CN108560248A - A kind of anion liner and preparation method thereof and mask - Google Patents
A kind of anion liner and preparation method thereof and mask Download PDFInfo
- Publication number
- CN108560248A CN108560248A CN201810040256.3A CN201810040256A CN108560248A CN 108560248 A CN108560248 A CN 108560248A CN 201810040256 A CN201810040256 A CN 201810040256A CN 108560248 A CN108560248 A CN 108560248A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- anion
- liner
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anion liners, it is raw material by using tourmaline, medical stone, titanium dioxide, makrolon, polylactic acid, poly- second lactone, diisobutyl phthalate, melamine and carries out suitable weight proportion, the anion liner being finally prepared, anion can be generated, release negative ion amount is up to 6,000 8000/cm3, it is good to the filtration of haze, air is facilitated clean up, health is beneficial to, immunity can be improved;Further by the anion liner for mask to be made, for user in breathing in a large amount of anion suction bodies, smooth breathing has the function of anti-PM2.5, antibacterial, haze, anti-sandstorm, anti-influenza etc..It can auxiliary treatment infectious respiratory disease and prevention infectious respiratory disease using health, safety based on mask made of the anion liner.
Description
Technical field
The invention belongs to mask technical fields, and in particular to a kind of anion liner and preparation method thereof and mask.
Background technology
Mask is a kind of amenities, refers generally to be worn over nose and mouth for filtering the air for entering mouth and nose, to reach resistance
The apparatus for keeping off harmful gas, smell, droplet disengaging wearer's mouth and nose, is made with gauze or paper etc..Mask is to entering lung
Air has certain filtration, and in respiratory infectious disease prevalence, in the environment of the pollutions such as dust when operation, wear masks tool
There is extraordinary effect.Mask can be divided into air filtering type mask and Gas feeding mask.
Air pollution was increasingly severe since in recent years, and especially since the beginning of this year, China occurs to continue mist on a large scale
The haze phenomenon of haze, dust and sand weather, especially Beijing-tianjin-hebei Region is even more serious.According to statistics, impacted haze region area accounts for about
The 1/4 of national territorial area, about 600,000,000 people of affected population.Because of the deterioration of air quality, thick weather phenomenon increases,
Harm aggravates.Haze, dust and sand weather phenomenon are incorporated to mist together as diastrous weather early-warning and predicting by Chinese many areas.It is referred to as
For " haze weather ".Expert advice haze weather reduces to the greatest extent outgoing, when outgoing, wear qualified mask, contributes to people
Body health.
The height of the dust collection efficiency of mask is with it to fine dust, especially to 2.5 microns of respirable dusts below
Barriering efficiency is standard.Because the dust of this grain size can directly enter alveolar, influenced caused by health maximum.It is general
Gauze mask, resistance dirt principle is mechanical filtration, exactly when dust crashes into gauze, by barrier from level to level, by one
A little large dust particle barriers are in the gauze.It, will be from yarn but to some fine dusts, especially less than 2.5 microns of dust
It goes through, enters the respiratory system in the mesh of cloth.PM2.5 crises are arrived, and air pollution is killed as the stealth for endangering human health
Hand.
Anion is a kind of negatively charged gas ion in air, and anion can not only promote human body to synthesize and store dimension
Raw element, strengthens the physiological activity with human activin, has highly important influence to the vital movement of human body and other biological, because
This it be otherwise known as " air vitamin ".And it is thought as the vitamin of food, it lives to the life of human body and other biological
Dynamic to have highly important influence, having it is even contemplated that negative aeroion is related with longevity, it is referred to as " long-lived element ".
Invention content
In order to solve the above problem of the existing technology, the present invention provides a kind of anion liners and preparation method thereof
And mask.Liner of the present invention can generate anion, good to the filtration of haze, facilitate clean up air, be beneficial to people
Body health, can be improved immunity.
The technical solution adopted in the present invention is:
A kind of anion liner, raw material components include:
Tourmaline 12-18 parts by weight, medical stone 1-5 parts by weight, titanium dioxide 1-5 parts by weight, makrolon 2-5 weight
Part, 2-6 parts by weight polylactic acid, the poly- second lactone of 2-6 parts by weight, 2-6 parts by weight diisobutyl phthalate, 2-8 parts by weight three
Poly cyanamid, water 80-120 parts by weight.
The raw material components of the further preferred anion liner include:
Tourmaline 14-16 parts by weight, medical stone 2-4 parts by weight, titanium dioxide 2-4 parts by weight, makrolon 3-4 weight
Part, 3-4 parts by weight polylactic acid, the poly- second lactone of 3-4 parts by weight, 3-4 parts by weight diisobutyl phthalate, 4-6 parts by weight three
Poly cyanamid, water 90-110 parts by weight.
The raw material components of the further preferred anion liner include:
15 parts by weight of tourmaline, 3 parts by weight of medical stone, 3 parts by weight of titanium dioxide, 3.5 parts by weight of makrolon, 3.5 weights
Measure part polylactic acid, the poly- second lactone of 3.5 parts by weight, 3.5 parts by weight diisobutyl phthalates, 5 parts by weight melamines, water
100 parts by weight.
