CN106579612A - 一种高档瑜伽服面料及其制备方法 - Google Patents

一种高档瑜伽服面料及其制备方法 Download PDF

Info

Publication number
CN106579612A
CN106579612A CN201611123095.1A CN201611123095A CN106579612A CN 106579612 A CN106579612 A CN 106579612A CN 201611123095 A CN201611123095 A CN 201611123095A CN 106579612 A CN106579612 A CN 106579612A
Authority
CN
China
Prior art keywords
fiber
fabric
grade
fibers
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611123095.1A
Other languages
English (en)
Other versions
CN106579612B (zh
Inventor
邱国萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Huan Feng Textile Co Ltd
Original Assignee
Zhejiang Huan Feng Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Huan Feng Textile Co Ltd filed Critical Zhejiang Huan Feng Textile Co Ltd
Priority to CN201611123095.1A priority Critical patent/CN106579612B/zh
Publication of CN106579612A publication Critical patent/CN106579612A/zh
Application granted granted Critical
Publication of CN106579612B publication Critical patent/CN106579612B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高档瑜伽服面料,采用多种纤维进行混纺,珍珠纤维具备非常好的保健功能,而加入竹原纤维可以使混纺面料抗菌除臭、耐磨性能良好;本发明的面料既有良好的透气性能,同时兼具轻柔、抗菌除臭、保健功效和环保性能;在制备过程中,降低了双氧水的加入量,同时加入了碱性果胶酶,控制了碱度和温度对纤维的伤害;加入了聚丙烯酸钠和有机酸,并采用逐渐升温的处理方式,不但染色效果好,而且对纤维的伤害小;最后将温度升至85‑90℃,使酶失活,本发明的制备方法,纤维的柔软度非常好,无需加入柔软剂对纤维进一步处理;采用一浴法进行处理,符合国家对纺织行业节水高效的流程要求。

