CN106566430A - An anti-blue-light antimagnetic film and a preparing method thereof - Google Patents
An anti-blue-light antimagnetic film and a preparing method thereof Download PDFInfo
- Publication number
- CN106566430A CN106566430A CN201610924963.XA CN201610924963A CN106566430A CN 106566430 A CN106566430 A CN 106566430A CN 201610924963 A CN201610924963 A CN 201610924963A CN 106566430 A CN106566430 A CN 106566430A
- Authority
- CN
- China
- Prior art keywords
- diamagnetic
- blue light
- resin
- thin film
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An anti-blue-light antimagnetic film and a preparing method thereof are disclosed. The film has a good antimagnetic property and good anti-blue-light effects, thus playing a role of protecting glasses of persons and protecting electronic elements. The film includes, from top to bottom, an upper release film, an anti-blue-light layer, an antimagnetic metal layer, an insulating substrate, an acrylic adhesive layer and a lower release film. The thickness of the anti-blue-light layer is 50-100 [mu]m. The thickness of the antimagnetic metal layer is 50-100 [mu]. The thickness of the carrier insulating substrate is 50-150 [mu]. Anti-blue-light and antimagnetic functions are combined, and therefore the anti-blue-light antimagnetic film not only protects eyes of persons from being damaged by blue light, but also protects electronic products from electromagnetic interferences.
Description
Technical field
The invention belongs to adhesive material technical field, specifically, is particularly to a kind of being mainly and is used on electronic component,
The diamagnetic thin film of anti-blue light.
Background technology
The progress of science and technology continues to bring out various lighting sources, these light sources abundant illuminating product with meet people and use
While demand as improper use and produce the harm to people.Wherein blue light can penetrate crystalline lenses and reach retina, right
It causes optical damage, accelerates the oxidation of macular area cell, produces a large amount of free radicals, causes cataract, macular area to be degenerated, even
The generation of cancer.Meanwhile, electromagnetic radiation and interference are also the key factor for affecting electronic component sensitivity and user health.Mesh
Possesses the effect protecting film of anti-electromagnetism while also there is no anti-blue light effect on front market.
The content of the invention
The invention aims to overcome the deficiencies in the prior art, be provide one kind can the diamagnetic thin film of anti-blue light, should
Thin film has good anti-blue light effect while with good diamagnetic performance, the blue light mistake that can be produced electronic product itself
Filter, interference of the external electromagnetic to electronic product can be prevented again, so as to play the work of protection people's glasses and protection electronic component
With.
To reach above-mentioned purpose, the present invention adopts below scheme:
A kind of diamagnetic thin film of anti-blue light, the diamagnetic thin film of anti-blue light includes from top to bottom:Upper mould release membrance, anti-blu-ray layer is diamagnetic
Metal level, insulating substrate, acrylic adhesive layer, lower mould release membrance;
Anti- blu-ray layer thickness is 50~100 μm;
Diamagnetic metal layer thickness is 50~100 μm;
Carrier insulating substrate is have any in polyimides, polyethylene, polyvinylidene fluoride or polytetrafluoroethylene film
One kind, thickness is 50 μm~150 μm.
Further, in certain embodiments, the material component of diamagnetic metal level is with weight proportion:
100 parts of resin
5~20 parts of diamagnetic metal material
20~40 parts of solvent;
Resin be acrylic resin, epoxy resin, the one kind in polyurethane resin or polyester resin;
Diamagnetic metal material be copper, silver, nickel, cobalt metal-powder or its alloy powder, diamagnetic metallic material particles diameter
Less than 10 μm;
Solvent adopts toluene, one kind of dimethylbenzene and mixture;
Solvent is added in preparation, is vapored away after preparation.
Further, in certain embodiments, the material component of anti-blu-ray layer is with weight proportion:
100 parts of resin
0.5~5 part of anti-blue light auxiliary agent
20~40 parts of solvent;
Resin be acrylic resin, epoxy resin, the one kind in polyurethane resin or polyester resin;
Anti- blue light auxiliary agent is salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile, triazines or hindered amine
One kind of apoplexy due to endogenous wind and combinations thereof;
Solvent adopts toluene, one kind of dimethylbenzene and mixture;
Solvent is added in preparation, is vapored away after preparation.
Further, in certain embodiments, the material component of acrylic adhesive layer is with weight proportion:
Solvent is added in preparation, is vapored away after preparation.
