CN106565168A - Quick-drying waterproof building material - Google Patents
Quick-drying waterproof building material Download PDFInfo
- Publication number
- CN106565168A CN106565168A CN201610923164.0A CN201610923164A CN106565168A CN 106565168 A CN106565168 A CN 106565168A CN 201610923164 A CN201610923164 A CN 201610923164A CN 106565168 A CN106565168 A CN 106565168A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- quick
- building material
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical field of building materials, and discloses a quick-drying waterproof building material, which comprises, by weight, 20-30 parts of quartz sand, 5-10 parts of talc powder, 3-6 parts of alumina, 15-20 parts of silicate cement, 5-10 parts of a plasticizer, 10-20 parts of a fluorine-containing acrylic resin, 6-8 parts of a polyacrylamide-modified resin, 5-10 parts of organosiloxane, 5-12 parts of a water reducing agent, and 50-70 parts of water. According to the present invention, the waterproof material has advantages of convenient use, good waterproof effect, cracking resistance, delamination resistance, long waterproof time and wide application range, is suitable for various working conditions, and further has characteristics of rapid coagulation and drying and rapid molding so as to easily treat the water leakage.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of quick-drying water-proof building material.
Background technology
Waterproof measure is to prevent water from being taken from construction material and on construction to the infiltration at some positions of building
Measure.Using in roofing, hypogee, the under ground portion of building and needing interior room and water storage structures of waterproof etc. more than waterproof.
The measure taken by which and the difference of means, are divided into two big class of material waterproofing and constructional waterproofing.Material waterproofing is by construction material
Blocking water path, with reach waterproof purpose or increase anti-leakage ability, such as waterproof coiled material, coating waterproofing, concrete and
Cement mortar rigid waterproofing and clay, grey great soil group waterproof etc..Waterproof material Jing of the prior art does not rise and exposes to the weather, especially
It is the waterproof for roof, water-proofing time is shorter, is typically only one or two years, and later stage loss zone is cumbersome, and it is existing anti-
Water material contains the poisonous and harmful substances such as Colophonium, and harmful gass are easily produced during high temperature, pollutes environment.
The content of the invention
The present invention is intended to provide a kind of quick-drying water-proof building material, solves the problems referred to above, easy to use, waterproof well
Effect is good, and water-proofing time is long, applied widely, and energy rapid condensation is dried, and molding is fast, is conducive to the process of leak.
A kind of quick-drying water-proof building material is the technical scheme is that, it is composed of the following components by weight:
Quartz sand 20-30 parts, Pulvis Talci 5-10 parts, aluminium oxide 3-6 parts, portland cement 15-20 parts, plasticiser 5-10
Part, fluoroacrylic resin 10-20 parts, polyacrylamide modified resin 6-8 part, organosiloxane 5-10 parts, water reducer 5-12
Part, water 50-70 parts.
Further, it is composed of the following components by weight:
15 parts of quartz sand, 8 parts of Pulvis Talci, 4 parts of aluminium oxide, 17 parts of portland cement, 8 parts of plasticiser, fluorine-containing tree
15 parts of fat, 7 parts of polyacrylamide modified resin, 8 parts of organosiloxane penetrating agent, 10 parts of water reducer, 60 parts of water.
Further, the water reducer is naphthalene water reducer.
Further, the fluoroacrylic resin is ten difluoro fat in heptan of methacrylic acid.
Further, the polyacrylamide modified resin is that polyacrylamide with methylcellulose as modifying agent is modified
Resin.
Further, the organosiloxane is two functional group's organosiloxanes.
The invention has the beneficial effects as follows:The waterproof material of the present invention is easy to use, good water-proof effect, delamination not easy to crack,
Water-proofing time is long, and waterproof effect at least continues more than 5 years, applied widely, is adapted to various operating modes, and energy rapid condensation is dried,
Molding is fast, is conducive to the process of leak.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, below, the present invention is carried out further
Describe in detail.
Embodiment one, the invention provides a kind of quick-drying water-proof building material, composed of the following components by weight:
20 parts of quartz sand, 5 parts of Pulvis Talci, 3 parts of aluminium oxide, 15 parts of portland cement, 5 parts of plasticiser, fluorine-containing tree
10 parts of fat, 6 parts of polyacrylamide modified resin, 5 parts of organosiloxane, 5 parts of water reducer, 50 parts of water.
Embodiment two, the invention provides a kind of quick-drying water-proof building material, composed of the following components by weight:
15 parts of quartz sand, 8 parts of Pulvis Talci, 4 parts of aluminium oxide, 17 parts of portland cement, 8 parts of plasticiser, fluorine-containing tree
15 parts of fat, 7 parts of polyacrylamide modified resin, 8 parts of organosiloxane penetrating agent, 10 parts of water reducer, 60 parts of water.
Embodiment three, the invention provides a kind of quick-drying water-proof building material, composed of the following components by weight:
30 parts of quartz sand, 10 parts of Pulvis Talci, 6 parts of aluminium oxide, 20 parts of portland cement, 10 parts of plasticiser, fluorine-containing
20 parts of resin, 8 parts of polyacrylamide modified resin, 10 parts of organosiloxane, 12 parts of water reducer, 70 parts of water.
Water reducer is naphthalene water reducer.Fluoroacrylic resin is ten difluoro fat in heptan of methacrylic acid.Polyacrylamide changes
Property resin is the polyacrylamide modified resin with methylcellulose as modifying agent.Organosiloxane is the organic silica of two functional groups
Alkane.
Compared with existing waterproof material, the waterproof material of the present invention is easy to use, good water-proof effect, not easy to crack de-
Layer, water-proofing time are long, and waterproof effect at least continues more than 5 years, applied widely, are adapted to various operating modes, and energy rapid condensation is done
Dry, molding is fast, is conducive to the process of leak.
Certainly, the present invention can also have other various embodiments, in the case of without departing substantially from spirit of the invention and its essence, ripe
Know those skilled in the art and various corresponding changes and deformation, but these corresponding changes and deformation can be made according to the present invention
The protection domain of appended claims of the invention should all be belonged to.
Claims (6)
1. a kind of quick-drying water-proof building material, it is characterised in that composed of the following components by weight:
Quartz sand 20-30 parts, Pulvis Talci 5-10 parts, aluminium oxide 3-6 parts, portland cement 15-20 parts, plasticiser 5-10 parts, contain
Perfluoroalkyl acrylate resin 10-20 parts, polyacrylamide modified resin 6-8 part, organosiloxane 5-10 parts, water reducer 5-12 parts, water
50-70 parts.
2. quick-drying water-proof building material according to claim 1, it is characterised in that composed of the following components by weight:
15 parts of quartz sand, 8 parts of Pulvis Talci, 4 parts of aluminium oxide, 17 parts of portland cement, 8 parts of plasticiser, fluoroacrylic resin 15
Part, 7 parts of polyacrylamide modified resin, 8 parts of organosiloxane, 10 parts of water reducer, 60 parts of water.
3. quick-drying water-proof building material according to claim 1, it is characterised in that the water reducer is naphthalene water reducer.
4. quick-drying water-proof building material according to claim 1, it is characterised in that the fluoroacrylic resin is methyl
Ten difluoro fat in heptan of acrylic acid.
5. quick-drying water-proof building material according to claim 1, it is characterised in that the polyacrylamide modified resin is
Polyacrylamide modified resin with methylcellulose as modifying agent.
6. quick-drying water-proof building material according to claim 1, it is characterised in that the organosiloxane is two functional groups
Organosiloxane.