CN106624613A - Adhesive honeycomb core preparation process - Google Patents
Adhesive honeycomb core preparation process Download PDFInfo
- Publication number
- CN106624613A CN106624613A CN201610873005.4A CN201610873005A CN106624613A CN 106624613 A CN106624613 A CN 106624613A CN 201610873005 A CN201610873005 A CN 201610873005A CN 106624613 A CN106624613 A CN 106624613A
- Authority
- CN
- China
- Prior art keywords
- honeycomb core
- gluing
- core preparation
- aluminium foil
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive honeycomb core preparation process, which comprises the following operation steps of (1) preparing a clean aluminum foil, and laminating; (2) hot press molding the laminated aluminum foil; and (3) saw cutting, and stretching to obtain a target product. According to the adhesive honeycomb core preparation process provided by the invention, in order to overcome the defect existed in operation of an existing process with full coverage of an adhesion agent during an adhesive coating process, 1/5 to 1/4 of positions are coated on the left side and the right side of an adhesion position, so that on one hand, a prepared honeycomb core can be ensured to have a favorable use performance, and on the other hand, the preparation cost is reduced, and the emission of hazardous substances is reduced.
Description
Technical field
The present invention relates to a kind of preparation method of honeycomb core, more particularly to a kind of gluing honeycomb core preparation technology.
Background technology
Cellular board is because lightweight, specific strength is high, rigidity is big, good stability, heat-and sound-insulating and pollution-free etc. a series of
Advantage, is used widely in the fields such as Aero-Space, aircraft, train, ship, building.It is common both at home and abroad at present
Either core itself is still compound between panel and core for cellular board, is adhesive means, in adjacent two plates
Bonding part fills binding agent, plays a part of connection.This connected mode is adopted at present, and the usage amount of binding agent is larger, while
The pollution for causing is also than more serious.
The defect for existing is prepared in view of above-mentioned existing honeycomb core, the present inventor manufactures based on such product design is engaged in
Abundant for many years practical experience and professional knowledge, and coordinate the utilization of scientific principle, actively in addition research and innovation, a kind of new to founding
The gluing honeycomb core preparation technology of type so as to more practicality.Through constantly research, design, and Jing study repeatedly sample and
After improvement, the present invention having practical value is created finally.
The content of the invention
Present invention is primarily targeted at, overcome existing honeycomb core to prepare the defect for existing, and a kind of Novel glue is provided
Viscous honeycomb core preparation technology, reduces cost reduces pollution, thus more suitable for practicality, and with the value in industry.
The object of the invention to solve the technical problems employs the following technical solutions to realize.According to present invention proposition
Gluing honeycomb core preparation technology, including following operating procedure,
Step one, prepares the aluminium foil of cleaning, and lamination；
Step 2, it is hot-forming to the aluminium foil of lamination；
Step 3, sawing, stretch processing, obtains target product.
Further, aforesaid gluing honeycomb core preparation technology, the thickness of the aluminium foil is 0.05 ~ 0.5mm.
For the effect for ensureing to clean, the aluminium foil for cleaning is obtained, can be selected to carrying out to aluminium foil first in step one
Lead is cleaned, and then carries out pickling or alkali cleaning, finally carries out steam purge, obtains the aluminium foil for cleaning.
Further, aforesaid gluing honeycomb core preparation technology, it is hot-forming in the step 2 to be preheated before,
Preheating temperature is 100 ~ 300 DEG C.
Further, aforesaid gluing honeycomb core preparation technology, it is hot-forming in the step 2 to carry out gluing before
Process, the position of gluing takes and is connected the 1/5 ~ 1/4 of the position left and right sides.
By above-mentioned technical proposal, the gluing honeycomb core preparation technology of the present invention at least has following advantages：
Gluing honeycomb core preparation technology proposed by the present invention, in order to overcome existing process to fill binding agent during gluing
The defect that operation is present, in the bonding position left and right sides 1/5 ~ 1/4 position is applied respectively, on the one hand ensure that the honeycomb of preparation
Core has good performance, on the other hand reduces preparation cost, the less discharge of harmful substance.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, described in detail as after with presently preferred embodiments of the present invention below.
