CN1065083A - Strong waterproof protecting and fixing agent - Google Patents
Strong waterproof protecting and fixing agent Download PDFInfo
- Publication number
- CN1065083A CN1065083A CN 91101681 CN91101681A CN1065083A CN 1065083 A CN1065083 A CN 1065083A CN 91101681 CN91101681 CN 91101681 CN 91101681 A CN91101681 A CN 91101681A CN 1065083 A CN1065083 A CN 1065083A
- Authority
- CN
- China
- Prior art keywords
- weight
- fixing agent
- waterproof
- agent
- asbestos
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to waterproof protecting and fixing agent.Waterproof protecting and fixing agent of the present invention contains water proofing asphalt, fibrous magnesium silicate and asbestos powder, stone flour, titanium dioxide, aluminium powder, red lead powder, heavy oil and diesel oil, and being made into suitable batching mode is half fluidity mixture.Have waterproof, anti-time, uvioresistant, heat-resisting, premium properties, easy construction, low price such as tackiness is good.
Description
The present invention relates to waterproof or sealing material field.
Strong waterproof protecting and fixing agent of the present invention is mainly used in the buildings in general waterproof, also can be used as the binding agent of glass, cement plate etc.
About being used for architectural water-resisting agent, what have contains rubber, as containing vulcanized rubber, synthetic polyisoprene, sulphur, thiuram, ethanol, benzene, petroleum pitch, quartz sand, asbestos etc. in the contained water-tight composition of SU971848.This water-resisting agent is used for the sealing and the waterproof of water conservancy structure, also is used for the sealing of reinforced concrete member assembling tie point.Be not suitable for though this waterproofing agent composite sealing property is strong general civil building waterproof because its price is more expensive, operation is trouble also.
Cheap, the easy to operate water-resisting agent of materials used often on buildings in general is such as with the grout waterproof: at roof coagulation loam cake last layer silk screen, layer overlay grout then.Because the joint of concrete and cement sand soil paste is bad, thereby can causes be full of cracks and leak; Employing pitch (pitch) waterproof is also arranged: on concrete, be coated with last layer pitch earlier, cover one deck tar felt then, cover with pitch more at last.This waterproof measure since the pitch adhesion relatively poor, after the high temperature solar radiation, peel off easily, thereby be easy to generate crack performance, therefore, in the male and fomale(M﹠F) space or the concrete cracking place leak, do not conform to practicality yet; The somebody is with the resin waterproof: coating resin on concrete earlier, and again coated with the grout pulvis.This water-resisting agent weathering resistance is bad, though concrete and resin are then good, may be caused that resin also produces be full of cracks and leaks by the be full of cracks of structure, so water-resisting agent that neither be splendid; Also has a kind of rubber layer waterproof person that utilizes in addition: directly rubber layer is fixed on the concrete with cakingagent.It is not tight that but rubber contacts with uneven place on the concrete surface, leaks from the gap entry and from the coagulation crack easily.Therefore, building trade is just being sought better water-proof material, to be applicable to the waterproof construction on the new-type rapidly buildings of development roof.
The object of the invention is: provide one respectively to be mainly used in buildings roof water-proof protecting and fixing agent, this waterproof protecting and fixing agent has anticorrosion, anti-be full of cracks, waterproof, good characteristics such as anti-time and acid-and base-resisting.
The objective of the invention is to reach like this: in protecting and fixing agent, allocate the asbestos of pitch, fire prevention and the solar heat protection of waterproof, the aluminium powder that increases the titanium dioxide increase weathering resistance of half mobile tintometric stone flour, reinforcement adhesion, antirust, the anti-time and anti-ultraviolet red lead powder (tri-lead tetroxide) and heavy oil and diesel oil by a certain percentage into, with specific manner of formulation, obtain required semimobile waterproof protecting and fixing agent, thereby the object of the invention has just reached fully.
Be elaborated below in conjunction with the invention of accompanying drawing additional copy.
Accompanying drawing 1 is a waterproof protecting and fixing agent preparation flow functional diagram of the present invention.
Waterproof protecting and fixing agent of the present invention adds two kinds of pitch (pitch), the water proofing asphalt of adopt numbering that Taiwan Chinese Petroleum Company produces No. 85 and No. 5, wherein No. 5 pitch is that to belong to the hard pitch viscosity be 113, proportion is 0.7) in use be easy to generate be full of cracks, No. 85 pitch then belongs to soft pitch, unstable and be easy to peel off that (viscosity is 120 when using separately, proportion is 0.5), account for this agent 50(weight altogether so the two is arranged in pairs or groups) %, wherein No. 5 pitch account for 20(weight) %, No. 85 pitch accounts for 30(weight) %, the such dosage and the diesel oil of back cooperate makes this agent keep the moving sexual state of semi-fluid, and can prevent be full of cracks, does not peel off.Contain 10(weight in this agent) asbestos, a kind of fibrous magnesium silicate of used asbestos for 1 centimetre of length, account for the 4(weight of whole asbestos consumptions) %, a kind of fibrous magnesium silicate for 0.3 centimetre of length, its consumption accounts for the 3(weight of whole asbestos consumptions) %, a kind of is asbestos powder, its consumption accounts for the 3(weight of whole asbestos consumptions) %, asbestos have fire prevention, and the effect of solar heat protection can make this agent rely on the pulling force of fiber simultaneously and increases steadiness with different asbestos of staple length and asbestos powder collocation.Asbestos content is as being less than 10(weight) %, then do not reach requirement, half of this agent of overslaugh is mobile at most.