A method of the anion liner is prepared, is included the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
It is spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and is heated;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, it is fully reacted under agitation, obtains slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics to get the anion liner.
In step (1), the grain size of each material is 200-300 mesh after crushing.
In step (2), the temperature for carrying out the heat treatment is 46-55 DEG C, and the time for carrying out the heat treatment is 25-
30min。
In step (3), the rate for carrying out the stirring is 350-450rpm, and the time for carrying out the stirring is 40-
45min。
In step (3), the temperature for carrying out the reaction is 60-80 DEG C.
In step (4), coating procedure controls scraper gauge 1-2mm, produces speed 8-12m/min, oven temperature 170-180
℃.Scraper gauge is less than 1mm, then the anion concentration uniformity declines, and scraper gauge is more than 2mm, and production efficiency reduces.
A kind of mask including the anion liner.
Beneficial effects of the present invention are:
Anion liner of the present invention, by using tourmaline, medical stone, titanium dioxide, makrolon, poly- breast
Sour, poly- second lactone, diisobutyl phthalate, melamine are raw material and carry out suitable weight proportion, are finally prepared into
The anion liner arrived, can generate anion, and release negative ion amount is up to 6000-8000/cm3, the filtering of haze is made
It makes good use of, facilitates clean up air, be beneficial to health, immunity can be improved;Further by the anion liner for being made
Mask, for user in breathing in a large amount of anion suction bodies, smooth breathing has anti-PM2.5, antibacterial, haze, sand prevention
Cruelly, the functions such as anti-influenza.It can auxiliary treatment respiratory tract biography using health, safety based on mask made of the anion liner
It contaminates disease and prevents infectious respiratory disease.
Specific implementation mode
With reference to embodiment, the invention will be further described.
In following example 1g is represented with 1 parts by weight.
Embodiment 1
The present embodiment provides a kind of anion liner, raw material components include:
12 parts by weight of tourmaline, 5 parts by weight of medical stone, 1 parts by weight of titanium dioxide, 5 parts by weight of makrolon, 2 parts by weight
The poly- second lactone of polylactic acid, 6 parts by weight, 2 parts by weight diisobutyl phthalates, 8 parts by weight melamines, 80 parts by weight of water.
Further, the present invention provides a kind of preparation method of the anion liner, includes the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
The grain size of each material is 200 mesh after crushing, spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and heat treatment 30min is carried out at 46 DEG C;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, under the stirring condition of 350rpm, 60 DEG C be stirred reaction 45min, obtain slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics, coating procedure controls scraper gauge
1mm, produces speed 8m/min, and the anion liner is finally made in 170 DEG C of oven temperature.
Embodiment 2
The present embodiment provides a kind of anion liner, raw material components include:
18 parts by weight of tourmaline, 1 parts by weight of medical stone, 5 parts by weight of titanium dioxide, 2 parts by weight of makrolon, 6 parts by weight
The poly- second lactone of polylactic acid, 2 parts by weight, 6 parts by weight diisobutyl phthalates, 2 parts by weight melamines, 120 parts by weight of water.
Further, the present invention provides a kind of preparation method of the anion liner, includes the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
The grain size of each material is 300 mesh after crushing, spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and heat treatment 25min is carried out at 55 DEG C;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, under the stirring condition of 450rpm, 80 DEG C be stirred reaction 40min, obtain slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics, coating procedure controls scraper gauge
2mm, produces speed 12m/min, and the anion liner is finally made in 180 DEG C of oven temperature.
Embodiment 3
The present embodiment provides a kind of anion liner, raw material components include:
14 parts by weight of tourmaline, 4 parts by weight of medical stone, 2 parts by weight of titanium dioxide, 4 parts by weight of makrolon, 3 parts by weight
The poly- second lactone of polylactic acid, 4 parts by weight, 3 parts by weight diisobutyl phthalates, 6 parts by weight melamines, 90 parts by weight of water.
Further, the present invention provides a kind of preparation method of the anion liner, includes the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
The grain size of each material is 250 mesh after crushing, spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and heat treatment 28min is carried out at 50 DEG C;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, under the stirring condition of 400rpm, 70 DEG C be stirred reaction 42min, obtain slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics, coating procedure controls scraper gauge
1.5mm, produces speed 10m/min, and the anion liner is finally made in 175 DEG C of oven temperature.
Embodiment 4
The present embodiment provides a kind of anion liner, raw material components include:
16 parts by weight of tourmaline, 2 parts by weight of medical stone, 4 parts by weight of titanium dioxide, 3 parts by weight of makrolon, 4 parts by weight
The poly- second lactone of polylactic acid, 3 parts by weight, 4 parts by weight diisobutyl phthalates, 4 parts by weight melamines, 110 parts by weight of water.
