CN106519887A - Scratch-resistant and wearproof paint special for elevators and preparation method thereof - Google Patents
Scratch-resistant and wearproof paint special for elevators and preparation method thereof Download PDFInfo
- Publication number
- CN106519887A CN106519887A CN201610769182.8A CN201610769182A CN106519887A CN 106519887 A CN106519887 A CN 106519887A CN 201610769182 A CN201610769182 A CN 201610769182A CN 106519887 A CN106519887 A CN 106519887A
- Authority
- CN
- China
- Prior art keywords
- parts
- scratch
- wear
- special coating
- elevator special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a scratch-resistant and wearproof paint special for elevators. The paint is prepared from the following raw materials by weight: 20-45 parts of epoxy resin; 5-10 parts of nano aluminium oxide; 2-4 parts of rosin soap; 15-30 parts of a silane coupling agent; 10-15 parts of glycerin; 1-5 parts of water-soluble acrylic resin; 10-15 parts of butanone; 20-45 parts of deionized water; 1-3 parts of sodium dodecyl benzene sulfonate; 1-5 parts of a dispersant; and 1-5 parts of a curing agent. The invention also discloses a preparation method of the scratch-resistant and wearproof paint special for elevators. The paint prepared by the method provided by the invention has the advantages of scratch resistance, wear resistance, high hardness, beautiful appearance and multicolor.
Description
Technical field
The present invention relates to elevators field, more particularly to a kind of anti-scratch spend wear-resisting elevator special coating.
Background technology
With the propulsion of urbanization process, increasing high buildings and large mansions are stood in people at one's side.Elevator becomes high-rise
Building is requisite to take instrument, and its demand grows with each passing day.The car of elevator typically using sheet metal as decoration panel,
But the decoration of sheet metal selects less, client is unsatisfactory for for elevator decorates diversified requirement.In addition, sheet metal holds
Trace is scratched easily, hardness is low.With the growth requirement of elevator, it is possible to provide a kind of high-quality, low cost and green coating, can realize
Scratch resistance, anti-stone hit, corrosion-resistant, high rigidity, colorful purpose attractive in appearance.
The content of the invention
The technical problem to be solved is, there is provided it is a kind of it is anti-scratch spend wear-resisting elevator special coating, it is scratch resistance, resistance to
Mill, high rigidity and attractive in appearance colorful.
In order to solve above-mentioned technical problem, the invention provides one kind is anti-scratch to spend wear-resisting elevator special coating, including it is following
Raw material by weight is obtained：
Epoxy resin 20-45 parts；
Nano-aluminium oxide 5-10 parts；
Rosin soap 2-4 parts；
Silane coupler 15-30 parts；
Glycerine 10-15 parts；
Water soluble acrylic resin's 1-5 parts；
Butanone 10-15 parts；
Deionized water 20-45 part；
Neopelex 1-3 parts；
Dispersant 1-5 parts；
Curing agent 1-5 parts.
Used as the improvement of such scheme, the dispersant is PEG 20000.
Used as the improvement of such scheme, silane coupler is aminomethylsilanes, aminoethylaminopropyl silane, aminoethyl ammonia
One kind or combination in hydroxypropyl methyl silane.
As the improvement of such scheme, also including bentonite, the bentonite is calculated as 5-10 parts by weight.
As the improvement of such scheme, also comprising selected from wetting agent, ultra-violet absorber, pigment, fluidity regulator, in
With the composition of one or more of agent and defoamer.
Used as the improvement of such scheme, the particle diameter of the nano-aluminium oxide is 50-150nm.
Used as the improvement of such scheme, the epoxy resin is bisphenol A type epoxy resin.
Correspondingly, the present invention also provides a kind of anti-scratch preparation method for spending wear-resisting elevator special coating, including following
Step：
The each raw material in formula is weighed by weight；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Implement the embodiment of the present invention, have the advantages that：
Three oxidation of nanometer that particle diameter is 50-150nm is added in the anti-scratch formula for spending wear-resisting elevator special coating of the present invention
Two aluminium, can effectively improve the hardness of coating, and scratch resistance and anti-wear performance have significant progress.And rosin is added in formula
Soap, cohesive force are good, can significantly improve anti-cracking ability, durable in use.And the material such as silane coupler, epoxy resin can strengthen
Adhesion of the coating to metal so as to which coating has the advantages that corrosion-resistant, high strength, electrical insulating property are good.Additionally, of the invention
In composition of raw materials, the functional group without phenyl ring, can avoid producing the noxious material of acute and chronic poisoning, harmless to health of human body.
