CN106587904A - 隔热涂料及其制备方法 - Google Patents

隔热涂料及其制备方法 Download PDF

Info

Publication number
CN106587904A
CN106587904A CN201611030603.1A CN201611030603A CN106587904A CN 106587904 A CN106587904 A CN 106587904A CN 201611030603 A CN201611030603 A CN 201611030603A CN 106587904 A CN106587904 A CN 106587904A
Authority
CN
China
Prior art keywords
parts
preparation
minutes
blender
revs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611030603.1A
Other languages
English (en)
Inventor
赖禄波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201611030603.1A priority Critical patent/CN106587904A/zh
Publication of CN106587904A publication Critical patent/CN106587904A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种隔热涂料及其制备方法，涉及涂料技术领域，由以下重量份的原材料制成：空心玻璃微珠30份~40份，滑石粉20份~30份，纳米金属氧化物8份~16份，水18份~26份，分散剂10份~16份，增稠剂5份~8份；其制备方法包括以下步骤：A.将空心玻璃微珠、滑石粉、纳米金属氧化物用搅拌机搅拌混合，搅拌机的转速为50转/分钟~80转/分钟，搅拌时间为15分钟~20分钟；B.混合后加入水、分散剂和增稠剂，再用搅拌机搅拌混合，搅拌机的转速为100转/分钟~500转/分钟，搅拌时间为20分钟~30分钟，静置后制得。与现有技术相比，本发明解决涂料不能隔热的问题。

Description

隔热涂料及其制备方法
技术领域
本发明涉及涂料技术领域，尤其是一种建筑材料用的隔热涂料及其制备方法。
背景技术
一些建筑材料与外界环境直接接触，需要经受太阳以及紫外线的照射，而多数的建筑材料由钢筋、钢板和混凝土构成，缺少较好的保温效果，长期处于高温状态下的建筑材料其使用寿命将会降低。申请号为2016105444188的专利申请公开的一种具有环保的涂料，但缺少隔热的作用。
发明内容
本发明所要解决的技术问题是提供一种隔热涂料及其制备方法，它可以解决现有涂料缺少隔热的问题。
为了解决上述问题，本发明所采用的技术方案是：这种隔热涂料及其制备方法，由以下重量份的原材料制成：空心玻璃微珠30份~40份，滑石粉20份~30份，纳米金属氧化物8份~16份，水18份~26份，分散剂10份~16份，增稠剂5份~8份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米金属氧化物用搅拌机搅拌混合，搅拌机的转速为50转/分钟~80转/分钟，搅拌时间为15分钟~20分钟；B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为100转/分钟~500转/分钟，搅拌时间为20分钟~30分钟，静置后制得。
上述技术方案中，更具体的技术方案还可以是：所述纳米金属氧化物包括纳米氧化锌和/或纳米氧化铝。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
1、空心玻璃微珠是一种微小、中空的圆球状粉末；粒径在30-100微米之间，密度在0.1-0.7g/ml，导热系数低、的优点；滑石粉具有润滑性、耐热性、熔点高、吸附力强的优点；纳米金属氧化物能阻隔空气中的90%的热量，具有较好的隔热效果；空心玻璃微珠，滑石粉和纳米金属氧化物通过用水和分散剂搅拌混合，相互交互作用，制备出来的涂料具有较好的隔热效果。
具体实施方式
以下结合具体实施例对本发明作进一步详述：
实施例1：
这种隔热涂料及其制备方法，由以下重量份的原材料制成：空心玻璃微珠30份，滑石粉20份，纳米氧化锌8份，水18份，分散剂10份，增稠剂5份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米氧化锌用搅拌机搅拌混合，搅拌机的转速为50转/分钟，搅拌时间为15分钟；
B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为100转/分钟，搅拌时间为20分钟，静置后制得。
实施例2：
这种隔热涂料及其制备方法，由以下重量份的原材料制成：空心玻璃微珠30份，滑石粉20份，纳米氧化铝8份，水18份，分散剂10份，增稠剂5份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米氧化铝用搅拌机搅拌混合，搅拌机的转速为50转/分钟，搅拌时间为15分钟；
B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为100转/分钟，搅拌时间为20分钟，静置后制得。
实施例3：
这种隔热涂料及其制备方法，由以下重量份的原材料制成：空心玻璃微珠40份，滑石粉30份，纳米氧化锌16份，水26份，分散剂16份，增稠剂8份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米氧化锌用搅拌机搅拌混合，搅拌机的转速为80转/分钟，搅拌时间为20分钟；
B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为500转/分钟，搅拌时间为30分钟，静置后制得。
实施例4：
这种隔热涂料及其制备方法，由以下重量份的原材料制成：空心玻璃微珠40份，滑石粉30份，纳米氧化铝16份，水26份，分散剂16份，增稠剂8份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米氧化铝用搅拌机搅拌混合，搅拌机的转速为80转/分钟，搅拌时间为20分钟；
B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为500转/分钟，搅拌时间为30分钟，静置后制得。

Claims (2)

1.一种隔热涂料及其制备方法，其特征在于：由以下重量份的原材料制成：空心玻璃微珠30份~40份，滑石粉20份~30份，纳米金属氧化物8份~16份，水18份~26份，分散剂10份~16份，增稠剂5份~8份；
其制备方法包括以下步骤：
A.将所述空心玻璃微珠、所述滑石粉、所述纳米金属氧化物用搅拌机搅拌混合，搅拌机的转速为50转/分钟~80转/分钟，搅拌时间为15分钟~20分钟；
B.混合后加入所述水、所述分散剂和所述增稠剂，再用搅拌机搅拌混合，搅拌机的转速为100转/分钟~500转/分钟，搅拌时间为20分钟~30分钟，静置后制得。
2.根据权利要求1所述的隔热涂料及其制备方法，其特征在于：所述纳米金属氧化物包括纳米氧化锌和/或纳米氧化铝。
CN201611030603.1A 2016-11-22 2016-11-22 隔热涂料及其制备方法 Pending CN106587904A (zh)