylene material.
PA resins are i.e. by the aliphatic polyamide resin of amido link-[NHCO]-couple together.PA resins and polypropylene crosslinking blending
Afterwards, the amido link in PA resins easily forms hydrogen bond between hydrone, realizes in acrylic resin surface or internal solid water
Effect, suppresses acrylic resin product to produce electrostatic because being excessively dried.Active oxidation aluminium powder is dispersed by functional agglomerate
Inside acrylic resin.The electrostatic charge that the excellent conductive performance of active oxidation aluminium powder can disperse polypropylene unnecessary in time.Together
When active oxidation aluminium powder, clay and magnesium chloride easily absorb water, especially under magnesium chloride wet condition absorb water deliquescence into six water crystallizations
Magnesium chloride, and decompose release water in drying or hot environment, so as to alleviate the degree of drying on acrylic resin surface, suppress
The generation of electrostatic.The surface of clay is presented the positive charge produced during certain elecrtonegativity can neutralize polypropylene in addition, keeps poly-
Propylene charge balance.So by the synergism of PA resins, active oxidation aluminium powder, clay and magnesium chloride, make addition functional
The polypropylene material of master batch has good antistatic property.Dispersant makes each component in functional agglomerate in acrylic resin
Dispersed, coupling agent is effectively improved active oxidation aluminium powder, the surface activity between clay, magnesium chloride and polypropylene material, carries
The performance of high polypropylene material is uniform and stable.
Used as a modification of the present invention, the dispersant is barium stearate.Barium stearate belongs to metallic soap salt, can be equal
Each component in even divergent function master batch.Barium stearate transmits electric charge, synergistic activity aluminium oxide inside polypropylene material simultaneously
Powder disperses charge effect.
Used as a modification of the present invention, the coupling agent is chelating titanate coupling agent.Chelating type titanium esters coupling agent
With good hydrolytic stability, show good coupled in polypropylene material.
A kind of preparation method of the functional agglomerate for improving polypropylene antistatic, comprises the following steps:
(1)Each material component of weight portion is put in mixing and blending machine in 40~50 DEG C of stirring mixing 1~2 hour, stirring speed
350~400 r/min of degree;
(2)Mixed material is put in double screw extruder, the mixing speed of holding double screw extruder is 150~200 r/
Min, the temperature range that each section of double screw extruder are 160~210 DEG C, Jing after fully melting and be combined extrude granulating;
(3)By step(2)Gained granule sieves through the screen cloth of -15 mesh of mesh~+20.
First raw material is stirred in mixing and blending machine high speed, the consistency of performance of functional agglomerate is improved.By double
Screw extruder melts compound extruded into graininess, improves dispersed degree of the functional agglomerate in polypropylene material, has
Help the performance uniformity of polypropylene material.The particle diameter of functional agglomerate can pass through the screen cloth of -15 mesh of mesh~+20, both ensure work(
Energy master batch is dispersed in polypropylene material, avoids the excessive impact functional agglomerate of particle diameter molten in polypropylene material preparation again
Melt dispersion effect.
As a modification of the present invention, step(2)The temperature control of each section of middle double screw extruder is respectively:One section
160~185 DEG C, 185~195 DEG C of two-stage nitration, three sections 195~200 DEG C, four sections 200~205 DEG C, five sections 205~210 DEG C,
Six sections 200~205 DEG C, die head temperature be 200~205 DEG C.By the operation temperature of each section of double screw extruder of setting gradually
Rise, each dispensing dispersion electric charge in abundant release function master batch, with reference to water and lubrication dispersing characteristic improves functional agglomerate performance equal
It is even consistent.
As a modification of the present invention, step is being carried out(3)By step before screening granule(2)Gained granule exists first
Aeration-drying 2~4 hours at 160~170 DEG C, obtain the granule of dry tack free.So can be equal with promotion functions master batch surface texture
It is even, also allow for the long-term storage of master batch.
Beneficial effects of the present invention are as follows:
The functional agglomerate of the present invention is compounded with PA resin particles, active oxidation aluminium powder, clay and magnesium chloride, makes to be added with the function
The polypropylene material of master batch has by approach chemically or physically with reference to water to improve the moistening degree of polypropylene material to press down
The function that electrostatic processed is produced, while the excess charge produced in polypropylene material can disperse in time, so as to improve polypropylene material
The antistatic effect of material.Dispersion effect of the granular functional agglomerate in polypropylene material is good in addition, polypropylene material performance
Uniformly.
