CN106630867A - Wood-like floor tile and preparation method thereof - Google Patents
Wood-like floor tile and preparation method thereof Download PDFInfo
- Publication number
- CN106630867A CN106630867A CN201611000170.5A CN201611000170A CN106630867A CN 106630867 A CN106630867 A CN 106630867A CN 201611000170 A CN201611000170 A CN 201611000170A CN 106630867 A CN106630867 A CN 106630867A
- Authority
- CN
- China
- Prior art keywords
- wood
- floor board
- quartz sand
- floor tile
- seaweed powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wood-like floor tile and a preparation method thereof. The main componnets of the wood-like floor tile are causticized white sludge, a seaweed powder solution, glass fiber, aluminosilicate cement, wood-like coating and quartz sand; the byproduct causticized white sludge in papermaking is used as the main raw material to prepare the wood-like floor tile, a large number of papermaking byproducts are recycled, the pollution is reduced, the cost is low, and the market competitiveness is strong; for enabling the floor tile produced by using the calcium carbonate matrix to be good in adhesive property and abrasion resistance, the micron-order quartz sand and the glass fiber are added as the aggregate, the seaweed powder and the aluminosilicate cement are added, the materials are pressed as a green tile under the high pressure in combination with own causticized white sludge with the alkali, and then a qualified wood-like floor tile can be formed by coating the wood-like painting.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of imitated wood floor board brick and preparation method thereof.
Background technology
With people's living environment continuous improvement with improve, requirement of the people to constructional ornamental material also increasingly compared with
It is high.And timber floor is used as the one kind in construction material, because it has, corrosion resistance is strong, heat insulation effect is substantially deep by people's
Like；And the making field of traditional timber floor is to make to form using wood, or formed using sawdust face pressure system, it is seen then that
The manufacturing process of the timber floor of both is to need to consume the substantial amounts of forest reserves, and then serious shadow will be caused to environment
Ring, cause ecology to be subjected to serious destruction.
China is pulping and paper-making big country, and at present using chemical pulp processes, chemical pulping (is divided into soda processes and sulphite
Method) it is exactly using various chemical agents, under given conditions by the most of lignin dissolution in plant fiber material being allowed to point
Dissipate into paper pulp.Soda processes are mainly used to produce some straw pulps, such as rice wheat straw, Chinese alpine rush, reed.Sulphite process is mainly used to
Production wood pulp, also has for bamboo pulp processed and straw pulp.No matter chemical pulp processes, will produce black liquor, in black liquor with which kind of raw material
It is one of severe contamination source of water body containing substantial amounts of salkali waste and organic matter.Domestic majority paper mill is not added with any process and just will
On the one hand black liquid discharging waste substantial amounts of alkali resource in the lake of river, another aspect severe contamination environment.Alkali collection is China
The first-selected measure of paper industry environmental improvement, it does not only have good economic benefit, and also good social benefit, to changing
Kind environment has very important function and significance.
China's paper industry is slurrying species with the essential distinction of European and American developed countries.Foreign countries based on wood pulp, China
Wood pulp, non-wood pulp (straw, wheat straw, Chinese alpine rush, reed etc. are raw material) paper technology about respectively account for 50%.Papermaking causticization clay-slag is
Refer to that the black liquor of pulp making that chemical pulping method-soda processes is produced is extracted, be concentrated by evaporation the alkali that forms solid content 50%～70% and have
Machine thing, then concentrate is placed in alkali recovery boiler burn, burning-off organic matter, and it is sodium carbonate and vulcanized sodium to obtain main component
Fused mass.Fused mass formation green liquor soluble in water, adds digestion lime, makes sodium carbonate be converted into hydroxide through causticization process
Sodium, calcium hydroxide forms precipitation of calcium carbonate.Suspension after causticization is clarified, washing, filter after filtrate recycle for making
Slurry, while the sediment calcium carbonate for obtaining is through concentration, vacuum dehydration formation-causticization clay-slag.
The content of the invention
Based on the technical problem that background technology is present, the present invention proposes a kind of imitated wood floor board brick and preparation method thereof.
