CN106367971A - Skin-touch wax polish treating agent for synthetic leather and preparation method thereof - Google Patents
Skin-touch wax polish treating agent for synthetic leather and preparation method thereof Download PDFInfo
- Publication number
- CN106367971A CN106367971A CN201610955218.1A CN201610955218A CN106367971A CN 106367971 A CN106367971 A CN 106367971A CN 201610955218 A CN201610955218 A CN 201610955218A CN 106367971 A CN106367971 A CN 106367971A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- skin sense
- wax
- synthetic leather
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a skin-touch wax polish treating agent for synthetic leather and a preparation method thereof. The skin-touch wax polish treating agent is prepared from the following ingredients of skin-touch polyurethane resin, fumed silica extinction powder, wax powder, BCS, isobutanol, DMF, acetic ether, a dispersing agent and a smooth feeling agent. According to the skin-touch wax polish treating agent for the synthetic leather, all the ingredients are in intercoordination and combined action; a skin-touch effect is strong after burning treatment, the effect is better after water kneading, the feel of infant skin is achieved, and a comprehensive effect is excellent.
Description
Technical field
The present invention relates to inorganic agent thrown by a kind of use for synthetic leather skin sense wax, particularly to the conjunction being applied to synthetic leather rear section technique
Finished leather throws inorganic agent with skin sense wax, simultaneously the invention also discloses the preparation method of inorganic agent thrown by this use for synthetic leather skin sense wax.
Background technology
At present, existing use for synthetic leather skin sense wax is thrown skin sense effect and water after inorganic agent scalds process and is rubbed rear effect not very
Preferable.Such skin sense wax is applied to throw the synthetic leather of inorganic agent, its skin sense effect is also not fully up to expectations.Accordingly, it would be desirable to one kind changes
Inorganic agent thrown by the skin sense wax entering.
Content of the invention
It is an object of the invention to provide inorganic agent thrown by a kind of use for synthetic leather skin sense wax.
The use for synthetic leather skin sense wax of the present invention is thrown inorganic agent and is achieved through the following technical solutions:
Inorganic agent thrown by use for synthetic leather skin sense wax disclosed in this invention, comprises following components: skin sense polyurethane resin, gas phase
Silicon dioxide flatting silica, wax powder, bcs, isobutanol, dmf, ethyl acetate, dispersant and smooth hand feeling agent.
On the basis of the gross weight of resin, the proportioning of each component of inorganic agent thrown by the use for synthetic leather skin sense wax that the present invention provides
Can be: skin sense polyurethane resin 20～40 mass parts, aerosil flatting silica 4～5 mass parts, wax powder 2～5 mass
Part, bcs 15～20 mass parts, isobutanol 15～20 mass parts, dmf 5～10 mass parts, ethyl acetate 25～30 mass parts,
Dispersant 0.4～1 mass parts, smooth hand feeling agent 0.4～1 mass parts.
In one embodiment of the invention, the proportioning of each component of use for synthetic leather skin sense wax throwing inorganic agent is as follows: skin sense
Polyurethane resin 20 mass parts, aerosil flatting silica 4 mass parts, wax powder 5 mass parts, bcs 19 mass parts, isobutanol
15 mass parts, dmf 5 mass parts, ethyl acetate 30 mass parts, dispersant 1 mass parts, smooth hand feeling agent 1 mass parts.
In another embodiment of the invention, the proportioning of each component of use for synthetic leather skin sense wax throwing inorganic agent is as follows: skin sense
Polyurethane resin 27.2 mass parts, aerosil flatting silica 5 mass parts, wax powder 2 mass parts, bcs 15 mass parts, isobutyl
Alcohol 15 mass parts, dmf 10 mass parts, ethyl acetate 25 mass parts, dispersant 0.4 mass parts, smooth hand feeling agent 0.4 mass parts.
