CN106633221A - Super-wear-resistant high-load engineering solid tire natural rubber - Google Patents
Super-wear-resistant high-load engineering solid tire natural rubber Download PDFInfo
- Publication number
- CN106633221A CN106633221A CN201611071493.3A CN201611071493A CN106633221A CN 106633221 A CN106633221 A CN 106633221A CN 201611071493 A CN201611071493 A CN 201611071493A CN 106633221 A CN106633221 A CN 106633221A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- agent
- super
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides super-wear-resistant high-load engineering solid tire natural rubber. The super-wear-resistant high-load engineering solid tire natural rubber is prepared from the following components: 70 to 85 parts of natural rubber, 65 to 80 parts of cis-butadiene rubber, 50 to 60 parts of super-wear-resistant carbon black, 5 to 10 parts of aromatic hydrocarbon oil, 2 to 4 parts of zinc oxide, 1 part of stearic acid, 1 to 2 parts of an anti-aging agent, 1 to 2 parts of a homogenizing agent, 1.5 parts of sulfur, 2 to 4 parts of a vulcanizing agent, 5 to 10 parts of a wear-resistant agent and 1.5 parts of an accelerant. The wear-resistant property of the tire is improved by adding the super-wear-resistant carbon black and the wear-resistant agent, and the shearing force of the rubber can be effectively improved due to the homogenizing agent and the accelerant, so that the dispersion of the cis-butadiene rubber and the super-wear-resistant carbon black is facilitated, and besides, the compatibility of different kinds of rubber can be improved; and the tire made of the rubber meets the application in ports and piers, mines, smelting companies and the like.
Description
Technical field
The present invention relates to rubber for tire technical field, more particularly to a kind of super abrasive high capacity engineering solid tyre that makes
Natural gum.
Background technology
Tire is the main driver part of driving in automobile, and its anti-wear performance determines the service life of this tire, existing
Tire is easy to blow out in the case of an overload, has a strong impact on the life security of driver, and the abrasion of tire is larger,
Service life is caused to reduce, therefore, solve the problems, such as that this class is particularly important.
The content of the invention
For the deficiencies in the prior art, the invention provides a kind of super abrasive high capacity engineering solid tyre natural gum, adds
It is poor to solve the problems, such as existing tire wear effect plus super abrasive carbon black and anti-wear agent improve the anti-wear performance of tire.
In order to solve the above problems, the invention provides a kind of super abrasive high capacity engineering solid tyre natural gum, including
There is consisting of composition:Natural gum 70-85 parts, cis-butadiene cement 65-80 parts, super abrasive carbon black 50-60 parts, aromatic naphtha 5-10 parts, oxygen
Change zinc 2-4 parts, 1 part of stearic acid, age resistor 1-2 parts, homogenizing agent 1-2 parts, 1.5 parts of sulphur, vulcanizing agent 2-4 parts, anti-wear agent 5-10
Part, 1.5 parts of accelerator.
Further improvement is that:The formula is included:85 parts of natural gum, 80 parts of cis-butadiene cement, 60 parts of super abrasive carbon black, aromatic hydrocarbons
10 parts of oil, 4 parts of zinc oxide, 1 part of stearic acid, 2 parts of age resistor, 2 parts of homogenizing agent, 1.5 parts of sulphur, 4 parts of vulcanizing agent, anti-wear agent 10
Part, 1.5 parts of accelerator.
Further improvement is that:The cis-butadiene cement is BR9000 materials, and the homogenizing agent is by aliphatic hydrocarbon, aromatic hydrocarbon, phenolic aldehyde
Resin and Petropols composition are formed, and the accelerator is the N- tert-butyl group -2- benzene.
The invention has the beneficial effects as follows:The present invention improves the wearability of tire by adding super abrasive carbon black and anti-wear agent
Can, and homogenizing agent and accelerator can effectively improve the shearing force of sizing material, contribute to cis-butadiene cement and super abrasive carbon black point
Dissipate, while the compatibility of different glue kinds can be promoted, exceeded by 3.5 tons of weight the examination of road results of tyre load of present invention manufacture
Do not blow out within 12 hours, meet port and pier, mine, smelting company etc. and use.
