CN104072030A - Thermal insulation mortar containing inorganic glass beads and preparation method thereof - Google Patents
Thermal insulation mortar containing inorganic glass beads and preparation method thereof Download PDFInfo
- Publication number
- CN104072030A CN104072030A CN201410221078.6A CN201410221078A CN104072030A CN 104072030 A CN104072030 A CN 104072030A CN 201410221078 A CN201410221078 A CN 201410221078A CN 104072030 A CN104072030 A CN 104072030A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- thermal insulation
- glass beads
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses thermal insulation mortar containing inorganic glass beads. The thermal insulation mortar is prepared from the following raw materials by weight parts: 300-340 parts of cement, 30-35 parts of glass beads, 30-35 parts of chromite sand powder, 2-4 parts of sodium metasilicate, 1-2 parts of glucose powder, 4-6 parts of urea, 4-6 parts of sodium borate, 12-14 parts of aluminum oxide, 12-15 parts of calcium oxide, 4-5 parts of boric acid, 10-12 parts of sodium sulfate, 4-6 parts of Arabic gum, 1-2 parts of tea polyphenol, 4-5 parts of guar gum, 1-2 parts of sodium hexametaphosphate, 4-6 parts of modified nanocarbon powder and 600-650 parts of water. The thermal insulation mortar is relatively good in thermal insulation effect and convenient to construct as the glass beads are used as lightweight aggregates to replace conventional general expanded perlite and polyphenyl granules.
Description
Technical field
The invention belongs to building material field, be specifically related to a kind of inorganic kervit microbead insulated sand slurry and preparation method thereof.
Background technology
China's exterior-wall heat insulation comprises organic heat-insulating system and inorganic heat preservation system and organic and inorganic composite heat-insulating material three classes.Wherein, be mainly organic lagging material, production and operating technique are very ripe, but can not prevent fires, and contaminate environment is easily aging.Mineral-type thermal insulation mortar material is because its finished product is low, and intensity is high, insulation, and fire prevention, the advantages such as weathering resistance are paid close attention to widely, but still have the shortcomings such as cost is higher, material source is limited, still have improved space.
Summary of the invention
The object of this invention is to provide a kind of inorganic kervit microbead insulated sand slurry and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of inorganic kervit microbead insulated sand slurry, is characterized in that being made up of the raw material of following weight part: cement 300-340, glass bead 30-35, chromite sand powder 30-35, Starso 2-4, glucose powder 1-2, urea 4-6, Sodium Tetraborate 4-6, aluminum oxide 12-14, calcium oxide 12-15, boric acid 4-5, sodium sulfate 10-12, gum arabic 4-6, tea-polyphenol 1-2, guar gum 4-5, Sodium hexametaphosphate 99 1-2, modified Nano carbon dust 4-6, water 600-650; Described modified Nano carbon dust is made up of the raw material of following weight part: nano-sized carbon 10-11, alum 5-6, iron ore ground-slag 1-2, jade powder 4-5, silane resin acceptor kh-550 1-2, Radix Angelicae Sinensis oil 1-2, magnet powder 1-2, silicon carbide 4-5, alcohol ester 12 1-2, tea-polyphenol 1-2, Radix Actinodaphnes Cupularis powder 1-2; Each material composition is mixed, and grinding distribution evenly and get final product.
The preparation method of described inorganic kervit microbead insulated sand slurry, it is characterized in that, by mixing except other later composition of cement, being heated to 60-70 DEG C, stirs 20-30 minute, and form slurry, then adds cement mixing become lotion and get final product.
Thermal insulation mortar of the present invention does light skeletal with glass bead, substitutes traditional normal expanded perlite and granular polystyrene, better heat preservation, and easy construction.
Embodiment
A kind of inorganic kervit microbead insulated sand slurry, by following weight part (kilogram) raw material make: cement 300, glass bead 30, chromite sand powder 35, Starso 2, glucose powder 2, urea 6, Sodium Tetraborate 6, aluminum oxide 12, calcium oxide 15, boric acid 4, sodium sulfate 12, gum arabic 4, tea-polyphenol 2, guar gum 4, Sodium hexametaphosphate 99 1, modified Nano carbon dust 6, water 650;
The preparation method of described inorganic kervit microbead insulated sand slurry, it is characterized in that, by mixing except other later composition of cement, being heated to 60-70 DEG C, stirs 20-30 minute, and form slurry, then adds cement mixing become lotion and get final product.
Described modified Nano carbon dust by following weight part (kilogram) raw material make: nano-sized carbon 10, alum 5, iron ore ground-slag 1, jade powder 4, silane resin acceptor kh-550 2, Radix Angelicae Sinensis oil 2, magnet powder 2, silicon carbide 5, alcohol ester 12, tea-polyphenol 2, Radix Actinodaphnes Cupularis powder 1; Each material composition is mixed, and grinding distribution evenly and get final product.
Mortar properties of the present invention is: thermal conductivity 0.051W/m.k, and frost resistance meets the requirements by (15 times are unchanged), 28d ultimate compression strength: 0.35Mpa, fire-protection rating is A level.
Claims (2)
1. an inorganic kervit microbead insulated sand slurry, is characterized in that being made up of the raw material of following weight part: cement 300-340, glass bead 30-35, chromite sand powder 30-35, Starso 2-4, glucose powder 1-2, urea 4-6, Sodium Tetraborate 4-6, aluminum oxide 12-14, calcium oxide 12-15, boric acid 4-5, sodium sulfate 10-12, gum arabic 4-6, tea-polyphenol 1-2, guar gum 4-5, Sodium hexametaphosphate 99 1-2, modified Nano carbon dust 4-6, water 600-650; Described modified Nano carbon dust is made up of the raw material of following weight part: nano-sized carbon 10-11, alum 5-6, iron ore ground-slag 1-2, jade powder 4-5, silane resin acceptor kh-550 1-2, Radix Angelicae Sinensis oil 1-2, magnet powder 1-2, silicon carbide 4-5, alcohol ester 12 1-2, tea-polyphenol 1-2, Radix Actinodaphnes Cupularis powder 1-2; Each material composition is mixed, and grinding distribution evenly and get final product.
2. according to the preparation method with inorganic kervit microbead insulated sand slurry claimed in claim 1, it is characterized in that, by mixing except other later composition of cement, being heated to 60-70 DEG C, stir 20-30 minute, form slurry, then adds cement mixing become lotion and get final product.