CN106590039A - 一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法 - Google Patents

一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法 Download PDF

Info

Publication number
CN106590039A
CN106590039A CN201610911411.5A CN201610911411A CN106590039A CN 106590039 A CN106590039 A CN 106590039A CN 201610911411 A CN201610911411 A CN 201610911411A CN 106590039 A CN106590039 A CN 106590039A
Authority
CN
China
Prior art keywords
calcium carbonate
parts
aluminate
inorganic filler
titanium dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610911411.5A
Other languages
English (en)
Inventor
陈永忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Original Assignee
QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd filed Critical QINGYANG HENGYUAN CHEMICAL MATERIALS Co Ltd
Priority to CN201610911411.5A priority Critical patent/CN106590039A/zh
Publication of CN106590039A publication Critical patent/CN106590039A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下重量份的原料制成：铝酸酯2‑4，氧化钙40‑50，环糊精1‑3，CO2适量，乙酰丙酮5‑10，硬脂酸钠6‑12，钛酸丁酯15‑25，凹凸棒土1‑2，聚乙烯树脂25‑35，二甲基硅油8‑12，去离子水200‑250。本发明利用二氧化钛和聚乙烯树脂对碳酸钙粉体进行双重包覆，不仅增强了碳酸钙粉体的耐酸度、白度和耐火性能，同时改善了其与有机基底的融合性，使其满足更广泛的应用要求；铝酸酯起到锚接颗粒包覆粉体作用，提高产品的韧性与刚性。

Description

一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备 方法
技术领域
本发明涉及一种复合改性碳酸钙粉体及其制备，尤其涉及一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法。
背景技术
碳酸钙（包括重钙和轻钙）具有原料易得，价格低廉，稳定性好，色泽单纯，无毒等诸多优点，而被广泛用于塑料，橡胶，造纸，油墨，建材，电线电缆等领域，成为用量最大的填充材料。但由于碳酸钙属无机粉体，粒子表面是亲水疏油的，呈强极性，在有机介质中难以分散均匀，与基材之间结合力低，在受外力冲击时，易造成界面缺陷，导致材料性能下降。纳米级的碳酸钙粉末，表面能高，吸附作用越强，粒子互相团聚，无法在聚合物基体中很好分散，从而影响其使用的实际效果。因此，只有对碳酸钙进行改性才能获得高性能且满足实际应用的功能性改性填充专用料。
梁锦在其硕士学位论文《纳米碳酸钙的制备与表面改性研究》中，利用碳化法制备了纳米碳酸钙，并用硬脂酸钠对其进行改性，但是当碳酸钙作为塑料、涂料等填料时，还存在着耐酸度不佳，与有机基底的融合性欠缺等缺点。
发明内容
基于以上的思考，本发明旨在提供一种复合改性碳酸钙无机填料及其制备方法，用以解决当碳酸钙作为塑料、涂料等填料时，存在的耐酸度不佳，与有机基底的融合性欠缺等缺点。
本发明所要解决的技术问题采用以下的技术方案来实现 ：
一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下重量份的原料制成：
铝酸酯2-4，氧化钙40-50，环糊精1-3，CO2适量，乙酰丙酮5-10，硬脂酸钠6-12，钛酸丁酯15-25，凹凸棒土1-2，聚乙烯树脂25-35，二甲基硅油8-12，去离子水200-250。
所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下步骤制成：
a. 将氧化钙固体粉碎成粉末状，加入去离子水，60-100℃下搅拌反应2-3h，反应后的浆液陈化1-3h后，将浆液转入到碳化反应釜中，CO2和空气通过转子流量计计量后混合，通入碳化反应釜底部的气体分布器；当 pH＜7 时，结束反应，得碳酸钙浆液；
b. 70-90℃下，向步骤a所得碳酸钙浆液中加入环糊精、凹凸棒土、乙酰丙酮、硬脂酸钠，在研磨机中研磨搅拌均匀后，边研磨边缓慢滴加钛酸丁酯，结束后继续研磨0.5-1h，钛酸丁酯在乙酰丙酮的作用下，水解生成二氧化钛微粒，并在硬脂酸钠、环糊精、凹凸棒土的作用下，包覆在碳酸钙颗粒表面；对已包覆二氧化钛微粒的碳酸钙进行过滤，烘干，然后粉碎，得包覆二氧化钛的混合物；
c. 将步骤b所得混合物投入高速混料机中，加入铝酸酯、聚乙烯树脂、二甲基硅油，搅拌升温至90-110℃，保温搅拌10-30min后，经双螺杆挤出机挤出造粒即可。
所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，步骤a中CO2流量为0.04-0.40L/g(CaO)·min，反应温度为15-45℃。
本发明的有益效果是：钛酸丁酯在乙酰丙酮的作用下，水解生成二氧化钛微粒，并在硬脂酸钠的活化作用下，包覆在碳酸钙颗粒表面，增强了碳酸钙粉体的耐酸度、白度和耐火性能，使其满足更广泛的应用要求；之后再用聚乙烯对包覆二氧化钛的碳酸钙粉体进行再次包覆，将所得粉体亲水的特性转变为亲油性，促进了其与有机基底的融合，使所得碳酸钙粉体能更好的应用到塑料、涂料等领域；其间加入的二甲基硅油，防止碳酸钙之间的团聚，同时促进了碳酸钙在聚乙烯树脂中的分散，使其包裹的更加均匀；铝酸酯等起到锚接颗粒包覆粉体作用，提高产品的韧性与刚性。
具体实施方式
下面结合实施例， 对本发明的具体实施方式作进一步描述。
实施例
一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下重量份的原料制成：
铝酸酯4，氧化钙50，环糊精3，CO2适量，乙酰丙酮10，硬脂酸钠12，钛酸丁酯25，凹凸棒土2，聚乙烯树脂35，二甲基硅油12，去离子水250。
所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下步骤制成：
a. 将氧化钙固体粉碎成粉末状，加入去离子水，60-100℃下搅拌反应2-3h，反应后的浆液陈化1-3h后，将浆液转入到碳化反应釜中，CO2和空气通过转子流量计计量后混合，通入碳化反应釜底部的气体分布器；当 pH＜7 时，结束反应，得碳酸钙浆液；
b. 70-90℃下，向步骤a所得碳酸钙浆液中加入环糊精、凹凸棒土、乙酰丙酮、硬脂酸钠，在研磨机中研磨搅拌均匀后，边研磨边缓慢滴加钛酸丁酯，结束后继续研磨0.5-1h，钛酸丁酯在乙酰丙酮的作用下，水解生成二氧化钛微粒，并在硬脂酸钠、环糊精、凹凸棒土的作用下，包覆在碳酸钙颗粒表面；对已包覆二氧化钛微粒的碳酸钙进行过滤，烘干，然后粉碎，得包覆二氧化钛的混合物；
c. 将步骤b所得混合物投入高速混料机中，加入铝酸酯、聚乙烯树脂、二甲基硅油，搅拌升温至90-110℃，保温搅拌10-30min后，经双螺杆挤出机挤出造粒即可。
所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，步骤a中CO2流量为0.04-0.40L/g(CaO)·min，反应温度为15-45℃。
本发明的技术参数为：活化度≥90%；吸油值≥0.25mL/g。

