CN106498744A - A kind of use for synthetic leather injection polishing agent and preparation method thereof - Google Patents
A kind of use for synthetic leather injection polishing agent and preparation method thereof Download PDFInfo
- Publication number
- CN106498744A CN106498744A CN201610961328.9A CN201610961328A CN106498744A CN 106498744 A CN106498744 A CN 106498744A CN 201610961328 A CN201610961328 A CN 201610961328A CN 106498744 A CN106498744 A CN 106498744A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- synthetic leather
- polishing agent
- dispersant
- butyl ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of use for synthetic leather injection polishing agent and preparation method thereof.The use for synthetic leather injection polishing agent includes following components：Modified polyurethane, butyl ether, dimethylformamide, ethyl ester, silicon dioxide flatting silica and dispersant.The each component of use for synthetic leather of the present invention injection polishing agent is mutually coordinated, collective effect, and feel is smooth, and the leather gloss nature that is made with this kind of inorganic agent, color clarification, leather effect are strong, and injection effect is excellent, and resultant effect is good.
Description
Technical field
The present invention relates to a kind of use for synthetic leather is molded polishing agent, the conjunction of synthetic leather FEOL is more particularly to applied to
Finished leather injection polishing agent, while the invention also discloses the use for synthetic leather is molded the preparation method of polishing agent.
Background technology
At present, existing use for synthetic leather injection polishing agent feel is not very good.At the such injection polishing of application
The synthetic leather of agent is managed, its gloss and color and luster are poor, leather effect and injection effect are also not fully up to expectations.Accordingly, it would be desirable to one kind changes
The injection polishing agent that enters.
Content of the invention
It is an object of the invention to provide a kind of use for synthetic leather is molded polishing agent.
The use for synthetic leather injection polishing agent of the present invention is achieved through the following technical solutions：
Use for synthetic leather disclosed in this invention is molded polishing agent, comprising following components：Modified polyurethane, butyl ether, two
Methylformamide, ethyl ester, silicon dioxide flatting silica and dispersant.
On the basis of the gross weight of resin, the proportioning of each component of the use for synthetic leather injection polishing agent that the present invention is provided
Can be：20～30 mass parts of modified polyurethane, 50～55 mass parts of butyl ether, 10～15 mass parts of dimethylformamide, ethyl ester 5
～10 mass parts, 5～10 mass parts of silicon dioxide flatting silica, 0～1 mass parts of dispersant.
In one embodiment of the invention, the proportioning of each component of use for synthetic leather injection polishing agent is as follows：Modified
20 mass parts of polyurethane, 55 mass parts of butyl ether, 10 mass parts of dimethylformamide, 10 mass parts of ethyl ester, silicon dioxide flatting silica 5
Mass parts, 0 mass parts of dispersant.
In another embodiment of the invention, the proportioning of each component of use for synthetic leather injection polishing agent is as follows：Modified
30 mass parts of polyurethane, 50 mass parts of butyl ether, 10 mass parts of dimethylformamide, 5 mass parts of ethyl ester, silicon dioxide flatting silica 5
Mass parts, 0 mass parts of dispersant.
In another embodiment of the invention, the proportioning of each component of use for synthetic leather injection polishing agent is as follows：Modified
23 mass parts of polyurethane, 13 mass parts of dimethylformamide, 52 mass parts of butyl ether, 5 mass parts of ethyl ester, silicon dioxide flatting silica 6
Mass parts, 1 mass parts of dispersant.
The present invention also provides the preparation method that a kind of use for synthetic leather is molded polishing agent, comprises the steps of：
1) by a part of modified polyurethane in formula, butyl ether, dimethylformamide, ethyl ester, silicon dioxide flatting silica and
Dispersant stirs to grind and filters；
2) in step 1) another part modified polyurethane, uniform stirring is added in the mixture that obtains.
The proportioning of each component in the preparation method of the use for synthetic leather injection polishing agent of the present invention can be as follows：Modified
20～30 mass parts of polyurethane, 50～55 mass parts of butyl ether, 10～15 mass parts of dimethylformamide, 5～10 mass parts of ethyl ester,
5～10 mass parts of silicon dioxide flatting silica, 0～1 mass parts of dispersant.