Further, in certain embodiments, the viscosity monomer of acrylic adhesive layer be butyl acrylate, ethyl acrylate,
One or more in Isooctyl acrylate monomer;Interior polycondensation monomer is one or two in vinylacetate, methyl methacrylate;
Modified monomer is one or more in acrylic acid, methacrylic acid, hydroxyethyl methylacrylate;Cross-linking agent be isocyanates,
One kind in benzoyl peroxide, anhydride;Solvent adopts toluene, one kind of dimethylbenzene and mixture.
Upper mould release membrance, lower mould release membrance are the PET of 20~100 μm of thickness, and off-type force is 30~50gf.
A kind of preparation method of the diamagnetic thin film of anti-blue light, method is as follows:
Diamagnetic metal is placed on carrier insulating substrate, on insulating substrate, using intaglio plate coating, nick coating, scraper
One kind in coating, is coated with diamagnetic metal level glue, and 140~180 DEG C of Jing baking boxs solidify 1~2min aftershapings;
Anti- blu-ray layer is coated with coated diamagnetic metal layer, using in intaglio plate coating, nick coating, scraper for coating
One kind, 140~180 DEG C of Jing baking boxs, solidify 1~2min aftershapings;
Mould release membrance is pasted above anti-blu-ray layer;
One layer of acrylic adhesive layer is coated with below insulating substrate so as to can be pasted onto on protected electronic product;
Acrylic adhesive layer adopts comma formula scraper for coating, and Jing after 80~150 DEG C of solidifications, (acrylic is gluing to obtain 20 μm of glue-line
Layer), then paste lower mould release membrance.
Present invention incorporates the function of the anti-electromagnetism of anti-blue light, not only protects the eyes of people from the harm of blue light, together
When protect electronic product from the interference of electromagnetism.
Description of the drawings
Fig. 1 is the structural representation of the present invention.
Description of reference numerals:
Upper mould release membrance 11, anti-blu-ray layer 22, diamagnetic metal level 23, insulating substrate 24, acrylic adhesive layer 25, lower mould release membrance
12。
Specific embodiment
For feature, technological means and the specific purposes for being reached, the function of the present invention can be further appreciated that, this is parsed
Bright advantage and spirit, by by the following examples the present invention is further elaborated.
The present invention the diamagnetic membrane structure of anti-blue light include insulating substrate 24, acrylic adhesive layer 25, diamagnetic metal level 23,
Anti- blu-ray layer 22 and mould release membrance (upper mould release membrance 11, lower mould release membrance 12).
Concrete preparation process is as follows:
Wherein, diamagnetic metal level 23 is placed on carrier insulating substrate 24, using intaglio plate coating, nick coating, scraper for coating
In one kind, 140~180 DEG C of Jing baking boxs, solidification 1~2min aftershapings are heat-conducting layer.
The component of diamagnetic metal level 23 is:100 parts of resin, 5~20 parts of diamagnetic metal material;50~100 μm of thickness.
Wherein, resin be acrylic resin, epoxy resin, the one kind in polyurethane resin, polyester resin.Diamagnetic metal material
Expect for the metal-powders such as copper, silver, nickel, cobalt or its alloy powder.Diamagnetic metallic material particles diameter is not more than 10 μm.
Anti- blu-ray layer 22 is coated with above coated diamagnetic metal level 23, using intaglio plate coating, nick coating, scraper
One kind in coating, 140~180 DEG C of Jing baking boxs solidify 1~2min aftershapings.
The component of anti-blu-ray layer 22 is:100 parts of resin, 0.5~5 part of anti-blue light auxiliary agent;50~100 μm of thickness.Anti- blu-ray layer
22 paste mould release membrance 11 above.
Wherein, resin be acrylic resin, epoxy resin, the one kind in polyurethane resin, polyester resin.Anti- blue light auxiliary agent
For one kind in salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile, triazines and hindered amines and combinations thereof.
One layer of acrylic adhesive layer 25 is coated with below insulating substrate 24 so as to protected electronic product can be pasted onto
On.Acrylic adhesive layer 25 adopts comma formula scraper for coating, and 20 μm of glue-line is obtained Jing after 80~150 DEG C of solidifications, paste down from
Type film 12.
