CN106520304A - Environment-friendly lubricating agent composition for molybdenum alloy spinning processing technology - Google Patents
Environment-friendly lubricating agent composition for molybdenum alloy spinning processing technology Download PDFInfo
- Publication number
- CN106520304A CN106520304A CN201610962492.1A CN201610962492A CN106520304A CN 106520304 A CN106520304 A CN 106520304A CN 201610962492 A CN201610962492 A CN 201610962492A CN 106520304 A CN106520304 A CN 106520304A
- Authority
- CN
- China
- Prior art keywords
- processing technology
- molybdenum alloy
- lubricant composition
- environmental friendliness
- pressing processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an environment-friendly lubricating agent composition for a molybdenum alloy spinning processing technology. The environment-friendly lubricating agent composition for the molybdenum alloy spinning processing technology adopts ester oil pentaerythritol dicaprate as base oil, which is matched with multiple composite additives comprising an antioxygen, a metal deactivator, an oiliness agent, a friction improver, an extreme pressure agent, an antiwear agent, an antirust agent, a tackifier, an oxidation and corrosion inhibitor and the like. The composition provided by the invention has favorable cooling performance, lubricating performance, diffusivity, cleaning ability, anti-rust property, antioxygen corrosion resistance, capability of reducing surface scrapes and scratches, and high adhesion.
Description
Technical field
A kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition of the present invention belongs to metal working lubricant neck
Domain.
Background technology
Molybdenum alloy adds other elements and the non-ferrous alloy that constituted based on molybdenum.Main alloy element have titanium, zirconium, hafnium,
Tungsten and rare earth element.Molybdenum alloy has good heat conduction, electric conductivity and the low coefficient of expansion, and (1100~1650 DEG C) have at high temperature
High intensity, is easily worked than tungsten.Can be used as the grid and anode of electron tube, the backing material of electric light source, and be used to make
Die casting and extrusion die, parts of spacecraft etc..The main reinforcing approach of molybdenum alloy is solution strengthening, precipitation strength and processing
Hardening.Molybdenum alloy sheet material, band, foil, tubing, bar, wire rod and section bar can be obtained by plastic working, moreover it is possible to improve which strong
Spend and improve cold plasticity.
Rotary pressure technology originates from ancient times pottery.He is that one kind combines forging, extruding, draw piece, bending, looping mill rolling, horizontal stroke
Roll the few advanced technologies without machining with the process characteristic such as edging.Generally metal letter base, plate blank or prefabricated blank are used
Tail top is held out against on spinning machine mould, drives plug and blank rotation by main shaft;Material is extruded by spinning wheel from blank side simultaneously
On the core of rotation, make material produce pointwise and be continuously plastically deformed, so as to obtain the hollow rotary body of various shape of generatrix
Part.According to the blank thickness situation of change during rotary pressing processing, spinning process is divided into conventional spinning and shear spinning two
Plant, i.e. conventional spinning and shear spinning.
The referred to as general rotation of conventional spinning.During general rotation, the thickness of blank is held essentially constant, and shaping relies primarily on blank edge
The contraction of circumference and along radial direction it is indeformable realizing with length.Which is mainly characterized by forming process, substantially can be seen
Go out the change of blank external diameter.The basic mode of conventional spinning has:Draw spinning (drawing rotation), necking in spindown (contracting rotation) and expanding bulging
Three kinds of (expanding rotation) etc..Environmental friendliness molybdenum alloy rotary pressing processing technology lubricant requires to reduce rotary pressing processing load, promotes metal
Flow in a mold, prevent mould stuck, reduce die wear and spillage of material, accelerate radiating, improve flow formed part quality, residual
The bits rate of recovery and production efficiency.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of with good cooling, lubricity, diffusivity, cleaning
Property, rust-preventing characteristic, antioxygen anti-corrosive properties, reduce galled spots and the strong environmental friendliness molybdenum alloy rotary pressing processing work of scratch and adhesiveness
Skill lubricant compositions.