Preferably, the proportioning of each component is as follows：20 mass parts of modified polyurethane, 55 mass parts of butyl ether, dimethylformamide
10 mass parts, 10 mass parts of ethyl ester, 5 mass parts of silicon dioxide flatting silica, 0 mass parts of dispersant.
It is highly preferred that the proportioning of each component is as follows：30 mass parts of modified polyurethane, 50 mass parts of butyl ether, dimethyl formyl
10 mass parts of amine, 5 mass parts of ethyl ester, 5 mass parts of silicon dioxide flatting silica, 0 mass parts of dispersant.
It is highly preferred that the proportioning of each component is as follows：23 mass parts of modified polyurethane, 13 mass parts of dimethylformamide, fourth
52 mass parts of ether, 5 mass parts of ethyl ester, 6 mass parts of silicon dioxide flatting silica, 1 mass parts of dispersant.
Due to adopting above technical scheme, the present invention to have the advantage that compared with prior art：
1. each component of use for synthetic leather of the present invention injection polishing agent is mutually coordinated, collective effect, and feel is slided
Refreshing, the leather gloss nature that is made with this kind of inorganic agent, color clarification, leather effect are strong, and injection effect is excellent, and resultant effect is good；
2. use for synthetic leather injection polishing agent of the present invention is applied on existing synthetic leather production line, technique letter
Single, it is a kind of new material of back segment process, need not change production equipment increases cost；
3. the preparation method of use for synthetic leather injection polishing agent of the present invention is simple, without the need for using complicated machinery
Process, saved production cost, be suitable to industrialized production.
Specific embodiment
Below by embodiment, technical solution of the present invention is described in detail, but protection scope of the present invention not office
It is limited to the embodiment.
Embodiment 1
Use for synthetic leather injection polishing agent includes 20 mass parts modified polyurethanes, 55 mass parts butyl ether, 10 mass parts two
Methylformamide, 10 mass parts ethyl esters, 5 mass parts silicon dioxide flatting silicas, 0 mass parts dispersant.
Above-mentioned use for synthetic leather is molded the preparation method of polishing agent：By 10 mass parts modified polyurethanes in formula,
55 mass parts butyl ether, 10 mass parts dimethylformamides, 10 mass parts ethyl esters, 5 mass parts silicon dioxide flatting silicas, 0 mass parts
Dispersant stirs to grind and filters；Then 10 mass parts modified polyurethanes are added in the mixture of gained, after uniform stirring
Obtain final product described use for synthetic leather injection polishing agent.The performance indications of obtained use for synthetic leather injection polishing agent are shown in Table
1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Embodiment 2
Use for synthetic leather injection polishing agent includes 30 mass parts modified polyurethanes, 50 mass parts butyl ether, 10 mass parts two
Methylformamide, 5 mass parts ethyl esters, 5 mass parts silicon dioxide flatting silicas, 0 mass parts dispersant.
Above-mentioned use for synthetic leather is molded the preparation method of polishing agent：By 20 mass parts modified polyurethanes in formula,
50 mass parts butyl ether, 10 mass parts dimethylformamides, 5 mass parts ethyl esters, 5 mass parts silicon dioxide flatting silicas, 0 mass parts point
Powder stirs to grind and filters；Then 10 mass parts modified polyurethanes are added in the mixture of gained, after uniform stirring i.e.
Obtain described use for synthetic leather injection polishing agent.The performance indications of obtained use for synthetic leather injection polishing agent are shown in Table 1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Embodiment 3
Use for synthetic leather injection polishing agent includes 23 mass parts modified polyurethanes, 13 mass parts dimethylformamides, fourth
52 mass parts ethers, 5 mass parts ethyl esters, 6 mass parts silicon dioxide flatting silicas, 1 mass parts dispersant.
Above-mentioned use for synthetic leather is molded the preparation method of polishing agent：By 13 mass parts modified polyurethanes in formula,
13 mass parts dimethylformamides, 52 mass parts ether of fourth, 5 mass parts ethyl esters, 6 mass parts silicon dioxide flatting silicas, 1 mass parts point
Powder stirs to grind and filters；Then 10 mass parts modified polyurethanes are added in the mixture of gained, after uniform stirring i.e.