And the present invention is water paint, overcomes pollution of the solvent based coating to environment, is a kind of environmental protection and safety type coating.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, will make further detailed to the present invention below
Description.
Present invention offer one kind is anti-scratch to spend wear-resisting elevator special coating, including following raw material to be by weight obtained：
Epoxy resin 20-45 parts；
Nano-aluminium oxide 5-10 parts；
Rosin soap 2-4 parts；
Silane coupler 15-30 parts；
Glycerine 10-15 parts；
Water soluble acrylic resin's 1-5 parts；
Butanone 10-15 parts；
Deionized water 20-45 part；
Neopelex 1-3 parts；
Dispersant 1-5 parts；
Curing agent 1-5 parts.
Preferably, it is of the present invention it is anti-scratch spend wear-resisting elevator special coating, including following raw material by weight is obtained：
Epoxy resin 25-35 parts；
Nano-aluminium oxide 6-8 parts；
Rosin soap 2-3 parts；
Silane coupler 18-25 parts；
Glycerine 12-15 parts；
Water soluble acrylic resin's 1-3 parts；
Butanone 13-15 parts；
Deionized water 30-40 part；
Neopelex 1-3 parts；
Dispersant 2-3 parts；
Curing agent 2-4 parts.
Nano material has special uvioresistant, anti-aging, high intensity and toughness, good electrostatic screening effect, color
The function such as damp conversion effect and antibacterial and deodorizing, adds particle diameter in the anti-scratch formula for spending wear-resisting elevator special coating of the present invention
For the nano-aluminium oxide of 50-150nm, the hardness of coating can be effectively improved, scratch resistance and anti-wear performance have significantly to enter
Step.And rosin soap is added in formula, cohesive force is good, can significantly improve anti-cracking ability, durable in use.
In addition, silane coupler causes coating and the car panel caking property of metal material to strengthen in inventive formulation, it is attached
Put forth effort strong.In addition, silane coupler can also improve the inorganic fillers such as nano-aluminium oxide and rosin soap in the epoxy
Dispersiveness and bonding force, improve the compatibility between nano silicon and rosin soap and epoxy resin.It should be noted that making
For the preferred version of silane coupler, silane coupler is aminomethylsilanes, aminoethylaminopropyl silane, aminoethylaminopropyl
One kind or combination in methyl-monosilane.
Epoxy resin of the present invention is water miscible bisphenol A type epoxy resin, and bisphenol A type epoxy resin is cured
There are the excellent properties of many protrusions afterwards, it is such as particularly very strong to the adhesion of metal to various materials, have very strong chemically-resistant rotten
Corrosion, mechanical strength are very high, electrical insulating property is good, corrosion-resistant etc..
Preferably, dispersant of the present invention is PEG 20000.
Preferably, also include bentonite in raw material of the present invention, the bentonite is calculated as 5-10 parts by weight.
Preferably, also comprising selected from wetting agent, ultra-violet absorber, pigment, mobility regulation in raw material of the present invention
The composition of one or more of agent, nertralizer and defoamer.
In composition of raw materials of the present invention, the functional group without phenyl ring, can avoid producing the noxious material of acute and chronic poisoning,
It is harmless to health of human body.And the present invention is water paint, overcomes pollution of the solvent based coating to environment, it is a kind of environmental protection peace
Holotype coating.
The invention also discloses a kind of anti-scratch preparation method for spending wear-resisting elevator special coating, comprises the following steps：
The each raw material in formula is weighed by weight；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Further illustrate below by way of specific embodiment
Embodiment 1
It is anti-scratch described in the present embodiment to spend wear-resisting elevator special coating, including following raw material to be by weight obtained：40 parts of epoxies
Resin；6 parts of nano-aluminium oxides；2 parts of rosin soaps；17 parts of silane couplers；15 parts of glycerine；3 parts of water soluble acrylic resins；
12 parts of butanone；35 parts of deionized waters；1 part of neopelex；2 parts of dispersants；2 parts of curing agent.