Specific embodiment
Just the specific embodiment of the present invention is described further below:
Embodiment 1:
A kind of functional agglomerate for improving polypropylene antistatic, is prepared from by the component of following weight portion:80 g of vector resin,
15 g of PA resin particles, 10 g of active oxidation aluminium powder, 10 g of clay, 10 g of magnesium chloride, dispersant are 0.5 g, coupling agent is 0.5
The preferred acrylic resin of g, wherein vector resin, improves the compatibility of functional agglomerate and polypropylene material, the preferred Hard Fat of dispersant
Sour barium, strengthens dispersion of the electric charge in polypropylene material, coupling agent preferred chelating type titanium while making each component dispersed
Ester acid coupling agent.
A kind of preparation method of the functional agglomerate for improving polypropylene antistatic, comprises the following steps:
(1)Each material component of weight portion is put in mixing and blending machine in 40 DEG C of stirring mixing 1 hour, mixing speed 350
r/min;
(2)Mixed material is put in double screw extruder, the mixing speed of holding double screw extruder is 150 r/min, double
The temperature range that each section of screw extruder is 160~210 DEG C, Jing after fully melting and be combined extrudes granulating;
(3)By step(2)Gained granule sieves through the screen cloth of -15 mesh of mesh~+20.
To obtain the functional agglomerate of better performances, step(2)The temperature control of each section of middle double screw extruder is respectively:One
Section 160~185 DEG C, 185~195 DEG C of two-stage nitration, three sections 195~200 DEG C, four sections 200~205 DEG C, five section 205~210
DEG C, six sections 200~205 DEG C, die head temperature be 200~205 DEG C.
To improve functional agglomerate surface texture uniformity coefficient, step is being carried out(3)Before screening, by step(2)Gained granule
Aeration-drying 4 hours first at 160 DEG C, obtain the granule of dry tack free, then carry out step again(3)Screening.
Pass through the granule that the screen cloth of -15 mesh of mesh~+20 sieves and be the functional agglomerate for improving polypropylene antistatic.
Embodiment 2:
The preferred barium stearate of dispersant, the preferred chelating type titanium esters acid coupling agent of coupling agent.
A kind of functional agglomerate for improving polypropylene antistatic, is prepared from by the component of following weight portion:Vector resin
90 g, PA resin particle, 17.5 g, 12.5 g of active oxidation aluminium powder, 12.5 g of clay, 12.5 g of magnesium chloride, dispersant are 0.6
G, coupling agent are 0.6 g, the wherein preferred acrylic resin of vector resin, improve the compatibility of functional agglomerate and polypropylene material,
The preferred barium stearate of dispersant, strengthens dispersion of the electric charge in polypropylene material while making each component dispersed, is coupled
The preferred chelating type titanium esters acid coupling agent of agent.
A kind of preparation method of the functional agglomerate for improving polypropylene antistatic, comprises the following steps:
(1)Each material component of weight portion is put in mixing and blending machine in 45 DEG C of stirring mixing 1 hour, mixing speed 370
r/min;
(2)Mixed material is put in double screw extruder, the mixing speed of holding double screw extruder is 170 r/min, double
The temperature range that each section of screw extruder is 160~210 DEG C, Jing after fully melting and be combined extrudes granulating;
(3)By step(2)Gained granule sieves through the screen cloth of -15 mesh of mesh~+20.
To obtain the functional agglomerate of better performances, step(2)The temperature control of each section of middle double screw extruder is respectively:One
Section 160~185 DEG C, 185~195 DEG C of two-stage nitration, three sections 195~200 DEG C, four sections 200~205 DEG C, five section 205~210
DEG C, six sections 200~205 DEG C, die head temperature be 200~205 DEG C.
To improve functional agglomerate surface texture uniformity coefficient, step is being carried out(3)Before screening, by step(2)Gained granule
Aeration-drying 3 hours first at 165 DEG C, obtain dry granule, then carry out step again(3)Screening.
Pass through the granule that the screen cloth of -15 mesh of mesh~+20 sieves and be the functional agglomerate for improving polypropylene antistatic.
Embodiment 3:
A kind of functional agglomerate for improving polypropylene antistatic, is prepared from by the component of following weight portion:Vector resin 100
20 g of g, PA resin particle, 15 g of active oxidation aluminium powder, 15 g of clay, 15 g of magnesium chloride, dispersant are 0.7 g, coupling agent is
The preferred acrylic resin of 0.7 g, wherein vector resin, improves the compatibility of functional agglomerate and polypropylene material, and dispersant is preferred
Barium stearate, strengthens dispersion of the electric charge in polypropylene material while making each component dispersed, and coupling agent is preferably chelated
Type titanium esters acid coupling agent.
A kind of preparation method of the functional agglomerate for improving polypropylene antistatic, comprises the following steps:
(1)Each material component of weight portion is put in mixing and blending machine in 50 DEG C of stirring mixing 2 hours, mixing speed 400
r/min;
(2)Mixed material is put in double screw extruder, the mixing speed of holding double screw extruder is 200 r/min, double
The temperature range that each section of screw extruder is 160~210 DEG C, Jing after fully melting and be combined extrudes granulating;
(3)By step(2)Gained granule sieves through the screen cloth of -15 mesh of mesh~+20.
