CN106567195A - Anti-flaming and wear-resisting non-woven fabric material - Google Patents
Anti-flaming and wear-resisting non-woven fabric material Download PDFInfo
- Publication number
- CN106567195A CN106567195A CN201610935233.XA CN201610935233A CN106567195A CN 106567195 A CN106567195 A CN 106567195A CN 201610935233 A CN201610935233 A CN 201610935233A CN 106567195 A CN106567195 A CN 106567195A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- fiber
- powder
- nonwoven cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a non-woven fabric material and specifically relates to an anti-flaming and wear-resisting non-woven fabric material. The non-woven fabric material is made of the ingredients including 60-70 parts by weight of syndiotactic polypropylene, 10-20 parts by weight of polyester fibers, 10-20 parts by weight of glass fiber powder, 5-10 parts by weight of nano-barium sulfate, 1-3 parts by weight of nano-zinc oxide, 4-8 parts by weight of Diethyl ethanephosphonate, 1-2 parts by weight of aluminum powder, 2-4 parts by weight of composite silk oil, 2-3 parts by weight of sodium hyaluronate, 1-3 parts by weight of folium artemisiae argyi, 1-2 parts by weight of galangal and 2-3 parts by weight of liquorice. The non-woven fabric material provided by the invention is characterized in that the material contains the ingredients such as nano-barium sulfate, glass fiber powder, Diethyl ethanephosphonate, composite silk oil and folium artemisiae argyi, so the non-woven fabric material has excellent properties such as high gloss, high strength, wear resistance and anti-flaming performance; and the material is applicable to fields such as industry, agriculture and medical treatment and has broad application prospect.
Description
Technical field
The invention belongs to field of textiles, and in particular to a kind of flame-proof abrasion-resistant nonwoven cloth material.
Background technology
Non-woven fabrics are to be made up of fiber orient or random, are environment-friendly materials of new generation also known as adhesive-bonded fabric, with anti-
Damp, ventilative, flexible, light weight, not combustion-supporting, easy decomposition, nontoxic nonirritant, rich color, cheap, recyclable regenerative,
And breach traditional weaving principle, and have that technological process is short, speed of production is fast, yield height, low cost, purposes extensively, raw material
The features such as originating many.It is bonded fabric product rich color, bright-coloured lucid and lively, Eco-Fashion, of many uses, elegant in appearance, pattern and money
Formula is all various, and light weight, environmental protection, recyclable, by the internationally recognized environment-friendly products for ecology of preserving our planet.Suitable for agricultural
The industries such as thin film, shoemaking, process hides, mattress, child-mother-covering, decoration, chemical industry, printing, automobile, building materials, furniture, and dress lining cloth, doctor
The gift bag of health disposable surgical clothing, mask, cap, sheet, the disposable tablecloth in hotel, beauty, Saunas or even current fashion is treated,
Fine work bag, shopping bag, advertising bag etc..Meanwhile, non-woven fabrics have many good qualities, such as aeration, filterability, heat insulating ability, water absorption,
Water proofing property, retractility, not fluffy and disorderly, good hand touch, softness, directivity that is slim and graceful, flexible, resilient, not having cloth and weaving cloth
Compare that productivity is high, speed of production is fast, price is low, size is fixed, be unlikely to deform, can produce in a large number etc..Therefore more than being directed to
It is described that to provide a kind of nonwoven cloth material be necessary.
The content of the invention
It is an object of the invention to provide a kind of flame-proof abrasion-resistant nonwoven cloth material.
To achieve these goals, the invention provides a kind of flame-proof abrasion-resistant nonwoven cloth material, the material is by following weight
The raw material of part is made：Syndiotactic polypropylene 60-70, polyester fiber 10-20, glass fiber powder 10-20, nano barium sulfate 5-10, receive
It is rice Zinc Oxide 1-3, diethyl ethylphosphate 4-8, aluminium powder 1-2, synthesis silkworm silk oil 2-4, hyaluronate sodium 2-3, Folium Artemisiae Argyi 1-3, good
Rhizoma Zingiberis Recens 1-2, Radix Glycyrrhizae 2-3.