Technical scheme is as follows：
A kind of imitated wood floor board brick, including following component：Causticization clay-slag, edible seaweed powder solution, glass fibre, aluminosilicate salt solution
Mud, imitation wood coating and quartz sand.
A kind of imitated wood floor board brick, including the composition of following percentage by weight:
Causticization clay-slag 60-75%
Edible seaweed powder solution 3-5%
Glass fibre 1-3%
Alumino-silicate cement 0.5-1%
Imitation wood coating 2-5%
Quartz sand surplus.
Preferably, the particle diameter of described quartz sand is 325 mesh.
Preferably, a diameter of 20-50 microns of the single fiber of described glass fibre.
A kind of preparation method of imitated wood floor board brick, comprises the following steps：
A, the drying under the conditions of 60-80 DEG C by causticization clay-slag, by its water content control in 5-8%, add alumino-silicate
Crush jointly after cement, cross 200 mesh sieves；
B, addition quartz sand, under the conditions of 600-800rpm, are stirred together for 25-35min；
C, addition edible seaweed amidin and glass fibre, regulation mixing speed is 200-300rpm, stirs 10-15min；
D, adobe is depressed in 80-100KN pressure using friction press, through being dried kiln drying after, by what is dried
Adobe one side is painted after imitation wood coating, 200-300 DEG C of sintering 0.5-1h；
After E, taking-up floor tile, side is polished, and corner is corrected, you can.
Preferably, described edible seaweed powder solution is prepared in using first 2 hours, and mass fraction of the edible seaweed powder in water is 8-
15%.
The invention has benefit that：The present invention is made using the accessory substance causticization clay-slag of papermaking as primary raw material
Standby imitated wood floor board brick, is not only reused substantial amounts of papermaking accessory substance, reduces pollution, and low cost, and market is competing
Strive power strong；The main component that causticization clay-slag is main problem is that in preparation process is calcium carbonate, how to make calcium carbonate-base
The floor tile that matter is generated possesses good adhesive property (being not pulverized easily) and scratch-resistant performance (durable), of the invention in order to overcome carbon
Original feature of sour calcium matrix, adds micron order quartz sand and glass fibre does aggregate and adds edible seaweed powder and aluminosilicate salt solution
Mud combines the causticization clay-slag inherently with alkalescence, adobe is pressed under high pressure, after coating imitation wood coating, you can become conjunction
The imitated wood floor board brick of lattice.
Specific embodiment
Embodiment 1：
A kind of imitated wood floor board brick, including the composition of following percentage by weight:
Causticization clay-slag 70%
Edible seaweed powder solution 4%
Glass fibre 2%
Alumino-silicate cement 0.8%
Imitation wood coating 2.2%
Quartz sand surplus.
The particle diameter of described quartz sand is 325 mesh.
The a diameter of 20-50 microns of single fiber of described glass fibre.
A kind of preparation method of imitated wood floor board brick, comprises the following steps：
A, the drying under the conditions of 70 DEG C by causticization clay-slag, by its water content control 6%, after adding alumino-silicate cement
It is common to crush, cross 200 mesh sieves；
B, addition quartz sand, under the conditions of 750rpm, are stirred together for 30min；
C, addition edible seaweed amidin and glass fibre, regulation mixing speed is 250rpm, stirs 12min；
D, adobe is depressed in 95KN pressure using friction press, through being dried kiln drying after, the adobe that will have been dried
One side is painted after imitation wood coating, 220 DEG C of sintering 0.8h；
After E, taking-up floor tile, side is polished, and corner is corrected, you can.
Described edible seaweed powder solution is prepared in using first 2 hours, and mass fraction of the edible seaweed powder in water is 12%.
Embodiment 2：
A kind of imitated wood floor board brick, including the composition of following percentage by weight:
Causticization clay-slag 75%
Edible seaweed powder solution 3%
Glass fibre 3%
Alumino-silicate cement 0.5%
Imitation wood coating 5%
Quartz sand surplus.
The particle diameter of described quartz sand is 325 mesh.
The a diameter of 20-50 microns of single fiber of described glass fibre.
