CN106519762A - Waterproof mechanical coating and preparation method thereof - Google Patents
Waterproof mechanical coating and preparation method thereof Download PDFInfo
- Publication number
- CN106519762A CN106519762A CN201610928186.6A CN201610928186A CN106519762A CN 106519762 A CN106519762 A CN 106519762A CN 201610928186 A CN201610928186 A CN 201610928186A CN 106519762 A CN106519762 A CN 106519762A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirred
- high speed
- preparation
- speed dispersor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to waterproof mechanical coating and a preparation method thereof. The waterproof mechanical coating is prepared from the following ingredients (by weight): 4-9 parts of styrene, 7-10 parts of tetrabutylphosphonium chloride, 2-5 parts of methyl styrene linear biopolymer, 1-3 parts of tartrate, 3-7 parts of a fluorinated acrylate prefabricated solution, 5-9 parts of epoxy resin, 3-5 parts of mica powder, 1-5 parts of sodium tripolyphosphate, 6-9 parts of coal tar, 4-9 parts of chlorinated paraffin, 2-5 parts of cobalt trifluoro acetylacetonate and 15-20 parts of deionized water. The invention has the following beneficial effects: the waterproof mechanical coating has high waterproofness, good wear resistance and high mechanical property.
Description
Technical field
The present invention relates to mechanical paint field, and in particular to a kind of mechanical coating and preparation method thereof.
Background technology
Plant equipment (such as planting machine) is present in all trades and professions, has brought many products and facility, in people
Life in play critically important effect.Plant equipment generally uses metal and makes, it is therefore desirable to do water-proofing treatment.Together
When, plant equipment is easily worn in use.It is exactly on planting machine top layer to solve one of method of these problems at present
Coating coating.But, the water resistance of existing planting machine coating is not high, easily weares and teares.
The content of the invention
In sum, in order to overcome the deficiencies in the prior art, the technical problem to be solved to be to provide a kind of machine
Tool coating and preparation method thereof.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of water proof machine coating, by following parts by weight
Component make:Styrene 4-9 parts, tetrabutyl phosphorus chloride 7-10 parts, methyl styrene linear dimeric 2-5 parts, tartaric acid 1-3
Part, fluorinated acrylate preformed solution 3-7 parts, epoxy resin 5-9 parts, mica powder 3-5 parts, sodium tripolyphosphate 1-5 parts, coal tar
6-9 parts, chlorinated paraffin 4-9 parts, trifluoroacetylacetone (TFA) cobalt 2-5 parts and deionized water 15-20 part.
A kind of preparation method of water proof machine coating, is obtained by the steps:
(1) each component of following parts by weight is weighed respectively:Styrene 4-9 parts, tetrabutyl phosphorus chloride 7-10 parts, methylbenzene
Ethene linear dimeric 2-5 parts, tartaric acid 1-3 parts, fluorinated acrylate preformed solution 3-7 parts, epoxy resin 5-9 parts, mica
Powder 3-5 parts, sodium tripolyphosphate 1-5 parts, coal tar 6-9 parts, chlorinated paraffin 4-9 parts, trifluoroacetylacetone (TFA) cobalt 2-5 parts and deionization
Water 15-20 parts.
(2) styrene that step (1) weighed, tetrabutyl phosphorus chloride, methyl styrene linear dimeric, tartaric acid, contain
Fluorinated monomer preformed solution, epoxy resin, mica powder, sodium tripolyphosphate and deionized water are added in reactor, in 30 DEG C
Under, after 50min being stirred in high speed dispersor obtain the first mixture;
(3) in the first mixture obtained in step (2), addition step (1) is weighed coal tar and chlorinated paraffin, in 40
At DEG C, obtain the second mixture after 60min being stirred in high speed dispersor;
(4) the trifluoroacetylacetone (TFA) cobalt that addition step (1) is weighed in the second mixture obtained in step (3), in 50 DEG C
Under, after stirring 70min in high speed dispersor.
Further, stirred with 500rpm rotating speeds in high speed dispersor in step (2).
Further, stirred with 600rpm rotating speeds in high speed dispersor in step (3).
Further, stirred with 700rpm rotating speeds in high speed dispersor in step (4).
The invention has the beneficial effects as follows:Not only water resistance is high, and wearability is good, with very high mechanical performance.
Specific embodiment
The principle and feature of the present invention are described below in conjunction with instantiation, example is served only for explaining this
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1
A kind of preparation method of water proof machine coating, is obtained by the steps:
(1) each component of following parts by weight is weighed respectively:4 parts of styrene, 7 parts of tetrabutyl phosphorus chloride, methyl styrene
2 parts of linear dimeric, 1 part of tartaric acid, 3 parts of fluorinated acrylate preformed solution, 5 parts of epoxy resin, 3 parts of mica powder, trimerization phosphorus
15 parts of 1 part of sour sodium, 6 parts of coal tar, 4 parts of chlorinated paraffin, 2 parts of trifluoroacetylacetone (TFA) cobalt and deionized water.
(2) styrene that step (1) weighed, tetrabutyl phosphorus chloride, methyl styrene linear dimeric, tartaric acid, contain
Fluorinated monomer preformed solution, epoxy resin, mica powder, sodium tripolyphosphate and deionized water are added in reactor, in 30 DEG C
Under, after 50min being stirred with 500rpm rotating speeds in high speed dispersor obtain the first mixture;
(3) in the first mixture obtained in step (2), addition step (1) is weighed coal tar and chlorinated paraffin, in 40
At DEG C, obtain the second mixture after 60min being stirred with 600rpm rotating speeds in high speed dispersor;
(4) the trifluoroacetylacetone (TFA) cobalt that addition step (1) is weighed in the second mixture obtained in step (3), in 50 DEG C
Under, stirred after 70min with 700rpm rotating speeds in high speed dispersor.