Specific embodiment
In order to deepen the understanding of the present invention, the present invention is further described below in conjunction with embodiment, the present embodiment
It is only used for explaining the present invention, does not constitute limiting the scope of the present invention.
Embodiment one
A kind of super abrasive high capacity engineering solid tyre natural gum is present embodiments provided, the formula is included:85 parts of natural gum,
80 parts of cis-butadiene cement, 60 parts of super abrasive carbon black, 10 parts of aromatic naphtha, 4 parts of zinc oxide, 1 part of stearic acid, age resistor 2,2 parts of homogenizing agent, sulphur
1.5 parts of sulphur, 4 parts of vulcanizing agent, 10 parts of anti-wear agent, 1.5 parts of accelerator, add up to 261 parts.
Embodiment two
A kind of super abrasive high capacity engineering solid tyre natural gum is present embodiments provided, consisting of composition is included:It is natural
It is 70 parts of glue, 65 parts of cis-butadiene cement, 50 parts of super abrasive carbon black, 5 parts of aromatic naphtha, 2 parts of zinc oxide, 1 part of stearic acid, 1 part of age resistor, uniform
1 part of agent, 1 part of sulphur, 2 parts of vulcanizing agent, 5 parts of anti-wear agent, 1 part of accelerator, add up to 222 parts.
Embodiment three
A kind of super abrasive high capacity engineering solid tyre natural gum is present embodiments provided, consisting of composition is included:It is natural
80 parts of glue, 70 parts of cis-butadiene cement, 55 parts of super abrasive carbon black, 7 parts of aromatic naphtha, 3 parts of zinc oxide, 1 part of stearic acid, 1.5 parts of age resistor,
Even dose 1.5 parts, 1.5 parts of sulphur, 3 parts of vulcanizing agent, 7 parts of anti-wear agent, 1.5 parts of accelerator, add up to 232 parts.
The present invention improves the anti-wear performance of tire, and homogenizing agent and promotion by adding super abrasive carbon black and anti-wear agent
Agent can effectively improve the shearing force of sizing material, contribute to the dispersion of cis-butadiene cement and super abrasive carbon black, while difference can be promoted
The compatibility of glue kind, was not blown out by 3.5 tons of weight the examination of road results of tyre load of present invention manufacture more than 12 hours, met port
Mouth harbour, mine, smelting company etc. use.
Claims (3)
1. a kind of super abrasive high capacity engineering solid tyre natural gum, it is characterised in that include consisting of composition:Natural gum
It is 70-85 parts, cis-butadiene cement 65-80 parts, super abrasive carbon black 50-60 parts, aromatic naphtha 5-10 parts, zinc oxide 2-4 parts, 1 part of stearic acid, anti-
Old agent 1-2 parts, homogenizing agent 1-2 parts, 1.5 parts of sulphur, vulcanizing agent 2-4 parts, anti-wear agent 5-10 parts, 1.5 parts of accelerator.
2. a kind of super abrasive high capacity engineering solid tyre natural gum as claimed in claim 1, it is characterised in that:The formula bag
Include:It is 85 parts of natural gum, 80 parts of cis-butadiene cement, 60 parts of super abrasive carbon black, 10 parts of aromatic naphtha, 4 parts of zinc oxide, 1 part of stearic acid, anti-old
Agent 2,2 parts of homogenizing agent, 1.5 parts of sulphur, 4 parts of vulcanizing agent, 10 parts of anti-wear agent, 1.5 parts of accelerator.
3. claim 1 and 2 arbitrarily as described in a kind of super abrasive high capacity engineering solid tyre natural gum, it is characterised in that:
The cis-butadiene cement is BR9000 materials, and the homogenizing agent is made up of aliphatic hydrocarbon, aromatic hydrocarbon, phenolic resin and Petropols and is formed,
The accelerator is the N- tert-butyl group -2- benzene.