A kind of preparation method of imitated wood floor board brick, comprises the following steps：
A, the drying under the conditions of 80 DEG C by causticization clay-slag, by its water content control 5%, after adding alumino-silicate cement
It is common to crush, cross 200 mesh sieves；
B, addition quartz sand, under the conditions of 800rpm, are stirred together for 25min；
C, addition edible seaweed amidin and glass fibre, regulation mixing speed is 300rpm, stirs 10min；
D, adobe is depressed in 100KN pressure using friction press, through being dried kiln drying after, the adobe that will have been dried
One side is painted after imitation wood coating, 200 DEG C of sintering 1h；
After E, taking-up floor tile, side is polished, and corner is corrected, you can.
Described edible seaweed powder solution is prepared in using first 2 hours, and mass fraction of the edible seaweed powder in water is 8%.
Embodiment 3：
A kind of imitated wood floor board brick, including the composition of following percentage by weight:
Causticization clay-slag 60%
Edible seaweed powder solution 5%
Glass fibre 1%
Alumino-silicate cement 1%
Imitation wood coating 2%
Quartz sand surplus.
The particle diameter of described quartz sand is 325 mesh.
The a diameter of 20-50 microns of single fiber of described glass fibre.
A kind of preparation method of imitated wood floor board brick, comprises the following steps：
A, the drying under the conditions of 60 DEG C by causticization clay-slag, by its water content control 8%, after adding alumino-silicate cement
It is common to crush, cross 200 mesh sieves；
B, addition quartz sand, under the conditions of 600rpm, are stirred together for 35min；
C, addition edible seaweed amidin and glass fibre, regulation mixing speed is 200rpm, stirs 15min；
D, adobe is depressed in 80KN pressure using friction press, through being dried kiln drying after, the adobe that will have been dried
One side is painted after imitation wood coating, 300 DEG C of sintering 0.5h；
After E, taking-up floor tile, side is polished, and corner is corrected, you can.
Described edible seaweed powder solution is prepared in using first 2 hours, and mass fraction of the edible seaweed powder in water is 15%.
Every physical property of the imitated wood floor board brick of embodiment of the present invention 1-3 is tested, following data are obtained：
This detection data is just for above-mentioned detection sample.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept equivalent or change in addition, all should be included within the scope of the present invention.
Claims (6)
1. a kind of imitated wood floor board brick, it is characterised in that including following component：Causticization clay-slag, edible seaweed powder solution, glass fibre,
Alumino-silicate cement, imitation wood coating and quartz sand.
2. imitated wood floor board brick as claimed in claim 1, it is characterised in that including the composition of following percentage by weight:
Causticization clay-slag 60-75%
Edible seaweed powder solution 3-5%
Glass fibre 1-3%
Alumino-silicate cement 0.5-1%
Imitation wood coating 2-5%
Quartz sand surplus.
3. imitated wood floor board brick as claimed in claim 2, it is characterised in that the particle diameter of described quartz sand is 325 mesh.
4. imitated wood floor board brick as claimed in claim 2, it is characterised in that a diameter of 20-50 microns of single fiber of glass fibre.
5. a kind of preparation method of imitated wood floor board brick, it is characterised in that comprise the following steps：
A, the drying under the conditions of 60-80 DEG C by causticization clay-slag, by its water content control in 5-8%, after adding alumino-silicate cement
It is common to crush, cross 200 mesh sieves；
B, addition quartz sand, under the conditions of 600-800rpm, are stirred together for 25-35min；
C, addition edible seaweed amidin and glass fibre, regulation mixing speed is 200-300rpm, stirs 10-15min；
D, adobe is depressed in 80-100KN pressure using friction press, through being dried kiln drying after, the adobe that will have been dried
One side is painted after imitation wood coating, 200-300 DEG C of sintering 0.5-1h；
After E, taking-up floor tile, side is polished, and corner is corrected, you can.
6. the preparation method of imitated wood floor board brick as claimed in claim 6, it is characterised in that described edible seaweed powder solution is being used
Prepare in first 2 hours, mass fraction of the edible seaweed powder in water is 8-15%.