CN106519965A - 9H ceramic paint - Google Patents
9H ceramic paint Download PDFInfo
- Publication number
- CN106519965A CN106519965A CN201610741669.5A CN201610741669A CN106519965A CN 106519965 A CN106519965 A CN 106519965A CN 201610741669 A CN201610741669 A CN 201610741669A CN 106519965 A CN106519965 A CN 106519965A
- Authority
- CN
- China
- Prior art keywords
- ceramic paint
- ceramic
- silicon solution
- paint
- monosilane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses 9H ceramic paint. The 9H ceramic paint is prepared from the following ingredients in percentage by mass: 40% of silicon solution, 40% of monosilane, 19.98% of titanium white, 0.01% of silicone oil and 0.01% of neutralizer. A method for preparing the 9H ceramic paint specifically comprises the following steps of proportionally weighing the raw materials, dispersing the silicon solution and the titanium white until the degree of fineness is 10 microns or less, then, adding the ingredients, i.e., the monosilane, the silicone oil and the neutralizer into the dispersion, and carrying out stirring for 6 hours. By adopting the technical scheme of the invention, the 9H ceramic paint has the following beneficial effects that the 9H ceramic paint disclosed by the invention can enable the hardness of a paint film to exceed 9H, is high in hardness and is scratch-resistant, fireproof, smokeless, environmentally friendly and pollution-free; and meanwhile, the 9H ceramic paint further has the characteristics of rich colors and delicate paint film hand feeling.
Description
Technical field
A kind of the present invention relates to technical field of coatings, more particularly to high-rigidity ceramic coating being applied on ceramics.
Background technology
Ceramic coating hardness itself is high, but toughness is poor, in use, is easily collided, is impacted, being scraped etc. and cause
Adhesive force is deteriorated, ftractures or come off；Chinese patent CN105566956A, discloses a kind of high abrasion-proof and high temperature resistant water boiling resistance aqueous
Ceramic coating, its main technical schemes is：By tri- component of A, B, C according to mass ratio：666：333：1 mixes, wherein：A groups
Point：Percentages based on ceramic coating gross mass：Ludox 26-30%, antimony solution 13-15%, inorganic high-temperature resistant face
Material 5-13% and silica 8-12%；B component：Percentages based on ceramic coating gross mass：Silane 30-34%,
Wetting agent 0.4-0.6%, levelling agent 0.4-0.6%；Component C：Percentages based on ceramic coating gross mass：Catalyst
0.1%, made by which, ceramic hardness can reach 8H, it is well known that, antimony is heavy metal, not only pollutes environment, and right
Health of human body is harmful to, and is clearly prohibitted the use of in some fields.
In today of the track traffics such as high ferro, city underground great development, the design that the disaster prevention in its place is related will be
Emphasis.Traditional solvent-borne coating is more with organic solvents such as toluene, dimethylbenzene, butyl acetates as diluent, and which manufactures and constructed
Journey causes huge pollution because of a large amount of discharges of organic solvent to environment.Traditional solvent-borne coating products are using in similar subway
Stand, the place of the enclosed environment such as station, once fire, produces a large amount of poisonous dense smokes, often increases and evacuates passenger, the disaster relief of putting out a fire
Difficulty.It is in addition, mobility of people is big during track traffic circulation, also big to the colliding with of ornament materials, abrasive probability,
The contaminated possibility in surface also increases.Existing ceramic water-soluble environmental protection coating material, the surface state in work progress to substrate
Requirement is relatively low, need to do sandblasting, bead, and operation is simple.
The content of the invention
It is an object of the invention to provide a kind of high rigidity, scratch resistance, the ceramics painting for preventing fires smokeless and environment friendly and pollution-free
Material.
Further object is that providing the preparation method of above-mentioned ceramic coating.
For solving above technical problem, the present invention provides a kind of 9H ceramic coatings, is made up of following component by mass fraction：
Silicon solution 40%
Monosilane 40%
Titanium dioxide 19.98%
Silicone oil：0.01%
Nertralizer 0.01%.
Preferably, the silicon solution is many alkoxy silane water-base resins and complex.
A kind of method for preparing 9H ceramic coatings, specifically includes following steps：Take above-mentioned raw materials in proportion, by silicon solution and
Titanium dioxide fineness of dispersion to below 10um, then plus monosilane, silicone oil, nertralizer component, stir 6 hours.
Had the advantages that using technical scheme：The 9H ceramic coatings of the present invention can allow hardness of paint film
9H is crossed, high rigidity, scratch resistance, fire prevention are smokeless and environment friendly and pollution-free, meanwhile, also with various colors, paint film feel is fine and smooth.
Specific embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below in conjunction with specific embodiment.
Embodiment 1
The present invention provides a kind of 9H ceramic coatings, is made up of following component by mass fraction：
Specifically, the silicon solution is many alkoxy silane water-base resins and complex.
Preparation method：Above-mentioned raw materials are taken in proportion, by silicon solution and titanium dioxide fineness of dispersion to below 10um, then plus first silicon
Alkane, silicone oil, nertralizer component, stir 6 hours.
The 9H ceramic coatings of the present invention can allow hardness of paint film to cross 9H, and high rigidity, scratch resistance, fire prevention are smokeless, and environmental protection
It is pollution-free, meanwhile, also with various colors, paint film feel is fine and smooth.
The testing result of embodiments of the invention 1 is as shown in the table：
As upper table can be seen that the ceramic coating using the present invention, hardness can reach 9H, and acidproof, water-fast, resistance to
Heat, it is wear-resisting, and flat appearance is smooth.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (3)
1. a kind of 9H ceramic coatings, it is characterised in that be made up of following component by mass fraction：
Silicon solution 40%
Monosilane 40%
Titanium dioxide 19.98%
Silicone oil：0.01%
Nertralizer 0.01%.
2. a kind of 9H ceramic coatings according to claim 1, it is characterised in that：The silicon solution is many alkoxy silane water
Property resin and complex.
3. a kind of method for preparing 9H ceramic coatings as claimed in claim 1, it is characterised in that comprise the following steps：By than
Example take above-mentioned raw materials, by silicon solution and titanium dioxide fineness of dispersion to below 10um, then plus monosilane, silicone oil, nertralizer component, stir
Mix 6 hours.