CN106621165A - 一种低温s型气溶胶灭火剂 - Google Patents

一种低温s型气溶胶灭火剂 Download PDF

Info

Publication number
CN106621165A
CN106621165A CN201610825471.5A CN201610825471A CN106621165A CN 106621165 A CN106621165 A CN 106621165A CN 201610825471 A CN201610825471 A CN 201610825471A CN 106621165 A CN106621165 A CN 106621165A
Authority
CN
China
Prior art keywords
fire extinguishing
agent
temperature
extinguishing agent
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610825471.5A
Other languages
English (en)
Other versions
CN106621165B (zh
Inventor
黄寅生
葛梦珠
王俊杰
张冬冬
郑红波
沈东�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing University of Science and Technology
Original Assignee
Nanjing University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing University of Science and Technology filed Critical Nanjing University of Science and Technology
Priority to CN201610825471.5A priority Critical patent/CN106621165B/zh
Publication of CN106621165A publication Critical patent/CN106621165A/zh
Application granted granted Critical
Publication of CN106621165B publication Critical patent/CN106621165B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种低温S型气溶胶灭火剂，采用氧化剂、还原剂、粘合剂、性能调节剂组成，氧化剂采用硝酸锶为主、硝酸钾为辅，还原剂采用双氰胺，粘合剂采用酚醛树脂，调节剂选用草酸钾、镁粉、六次甲基四胺。本发明的灭火剂保证燃烧产物腐蚀性能降低的同时，又能保证良好的灭火效能，灭火效能达35g/m3，远低于国标用量。本发明的灭火剂具有优异的绝缘性能，可以有效保护燃烧区域的精密设备及文件。灭火剂反应温度在600℃左右，缩短灭火时间的同时，大大降低了现场设备的二次燃烧的可能性，适用于汽车发动机舱、飞机燃料舱、配电柜、电气设备、档案馆等环境。

