CN1065667A - A kind of transparent fire-resisting paint and manufacture method thereof - Google Patents
A kind of transparent fire-resisting paint and manufacture method thereof Download PDFInfo
- Publication number
- CN1065667A CN1065667A CN 91102370 CN91102370A CN1065667A CN 1065667 A CN1065667 A CN 1065667A CN 91102370 CN91102370 CN 91102370 CN 91102370 A CN91102370 A CN 91102370A CN 1065667 A CN1065667 A CN 1065667A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- sodium
- manufacture method
- resisting paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of transparent fire-resisting paint and manufacture method thereof.Main raw only is five kinds of cheap material manufacturings such as borax, sodium sulphite anhydrous 99.3, sodium-chlor, talcum powder, sodium silicate solution.Method is very simple, safety non-toxic.Coating is transparent, fire resistance property is very strong, even the anti-combustion fire time also reached more than 90 minutes less than 1mm in coating on the glued board.Be applicable to the various materials in steel, timber, glued board, flax board, Straw Board, wallpaper, glass and the covil construction.
Description
The present invention relates to a kind of transparent, nontoxic frie retardant coating, is a kind of frie retardant coating that is suitable for being coated on timber structure, steel construction and the various material of construction.
A lot of work have been done about frie retardant coating both at home and abroad at present.The main starting point is that (1) fire resistance is good, has the long anti-combustion time to reach than extensive applicability; (2) nontoxic, using and make all should safety; (3) price is low, and technological process is simple.Therefore correlation technique data and corresponding product are a lot of both at home and abroad.Chinese patent CN1031708A(1989 March 1 is open) application documents in disclosed technology, only strive having accomplished a kind ofly being hypotoxic frie retardant coating, and fire resistance period 46 minutes, and have a variety of cost of material more expensive.Open in CN89105700.5(1990 October 17) application documents in contain asbestos in the disclosed technology raw material, this is also dangerous to user and producer.Can see that from present disclosed various kinds of document above-mentioned existing problems are that present used technical scheme is all very not satisfactory.
The objective of the invention is to develop a kind of fire resistance period length, totally nontoxic, cheap transparent fire-resisting paint.
The solution of the present invention is as follows: all starting material are low price, nontoxic, and its component is:
Borax 26-32(parts by weight)
Sodium sulphite anhydrous 99.3 12-16(parts by weight)
Sodium-chlor 40-50(parts by weight)
Talcum powder: the 6-10(parts by weight)
Sodium silicate solution (degree Beaume 40 ± 0.5, modulus 3-3.3): the 898-948(parts by weight).
In the above-mentioned prescription, sodium sulphite anhydrous 99.3 can replace with sodium sulfate, and talcum powder can replace with dry powder, and sodium-chlor can replace with magnesium chloride.
Manufacture method is as follows:
(1) batching: with the above-mentioned raw material precision that has a degree of precision through screening is that 1% pound title is respectively by than weighing.
(2) mix to stir: earlier will by than four kinds of raw materials such as alleged borax, sodium sulphite anhydrous 99.3, sodium-chlor, talcum powder by stirring 20-30 minute than the stirrer of putting into about 200 rev/mins.
(3) secondary stirring: will stir 1-1.5 hour by the stirrer of putting into than the sodium silicate solution that weighs up and aforementioned four kinds of batchings of having stirred about 500 rev/mins.
(4) filter: filter with 30-40 purpose mesh screen.
(5) barrelling: add a cover or seal.
(6) warehouse-in: deposit more than 30 days.
(7) finished product dispatches from the factory.
Material component of the present invention only has five kinds, is the material that extensively should adopt, exhausted nontoxicity, and dispatching from the factory from starting material to the finished product only needs to stir secondary.Need not heat, not need excessive fine grinding, technological process is simple, equipment is few.Fire resistance is higher than existing frie retardant coating far away, for example the disclosed anti-combustion time of CN87106082.5 is 46 minutes, and coating of the present invention is coated on glued board and the aluminium sheet, and coating only is 0.5-0.8mm, spray with 1180 ℃ alcohol blast burners, the anti-combustion time is more than 90 minutes.Though as be coated in that the barbecue through 700 ℃-1000 ℃ can not make glass burst in 120 minutes on the ordinary plate glass.
Embodiment:
In the component of the present invention:
Sodium sulphite anhydrous 99.3 can replace with the sodium sulfate of equal proportioning, and talcum powder can replace with the dry powder of equal proportioning, and sodium-chlor can replace with the magnesium chloride of equal proportioning.
Coating of the present invention forms the netted honeycomb fire proof heat-insulation layer of 10-30mm, has effectively stoped the burning of protoplasm base material in high temperature.The present invention is applicable to: various materials such as steel, timber, glued board, flax board, yellow plate paper, wallpaper, glass because transparent, do not hinder the decorative effect behind the additive color.
Claims (5)
1, a kind of transparent fire-resisting paint and manufacture method thereof is characterized in that the component of above-mentioned transparent fire-resisting paint is as follows:
Borax 26-32 (parts by weight)
Sodium sulphite anhydrous 99.3 12-16 (parts by weight)
Sodium-chlor 40-50 (parts by weight)
Talcum powder 6-10 (parts by weight)
Sodium silicate solution (degree Beaume 40 ± 0.5, modulus 3-3.3) 898-948 (parts by weight)
2, a kind of transparent fire-resisting paint according to claim 1 and manufacture method thereof is characterized in that the manufacture method of above-mentioned frie retardant coating is:
The first step: batching is that a pound title of 1% is weighed respectively in proportion with the above-mentioned raw material precision with degree of precision through screening,
Second step: mix and stir, will stir 20-30 minute by the stirrer of putting into than the borax that weighs up, sodium sulphite anhydrous 99.3, sodium-chlor, four kinds of raw materials of talcum powder about 200 rev/mins,
The 3rd step: secondary stirring, will stir 1-1.5 hour by the stirrer of putting into 500 rev/mins than the sodium silicate solution that weighs up and aforementioned four kinds of compounds that stirred;
The 4th step: filter, filter with 30-40 purpose mesh screen,
The 5th step: barrelling is added a cover or is sealed,
The 6th step: warehouse-in, deposit more than 30 days,
The 7th step: finished product dispatches from the factory.
3, a kind of transparent fire-resisting paint according to claim 1 and manufacture method thereof, it is characterized in that above-mentioned transparent fire-resisting paint component can for:
Borax: the 26-32(parts by weight)
Sodium sulfate: the 12-16(parts by weight)
Sodium-chlor: the 40-50(parts by weight)
Talcum powder: the 6-10(parts by weight)
Sodium silicate solution (degree Beaume 40 ± 0.5, modulus 3 ± 3.3): the 898-948(parts by weight).
4, a kind of transparent fire-resisting paint according to claim 1 and manufacture method thereof is characterized in that sodium-chlor can replace with equivalent weight umber magnesium chloride in the above-mentioned component.
5, a kind of transparent fire-resisting paint according to claim 1 and manufacture method thereof is characterized in that the talcum powder in the above-mentioned component can replace with the dry powder of equivalent weight umber.