Embodiment 2
A kind of preparation method of water proof machine coating, is obtained by the steps:
(1) each component of following parts by weight is weighed respectively:7 parts of styrene, 8 parts of tetrabutyl phosphorus chloride, methyl styrene
4 parts of linear dimeric, 2 parts of tartaric acid, 5 parts of fluorinated acrylate preformed solution, 7 parts of epoxy resin, 4 parts of mica powder, trimerization phosphorus
17 parts of 2 parts of sour sodium, 8 parts of coal tar, 7 parts of chlorinated paraffin, 3 parts of trifluoroacetylacetone (TFA) cobalt and deionized water.
(2) styrene that step (1) weighed, tetrabutyl phosphorus chloride, methyl styrene linear dimeric, tartaric acid, contain
Fluorinated monomer preformed solution, epoxy resin, mica powder, sodium tripolyphosphate and deionized water are added in reactor, in 30 DEG C
Under, after 50min being stirred with 500rpm rotating speeds in high speed dispersor obtain the first mixture;
(3) in the first mixture obtained in step (2), addition step (1) is weighed coal tar and chlorinated paraffin, in 40
At DEG C, obtain the second mixture after 60min being stirred with 600rpm rotating speeds in high speed dispersor;
(4) the trifluoroacetylacetone (TFA) cobalt that addition step (1) is weighed in the second mixture obtained in step (3), in 50 DEG C
Under, stirred after 70min with 700rpm rotating speeds in high speed dispersor.
Embodiment 3
A kind of preparation method of water proof machine coating, is obtained by the steps:
(1) each component of following parts by weight is weighed respectively:9 parts of styrene, 10 parts of tetrabutyl phosphorus chloride, methyl styrene
5 parts of linear dimeric, 3 parts of tartaric acid, 7 parts of fluorinated acrylate preformed solution, 9 parts of epoxy resin, 5 parts of mica powder, trimerization phosphorus
20 parts of 5 parts of sour sodium, 9 parts of coal tar, 9 parts of chlorinated paraffin, 5 parts of trifluoroacetylacetone (TFA) cobalt and deionized water.
(2) styrene that step (1) weighed, tetrabutyl phosphorus chloride, methyl styrene linear dimeric, tartaric acid, contain
Fluorinated monomer preformed solution, epoxy resin, mica powder, sodium tripolyphosphate and deionized water are added in reactor, in 30 DEG C
Under, after 50min being stirred with 500rpm rotating speeds in high speed dispersor obtain the first mixture;
(3) in the first mixture obtained in step (2), addition step (1) is weighed coal tar and chlorinated paraffin, in 40
At DEG C, obtain the second mixture after 60min being stirred with 600rpm rotating speeds in high speed dispersor;
(4) the trifluoroacetylacetone (TFA) cobalt that addition step (1) is weighed in the second mixture obtained in step (3), in 50 DEG C
Under, stirred after 70min with 700rpm rotating speeds in high speed dispersor.
The foregoing is only presently preferred embodiments of the present invention, not to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (5)
1. a kind of water proof machine coating, it is characterised in that be made up of the component of following parts by weight:Styrene 4-9 parts, the tetrabutyl
Phosphorus chloride 7-10 parts, methyl styrene linear dimeric 2-5 parts, tartaric acid 1-3 parts, fluorinated acrylate preformed solution 3-7 parts,
Epoxy resin 5-9 parts, mica powder 3-5 parts, sodium tripolyphosphate 1-5 parts, coal tar 6-9 parts, chlorinated paraffin 4-9 parts, trifluoroacetyl
Acetone cobalt 2-5 parts and deionized water 15-20 part.
2. a kind of preparation method of water proof machine coating, it is characterised in that be obtained by the steps:
(1) each component of following parts by weight is weighed respectively:Styrene 4-9 parts, tetrabutyl phosphorus chloride 7-10 parts, methyl styrene
Linear dimeric 2-5 parts, tartaric acid 1-3 parts, fluorinated acrylate preformed solution 3-7 parts, epoxy resin 5-9 parts, mica powder 3-5
Part, sodium tripolyphosphate 1-5 parts, coal tar 6-9 parts, chlorinated paraffin 4-9 parts, trifluoroacetylacetone (TFA) cobalt 2-5 parts and deionized water 15-
20 parts;
(2) styrene that step (1) weighed, tetrabutyl phosphorus chloride, methyl styrene linear dimeric, tartaric acid, fluorine-containing third
Olefin(e) acid ester preformed solution, epoxy resin, mica powder, sodium tripolyphosphate and deionized water are added in reactor, at 30 DEG C,
The first mixture is obtained after 50min is stirred in high speed dispersor;
(3) in the first mixture obtained in step (2), addition step (1) is weighed coal tar and chlorinated paraffin, at 40 DEG C,
The second mixture is obtained after 60min is stirred in high speed dispersor;
(4) the trifluoroacetylacetone (TFA) cobalt that addition step (1) is weighed in the second mixture obtained in step (3), at 50 DEG C,
After 70min is stirred in high speed dispersor.
3. preparation method according to claim 2, it is characterised in that with 500rpm in high speed dispersor in step (2)
Rotating speed is stirred.
4. preparation method according to claim 2, it is characterised in that with 600rpm in high speed dispersor in step (3)
Rotating speed is stirred.
5. preparation method according to claim 2, it is characterised in that with 700rpm in high speed dispersor in step (4)
Rotating speed is stirred.