Description

一种高档瑜伽服面料及其制备方法
技术领域
本发明涉及一种面料,属于纺织面料领域,尤其涉及一种高档瑜伽服面料及其制备方法。
背景技术
传统的瑜伽服面料只是着眼于透气性,但随着人们生活品质的不断提高,人们对瑜伽服的要求越来越高,高品质的瑜伽服不但要求透气性能好,还对面料的轻柔度、抗菌除臭性能、保健功效以及环保性能都有一定的要求,故有必要研发一种高档瑜伽服面料。
发明内容
基于背景技术存在的技术问题,本发明提出了一种高档瑜伽服面料及其制备方法。
本发明的技术方案如下:
一种高档瑜伽服面料,由以下纤维混纺而成:珍珠纤维、竹原纤维、棉纤维和Coolplus纤维。
优选的,所述的高档瑜伽服面料,包括以下重量百分比的成分:
珍珠纤维 50-60%
竹原纤维 15-25%
棉纤维 6-10%
Coolplus纤维 余量。
一种高档瑜伽服面料的制备方法,包括以下步骤:
A、以珍珠纤维和竹原纤维为经纱,以棉纤维和Coolplus纤维为纬纱,采用喷水织布机,织成混纺面料;
B、将混纺面料放入预先配置好的一体化处理液中进行处理,处理条件为:调节pH值为5.5-6.0,处理时间为30-40min,浴比为1:(40-50),将温度从常温逐渐升温至85-90℃,并将温度保持在85-90℃,保温时间为5-8min;所述的一体化处理液,包括以下主要成分:双氧水、螯合剂、有机酸、聚丙烯酸钠、染色剂和碱性果胶酶;
C、将面料取出后,用90℃的温水反复冲洗3-5min,沥干;
D、在120-140℃迅速脱水高温定型,即可。
优选的,所述的步骤B中,所述的一体化处理液,包括以下重量百分比的成分:
双氧水 0.4-0.7%
螯合剂 0.4-0.8%
有机酸 0.2-0.5%
聚丙烯酸钠 1-3%
染色剂 2-8%
碱性果胶酶 0.8-1.5%
水 余量。
优选的,所述的螯合剂为EDTA。
优选的,所述的染色剂为植物染色剂。
优选的,所述的有机酸为柠檬酸。
珍珠纤维是采用高科技手段将纳米级珍珠粉在粘胶纤维纺丝时加入纤维内,使纤维体内和外表均匀分布着纳米珍珠微粒。具体为珍珠蛋白功能母粒和纤维级树脂切片构成,使纤维体内和外表均匀分布着纳米珍珠微粒,一根根纤维犹如一串串珍珠项链,异常光亮滑爽。是由东华大学和上海新型纺纱中心合作共同研发的一种新型纤维,属国内外首创的高档功能性纤维。
珍珠纤维既有珍珠养颜护肤功效,又有粘胶纤维吸湿透气、穿着舒适的特性。珍珠纤维表面均匀分布着珍珠微粒,长期于皮肤接触,具有珍珠养颜护肤、清火败毒、嫩白肌肤、抗紫外线的功效。珍珠纤维含有多种氨基酸和微量元素,纤维表面光滑凉爽,有珍珠般光泽。
珍珠粉被人体吸收后,通过参与肌体代谢,达到全身肌肤的整体调理和保养。它能促进新生细胞合成,并不断补充到皮肤表层,使皮肤光滑、细腻、有弹性。科学地服用珍珠粉有明显地减轻血清过氧化脂的作用,而此脂质与蛋白质结合成能生成脂褐素(老人斑),这正是慈禧太后用珍珠善养颜容的秘密所在。
用珍珠粉涂面后,可以促进人体肌肤超氧化物歧化酶(SOD)的活性,抑制黑色素的合成,保持皮肤白皙。此外,由于SOD具有清除自由基的作用,可防止皮肤衰老、起皱。
⑴养颜护肤、嫩白皮肤
人体穿着珍珠纤维内衣,纤维上的珍珠纳米微粒与肌肤亲密接触,汗液中的乳酸会溶出纤维中部分珍珠营养成分,通过皮肤被吸收,促进人体肌肤超氧化物歧化酶(SOD)的活性,抑制黑色素的合成保持皮肤白皙。此外,由于SOD具有清除自由基的作用,可防止皮肤衰老起皱。中医认为:珍珠性寒味甘咸,归心肝经,功能容颜美肤,润肤生肌,清斑减皱,延缓衰老;主要用于面部雀斑、黄褐斑、寿斑、皱纹、肌肉松弛、皮肤粗糙乏泽、面色苍老以及痤疮、烧烫伤、疮疡、伤口不收、皮炎等。珍珠生长在水中,性寒,具有清火败毒功效,长期穿着珍珠纤维内衣可清除皮肤表面热痘毒,具有祛斑、除痘、养护肌肤的功效。
⑵抗紫外线
珍珠的主要成分为碳酸钙,其本身具有防紫外线功能,当其粉碎成纳米状态加入纤维时,其功能大大加强。珍珠纤维具有防紫外线防皮肤老化作用。据最新研究表明:纳米珍珠粉还具有发射红外波的功能,它可改善人体微循环,对人体有保健作用。
⑶吸湿透气、服用舒适
纳米珍珠纤维的载体是粘胶纤维,它吸湿透气服用舒适,加入耐珍珠粉后纤维内部及表面均匀分布着珍珠纳米微粒,纤维手感光滑凉爽,外观亮丽。
⑷全天然
纳米珍珠粉是由优质淡水珍珠经纯物理方法加工而成,粘胶纤维素由棉短绒提取,因此珍珠纤维不含任何化学性产品之有害物质,与肌肤有天然的亲和性。
⑸经久耐用
珍珠纤维中珍珠纳米微粒与纤维亲密结合,具有永久性,长期洗涤穿着不会脱落。珍珠耐碱不耐酸,碱性洗涤不伤毫发,只有在酸性汗液作用下珍珠纳米微粒才会产生部分析出,珍珠内衣实乃转着与洗涤之完美结合。
现有的珍珠纤维具有非常好的保健功效,但是现在的消费者,尤其是女性消费者对环保、抗菌、健康的内衣需求越来越强烈,故有必要在兼顾保健功效的同时,进一步提升面料的抗菌功效。