Also contain 5(weight in this agent) stone flour of %, this stone flour is exactly general stone flour, and its globule size is 100 sieve meshes.The effect of stone flour is to increase the gravity of this agent half fluidity mixture, makes this agent be easier to infiltrate in the weave construction of dirt settling and forms one.Use stone flour, cheap, desirable everywhere, than cheap with quartz sand.Be less than 5(weight) % institute's weightening finish power deficiency then, more than 5(weight) % other characteristic of this agent of overslaugh then.
Contain 5(weight in this agent) titanium dioxide of %, its objective is the adhesion of strengthening this agent and dirt settling, make tissue firm, the raising water resistance.Its amount as surpass 5(weight) % then increases cost, is less than 5(weight) % do not reach the requirement that increases adhesion again.
Contain 5(weight in this agent) aluminium powder of %, the purpose that adds aluminium powder is to increase and anti-ly waits, heat-resisting, cold-resistant, antirust and make the joint portion combination firm, with 5(weight) % is advisable.
Also add 5(weight in this agent) red lead (tri-lead tetroxide) powder of %, be used to prevent that hard goods from getting rusty, the protection buildings is not corroded, and anti-ly waits and resists ultraviolet destruction, more than 5(weight) % is then useless, is less than 5(weight) % then do not reach requirement.
This agent also contains 15(weight) heavy oil of %, utilize heavy oil to increase the stickiness bonding force of this agent half fluidity mixture, this agent is attached on any roof or the object, glass for example, cement plate or metal sheet etc. are 15(weight with content) % is the most suitable.
In addition, this agent also contains 5(weight) diesel oil of %, its effect is to make this agent keep its half mobile and unlikely solidifying, increase the seepage force of this agent simultaneously, so that go deep in the object tissue by the capillary action principle, make this agent cemented after forming rete on the object, exclusion is invaded forever.
As seen, the composition and the content of waterproof protecting and fixing agent of the present invention are as follows, by joining 100 kilograms:
50 kilograms of water proofing asphalts
(wherein No. 5 water proofing asphalts are 20 kilograms, No. 85 water proofing asphalt 30 kilograms).
10 kilograms in asbestos
(wherein, the long 1 centimetre of person of fiber accounts for 4 kilograms, and fiber length is that 0.3 centimetre of person accounts for 3 kilograms; Asbestos powder accounts for 3 kilograms).
5 kilograms of stone flours (100 sieve mesh)
5 kilograms of titanium dioxides
5 kilograms of aluminium powders
5 kilograms of red lead powders
15 kilograms in heavy oil
5 kilograms of diesel oil
The compound method of waterproof protecting and fixing agent of the present invention is as follows:
By 100 kilograms of proportion meters, the compound method of waterproof protecting and fixing agent of the present invention is as follows:
20 kilograms of No. 5 bituminous grouts and 30 kilograms of No. 85 water proofing asphalts are mixed, be heated to 200 ℃～300 ℃, make fully fused a kind of semi-fluid hydrodynamic body that becomes, add 15 kilograms of heavy oil then, 5 kilograms of diesel oil, stir, add 10 kilograms of asbestos, wherein long 1 centimetre fibrous magnesium silicate is 4 kilograms, 3 kilograms of long 0.3 centimetre fibrous magnesium silicates, 3 kilograms of asbestos powders, usefulness has a plurality of agitating vanes and the big leafy gear stirrer of torsion stirs it, sneaks into the stone flour of 5 kilogram of 100 sieve mesh immediately, order adds 5 kilograms titanium dioxide in stirring, the red lead powder of 5 kilograms aluminium powder and 5 kilograms, after stirring.
Waterproof protecting and fixing agent of the present invention was driven bucket and can be used in when construction, with after promptly do, the time spent only must add a little fine sand or grout again and whitewash and get final product.Easy construction is rapid, and this layer waterproof protecting and fixing film is waterproof, anti-time, uvioresistant, antiacid, alkali resistant simultaneously, coheres firmly, do not chap,, thereby do not increase the load of building foundation because of it only covers with film, therefore, waterproof protecting and fixing agent of the present invention is a splendid water-proof material in fact.Waterproof protecting and fixing agent of the present invention is half fluidity mixture, can plug the gap automatically to the expansion joint, and is not aging, do not come off and never degenerates, and cohesive force is strong, is a kind of novel waterproof protecting and fixing agent with industrial value.
Claims (2)
1, waterproof protecting and fixing agent is characterized in that: be half fluidity mixture, contain:
Water proofing asphalt 50 (weight) %
Be numbered No. 5 water proofing asphalts (viscosity is 113, and proportion is 0.7) 20 (weight) % and be numbered No. 85 water proofing asphalts (viscosity is 120, and proportion is 0.5) 30 (weight) % comprising Taiwan Chinese Petroleum Company product;
Asbestos 10 (weight) %
Wherein long 1 centimetre fibrous magnesium silicate accounts for 4 (weight) %, and long 0.3 centimetre fibrous magnesium silicate accounts for 3 (weight) %, and asbestos powder accounts for 3 (weight) %;
Stone flour 5 (weight) %
Titanium dioxide 5 (weight) %
Aluminium powder 5 (weight) %
Red lead powder 5 (weight) %
Heavy oil 15 (weight) %
Diesel oil 5 (weight) %.
2, according to the described waterproof protecting and fixing agent of claim 1, it is characterized in that: said stone flour granularity is 100 sieve meshes.