The present invention solves above-mentioned technical problem by following technical solution:
A kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition, using Esters oil pentaerythrite dicaprate
Based on oil, coordinate various compound additives, its each mass percent into being grouped into:
Component | Mass percentage content |
Base oil | Surplus |
Antioxidant | 0.05~0.3% |
Metal deactivator | 0.05~0.3% |
Oiliness improver | 4~6% |
Friction improver | 1~2% |
Extreme pressure agent | 3~5% |
Antiwear additive | 5~7% |
Antirust agent | 0.06~0.3% |
Oxidation and corrosion inhibitor | 0.5~1.2% |
Tackifier | 2~6% |
Filler | 3~5% |
The mass percent summation of above each component is 100%.
Antioxidant is the N of the sulfenyl phenolate T514 and 50% using mass ratio 50%, and accelerine is combined.
Metal deactivator is the complexing agent T532 of derivative containing benzotriazole.
Oiliness improver is sulfurized lard.Friction improver is sulphur molybdenum phosphate T461.
Extreme pressure agent is tricresol phosphate fat T306.Antiwear additive is chlorinated paraffin T302.
Antirust agent is that the alkenyl succinic acid T746 of the BTA T706 and 50% of mass ratio 50% is combined.
Oxidation and corrosion inhibitor is dialkyl dithio amino acid tungsten.Tackifier are ethylene-propylene copolymer T613A.
Filler is dialkyldithiocarbamacompositions sulfuration oxygen molybdenum MoPTC.
It is an advantage of the current invention that:The composition of the present invention has good cooling, lubricity, and (extreme-pressure anti-wear is carried
Property), diffusivity, cleaning, rust-preventing characteristic, antioxygen anti-corrosive properties, reduce galled spots and scratch and adhesiveness be strong, spinning can be reduced
Machining load, promotes metal to flow in a mold, prevents mould stuck, reduce die wear and spillage of material, accelerate radiating, carry
High flow formed part quality, the detritus rate of recovery and production efficiency.
Specific embodiment
Embodiment 1:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
Esters oil (pentaerythrite dicaprate) | Surplus |
The sulfenyl phenolate (T514) of mass ratio 50% and 50% N, accelerine are combined | 0.1% |
The complexing agent of derivative containing benzotriazole (T532) | 1.9% |
Sulfurized lard (T404) | 4.0% |
Sulphur molybdenum phosphate (T461) | 1.5% |
Tricresol phosphate fat (T306) | 3.5% |
Chlorinated paraffin (T302) | 4.0% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid (T746) are compound | 0.2% |
Ethylene-propylene copolymer (T613A) | 3.4% |
Dialkyldithiocarbamacompositions sulfuration oxygen molybdenum (MoPTC) | 1.1% |
Dialkyl dithio amino acid tungsten | 0.8% |
Above each component mass percentage content summation is 100%.
Embodiment 2:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
Esters oil (pentaerythrite dicaprate) | Surplus |
The sulfenyl phenolate (T514) of mass ratio 50% and 50% N, accelerine are combined | 0.2% |
The complexing agent of derivative containing benzotriazole (T532) | 1.8% |
Sulfurized lard (T404) | 5.3% |
Sulphur molybdenum phosphate (T461) | 1.5% |
Tricresol phosphate fat (T306) | 4.7% |
Chlorinated paraffin (T302) | 4.1% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid (T746) are compound | 0.1% |
Ethylene-propylene copolymer (T613A) | 4.4% |
Dialkyldithiocarbamacompositions sulfuration oxygen molybdenum (MoPTC) | 1.1% |
Dialkyl dithio amino acid tungsten | 1.2% |
Above each component mass percentage content summation is 100%.