Further, the present invention provides a kind of preparation method of the anion liner, includes the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
The grain size of each material is 250 mesh after crushing, spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and heat treatment 28min is carried out at 50 DEG C;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, under the stirring condition of 400rpm, 70 DEG C be stirred reaction 42min, obtain slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics, coating procedure controls scraper gauge
1.5mm, produces speed 10m/min, and the anion liner is finally made in 175 DEG C of oven temperature.
Embodiment 5
The present embodiment provides a kind of anion liner, raw material components include:
15 parts by weight of tourmaline, 3 parts by weight of medical stone, 3 parts by weight of titanium dioxide, 3.5 parts by weight of makrolon, 3.5 weights
Measure part polylactic acid, the poly- second lactone of 3.5 parts by weight, 3.5 parts by weight diisobutyl phthalates, 5 parts by weight melamines, water
100 parts by weight.
Further, the present invention provides a kind of preparation method of the anion liner, includes the following steps:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively,
The grain size of each material is 250 mesh after crushing, spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and heat treatment 28min is carried out at 50 DEG C;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate are sequentially added in material after being heated to step (2)
And melamine, under the stirring condition of 400rpm, 70 DEG C be stirred reaction 42min, obtain slurry, it is spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics, coating procedure controls scraper gauge
1.5mm, produces speed 10m/min, and the anion liner is finally made in 175 DEG C of oven temperature.
Experimental example
Experimental subjects:In the mask for choosing common cotton mask liner, General Purpose Rubber mask liner and the embodiment of the present application 5
Lining is compared.
Requirement of experiment:Above-mentioned common cotton mask liner, General Purpose Rubber mask liner and the embodiment of the present application 5 bear from
Rim of the mouth cover inner lining material thickness with it is in the same size.
Experimental result is as shown in table 1.
The performance table of comparisons of table 1- difference mask liners
As it can be seen from table 1 anion mask of the present invention can generate anion, the service life is longer, and tension is strong
Higher is spent, toxic gas benzene can be effectively adsorbed, to the filter effect higher of PM2.5.
The present invention is not limited to above-mentioned preferred forms, anyone can show that other are various under the inspiration of the present invention
The product of form, however, make any variation in its shape or structure, it is every that there is skill identical or similar to the present application
Art scheme, is within the scope of the present invention.
Claims (10)
1. a kind of anion liner, which is characterized in that raw material components include:
Tourmaline 12-18 parts by weight, medical stone 1-5 parts by weight, titanium dioxide 1-5 parts by weight, makrolon 2-5 parts by weight, 2-6
The poly- second lactone of parts by weight polylactic acid, 2-6 parts by weight, 2-6 parts by weight diisobutyl phthalate, 2-8 parts by weight melamine,
Water 80-120 parts by weight.
2. anion liner according to claim 1, which is characterized in that raw material components include:
Tourmaline 14-16 parts by weight, medical stone 2-4 parts by weight, titanium dioxide 2-4 parts by weight, makrolon 3-4 parts by weight, 3-4
The poly- second lactone of parts by weight polylactic acid, 3-4 parts by weight, 3-4 parts by weight diisobutyl phthalate, 4-6 parts by weight melamine,
Water 90-110 parts by weight.
3. anion liner according to claim 1, which is characterized in that raw material components include:
15 parts by weight of tourmaline, 3 parts by weight of medical stone, 3 parts by weight of titanium dioxide, 3.5 parts by weight of makrolon, 3.5 parts by weight
The poly- second lactone of polylactic acid, 3.5 parts by weight, 3.5 parts by weight diisobutyl phthalates, 5 parts by weight melamines, 100 weight of water
Measure part.
4. a kind of method preparing claim 1-3 any one of them anion liners, which is characterized in that including walking as follows
Suddenly:
(1) tourmaline, medical stone, titanium dioxide, makrolon, polymethacrylates are crushed into processing respectively, it is spare;
(2) step (1) crushing rear material is sufficiently mixed uniformly, and is heated;
(3) water, polylactic acid, poly- second lactone, diisobutyl phthalate and three are sequentially added in material after being heated to step (2)
Poly cyanamid is fully reacted under agitation, obtains slurry, spare;
(4) use coating processes that step (3) described slurry is coated on non-woven fabrics to get the anion liner.
5. the preparation method of anion liner according to claim 4, which is characterized in that in step (1), each object after crushing
The grain size of material is 200-300 mesh.
6. the preparation method of anion liner according to claim 4, which is characterized in that in step (2), carry out described add
The temperature of heat treatment is 46-55 DEG C, and the time for carrying out the heat treatment is 25-30min.
7. the preparation method of anion liner according to claim 4, which is characterized in that in step (3), stirred described in progress
The rate mixed is 350-450rpm, and the time for carrying out the stirring is 40-45min.
8. the preparation method of anion liner according to claim 4, which is characterized in that in step (3), carry out described anti-
The temperature answered is 60-80 DEG C.
9. the preparation method of anion liner according to claim 4, which is characterized in that coated program-controlled in step (4)
Scraper gauge 1-2mm processed produces speed 8-12m/min, 170-180 DEG C of oven temperature.
10. a kind of mask including any one of the claim 1-3 anion liners.