CN106521336B - 代替40Cr调质钢的转向节用非调质钢及其生产方法 - Google Patents
代替40Cr调质钢的转向节用非调质钢及其生产方法 Download PDFInfo
- Publication number
- CN106521336B CN106521336B CN201610981662.0A CN201610981662A CN106521336B CN 106521336 B CN106521336 B CN 106521336B CN 201610981662 A CN201610981662 A CN 201610981662A CN 106521336 B CN106521336 B CN 106521336B
- Authority
- CN
- China
- Prior art keywords
- steel
- tempered steel
- hardened
- quenched
- knuckle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
转向节性能 | Rm/MPa | Rp0.2/MPa | Z(%) | A(%) | AKU2/J | HB |
标准值要求 | ≥850 | ≥580 | ≥20 | ≥10 | ≥35 | 250~298 |
实施例1 | 921 | 628 | 44 | 12 | 55 | 280 |
实施例2 | 911 | 637 | 55 | 15 | 53 | 278 |
实施例3 | 908 | 623 | 52 | 17 | 58 | 273 |
Claims (6)