CN106515102A - Health care fabric with magnetic therapy function and preparation method thereof - Google Patents
Health care fabric with magnetic therapy function and preparation method thereof Download PDFInfo
- Publication number
- CN106515102A CN106515102A CN201610772309.1A CN201610772309A CN106515102A CN 106515102 A CN106515102 A CN 106515102A CN 201610772309 A CN201610772309 A CN 201610772309A CN 106515102 A CN106515102 A CN 106515102A
- Authority
- CN
- China
- Prior art keywords
- layer
- magnetic therapy
- fabric
- intermediate layer
- therapy functions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Relating to the field of functional fabrics, the invention provides a health care fabric with magnetic therapy function and a preparation method thereof. The health care fabric with magnetic therapy function is composed of an inner layer, a middle layer and an outer layer that are bonded by an adhesive, the inner layer and the outer layer are both made of natural fiber fabric, and the middle layer is composed of organic fiber cloth, far infrared magnetic powder, negative ion natural mineral powder, and polytetrafluoroethylene. The functional fabric provided by the invention has the health care effects of activating human cells, enhancing immunity, promoting metabolism and improving blood circulation, and also has breathable and waterproof effects, long-standing health care effect. The fabric is comfortable, soft, safe and non-irritant.
Description
Technical field
The present invention relates to functional fabric, and in particular to a kind of healthcare face fabric with magnetic therapy functions and preparation method thereof.
Background technology
Current era, people more pursue the health level of body, and people ill are asked by past to the theory of health
Doctor develops into active prevention.From last century, people have begun to research and develop far-infrared textiles and magnetic textile.Far infrared
Fiber be it is a kind of by efficient absorption and transmitting infrared ray and there is the function of heat-preserving health-care；Magnetic textile then has textile
With the characteristic of magnetic material, with magnetotherapy effect, magnetic therapy has the effect that：1st, the magnetic force sent by magnetic material has very strong
Penetrance, magnetic field be delivered to deep layer cells tissue, make the biological magnetic field of cell change, produce Magnetic Induction, activation
Cell, accelerates metabolism, adjusts nerve, Xie Teng towns pain；2nd, make the macromolecular mass of assembly be cut into subset, then cut
Into monomer molecule, intermolecular affinity is reduced, reduce aggregation, increased mobility, prevent the diseases such as cerebral thrombosiss, cerebral embolism disease
Occur；3rd, proliferative cell is controlled, improves microcirculation, pathological changes is controlled and is treated；4th, strengthen local blood circulation, organize
Permeability improves, and is conducive to dissipation, the absorption of exudate；In addition the nonspecific immunity power of human body can also be improved in magnetic field, make white thin
Born of the same parents enliven, and phagocytic activity strengthens, so have detumescence antiinflammation.
103088628 A of Chinese patent CN disclose a kind of preparation side for having thermotherapy and the silk fabric of magnetotherapeutic function concurrently
Method, the invention mid-infrared/magnetic powder and silkworm silk are combined by contaminating, and infrared/magnetic powder is the powder of solid-state
End, so in its aqueous dispersion, so its adhesion and silkworm silk between is very weak, can only play magnetic therapy at short notice
Effect, and the sulfate used in the invention is irritant to human body.
The content of the invention
For the deficiencies in the prior art, the invention provides a kind of healthcare face fabric, not only with Magnetotherapeutic health effect, meets
Demand of the people to health, and human body is not stimulated, it is safe.
A kind of healthcare face fabric with magnetic therapy functions, is made up of internal layer, intermediate layer and outer layer, internal layer, intermediate layer and outer layer
Bondd by adhesive between composition, the internal layer and outer layer are constituted by natural fabric material, and the intermediate layer is by organic fibre
Wei Bu, far infrared magnetic powder, anion natural mineral powder, politef composition.
Preferably, the natural fiber be cotton, the one kind in silkworm silk.
Preferably, the organic fiber is the one kind in milk protein fiber, bamboo fibre and tencel fiber.
Preferably, the adhesive is TPU.
Preferably, the anion natural minerals are hexacyclic ring stone, opal shale, energy stone, the one kind in tourmaline
Or numerous compositions.
Preferably, the anion natural minerals for 30～50nm.
A kind of preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) far infrared magnetic powder, anion natural mineral powder are added in ptfe emulsion, with ball mill grinding 1～
3h, then 30～60min of ultrasonic disperse, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of organic fiber cloth, coating layer thickness is 0.25～
0.75mm, is then put into organic fiber cloth in 80～120 DEG C of baking oven and is dried 5～12h, obtain intermediate layer；
(3) upper surface in intermediate layer applies the adhesive that thickness is 0.05～0.1mm, then natural fabric material is laid in
Top, is plated with flatiron, naturally cools to room temperature, then in the same way in another side one layer of natural fiber of bonding in intermediate layer
Fabric, obtains the healthcare face fabric with magnetic therapy functions.