The glass fiber powder model is XGFA11300.
The polyester fiber is selected from dacron fibre, poly fiber, gathers to benzene
In dioctyl phthalate propylene diester fiber, poly terephthalic acid -1,4- cyclohexyl dicarboxylic acid fibers, poly- two ester fiber of 2,6- naphthalenes diacid second
It is a kind of.
The Folium Artemisiae Argyi is the dried leaves of feverfew Chinese mugwort；Summer flower is plucked when not opening, and is removed impurity, is dried.
Described flame-proof abrasion-resistant nonwoven cloth material is obtained by following technique：
(1) Folium Artemisiae Argyi, Rhizoma Alpiniae Officinarum, Radix Glycyrrhizae are ground into into 300-400 mesh powder mix homogeneously, it is stand-by；
(2) nano zine oxide, nano barium sulfate, aluminium powder are placed in the ultrasonic cleaning instrument of 35-45KHz, using anhydrous second
Alcohol ultrasound 30-50min；After ultrasound is finished, with absolute ethanol washing 2-3 time, 60-80 DEG C of drying is to constant weight, stand-by；
(3) syndiotactic polypropylene, polyester fiber are heated to into molten condition, add step (1), the material of (2), be sufficiently stirred for
Uniformly；
(4) addition glass fiber powder, diethyl ethylphosphate, synthesis silkworm silk oil, hyaluronic acid in step (3) material
Sodium, is sufficiently stirred for, mix homogeneously, makes non-woven fabrics by nozzle spray webbing.
Beneficial effects of the present invention：The nonwoven cloth material of the present invention, containing nano barium sulfate, glass fiber powder, ethyl phosphine
Diethyl phthalate, synthesis silkworm silk oil, the raw material such as Folium Artemisiae Argyi so that the nonwoven cloth material have good high glaze, intensity, wearability,
The characteristic such as fire-retardant, can be used for the fields such as industry, agricultural, medical treatment, and application prospect is extensive.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.In embodiment, syndiotactic polypropylene, polyester are fine
Dimension, diethyl ethylphosphate, nano zine oxide, glass fiber powder, synthesis silkworm silk oil, hyaluronate sodium, nano barium sulfate are lid
Dehua work net commercially available product.
Embodiment 1
A kind of flame-proof abrasion-resistant nonwoven cloth material, the material are prepared by the raw materials in：Syndiotactic polypropylene 66, polyester
Fiber 15, glass fiber powder 13, nano barium sulfate 8, nano zine oxide 2, diethyl ethylphosphate 5, aluminium powder 2, synthesis silkworm silk oil
3rd, hyaluronate sodium 2, Folium Artemisiae Argyi 2, Rhizoma Alpiniae Officinarum 1, Radix Glycyrrhizae 2.
The polyester fiber is dacron fibre.
Described flame-proof abrasion-resistant nonwoven cloth material is obtained by following technique：
(1) Folium Artemisiae Argyi, Rhizoma Alpiniae Officinarum, Radix Glycyrrhizae are ground into into 300-400 mesh powder mix homogeneously, it is stand-by；
(2) nano zine oxide, nano barium sulfate, aluminium powder are placed in the ultrasonic cleaning instrument of 45KHz, it is super using dehydrated alcohol
Sound 40min；After ultrasound is finished, with absolute ethanol washing 2 times, 60 DEG C of dryings are to constant weight, stand-by；
(3) syndiotactic polypropylene, polyester fiber are heated to into molten condition, add step (1), the material of (2), be sufficiently stirred for
Uniformly；
(4) addition glass fiber powder, diethyl ethylphosphate, synthesis silkworm silk oil, hyaluronic acid in step (3) material
Sodium, is sufficiently stirred for, mix homogeneously, makes non-woven fabrics by nozzle spray webbing.