竹纤维是从自然生长的竹子中提取出的纤维素纤维,继棉、麻、毛、丝后的第五大天然纤维。竹原纤维具有良好的透气性、瞬间吸水性、较强的耐磨性和良好的染色性等特性,具有天然抗菌、抑菌、除螨、防臭和抗紫外线功能。
Coolplus纤维表面带有众多微孔及细微沟槽,可以产生毛细效应,可以将人体肌肤表层的汗水和湿气,很快吸收到织物外层,快速散发湿气和汗水,使人体表面保持干爽、清凉、舒适,具有调节体温的作用。纤维截面为“+”型,表面为细微沟槽,同时添加特殊的聚合体利用该材料溶解性的差异,赋予纤维无数细微空洞。通过这些细微沟槽产生的毛细现象,将肌肤表层排出的湿气与汗水经由芯吸扩散、传输等作用,瞬间排出体外。Coolplus纤维应用广泛,能纯纺,也能与棉、毛、丝、麻及各类化纤混纺或交织,可梭织、也可针织。既拥有如棉、麻、丝、羊毛等天然纤维之触感,且超越了天然纤维,Coolplus织物无论在速干性、透气性、防褪色性、防缩性及防皱性上均优于天然棉。
本发明的有益效果在于:
1、采用多种纤维进行混纺,珍珠纤维具备非常好的保健功能,而加入竹原纤维可以使混纺面料抗菌除臭、耐磨性能良好;本发明的面料既有良好的透气性能,同时兼具轻柔、抗菌除臭、保健功效和环保性能;
2、在制备过程中,采用一浴法进行处理,符合国家对纺织行业节水高效的流程要求;
3、采用一浴法进行处理主要需要克服两个困难,一是多种混纺纤维的染色均匀性;二是防止制备过程对Coolplus纤维、竹原纤维和珍珠纤维的结构破坏,从而影响舒适性强的Coolplus纤维、抗菌除臭性能佳的竹原纤维和保健效果好的珍珠纤维的性能;本发明中,降低了双氧水的加入量,同时加入了碱性果胶酶,控制了碱度和温度对纤维的伤害;加入了聚丙烯酸钠和有机酸,并采用逐渐升温的处理方式,不但染色效果好,而且对纤维的伤害小;最后将温度升至85-90℃,使酶失活,本发明的制备方法,纤维的柔软度非常好,无需加入柔软剂对纤维进一步处理。
具体实施方式
实施例1
一种高档瑜伽服面料,包括以下重量百分比的成分:
珍珠纤维 56%
竹原纤维 20%
棉纤维 8%
Coolplus纤维 余量。
一种高档瑜伽服面料的制备方法,包括以下步骤:
A、以珍珠纤维和竹原纤维为经纱,以棉纤维和Coolplus纤维为纬纱,采用喷水织布机,织成混纺面料;
B、将混纺面料放入预先配置好的一体化处理液中进行处理,处理条件为:调节pH值为5.5-6.0,处理时间为35min,浴比为1:45,将温度从常温逐渐升温至88℃,并将温度保持在88℃,保温时间为7min;
C、将面料取出后,用90℃的温水反复冲洗4min,沥干;
D、在125℃迅速脱水高温定型,即可。
所述的步骤B中,所述的一体化处理液,包括以下重量百分比的成分:
双氧水 0.45%
螯合剂 0.5%
有机酸 0.3%
聚丙烯酸钠 1.5%
染色剂 5%
碱性果胶酶 1.2%
水 余量。
实施例2
一种高档瑜伽服面料,包括以下重量百分比的成分:
珍珠纤维 60%
竹原纤维 15%
棉纤维 6%
Coolplus纤维 余量。
一种高档瑜伽服面料的制备方法,包括以下步骤:
A、以珍珠纤维和竹原纤维为经纱,以棉纤维和Coolplus纤维为纬纱,采用喷水织布机,织成混纺面料;
B、将混纺面料放入预先配置好的一体化处理液中进行处理,处理条件为:调节pH值为5.5-6.0,处理时间为40min,浴比为1:40,将温度从常温逐渐升温至90℃,并将温度保持在90℃,保温时间为5min;
C、将面料取出后,用90℃的温水反复冲洗3min,沥干;
D、在140℃迅速脱水高温定型,即可。
所述的步骤B中,所述的一体化处理液,包括以下重量百分比的成分:
双氧水 0.7%
螯合剂 0.4%
有机酸 0.5%
聚丙烯酸钠 1%
染色剂 8%
碱性果胶酶 0.8%
水 余量。
实施例3
一种高档瑜伽服面料,包括以下重量百分比的成分:
珍珠纤维 50%
竹原纤维 15%
棉纤维 10%
Coolplus纤维 余量。
一种高档瑜伽服面料的制备方法,包括以下步骤:
A、以珍珠纤维和竹原纤维为经纱,以棉纤维和Coolplus纤维为纬纱,采用喷水织布机,织成混纺面料;
B、将混纺面料放入预先配置好的一体化处理液中进行处理,处理条件为:调节pH值为5.5-6.0,处理时间为45min,浴比为1:50,将温度从常温逐渐升温至85℃,并将温度保持在85℃,保温时间为8min;
C、将面料取出后,用90℃的温水反复冲洗5min,沥干;
D、在120℃迅速脱水高温定型,即可。
所述的步骤B中,所述的一体化处理液,包括以下重量百分比的成分:
双氧水 0.4%
螯合剂 0.8%
有机酸 0.2%
聚丙烯酸钠 3%
染色剂 2%
碱性果胶酶 1.5%
水 余量。
对实施例1-3进行检测:
此检测数据只针对上述检测样品。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。