The component of acrylic adhesive layer 25 is:50~60 parts of viscosity monomer, 5~15 parts of interior polycondensation monomer, modified monomer 3~10
Part, 0.1~1 part of cross-linking agent.
Acrylic adhesive layer raw material composition and ratio table (weight portion)
Raw material | A groups | B groups | C groups | D groups | E groups |
Viscosity monomer | 50 | 52 | 60 | 55 | 57 |
Interior polycondensation monomer | 6 | 9 | 8 | 7 | 8 |
Modified monomer | 8 | 4 | 9 | 7 | 5 |
Cross-linking agent | 0.3 | 0.7 | 0.9 | 0.2 | 0.5 |
Solvent | 30 | 26 | 38 | 35 | 22 |
Viscosity monomer is one or more in butyl acrylate, ethyl acrylate, Isooctyl acrylate monomer;Interior polycondensation monomer is
One or two in vinylacetate, methyl methacrylate.Modified monomer is acrylic acid, methacrylic acid, metering system
One or more in sour hydroxyl ethyl ester;Cross-linking agent is the one kind in isocyanates, benzoyl peroxide, anhydride;Solvent adopts first
Benzene, one kind of dimethylbenzene and mixture.
Carrier insulating substrate 24 can have in polyimides, polyethylene, polyvinylidene fluoride, polytetrafluoroethylene film
Any one, wherein based on modified PET, thickness is 50 μm~150 μm.Mould release membrance (upper mould release membrance 11, lower mould release membrance 12) is
20~100 μm of PET, off-type force is 30~50gf.
Embodiment one:
The diamagnetic membrane structure of anti-blue light includes insulating substrate 24, acrylic adhesive layer 25, diamagnetic metal level 23, anti-blu-ray layer
22 and mould release membrance (upper mould release membrance 11, lower mould release membrance 12).
Concrete preparation process is as follows:
Wherein, diamagnetic metal level 23 is placed on carrier insulating substrate 24, using scraper for coating, the 150 DEG C of solidifications of Jing baking boxs
The diamagnetic metal level 23 of 2min aftershapings.
The component of diamagnetic metal level 23 is:100 parts of resin, 10 parts of diamagnetic metal material;75 μm of thickness.
Wherein, resin preferred acrylic resins.Diamagnetic metal material is silver-colored bronze end.Silver metal particles diameter is not more than 10
μm。
Anti- blu-ray layer 22 is coated with above coated diamagnetic metal level 23, using scraper for coating, 160 DEG C of Jing baking boxs are solid
Change the anti-blu-ray layer 22 of 1min aftershapings;Anti- blu-ray layer 22 pastes mould release membrance 11 above.
The component of anti-blu-ray layer 22 is:100 parts of resin, 2.5 parts of anti-blue light auxiliary agent;100 μm of thickness.
Wherein, resin preferred epoxy, the preferred salicylic acid esters of anti-blue light auxiliary agent.
It is last that acrylic adhesive layer 25 is coated with below insulating substrate 24 so as to protected electronics can be pasted onto and produced
On product.Acrylic adhesive layer 25 adopts comma formula scraper for coating, Jing after 140 DEG C of solidifications, obtains 20 μm of glue-line, pastes down release
Film 12.
The component of acrylic adhesive layer 25 is:60 parts of viscosity monomer, 6 parts of interior polycondensation monomer, 5 parts of modified monomer, cross-linking agent 0.1
Part.
Wherein in one embodiment, the viscosity monomer of acrylic adhesive layer 25 is butyl acrylate;Interior polycondensation monomer is vinegar
Vinyl acetate, methyl methacrylate mixing;
Cohesion raw material monomer component is with weight proportion:
The weight portion of vinylacetate 30, the weight portion of methyl methacrylate 70;
Modified monomer material component is with weight proportion:
20 parts by weight of acrylic acid, 60 weight parts of methacrylic acid, 20 weight parts of methacrylic acid hydroxyl ethyl esters composition;
Cross-linking agent is isocyanates.
Insulating carrier film (insulating substrate 24) preferably modified PET film, thickness is 100 μm.Mould release membrance is 50 μm of PET, from
Type power is 30~50gf.