Obtain described use for synthetic leather injection polishing agent.The performance indications of obtained use for synthetic leather injection polishing agent are shown in Table 1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Table 1
Presently preferred embodiments of the present invention is the foregoing is only, is not used for the practical range for limiting the present invention；If do not taken off
From the spirit and scope of the present invention, the present invention is modified or equivalent, all should be covered in the claims in the present invention
In the middle of protection domain.
Claims (10)
1. a kind of use for synthetic leather is molded polishing agent, it is characterised in that comprising following components：Modified polyurethane, butyl ether, diformazan
Base Methanamide, ethyl ester, silicon dioxide flatting silica and dispersant.
2. use for synthetic leather according to claim 1 is molded polishing agent, it is characterised in that each component with such as
Under：20～30 mass parts of modified polyurethane, 50～55 mass parts of butyl ether, 10～15 mass parts of dimethylformamide, ethyl ester 5～10
Mass parts, 5～10 mass parts of silicon dioxide flatting silica, 0～1 mass parts of dispersant.
3. use for synthetic leather according to claim 2 is molded polishing agent, it is characterised in that each component with such as
Under：20 mass parts of modified polyurethane, 55 mass parts of butyl ether, 10 mass parts of dimethylformamide, 10 mass parts of ethyl ester, silicon dioxide
5 mass parts of flatting silica, 0 mass parts of dispersant.
4. use for synthetic leather according to claim 2 is molded polishing agent, it is characterised in that each component with such as
Under：30 mass parts of modified polyurethane, 50 mass parts of butyl ether, 10 mass parts of dimethylformamide, 5 mass parts of ethyl ester, silicon dioxide
5 mass parts of flatting silica, 0 mass parts of dispersant.
5. use for synthetic leather according to claim 2 is molded polishing agent, it is characterised in that each component with such as
Under：23 mass parts of modified polyurethane, 13 mass parts of dimethylformamide, 52 mass parts of butyl ether, 5 mass parts of ethyl ester, silicon dioxide
6 mass parts of flatting silica, 1 mass parts of dispersant.
6. the use for synthetic leather described in claim 1 is molded the preparation method of polishing agent, it is characterised in that comprising following step
Suddenly：
1) by a part of modified polyurethane in formula, butyl ether, dimethylformamide, ethyl ester, silicon dioxide flatting silica and dispersion
Agent stirs to grind and filters；
2) in step 1) another part modified polyurethane, uniform stirring is added in the mixture that obtains.
7. use for synthetic leather according to claim 6 is molded the preparation method of polishing agent, it is characterised in that each component
Proportioning is as follows：20～30 mass parts of modified polyurethane, 50～55 mass parts of butyl ether, 10～15 mass parts of dimethylformamide, second
5～10 mass parts of ester, 5～10 mass parts of silicon dioxide flatting silica, 0～1 mass parts of dispersant.
8. use for synthetic leather according to claim 7 is molded the preparation method of polishing agent, it is characterised in that each component
Proportioning is as follows：20 mass parts of modified polyurethane, 55 mass parts of butyl ether, 10 mass parts of dimethylformamide, 10 mass parts of ethyl ester, two
5 mass parts of silicon oxide flatting silica, 0 mass parts of dispersant.
9. use for synthetic leather according to claim 7 is molded the preparation method of polishing agent, it is characterised in that each component
Proportioning is as follows：30 mass parts of modified polyurethane, 50 mass parts of butyl ether, 10 mass parts of dimethylformamide, 5 mass parts of ethyl ester, two
5 mass parts of silicon oxide flatting silica, 0 mass parts of dispersant.
10. use for synthetic leather according to claim 7 is molded the preparation method of polishing agent, it is characterised in that each component
Proportioning as follows：23 mass parts of modified polyurethane, 13 mass parts of dimethylformamide, 52 mass parts of butyl ether, 5 mass parts of ethyl ester,
6 mass parts of silicon dioxide flatting silica, 1 mass parts of dispersant.