To obtain the functional agglomerate of better performances, step(2)The temperature control of each section of middle double screw extruder is respectively:One
Section 160~185 DEG C, 185~195 DEG C of two-stage nitration, three sections 195~200 DEG C, four sections 200~205 DEG C, five section 205~210
DEG C, six sections 200~205 DEG C, die head temperature be 200~205 DEG C.
To improve functional agglomerate surface texture uniformity coefficient, step is being carried out(3)Before screening, by step(2)Gained granule
Aeration-drying 2 hours first at 170 DEG C, obtain dry granule, then carry out step again(3)Screening.
Pass through the granule that the screen cloth of -15 mesh of mesh~+20 sieves and be the functional agglomerate for improving polypropylene antistatic.
The acrylic sheet sample of the functional agglomerate of embodiment 1,2,3 is added with respectively(Correspondence be respectively test specimens 1,2,
3)With commercially available acrylic sheet sample(Control sample)Test performance the results are shown in Table 1.Lamella thickness is 2 mm, wherein testing
Sample clean is placed in into temperature to put in 23 ± 2 DEG C, the dustfree environment that relative humidity is 50 ± 5% during surface resistivity after clean
Carry out after putting 24 hours.
1 test data of table
Test event | Testing standard | Test specimens 1 | Test specimens 2 | Test specimens 3 | Control sample |
Surface resistivity | —— | 9.1×1011Ω | 8.5×1011 Ω | 7.9×1011 Ω | > 1012 Ω |
Tensile strength | ASTM D638 | 24 MPa | 26 MPa | 23 MPa | 23 MPa |
Izod notched impact strength | GB/T 1843-2008 | 20.5 KJ/m2 | 19.0 KJ/m2 | 20.6 KJ/m2 | 19.3 KJ/m2 |
It is added with tensile strength, the Izod notched impact strength of the acrylic sheet sample of the functional agglomerate of embodiment 1,2,3
Compared with commercial polypropylene thin plate sample, change is obvious, but surface resistivity is decreased obviously, and with the addition of the poly- of functional agglomerate
The antistatic effect of propylene thin plate sample is obviously improved.
The functional agglomerate of the present invention combines the moistening degree of the high polypropylene material of water extraction, suppression by approach chemically or physically
The function that electrostatic processed is produced, while the excess charges disperseed in polypropylene material in time, so as to improve the anti-quiet of polypropylene material
Electric energy power.
Claims (6)
1. a kind of functional agglomerate for improving polypropylene antistatic, it is characterised in that be prepared from by the component of following weight portion:
80~100 parts of vector resin, 15~20 parts of PA resin particles, 10~15 parts of active oxidation aluminium powder, 10~15 parts of clay, magnesium chloride
10~15 parts, dispersant be 0.5~0.7 part, coupling agent be 0.5~0.7 part, wherein vector resin be acrylic resin.
2. a kind of functional agglomerate for improving polypropylene antistatic according to claim 1, it is characterised in that the dispersion
Agent is barium stearate.
3. a kind of functional agglomerate for improving polypropylene antistatic according to claim 1, it is characterised in that the coupling
Agent is chelating titanate coupling agent.
4. a kind of preparation method of the functional agglomerate for improving polypropylene antistatic as described in claims 1 to 3 is arbitrary, including
Following steps:
(1)Each material component of weight portion is put in mixing and blending machine in 40~50 DEG C of stirring mixing 1~2 hour, stirring speed
350~400 r/min of degree;
(2)Mixed material is put in double screw extruder, the mixing speed of holding double screw extruder is 150~200 r/
Min, the temperature range that each section of double screw extruder are 160~210 DEG C, Jing after fully melting and be combined extrude granulating;
(3)By step(2)Gained granule sieves through the screen cloth of -15 mesh of mesh~+20.
5. the preparation method of a kind of functional agglomerate for improving polypropylene antistatic according to claim 4, its feature exist
In step(2)The temperature control of each section of middle double screw extruder is respectively:One section 160~185 DEG C, 185~195 DEG C of two-stage nitration,
Three sections 195~200 DEG C, four sections 200~205 DEG C, five sections 205~210 DEG C, six sections 200~205 DEG C, die head temperature be 200
~205 DEG C.
6. the preparation method of a kind of functional agglomerate for improving polypropylene antistatic according to claim 4, its feature exist
In carrying out step(3)By step before screening granule(2)At 160~170 DEG C, aeration-drying 2~4 is little first for gained granule
When, obtain the granule of dry tack free.