Description of the drawings
Fig. 1 is preparation technology flow chart of the present invention；
Fig. 2 is traditional handicraft glue sites schematic diagram；
Fig. 3 is gluing schematic diagram of the present invention；
Connotation is marked in figure：1.Glue sites.
Specific embodiment
Further to illustrate the present invention to reach technological means and effect that predetermined goal of the invention is taken, to according to this
Gluing its specific embodiment of honeycomb core preparation technology, feature and its effect that invention is proposed, describe in detail as after.
Embodiment 1
The gluing honeycomb core preparation technology of the present invention, including following operating procedure,
Step one, preparation needs the aluminium foil of quantity, and the thickness of aluminium foil is 0.05mm or so, and to aluminium foil surface cleaning is carried out, and is obtained
Lamination behind the surface of cleaning；Steam is cleaned, and obtains the aluminium foil for cleaning.
Step 2, to needing hot-forming position to smear binding agent in the aluminium foil of lamination, using commercially available binding agent material
Material, the position that wherein binding agent is smeared takes and is connected the 1/5 of the position left and right sides, it is hot-forming before under the conditions of 150 DEG C
Insulation 4h.
Step 3, carries out stretch processing, and cutting and corresponding later stage process is carried out after cooling, and target product is obtained after sizing
Thing.
Embodiment 2
The gluing honeycomb core preparation technology of the present invention, including following operating procedure,
Step one, preparation needs the aluminium foil of quantity, and the thickness of aluminium foil is 0.15mm or so, and to aluminium foil surface cleaning is carried out, and is obtained
Lamination behind the surface of cleaning；Preferred cleaning mode, including the alkali cleaning of early stage, are finally cleaned with vapor, are cleaned
Aluminium foil.
Step 2, to needing hot-forming position to smear binding agent in the aluminium foil of lamination, using commercially available binding agent material
Material, the position that wherein binding agent is smeared takes and is connected the 1/5 of the position left and right sides, it is hot-forming before under the conditions of 250 DEG C
Insulation 3h.
Step 3, carries out stretch processing, and cutting and corresponding later stage process is carried out after cooling, and target product is obtained after sizing
Thing.
Embodiment 3
The gluing honeycomb core preparation technology of the present invention, including following operating procedure,
Step one, preparation needs the aluminium foil of quantity, and the thickness of aluminium foil is 0.25mm or so, and to aluminium foil surface cleaning is carried out, and is obtained
Lamination behind the surface of cleaning；Used as preferred mode, specific cleaning includes alkali cleaning, is finally cleaned with vapor, obtains
The aluminium foil of cleaning.
Step 2, to needing hot-forming position to smear binding agent in the aluminium foil of lamination, using commercially available binding agent material
Material, the position that wherein binding agent is smeared takes and is connected the 1/4 of the position left and right sides, it is hot-forming before under the conditions of 220 DEG C
Insulation 2.5h.
Step 3, carries out stretch processing, and cutting and corresponding later stage process is carried out after cooling, and target product is obtained after sizing
Thing.
Using preparation technology of the present invention prepare honeycomb core, under equal conditions, than traditional handicraft save preparation cost 8 ~
15% or so, reduce environmental pollution and the discharge of harmful components.
The above, is only presently preferred embodiments of the present invention, and any pro forma restriction is not made to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, in the range of without departing from technical solution of the present invention, when making a little change or modification using the technology contents of the disclosure above
For the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention
Any simple modification, equivalent variations and the modification made to above example, still falls within the range of technical solution of the present invention.
Claims (4)
1. a kind of gluing honeycomb core preparation technology, it is characterised in that：Including following operating procedure,
Step one, prepares the aluminium foil of cleaning, and lamination；
Step 2, it is hot-forming to the aluminium foil of lamination；
Step 3, sawing, stretch processing, obtains target product.
2. gluing honeycomb core preparation technology according to claim 1, it is characterised in that：The thickness of the aluminium foil be 0.05 ~
0.5mm。
3. gluing honeycomb core preparation technology according to claim 1, it is characterised in that：In the step 2 it is hot-forming it
Before preheated, preheating temperature be 100 ~ 300 DEG C.
4. gluing honeycomb core preparation technology according to claim 1, it is characterised in that：In the step 2 it is hot-forming it
Before carry out gluing process, the position of gluing takes and is connected the 1/5 ~ 1/4 of the position left and right sides.