Claims (3)

1.一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下重量份的原料制成：
铝酸酯2-4，氧化钙40-50，环糊精1-3，CO2适量，乙酰丙酮5-10，硬脂酸钠6-12，钛酸丁酯15-25，凹凸棒土1-2，聚乙烯树脂25-35，二甲基硅油8-12，去离子水200-250。
2.根据权利要求1所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，由以下步骤制成：
a. 将氧化钙固体粉碎成粉末状，加入去离子水，60-100℃下搅拌反应2-3h，反应后的浆液陈化1-3h后，将浆液转入到碳化反应釜中，CO2和空气通过转子流量计计量后混合，通入碳化反应釜底部的气体分布器；当 pH＜7 时，结束反应，得碳酸钙浆液；
b. 70-90℃下，向步骤a所得碳酸钙浆液中加入环糊精、凹凸棒土、乙酰丙酮、硬脂酸钠，在研磨机中研磨搅拌均匀后，边研磨边缓慢滴加钛酸丁酯，结束后继续研磨0.5-1h，钛酸丁酯在乙酰丙酮的作用下，水解生成二氧化钛微粒，并在硬脂酸钠、环糊精、凹凸棒土的作用下，包覆在碳酸钙颗粒表面；对已包覆二氧化钛微粒的碳酸钙进行过滤，烘干，然后粉碎，得包覆二氧化钛的混合物；
c. 将步骤b所得混合物投入高速混料机中，加入铝酸酯、聚乙烯树脂、二甲基硅油，搅拌升温至90-110℃，保温搅拌10-30min后，经双螺杆挤出机挤出造粒即可。
3.根据权利要求2所述的一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法，其特征在于，步骤a中CO2流量为0.04-0.40L/g(CaO)·min，反应温度为15-45℃。
CN201610911411.5A 2016-10-20 2016-10-20 一种含铝酸酯的、二氧化钛包覆碳酸钙无机填料及其制备方法 Pending CN106590039A (zh)