Preferably, the preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) far infrared magnetic powder, anion natural mineral powder are added in ptfe emulsion, uses ball mill grinding
1.5h, then the ultrasonic disperse 60min under 40KHz, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of organic fiber cloth, coating layer thickness is 0.25mm,
Then organic fiber cloth is put in 80 DEG C of baking oven and is dried 10h, obtain intermediate layer；
(3) upper surface in intermediate layer applies adhesive of the thickness for 0.08mm, then natural fabric material is laid in top,
Plated with flatiron, naturally cool to room temperature, then in the same way in another side one layer of natural fabric material of bonding in intermediate layer,
Obtain the healthcare face fabric with magnetic therapy functions.
Beneficial effects of the present invention：(1) functional fabric of the invention has, activating human body cells, increases immunity, promotes
Metabolism, improves blood circulation, the healthy favourable effect to people；(2) politef has air permeable waterproof
Effect, allows far infrared magnetic powder, anion natural mineral powder through film permeation in meridians, and fabric is being used and cleaned
During, far infrared magnetic powder, anion natural mineral powder will not be lost in, drop, with permanent health-care effect；(3) in health care
The surface of layer is in composite natral cotton fiber so that the comfortableness of fabric and flexibility increase；(4) it is all in fabric of the invention to add
Plus agent be it is nontoxic, it is non-stimulated, it is safe.
Specific embodiment
Technical scheme is clearly and completely illustrated below in conjunction with the embodiment of the present invention.
Embodiment 1：
A kind of healthcare face fabric with magnetic therapy functions, is made up of internal layer, intermediate layer and outer layer, internal layer, intermediate layer and outer layer
Bondd by adhesive between composition, the internal layer and outer layer are constituted by natural fabric material, and the intermediate layer is by organic fibre
Wei Bu, far infrared magnetic powder, anion natural mineral powder, politef composition.
The preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) tourmaline powder that far infrared magnetic powder, particle diameter are 50nm is added in ptfe emulsion, ground with ball mill
Mill 1.5h, then the ultrasonic disperse 60min under 40KHz, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of organic fiber cloth, coating layer thickness is 0.25mm,
Then tencel fiber is put in 80 DEG C of baking oven and is dried 10h, obtain intermediate layer；
(3) upper surface in intermediate layer applies TPU emulsion of the thickness for 0.08mm, then silk fiber fabric is laid in
Side, is plated with flatiron, naturally cools to room temperature, then in the same way in one layer of natural fiber face of another side bonding in intermediate layer
Material, obtains the healthcare face fabric with magnetic therapy functions.
Embodiment 2：
A kind of healthcare face fabric with magnetic therapy functions, is made up of internal layer, intermediate layer and outer layer, internal layer, intermediate layer and outer layer
Bondd by adhesive between composition, the internal layer and outer layer are constituted by natural fabric material, and the intermediate layer is by organic fibre
Wei Bu, far infrared magnetic powder, anion natural mineral powder, politef composition.
The preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) the opal shale that far infrared magnetic powder, particle diameter are 30nm is added in ptfe emulsion, ground with ball mill
Mill 1h, then in 28KHz ultrasonic disperse 60min, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of milk protein fiber, coating layer thickness is 0.5mm,
Then organic fiber cloth is put in 100 DEG C of baking oven and is dried 12h, obtain intermediate layer；
(3) upper surface in intermediate layer applies TPU emulsion of the thickness for 0.1mm, then natural cotton fiber fabric is laid in
Side, is plated with flatiron, naturally cools to room temperature, then in the same way in one layer of natural fiber face of another side bonding in intermediate layer
Material, obtains the healthcare face fabric with magnetic therapy functions.
Embodiment 3：
A kind of healthcare face fabric with magnetic therapy functions, is made up of internal layer, intermediate layer and outer layer, internal layer, intermediate layer and outer layer
Bondd by adhesive between composition, the internal layer and outer layer are constituted by natural fabric material, and the intermediate layer is by organic fibre
Wei Bu, far infrared magnetic powder, anion natural mineral powder, politef composition.
The preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) tourmaline that far infrared magnetic powder, particle diameter are 30nm is added in ptfe emulsion, use ball mill grinding
2h, then in 40KHz ultrasonic disperse 30min, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of bamboo fibre, coating layer thickness is 0.75mm, then
Organic fiber cloth is put in 120 DEG C of baking oven and is dried 5h, obtain intermediate layer；
(3) upper surface in intermediate layer applies TPU emulsion of the thickness for 0.05mm, then natural cotton fiber fabric is laid in
Side, is plated with flatiron, naturally cools to room temperature, then in the same way in one layer of natural fiber face of another side bonding in intermediate layer
Material, obtains the healthcare face fabric with magnetic therapy functions.
