CN103043983A - Vitrified microbead heat-preserving mortar - Google Patents
Vitrified microbead heat-preserving mortar Download PDFInfo
- Publication number
- CN103043983A CN103043983A CN2012105738446A CN201210573844A CN103043983A CN 103043983 A CN103043983 A CN 103043983A CN 2012105738446 A CN2012105738446 A CN 2012105738446A CN 201210573844 A CN201210573844 A CN 201210573844A CN 103043983 A CN103043983 A CN 103043983A
- Authority
- CN
- China
- Prior art keywords
- heat
- preserving
- sand slurry
- insulated sand
- kervit microbead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses vitrified microbead heat-preserving mortar. The vitrified microbead heat-preserving mortar comprises the following substances in mass percentage: 60-65% of cementing material, 30-35% of heat-preserving aggregate, 0.5-1% of redispersible latex powder and 1-1.5% of functional material. The vitrified microbead heat-preserving mortar is short in solidification time, good in fire-proof performance and heat-preserving effect and stable in construction performance.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of kervit microbead insulated sand slurry.
Background technology
China's exterior-wall heat insulation comprises organic heat-insulating system and inorganic heat preservation system and organic and inorganic composite heat-insulating material three classes.Wherein, be mainly the organic lagging material, production and operating technique are very ripe, but can not prevent fires, and contaminate environment is easily aging.Mineral-type thermal insulation mortar material is because its finished product is low, and intensity is high, insulation, and fire prevention, the advantages such as weathering resistance are paid close attention to widely, and especially kervit microbead insulated sand slurry has huge development prospect.
But existing vitreous mortar is owing to add wood fibre, the slowly shortcoming but existence is condensed.
Summary of the invention
For addressing the above problem, the present invention adds starch ethers in thermal insulation mortar, and has added gypsum in the gelling composition, and its summary of the invention is: mainly the material by following quality proportioning forms:
Gelling material 60 ~ 65%
Heat preserving aggregate 30 ~ 35%
Redispersable latex powder 0.5 ~ 1%
Functional materials 1 ~ 1.5%
Be water in fact.
Further, described gelling material is that mass ratio is silicate cement and the gypsum of 4:1.
Further, described heat preserving aggregate is that tap density is 110kg/cm
3Glass bead and carbon aerogels.The mass ratio of glass bead and carbon aerogels is 1:2.
Further, described functional materials is that mass ratio is the Mierocrystalline cellulose of 1 ~ 2:1:1:1, xylogen, starch ethers and polypropylene fibre.
Positively effect of the present invention is: setting time is short, fire resistance and high insulating effect, and workability is stable.
Embodiment
Describe technical scheme of the present invention in detail below in conjunction with embodiment, but protection domain is not so limited.
1 one kinds of kervit microbead insulated sand slurries of embodiment; material by following quality proportioning forms: 48% silicate cement; 12% gypsum, 11% glass bead, 22% carbon aerogels; 1% redispersable latex powder; 0.4% Mierocrystalline cellulose, 0.2% xylogen, 0.2% starch ethers; 0.2% polypropylene fibre, 9.8% water.
2 one kinds of kervit microbead insulated sand slurries of embodiment; material by following quality proportioning forms: 52% silicate cement; 13% gypsum, 10% glass bead, 20% carbon aerogels; 1% redispersable latex powder; 0.4% Mierocrystalline cellulose, 0.2% xylogen, 0.2% starch ethers; 0.2% polypropylene fibre, 3% water.
This mortar properties is: thermal conductivity 0.063W/m.k, coefficient of softening are 0.59, and frost resistance meets the requirements by (15 times unchanged), and anti-scorching grade is the A level.
Claims (4)
1. a kervit microbead insulated sand slurry is characterized in that, mainly the material by following quality proportioning forms:
Gelling material 60 ~ 65%
Heat preserving aggregate 30 ~ 35%
Redispersable latex powder 0.5 ~ 1%
Functional materials 1 ~ 1.5%.
2. kervit microbead insulated sand slurry according to claim 1, it is characterized in that: described gelling material is that mass ratio is silicate cement and the gypsum of 4:1.
3. kervit microbead insulated sand slurry according to claim 1, it is characterized in that: described heat preserving aggregate is that tap density is 110kg/cm
3Glass bead and carbon aerogels;
The mass ratio of glass bead and carbon aerogels is 1:2.
4. kervit microbead insulated sand slurry according to claim 1, it is characterized in that: described functional materials is that mass ratio is the Mierocrystalline cellulose of 1 ~ 2:1:1:1, xylogen, starch ethers and polypropylene fibre.