The diamagnetic films test result of the anti-blue light of the present invention:
Blue light rejection rate (%) | Electromagnetism rejection rate (%) | Visible light transmissivity (%) |
65 | 72 | 19 |
Embodiment described above only expresses some embodiments of the present invention, and its description is more concrete and detailed, but and
Therefore limitation of the scope of the invention can not be interpreted as.It should be pointed out that for the person of ordinary skill of the art,
Without departing from the inventive concept of the premise, some deformations and improvement can also be made, these belong to the protection model of the present invention
Enclose.Therefore, protection scope of the present invention should be defined by claims.
Claims (7)
1. the diamagnetic thin film of a kind of anti-blue light, it is characterised in that the diamagnetic thin film of the anti-blue light includes from top to bottom:Upper mould release membrance
(11), anti-blu-ray layer (22), diamagnetic metal level (23), insulating substrate (24), acrylic adhesive layer (25), lower mould release membrance (12);
Anti- blu-ray layer (22) thickness is 50~100 μm;
Diamagnetic metal level (23) thickness is 50~100 μm;
Insulating substrate (24) is have any one in polyimides, polyethylene, polyvinylidene fluoride or polytetrafluoroethylene film,
Thickness is 50 μm~150 μm.
2. a kind of diamagnetic thin film of anti-blue light according to claim 1, it is characterised in that the original of the diamagnetic metal level (23)
Expect that component is with weight proportion:
100 parts of resin
5~20 parts of diamagnetic metal material
20~40 parts of solvent;
Resin be acrylic resin, epoxy resin, the one kind in polyurethane resin or polyester resin;
Diamagnetic metal material is copper, silver, nickel, cobalt metal-powder or its alloy powder, and diamagnetic metallic material particles diameter is less than
10μm;
Solvent adopts toluene, one kind of dimethylbenzene and mixture;
Solvent is added in preparation, is vapored away after preparation.
3. a kind of diamagnetic thin film of anti-blue light according to claim 1, it is characterised in that the raw material of the anti-blu-ray layer (22)
Component is with weight proportion:
100 parts of resin
0.5~5 part of anti-blue light auxiliary agent
20~40 parts of solvent;
Resin be acrylic resin, epoxy resin, the one kind in polyurethane resin or polyester resin;
Anti- blue light auxiliary agent is in salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile, triazines or hindered amines
One kind and combinations thereof;
Solvent adopts toluene, one kind of dimethylbenzene and mixture;
Solvent is added in preparation, is vapored away after preparation.
4. the diamagnetic thin film of a kind of anti-blue light according to claim 1, it is characterised in that the acrylic adhesive layer (25)
Material component is with weight proportion:
Solvent is added in preparation, is vapored away after preparation.
5. the diamagnetic thin film of a kind of anti-blue light according to claim 4, it is characterised in that the acrylic adhesive layer (25)
Viscosity monomer is one kind and mixture in butyl acrylate, ethyl acrylate, Isooctyl acrylate monomer;
Interior polycondensation monomer is one or two in vinylacetate, methyl methacrylate;
Modified monomer is one kind and mixture in acrylic acid, methacrylic acid, hydroxyethyl methylacrylate;
Cross-linking agent is the one kind in isocyanates, benzoyl peroxide or anhydride;
Solvent adopts toluene, one kind of dimethylbenzene and mixture.
6. the diamagnetic thin film of a kind of anti-blue light according to claim 1, it is characterised in that the upper mould release membrance (11), under from
Type film (12) for 20~100 μm of thickness PET, off-type force is 30~50gf.
7. the preparation method of the diamagnetic thin film of a kind of blue light anti-as described in any one of claim 1~6, it is characterised in that method is such as
Under:
Diamagnetic metal level (23) is placed on carrier insulating substrate (24), on insulating substrate (24), is applied using intaglio plate coating, nick
One kind in cloth, scraper for coating, is coated with diamagnetic metal level (23) glue, 140~180 DEG C of Jing baking boxs, after 1~2min of solidification into
Type;
In the coated anti-blu-ray layer (22) of diamagnetic metal level (23) coated thereon, using intaglio plate coating, nick coating, cutter painting is scraped
One kind in cloth, 140~180 DEG C of Jing baking boxs solidify 1~2min aftershapings;
Anti- blu-ray layer (22) pastes mould release membrance (11) above;
One layer of acrylic adhesive layer (25) is coated with below in insulating substrate (24), and acrylic adhesive layer (25) is using comma formula scraper
Coating, Jing after 80~150 DEG C of solidifications, obtains 20 μm of acrylic adhesive layer (25), then pastes lower mould release membrance (12).