CN106542783A - A kind of diatom ooze coating - Google Patents
A kind of diatom ooze coating Download PDFInfo
- Publication number
- CN106542783A CN106542783A CN201610842582.7A CN201610842582A CN106542783A CN 106542783 A CN106542783 A CN 106542783A CN 201610842582 A CN201610842582 A CN 201610842582A CN 106542783 A CN106542783 A CN 106542783A
- Authority
- CN
- China
- Prior art keywords
- parts
- white
- powder
- coating
- diatom ooze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of diatom ooze coating, the coating is by making after the raw material mix homogeneously of following weight parts：215 ~ 235 parts of kieselguhr, 40 ~ 60 parts of triple superphosphate, 40 ~ 60 parts of Pulvis Talci, 40 ~ 60 parts of titanium dioxide, 65 ~ 85 parts of latex powder, 2 ~ 6 parts of hydroxypropyl methylcellulose, 180 ~ 220 parts of the white cement that strength grade is 42.5 grades, 20 ~ 40 parts of mica powder, 10 ~ 20 parts of wooden white fiber, 3 ~ 7 parts of bentonite, Snow Flower White 290 ~ 295 parts of sand of coloured silk, 1 ~ 3 part of water reducer, resistance to 0.5 ~ 1.5 part of dimension of towing, 0.2 ~ 0.8 part of anion powder.It is of the invention easily to construct, it is pollution-free, nonpoisonous and tasteless, and good endurance, it is adaptable to dry the Northwest uses.
Description
Technical field
The present invention relates to a kind of coating, more particularly to a kind of diatom ooze coating.
Background technology
Diatom ooze coating in the market, due to itself having stronger adsorptivity, therefore, it is especially suitable for moist gas
The south of time uses, and is not particularly suited for dry the Northwest, and is difficult to grasp the big of muzzle discharging in work progress
It is little.
The content of the invention
The technical problem to be solved is to provide the good diatom ooze coating of a kind of easy construction, durability.
To solve the above problems, a kind of diatom ooze coating of the present invention, it is characterised in that：The coating is by following weight
Make after the raw material mix homogeneously of part：215 ~ 235 parts of kieselguhr, 40 ~ 60 parts of triple superphosphate, 40 ~ 60 parts of Pulvis Talci, titanium dioxide 40 ~ 60
Part, 65 ~ 85 parts of latex powder, 2 ~ 6 parts of hydroxypropyl methylcellulose, 180 ~ 220 parts of the white cement that strength grade is 42.5 grades, mica powder
20 ~ 40 parts, 10 ~ 20 parts of wooden white fiber, 3 ~ 7 parts of bentonite, Snow Flower White 290 ~ 295 parts of sand of coloured silk, 1 ~ 3 part of water reducer, resistance to tow
Dimension 0.5 ~ 1.5 part, 0.2 ~ 0.8 part of anion powder.
The present invention has advantages below compared with prior art：
It is of the invention easily to construct, it is pollution-free, nonpoisonous and tasteless, and good endurance, it is adaptable to dry the Northwest uses.
Specific embodiment
A kind of 1 diatom ooze coating of embodiment, the coating is by following weight parts（Unit：kg）Raw material mix homogeneously after make
Into：It is 215 parts of kieselguhr, 40 parts of triple superphosphate, 40 parts of Pulvis Talci, 40 parts of titanium dioxide, 65 parts of latex powder, 2 parts of hydroxypropyl methylcellulose, strong
Spend 180 parts of white cement, 20 parts of mica powder, 10 parts of wooden white fiber, 3 parts of bentonite, Snow Flower White coloured silk sand 290 that grade is 42.5 grades
Part, 1 part of water reducer, resistance to dimension 0.5 part, 0.2 part of the anion powder of towing.
A kind of 2 diatom ooze coating of embodiment, the coating is by following weight parts（Unit：kg）Raw material mix homogeneously after make
Into：It is 235 parts of kieselguhr, 60 parts of triple superphosphate, 60 parts of Pulvis Talci, 60 parts of titanium dioxide, 85 parts of latex powder, 6 parts of hydroxypropyl methylcellulose, strong
Spend 220 parts of white cement, 40 parts of mica powder, 20 parts of wooden white fiber, 7 parts of bentonite, Snow Flower White coloured silk sand 295 that grade is 42.5 grades
Part, 3 parts of water reducer, resistance to dimension 1.5 parts, 0.8 part of the anion powder of towing.
A kind of 3 diatom ooze coating of embodiment, the coating is by following weight parts（Unit：kg）Raw material mix homogeneously after make
Into：It is 225 parts of kieselguhr, 50 parts of triple superphosphate, 50 parts of Pulvis Talci, 50 parts of titanium dioxide, 75 parts of latex powder, 4 parts of hydroxypropyl methylcellulose, strong
Spend 200 parts of white cement, 30 parts of mica powder, 15 parts of wooden white fiber, 5 parts of bentonite, Snow Flower White coloured silk sand that grade is 42.5 grades
292.5 parts, 2 parts of water reducer, it is resistance to tow dimension 1 part, 0.5 part of anion powder.
In above-described embodiment 1 ~ 3, kieselguhr is produced by Linjiang City of Jilin Province great Hua diatomaceous earth products company limited；Triple superphosphate by
Shimian, Sichuan Ju Feng powder body company limited produces, KKS-1250；Pulvis Talci is by the modest and amiable Mining Market in Liaoning, TLH-902；Titanium dioxide
By one hundred profit connection production, BLR-699；Latex powder is produced by Anhui latex powder company, WWJF-8020；Hydroxypropyl methylcellulose is by mountain
East production, HD6100；Strength grade is that 42.5 grades of white cement is produced by Ningxia；Mica powder is produced by Xuzhou, CJ-A4；It is wooden
White fiber by middle material produce wood fibre, 3000；Bentonite is produced by middle material, CT062；Snow Flower White coloured silk sand is given birth to by Hebei Shijiazhuang
Produce 40 ~ 80 mesh；Water reducer is produced by Sichuan；Resistance to dimension of towing produces chopped fiber 6mm by middle material；Anion powder is by Hebei stone
The family village produces 100 ~ 200 mesh.
Claims (1)
1. a kind of diatom ooze coating, it is characterised in that：The coating is by making after the raw material mix homogeneously of following weight parts：Kieselguhr
215 ~ 235 parts, 40 ~ 60 parts of triple superphosphate, 40 ~ 60 parts of Pulvis Talci, 40 ~ 60 parts of titanium dioxide, 65 ~ 85 parts of latex powder, hydroxypropyl methylcellulose
It is 2 ~ 6 parts of element, 180 ~ 220 parts of the white cement that strength grade is 42.5 grades, 20 ~ 40 parts of mica powder, 10 ~ 20 parts of wooden white fiber, swollen
3 ~ 7 parts of profit soil, Snow Flower White 290 ~ 295 parts of sand of coloured silk, 1 ~ 3 part of water reducer, resistance to 0.5 ~ 1.5 part of dimension, the anion powder 0.2 ~ 0.8 of towing
Part.