Embodiment 2
A kind of flame-proof abrasion-resistant nonwoven cloth material, the material are prepared by the raw materials in：Polypropylene 62, polyester fiber
17th, glass fiber powder 15, nano barium sulfate 7, nano zine oxide 1, diethyl ethylphosphate 4-8, aluminium powder 1.5, synthesis silkworm silk oil
2.5th, hyaluronate sodium 2.5, Folium Artemisiae Argyi 1.5, Rhizoma Alpiniae Officinarum 2, Radix Glycyrrhizae 3.
The polyester fiber is PTT Fiber.
Described flame-proof abrasion-resistant nonwoven cloth material is obtained by following technique：
(1) Folium Artemisiae Argyi, Rhizoma Alpiniae Officinarum, Radix Glycyrrhizae are ground into into 300-400 mesh powder mix homogeneously, it is stand-by；
(2) nano zine oxide, nano barium sulfate, aluminium powder are placed in the ultrasonic cleaning instrument of 40KHz, it is super using dehydrated alcohol
Sound 50min；After ultrasound is finished, with absolute ethanol washing 3 times, 80 DEG C of dryings are to constant weight, stand-by；
(3) syndiotactic polypropylene, polyester fiber are heated to into molten condition, add step (1), the material of (2), be sufficiently stirred for
Uniformly；
(4) addition glass fiber powder, diethyl ethylphosphate, synthesis silkworm silk oil, hyaluronic acid in step (3) material
Sodium, is sufficiently stirred for, mix homogeneously, makes non-woven fabrics by nozzle spray webbing.
Technical parameter using nonwoven cloth material obtained in the present invention is as follows：
Claims (4)
1. a kind of flame-proof abrasion-resistant nonwoven cloth material, it is characterised in that the material is prepared by the raw materials in：Between advise poly- third
Alkene 60-70, polyester fiber 10-20, glass fiber powder 10-20, nano barium sulfate 5-10, nano zine oxide 1-3, ethylphosphonic acid two
Ethyl ester 4-8, aluminium powder 1-2, synthesis silkworm silk oil 2-4, hyaluronate sodium 2-3, Folium Artemisiae Argyi 1-3, Rhizoma Alpiniae Officinarum 1-2, Radix Glycyrrhizae 2-3.
2. a kind of flame-proof abrasion-resistant nonwoven cloth material according to claim 1, it is characterised in that：The glass fiber powder model
It is XGFA11300.
3. a kind of flame-proof abrasion-resistant nonwoven cloth material according to claim 1, it is characterised in that：The polyester fiber is selected from poly-
PETP fiber, poly fiber, PTT Fiber, poly- terephthaldehyde
One kind in acid -1,4- cyclohexyl dicarboxylic acid fibers, poly- two ester fiber of 2,6- naphthalenes diacid second.
4. a kind of flame-proof abrasion-resistant nonwoven cloth material according to claim 1, it is characterised in that described nonwoven cloth material by
Following technique is obtained：
(1) Folium Artemisiae Argyi, Rhizoma Alpiniae Officinarum, Radix Glycyrrhizae are ground into into 300-400 mesh powder mix homogeneously, it is stand-by；
(2) nano zine oxide, nano barium sulfate, aluminium powder are placed in the ultrasonic cleaning instrument of 35-45KHz, it is super using dehydrated alcohol
Sound 30-50min；After ultrasound is finished, with absolute ethanol washing 2-3 time, 60-80 DEG C of drying is to constant weight, stand-by；
(3) syndiotactic polypropylene, polyester fiber are heated to into molten condition, add step (1), the material of (2), be sufficiently stirred for
It is even；
(4) glass fiber powder, diethyl ethylphosphate, synthesis silkworm silk oil, hyaluronate sodium are added in step (3) material, is filled
Stirring, mix homogeneously is divided to make non-woven fabrics by nozzle spray webbing.