Embodiment 3:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
Esters oil (pentaerythrite dicaprate) | Surplus |
The sulfenyl phenolate (T514) of mass ratio 50% and 50% N, accelerine are combined | 0.15% |
The complexing agent of derivative containing benzotriazole (T532) | 1.85% |
Sulfurized lard (T404) | 4.2% |
Sulphur molybdenum phosphate (T461) | 1.3% |
Tricresol phosphate fat (T306) | 2.5% |
Chlorinated paraffin (T302) | 3.0% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid (T746) are compound | 0.2% |
Ethylene-propylene copolymer (T613A) | 5.4% |
Dialkyldithiocarbamacompositions sulfuration oxygen molybdenum (MoPTC) | 1.0% |
Dialkyl dithio amino acid tungsten | 0.5% |
Above each component mass percentage content summation is 100%.
The key technical indexes of 3 product of embodiment
Project | Index |
100 DEG C of kinematic viscosity/(mm2S-1) | 24.5 |
Flash-point/DEG C | 271 |
Condensation point/DEG C | -32 |
Viscosity index (VI) | 147 |
Corrosion (copper sheet, 100 DEG C, 3h)/level | 1 |
82 DEG C of (40-40-6)/min of demulsification number | 10 |
Tetra-ball machine test, Pb/N | 965 |
Sintering load, PD/N | 6850 |
Terraced nurse is agreed, N | 315 |
FZG, level | 13 |
Moisture, % | Vestige |
Mechanical admixture, % | Nothing |
Evaporation loss (Noack methods, 250 DEG C, 1h) (m), % | 8.2 |
The key technical indexes of 2 product of embodiment
Project | Index |
100 DEG C of kinematic viscosity/(mm2S-1) | 23.9 |
Flash-point/DEG C | 272 |
Condensation point/DEG C | -31 |
Viscosity index (VI) | 169 |
Corrosion (copper sheet, 100 DEG C, 3h)/level | 1 |
82 DEG C of (40-40-6)/min of demulsification number | 9 |
Tetra-ball machine test, Pb/N | 961 |
Sintering load, PD/N | 6880 |
Terraced nurse is agreed, N | 325 |
FZG, level | 13 |
Moisture, % | Vestige |
Mechanical admixture, % | Nothing |
Evaporation loss (Noack methods, 250 DEG C, 1h) (m), % | 8.3 |
The key technical indexes of 1 product of embodiment
Project | Index |
100 DEG C of kinematic viscosity/(mm2S-1) | 24.5 |
Flash-point/DEG C | 276 |
Condensation point/DEG C | -33 |
Viscosity index (VI) | 177 |
Corrosion (copper sheet, 100 DEG C, 3h)/level | 1 |
82 DEG C of (40-40-6)/min of demulsification number | 8 |
Tetra-ball machine test, Pb/N | 972 |
Sintering load, PD/N | 6755 |
Terraced nurse is agreed, N | 315 |
FZG, level | 13 |
Moisture, % | Vestige |
Mechanical admixture, % | Nothing |
Evaporation loss (Noack methods, 250 DEG C, 1h) (m), % | 6.8 |
Claims (10)
1. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition, it is characterised in that:Using Esters oil Ji Wusi
Oil based on alcohol dicaprate, coordinates various compound additives, its each mass percent into being grouped into:
The mass percent summation of above each component is 100%.
2. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Antioxidant is the N of the sulfenyl phenolate T514 and 50% using mass ratio 50%, and accelerine is combined.
3. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Metal deactivator is the complexing agent T532 of derivative containing benzotriazole.
4. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Oiliness improver is sulfurized lard.
5. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Friction improver is sulphur molybdenum phosphate T461.
6. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Extreme pressure agent is tricresol phosphate fat T306.
7. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Antiwear additive is chlorinated paraffin T302.
8. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Antirust agent is that the alkenyl succinic acid T746 of the BTA T706 and 50% of mass ratio 50% is combined.
9. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Oxidation and corrosion inhibitor is dialkyl dithio amino acid tungsten.
10. a kind of environmental friendliness molybdenum alloy rotary pressing processing technology lubricant composition as claimed in claim 1, it is characterised in that
Tackifier are ethylene-propylene copolymer T613A;Filler is dialkyldithiocarbamacompositions sulfuration oxygen molybdenum MoPTC.