Embodiment 4：
A kind of healthcare face fabric with magnetic therapy functions, is made up of internal layer, intermediate layer and outer layer, internal layer, intermediate layer and outer layer
Bondd by adhesive between composition, the internal layer and outer layer are constituted by natural fabric material, and the intermediate layer is by organic fibre
Wei Bu, far infrared magnetic powder, anion natural mineral powder, politef composition.
The preparation method of the healthcare face fabric with magnetic therapy functions, comprises the following steps：
(1) in ptfe emulsion far infrared magnetic powder, particle diameter is added to be 50 nanometers for the tourmaline of 40nm, particle diameter
Opal shale, uses ball mill grinding 3h, then in 28KHz ultrasonic disperse 30min, obtains mixed emulsion；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of milk protein fiber, coating layer thickness is 0.5mm,
Then organic fiber cloth is put in 100 DEG C of baking oven and is dried 10h, obtain intermediate layer；
(3) upper surface in intermediate layer applies TPU emulsion of the thickness for 0.06mm, then silk fiber fabric is laid in
Side, is plated with flatiron, naturally cools to room temperature, then in the same way in one layer of natural fiber face of another side bonding in intermediate layer
Material, obtains the healthcare face fabric with magnetic therapy functions.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any those familiar with the art the invention discloses technical scope in, the change or replacement that can be readily occurred in,
Should all be included within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection model of claims
Enclose and be defined.
Claims (8)
1. a kind of healthcare face fabric with magnetic therapy functions, it is characterised in that：It is made up of internal layer, intermediate layer and outer layer, internal layer, centre
Bondd by adhesive between layer and outer layer composition, the internal layer and outer layer are constituted by natural fabric material, the intermediate layer
It is made up of organic fiber cloth, far infrared magnetic powder, anion natural mineral powder, politef.
2. there is the healthcare face fabric of magnetic therapy functions as claimed in claim 1, it is characterised in that：The natural fiber is cotton, silkworm
One kind in silk.
3. there is the healthcare face fabric of magnetic therapy functions as claimed in claim 2, it is characterised in that the organic fiber is milk egg
One kind in white fiber, bamboo fibre and tencel fiber.
4. there is the healthcare face fabric of magnetic therapy functions as claimed in claim 3, it is characterised in that：The adhesive is TPU.
5. there is the healthcare face fabric of magnetic therapy functions as claimed in claim 4, it is characterised in that：The anion natural minerals are
One or more compositions in hexacyclic ring stone, opal shale, energy stone, tourmaline.
6. there is the healthcare face fabric of magnetic therapy functions as claimed in claim 5, it is characterised in that the anion natural minerals
For 30～50nm.
7. a kind of preparation method of the healthcare face fabric with magnetic therapy functions as described in claim 1～6 is arbitrary, its feature exist
In comprising the following steps：
(1) far infrared magnetic powder, anion natural mineral powder are added in ptfe emulsion, with 1～3h of ball mill grinding, so
30～60min of ultrasonic disperse, obtains mixed emulsion afterwards；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of organic fiber cloth, coating layer thickness is 0.25～
0.75mm, is then put into organic fiber cloth in 80～120 DEG C of baking oven and is dried 5～12h, obtain intermediate layer；
(3) upper surface in intermediate layer applies the adhesive that thickness is 0.05～0.1mm, then natural fabric material is laid in
Side, is plated with flatiron, naturally cools to room temperature, then in the same way in one layer of natural fiber face of another side bonding in intermediate layer
Material, obtains the healthcare face fabric with magnetic therapy functions.
8. there is the preparation method of the healthcare face fabric of magnetic therapy functions as claimed in claim 7, it is characterised in that including following step
Suddenly：
(1) far infrared magnetic powder, anion natural mineral powder are added in ptfe emulsion, uses ball mill grinding 1.5h, so
The ultrasonic disperse 60min under 40KHz, obtains mixed emulsion afterwards；
(2) mixed emulsion of step (1) is uniformly coated on the two sides of organic fiber cloth, coating layer thickness is 0.25mm, then
Organic fiber cloth is put in 80 DEG C of baking oven and is dried 10h, obtain intermediate layer；
(3) upper surface in intermediate layer applies adhesive of the thickness for 0.08mm, then natural fabric material is laid in top, with pressing
Bucket plates, and naturally cools to room temperature, then obtains in another side one layer of natural fabric material of bonding in intermediate layer in the same way
Healthcare face fabric with magnetic therapy functions.