Description

一种低温S型气溶胶灭火剂
技术领域
本发明涉及一种低温S型气溶胶灭火剂，属于消防灭火领域。
背景技术
气溶胶灭火剂具有灭火效率高，成本低廉，对大气臭氧层没有破坏作用，在空气存留时间短，无污染的优点，应用广泛。现有技术常使用高氯酸盐作为氧化剂，这种物质有毒，对人体和环境均有一定的损伤(查理斯·丁·吉伯特.固体微粒气溶胶灭火剂[J].国际消防.)。以硝酸钾为主要氧化剂的气溶胶，灭火效能很好，但是由于产物中氧化钾极易吸收空气中的水分发生潮解，会腐蚀保护区域的设备和文件，严重的话会导致设备报废，造成巨大的经济损失(马剑.钾盐型气溶胶灭火剂弥漫性及二次损害性研究[J].消防科学与技术.)。此外，现有的以硝酸钾为主要氧化剂的气溶胶还存在燃烧温度过高的问题，烟火药的燃烧温度过高会引起二次燃烧，对灭火效能产生很大影响(朱静丽.可燃剂对气溶胶灭火剂燃烧温度的影响[J].消防科学与技术)。
发明内容
本发明的目的在于提供一种低温S型气溶胶灭火剂，该灭火剂不仅灭火效果好，节能无污染，成本低廉，而且燃烧温度低，能避免设备和文件的二次燃烧，另外燃烧产物对电气设备无腐蚀和损坏。
实现上述目的的技术方案如下：
一种低温S型气溶胶灭火剂，采用氧化剂、还原剂、粘合剂、性能调节剂组成，氧化剂采用硝酸锶为主、硝酸钾为辅，还原剂采用双氰胺，粘合剂采用酚醛树脂，调节剂选用草酸钾、镁粉、六次甲基四胺，按质量份数计，由以下组份组成：
硝酸锶40～55份，硝酸钾20～30份，双氰胺20～30份，酚醛树脂3～8份，草酸钾1～5份，镁粉1～4份，六次甲基四胺1～3份。
优选地，所述的低温S型气溶胶灭火剂中，硝酸锶40～45份，硝酸钾22～27份，双氰胺23～30份，酚醛树脂5～7份，草酸钾2～4份，镁粉2～3份，六次甲基四胺2～3份。
本发明的灭火剂中，六次甲基四胺能够吸收气溶胶灭火剂燃烧时产生的氮氧化物，对气溶胶灭火剂产物进行消毒净化；镁粉能够控制气溶胶灭火剂的燃烧速度，使其稳定燃烧；草酸钾、草酸镁能够降低气溶胶灭火剂燃烧温度，防止温度过高。
与现有技术相比，本发明具有以下优点：
本发明以硝酸锶为主硝酸钾为辅的氧化剂，调节硝酸锶和硝酸钾的比例，制得的灭火剂保证燃烧产物腐蚀性能降低的同时，又能保证良好的灭火效能，灭火效能35g/m3，远低于国标用量；本发明的灭火剂具有优异的绝缘性能，可以有效保护燃烧区域的精密设备及文件；灭火剂反应温度在600℃左右，缩短灭火时间的同时，大大降低了现场设备的二次燃烧的可能性，适用于汽车发动机舱、飞机燃料舱、配电柜、电气设备、档案馆等环境。
附图说明
图1为实施例4的低温S型气溶胶灭火剂预燃实验结果图。
图2为实施例4的低温S型气溶胶灭火剂的红外测温图。
具体实施方式
本发明实施例中灭火时间是通过摄像机拍摄，后经过图片转换器转换后计算得到。
实施例中的腐蚀性测试实验如下：将去掉氧化膜的铜板和铝板(100mm*50mm*1mm)放入表面皿中，并将表面皿对角放入气溶胶收集箱(50mm*50mm*50mm)底部。在温度23℃相对湿度55％下进行测试。将反应器放入气溶胶收集箱内。用起爆器做电源引燃试样，释放气溶胶，在试样燃烧结束30min后取出。放入温度30℃、相对湿度85％的恒温恒湿箱中，保持48h，以便观察气溶胶沉积物对金属片的腐蚀情况，最后通过去除表面锈蚀物来计算铜片和铝片的腐蚀失重。
实施例中的绝缘性测试实验如下：将干燥后的PVC试板(100mm*100mm*1mm)平放在培养皿中，然后将培养皿放于气溶胶收集箱(50mm*50mm*50mm)内距离地面100mm，距离相邻强50mm。在温度23℃相对湿度55％下进行测试。用起爆器做电源引燃试样，释放气溶胶，在试样燃烧结束30min后取出。放入温度35℃、相对湿度90％的恒温恒湿箱中，保持30min，取出后用上海西利光ZC25-3兆欧表(500V)进行测量电阻(两电极间距离10mm)。
下面结合实施例和附图对本发明作进一步详述。
实施例1
按下述质量份数称取各组成成分：
硝酸锶 45
硝酸钾 20
双氰胺 23
酚醛树脂 3
草酸钾 2
六次甲基四胺 4
镁粉 2
称取5g配方在0.15m3进行灭火实验，灭火时间39s，灭火效能33.33g/m3。对燃烧产物进行腐蚀性测试，铜片失重率0.354％、铝片失重率0.859％，绝缘性测试结果120MΩ。
实施例2
按下述质量份数称取各组成成分：
硝酸锶 43
硝酸钾 22
双氰胺 26
酚醛树脂 5
草酸钾 4
六次甲基四胺 2
镁粉 3
称取5g配方在0.15m3进行灭火实验，灭火时间41s，灭火效能33.33g/m3。对燃烧产物进行腐蚀性测试，铜片失重率0.209％、铝片失重率0.41％，绝缘性测试结果120MΩ。
实施例3
按下述质量份数称取各组成成分：
硝酸锶 55
硝酸钾 30
双氰胺 20
酚醛树脂 7
草酸钾 5
六次甲基四胺 3
镁粉 1
称取5g配方在0.15m3进行灭火实验，灭火时间34s，灭火效能33.33g/m3。对燃烧产物进行腐蚀性测试，铜片失重率0.241％、铝片失重率0.422％，绝缘性测试结果122MΩ。
实施例4
按下述质量份数称取各组成成分：
硝酸锶 40
硝酸钾 27
双氰胺 26
酚醛树脂 8
草酸钾 1
六次甲基四胺 1
镁粉 1
称取5g配方在0.15m3进行灭火实验，灭火时间29s，灭火效能33.33g/m3。对燃烧产物进行腐蚀性测试，铜片失重率0.059％、铝片失重率0.307％，,绝缘性测试结果125MΩ。
图1为低温S型气溶胶灭火剂预燃实验，可以看出燃烧产烟量很大。图2为低温S型气溶胶灭火剂的红外测温图，可以看出，整个燃烧过程的最高温度595℃远低于现有技术报道的燃烧温度。综上可知，本发明的灭火剂在保证燃烧产物腐蚀性能降低的同时，又具有良好的灭火效能，灭火效能达35g/m3，远低于国标用量。此外本发明的灭火剂具有优异的绝缘性能，可以有效保护燃烧区域的精密设备及文件。灭火剂反应温度在600℃左右，缩短灭火时间的同时，大大降低了现场设备的二次燃烧的可能性，适用于汽车发动机舱、飞机燃料舱、配电柜、电气设备、档案馆等环境。

Claims (2)

1.一种低温S型气溶胶灭火剂，其特征在于，按质量份数计，由以下组份组成：硝酸锶40～55份，硝酸钾20～30份，双氰胺20～30份，酚醛树脂3～8份，草酸钾1～5份，镁粉1～4份，六次甲基四胺1～3份。
2.根据权利要求1所述的低温S型气溶胶灭火剂，其特征在于，硝酸锶40～45份，硝酸钾22～27份，双氰胺23～30份，酚醛树脂5～7份，草酸钾2～4份，镁粉2～3份，六次甲基四胺2～3份。
CN201610825471.5A 2016-09-14 2016-09-14 一种低温s型气溶胶灭火剂 Active CN106621165B (zh)