The anti-scratch preparation method for spending wear-resisting elevator special coating, comprises the following steps：Weighed in formula by weight
Each raw material；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Embodiment 2
It is anti-scratch described in the present embodiment to spend wear-resisting elevator special coating, including following raw material to be by weight obtained：35 parts of epoxies
Resin；7 parts of nano-aluminium oxides；3 parts of rosin soaps；22 parts of silane couplers；12 parts of glycerine；2 parts of water soluble acrylic resins；
13 parts of butanone；40 parts of deionized waters；2 parts of neopelexes；3 parts of dispersants；4 parts of curing agent.
The anti-scratch preparation method for spending wear-resisting elevator special coating, comprises the following steps：Weighed in formula by weight
Each raw material；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Embodiment 3
It is anti-scratch described in the present embodiment to spend wear-resisting elevator special coating, including following raw material to be by weight obtained：28 parts of epoxies
Resin；8 parts of nano-aluminium oxides；2 parts of rosin soaps；25 parts of silane couplers；14 parts of glycerine；5 parts of water soluble acrylic resins；
11 parts of butanone；38 parts of deionized waters；3 parts of neopelexes；5 parts of dispersants；3 parts of curing agent.
The anti-scratch preparation method for spending wear-resisting elevator special coating, comprises the following steps：Weighed in formula by weight
Each raw material；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Embodiment 4
It is anti-scratch described in the present embodiment to spend wear-resisting elevator special coating, including following raw material to be by weight obtained：33 parts of epoxies
Resin；9 parts of nano-aluminium oxides；4 parts of rosin soaps；28 parts of silane couplers；11 parts of glycerine；3 parts of water soluble acrylic resins；
10 parts of butanone；35 parts of deionized waters；3 parts of neopelexes；2 parts of dispersants；2 parts of curing agent.
The anti-scratch preparation method for spending wear-resisting elevator special coating, comprises the following steps：Weighed in formula by weight
Each raw material；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.
Last should be noted that above example is only to illustrate technical scheme rather than the present invention is protected
The restriction of shield scope, although being explained in detail to the present invention with reference to preferred embodiment, one of ordinary skill in the art should
Understand, technical scheme can be modified or equivalent, without deviating from the essence of technical solution of the present invention
And scope.
Claims (8)
1. one kind is anti-scratch spends wear-resisting elevator special coating, it is characterised in that be obtained including following raw material by weight：
Epoxy resin 20-45 parts；
Nano-aluminium oxide 5-10 parts；
Rosin soap 2-4 parts；
Silane coupler 15-30 parts；
Glycerine 10-15 parts；
Water soluble acrylic resin's 1-5 parts；
Butanone 10-15 parts；
Deionized water 20-45 part；
Neopelex 1-3 parts；
Dispersant 1-5 parts；
Curing agent 1-5 parts.
2. it is anti-scratch as claimed in claim 1 to spend wear-resisting elevator special coating, it is characterised in that the dispersant is polyethylene glycol
20000。
3. it is anti-scratch as claimed in claim 1 to spend wear-resisting elevator special coating, it is characterised in that silane coupler is amino methyl silicon
One kind or combination in alkane, aminoethylaminopropyl silane, aminoethylaminopropyl methyl-monosilane.
4. it is anti-scratch as claimed in claim 1 to spend wear-resisting elevator special coating, it is characterised in that also including bentonite, the swelling
Soil is calculated as 5-10 parts by weight.
5. it is as claimed in claim 1 anti-scratch to spend wear-resisting elevator special coating, it is characterised in that also comprising selected from wetting agent, ultraviolet
The composition of one or more of light absorbers, pigment, fluidity regulator, nertralizer and defoamer.
6. it is anti-scratch as claimed in claim 1 to spend wear-resisting elevator special coating, it is characterised in that the grain of the nano-aluminium oxide
Footpath is 50-150nm.
7. it is anti-scratch as claimed in claim 1 to spend wear-resisting elevator special coating, it is characterised in that the epoxy resin is bisphenol A-type
Epoxy resin.
8. a kind of as claimed in claim 1 anti-scratch preparation method for spending wear-resisting elevator special coating, it is characterised in that including following
Step：
The each raw material in formula is weighed by weight；
By nano-aluminium oxide, rosin soap, epoxy resin, silane coupler, glycerine, butanone, neopelex, point
Powder is poured in the container equipped with deionized water, stirs 60-120 minutes, obtain mixed solution at a temperature of 50-70 DEG C；
The mixed solution, curing agent and water soluble acrylic resin are uniformly mixing to obtain described anti-scratch spends wear-resisting elevator special
Coating.