Claims (7)

1.一种高档瑜伽服面料,其特征在于,由以下纤维混纺而成:珍珠纤维、竹原纤维、棉纤维和Coolplus纤维。
2.如权利要求1所述的高档瑜伽服面料,其特征在于,包括以下重量百分比的成分:
珍珠纤维 50-60%
竹原纤维 15-25%
棉纤维 6-10%
Coolplus纤维 余量。
3.一种高档瑜伽服面料的制备方法,其特征在于,包括以下步骤:
A、以珍珠纤维和竹原纤维为经纱,以棉纤维和Coolplus纤维为纬纱,采用喷水织布机,织成混纺面料;
B、将混纺面料放入预先配置好的一体化处理液中进行处理,处理条件为:调节pH值为5.5-6.0,处理时间为30-40min,浴比为1:(40-50),将温度从常温逐渐升温至85-90℃,并将温度保持在85-90℃,保温时间为5-8min;所述的一体化处理液,包括以下主要成分:双氧水、螯合剂、有机酸、聚丙烯酸钠、染色剂和碱性果胶酶;
C、将面料取出后,用90℃的温水反复冲洗3-5min,沥干;
D、在120-140℃迅速脱水高温定型,即可。
4.如权利要求1所述的高档瑜伽服面料的制备方法,其特征在于,所述的步骤B中,所述的一体化处理液,包括以下重量百分比的成分:
双氧水 0.4-0.7%
螯合剂 0.4-0.8%
有机酸 0.2-0.5%
聚丙烯酸钠 1-3%
染色剂 2-8%
碱性果胶酶 0.8-1.5%
水 余量。
5.如权利要求1所述的高档瑜伽服面料的制备方法,其特征在于,所述的螯合剂为EDTA。
6.如权利要求1所述的高档瑜伽服面料的制备方法,其特征在于,所述的染色剂为植物染色剂。
7.如权利要求1所述的高档瑜伽服面料的制备方法,其特征在于,所述的有机酸为柠檬酸。
CN201611123095.1A 2016-12-08 2016-12-08 一种高档瑜伽服面料及其制备方法 Active CN106579612B (zh)