CN106566974A - Automobile magnetic water pump powder metallurgy inner/outer magnet ring and preparation method thereof - Google Patents
Automobile magnetic water pump powder metallurgy inner/outer magnet ring and preparation method thereof Download PDFInfo
- Publication number
- CN106566974A CN106566974A CN201610934357.6A CN201610934357A CN106566974A CN 106566974 A CN106566974 A CN 106566974A CN 201610934357 A CN201610934357 A CN 201610934357A CN 106566974 A CN106566974 A CN 106566974A
- Authority
- CN
- China
- Prior art keywords
- magnet ring
- water pump
- powder metallurgy
- magnetic water
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an automobile magnetic water pump powder metallurgy inner/outer magnet ring and a preparation method thereof. The magnet ring is composed of the following components in percentage by weight: 3 to 5% of copper (Cu), 10 to 15% of Mn, 0.8 to 1% of Ni, 0.5 to 0.8% of Mo, 0.5 to 0.6% of MoS2, 2 to 3% of organic silicone resin adhesive, and the balance being a basic material (stainless steel powder). A high density moulding technology and a precise temperature controlled sintering technology are adopted; an advanced mould structure is developed; an automatic powder feeding and mould wall lubricating mechanism and a high precision processing key facility are designed, and the obtained high precision stainless steel outer magnetic ring powder metallurgy tool is resistant to acid, alkali, and corrosion, and thus has a good industrialization prospect.
Description
Technical field
The present invention relates to automobile magnetic pump preparation field, particularly belong to the inside and outside magnet ring of automobile magnetic water pump powder metallurgy and
Its preparation method.
Background technology
With the continuous development of international and domestic automobile industry, environmental friendliness, energy-saving and emission-reduction, the popularization of green novel energy source automobile
Rate cumulative year after year, the magnetic water pump for electrical equipment such as the motor of new energy vehicle, controllers also will grow with each passing day, the project research
The inside and outside magnet ring of stainless steel magnetic water pump vital part of exploitation,, used as the major part of magnetic water pump, market scale will increasingly for it
Increase.Jing market surveys find that at present domestic production process technology is not yet ripe in China, the inside and outside magnetic of magnetic water pump stainless steel
Ring product not yet realizes volume production, mass marketing, most still using German import.
The content of the invention
It is an object of the invention to provide inside and outside magnet ring of a kind of automobile magnetic water pump powder metallurgy and preparation method thereof, adopts
High density shaping, accurate temperature controlling sintering technology, develop advanced mould structure, design automatic powder feeding and die wall lubrication mechanism and high-precision
Degree processing key equipment, obtains acidproof, alkaline-resisting, corrosion-resistant, high accuracy stainless steel outer magnetic ring metallic sintered products, and industrial prospect is good
It is good.
Technical scheme is as follows:
A kind of inside and outside magnet ring of automobile magnetic water pump powder metallurgy, is made up of following mass percent raw material components:Copper Cu 3-5%,
Mn 10-15%, Ni 0.8-1%, Mo 0.5-0.8%, MoS2 0.5-0.6%, organic siliconresin adhesive 2-3%, balance of base
Material powder of stainless steel.
A kind of inside and outside magnet ring preparation method of automobile magnetic water pump powder metallurgy, specific processing step is as follows:First will be above-mentioned
Raw material is sufficiently mixed in batch mixer, then using high density shaping, accurate temperature controlling sintering technology, while by the use of hydrogen as protection
Atmosphere, makes the abundant decarburization of product, toughness of material is improved, finally using the reciprocating grinding mode of honing, it is ensured that inside and outside magnet ring
Fineness and dimensional accuracy.
The Advantageous Effects of the present invention are as follows:
1st, powder of stainless steel is adopted for raw material, metallic element and the organic siliconresin adhesive such as addition copper, manganese, nickel, in batch mixer
In be sufficiently mixed, product composition is controllable, Cutting free processing.
2nd, using high density shaping, accurate temperature controlling sintering technology, the hydrogen by the use of certain purity fills as protective atmosphere, makes
The abundant decarburization of product, improves toughness of material.
3rd, the once-forming high density of powder metallurgy production technology, variable cross-section, thin-walled outer magnetic ring product, improve production efficiency,
Reduce production cost.
4th, using the reciprocating grinding mode of honing, it is ensured that inside and outside magnet ring fineness and dimensional accuracy.
Specific embodiment
A kind of inside and outside magnet ring of automobile magnetic water pump powder metallurgy, is made up of following mass percent raw material components:Copper Cu
3-5%, Mn 10-15%, Ni 0.8-1%, Mo 0.5-0.8%, MoS2 0.5-0.6%, organic siliconresin adhesive 2-3%, surplus
For base-material powder of stainless steel.
A kind of inside and outside magnet ring preparation method of automobile magnetic water pump powder metallurgy, specific processing step is as follows:First will be above-mentioned
Raw material is sufficiently mixed in batch mixer, then using high density shaping, accurate temperature controlling sintering technology, while by the use of hydrogen as protection
Atmosphere, makes the abundant decarburization of product, toughness of material is improved, finally using the reciprocating grinding mode of honing, it is ensured that inside and outside magnet ring
Fineness and dimensional accuracy.
Preparation method of the present invention adopts automatic powder feeding, the outer magnetic of the once-forming high density of die wall lubrication technology, variable cross-section, thin-walled
Ring product;The reciprocating processing mode of honing, it is ensured that internal magnetic ring, outer magnetic ring fineness and dimensional accuracy, fineness reaches Ra0.2, produces
Product axle degree reaches 0.0015mm.
Claims (2)
1. the inside and outside magnet ring of a kind of automobile magnetic water pump powder metallurgy, it is characterised in that by following mass percent raw material components group
Into:Copper Cu 3-5%, Mn 10-15%, Ni 0.8-1%, Mo 0.5-0.8%, MoS2 0.5-0.6%, organic siliconresin adhesive
2-3%, balance of base-material powder of stainless steel.
2. the inside and outside magnet ring preparation method of a kind of automobile magnetic water pump powder metallurgy, it is characterised in that specific processing step is such as
Under:First above-mentioned raw materials are sufficiently mixed in batch mixer, then using high density shaping, accurate temperature controlling sintering technology, while utilizing
Hydrogen makes the abundant decarburization of product as protective atmosphere, improves toughness of material, finally using the reciprocating grinding mode of honing,
Ensure inside and outside magnet ring fineness and dimensional accuracy.