CN106602799A - Processing method for three-phase asynchronous motor terminal welding - Google Patents
Processing method for three-phase asynchronous motor terminal welding Download PDFInfo
- Publication number
- CN106602799A CN106602799A CN201510678462.3A CN201510678462A CN106602799A CN 106602799 A CN106602799 A CN 106602799A CN 201510678462 A CN201510678462 A CN 201510678462A CN 106602799 A CN106602799 A CN 106602799A
- Authority
- CN
- China
- Prior art keywords
- lead wire
- wire
- cloth
- copper wire
- wiring terminal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a processing method for three-phase asynchronous motor terminal welding. The method comprises: step (a), tools and materials are prepared; to be specific, a heat gun, a welding stand, a tin wire, a wiring terminal and a piece of cloth are prepared; step (b), a lead wire is protected by the cloth to ensure correct and proper protection and avoid the potential quality hazard, wherein the copper wire length allowance of the lead wire is controlled to be 8mm to 11mm; step (c), the end portion of the lead wire is coated with a soldering paste, the wiring terminal sleeves the processed end portion, and the to-be-welded lead wire is coated by a piece of slightly wet cloth, so that any burning or damage of the lead wire can be prevented; and step (d), the wiring terminal and the lead wire copper wire are heated locally; when the copper wire in the wiring terminal becomes red, the tin wire is added and thus heat is transferred to the tin wire to enable the tin wire to be heated and melted, so that a weld joint is filled. And the appearance is required to be plumb and flat without any missing and weld beading. With the method provided by the invention, raw materials can be saved; the efficiency can be improved; the overall appearance is beautiful and consistent; and the quality problem is solved during the application process of the method.
Description
Technical field
The invention belongs to stator coil fixed network, is related to a kind of processing method of Terminal of motor welding.
Background technology
The connection of existing threephase asynchronous terminal it is critical that a step, as the development people of society also have higher requirement to the outward appearance of motor.Conventional terminal is connected to and manufactures with place of method for subsequent processing often Shortcomings, causes binding post to there is appearance poor, and the problem of short life.
The content of the invention
It is an object of the invention to overcome above-mentioned weak point of the prior art and provide that a kind of outward appearance is good, the processing method of life-span length solder terminal.
The processing method of the solder terminal that the present invention is provided, it is characterised in that below scheme:
a), preparation tool and material:Heat gun, welding stage, solder stick, binding post, cloth;
b), by lead wire cloth protection get up, with guarantee protection in place, massless hidden danger, lead wire copper wire length surplus control between 8mm-11mm;
c), lead wire end is smeared solder(ing) paste, cover upper connecting terminal, encase lead wire to be welded with micro- wet cloth, in case which is produced and being burnt and being damaged;
d), by binding post and lead wire copper wire local heating, when copper wire takes on a red color in binding post, add solder stick, allow its heat pass to solder stick make its heating fusing, fill weld seam.Shape requirement reaches full, smooth, exhaustive, without overlap.
The outward appearance class of solder terminal can be effectively improved using the present invention, the quality of solder terminal is improved.
Specific embodiment
A kind of processing method of threephase asynchronous terminal welding, it is characterised in that below scheme:
a), preparation tool and material:Heat gun, welding stage, solder stick, binding post, cloth;
b), by lead wire cloth protection get up, with guarantee protection in place, massless hidden danger, lead wire copper wire length surplus control between 8mm-11mm;
c), lead wire end is smeared solder(ing) paste, cover upper connecting terminal, encase lead wire to be welded with micro- wet cloth, in case which is produced and being burnt and being damaged;
d), by binding post and lead wire copper wire local heating, when copper wire takes on a red color in binding post, add solder stick, allow its heat pass to solder stick make its heating fusing, fill weld seam.Shape requirement reaches full, smooth, exhaustive, without overlap.
It should be noted that, above example is only to illustrate technical scheme and unrestricted, although being described in detail to the present invention with reference to above-described embodiment, still technical scheme can be modified or equivalent, without deviating from the spirit and scope of technical solution of the present invention, all should cover in the middle of scope of the presently claimed invention.
Claims (1)
1. a kind of processing method that threephase asynchronous terminal is welded, it is characterised in that below scheme:
a), preparation tool and material:Heat gun, welding stage, solder stick, binding post, cloth;
b), by lead wire cloth protection get up, with guarantee protection in place, massless hidden danger, lead wire copper wire length surplus control between 8mm-11mm;
c), lead wire end is smeared solder(ing) paste, cover upper connecting terminal, encase lead wire to be welded with micro- wet cloth, in case which is produced and being burnt and being damaged;
d), by binding post and lead wire copper wire local heating, when copper wire takes on a red color in binding post, add solder stick, allow its heat to pass to solder stick and make its heating fusing, fill weld seam, shape requirement reaches full, smooth, exhaustive, without overlap.