In another embodiment of the invention, the proportioning of each component of use for synthetic leather skin sense wax throwing inorganic agent is as follows: skin sense
Polyurethane resin 23 mass parts, wax powder 2 mass parts, dispersant 0.5 mass parts, smooth hand feeling agent 0.5 mass parts, gas phase titanium dioxide
Silicon flatting silica 4.5 mass parts, bcs17 mass parts, dmf8.5 mass parts, isobutanol 17 mass parts, ethyl acetate 27 mass parts.
The present invention also provides a kind of use for synthetic leather skin sense wax to throw the preparation method of inorganic agent, comprises the steps of
To comprise skin sense polyurethane resin, aerosil flatting silica, wax powder, bcs, isobutanol, dmf, ethyl acetate,
The formula of dispersant and smooth hand feeling agent disperses at a high speed.
The proportioning that each component in the preparation method of inorganic agent thrown by the use for synthetic leather skin sense wax of the present invention can be such that skin sense
Polyurethane resin 20～40 mass parts, aerosil flatting silica 4～5 mass parts, wax powder 2～5 mass parts, bcs 15～20
Mass parts, isobutanol 15～20 mass parts, dmf 5～10 mass parts, ethyl acetate 25～30 mass parts, dispersant 0.4～1 matter
Amount part, smooth hand feeling agent 0.4～1 mass parts.
Preferably, the proportioning of each component is as follows: skin sense polyurethane resin 20 mass parts, aerosil flatting silica 4 matter
Amount part, wax powder 5 mass parts, bcs 19 mass parts, isobutanol 15 mass parts, dmf 5 mass parts, ethyl acetate 30 mass parts, point
Powder 1 mass parts, smooth hand feeling agent 1 mass parts.
It is highly preferred that the proportioning of each component is as follows: skin sense polyurethane resin 27.2 mass parts, aerosil flatting silica
5 mass parts, wax powder 2 mass parts, bcs 15 mass parts, isobutanol 15 mass parts, dmf 10 mass parts, ethyl acetate 25 mass
Part, dispersant 0.4 mass parts, smooth hand feeling agent 0.4 mass parts.
It is highly preferred that the proportioning of each component is as follows: 23 parts of skin sense polyurethane resin, 2 parts of wax powder, 0.5 part of dispersant is smooth
0.5 part of hand feeling agent, 4.5 parts of aerosil flatting silica, bcs17 part, 8.5 parts of dmf, 17 parts of isobutanol, ethyl acetate 27
Part.
Because using above technical scheme, the present invention compared with prior art has the advantage that
1. each group of use for synthetic leather skin sense wax throwing inorganic agent of the present invention divides mutually coordinated, collective effect, scalds and processes
Skin sense effect is strong afterwards, and water rubs rear effect more preferably, has the sensation of infant skin, resultant effect is excellent；
2. use for synthetic leather skin sense wax of the present invention is thrown inorganic agent and is applied on existing synthetic leather production line, technique letter
Single, it is a kind of new material that back segment is processed, need not change production equipment increases cost.
3. the preparation method of use for synthetic leather skin sense wax throwing inorganic agent of the present invention is simple, need not be using complicated machinery
Process, saved production cost, be suitable to industrialized production.
Specific embodiment
Below by embodiment, technical solution of the present invention is described in detail, but protection scope of the present invention not office
It is limited to described embodiment.
Embodiment 1
Use for synthetic leather skin sense wax is thrown inorganic agent and is comprised 20 mass parts skin sense polyurethane resins, 4 mass parts aerosils
Flatting silica, 5 mass parts wax powders, 19 mass parts bcs, 15 mass parts isobutanol, 5 mass parts dmf, 30 mass parts ethyl acetates, 1 matter
Amount part dispersant, the smooth hand feeling agent of 1 mass parts.
The preparation method that inorganic agent thrown by above-mentioned use for synthetic leather skin sense wax is: will comprise 20 mass parts skin sense polyurethane resins, 4
Mass parts aerosil flatting silica, 5 mass parts wax powders, 19 mass parts bcs, 15 mass parts isobutanol, 5 mass parts dmf, 30
Mass parts ethyl acetate, 1 mass parts dispersant, the formula of the smooth hand feeling agent of 1 mass parts obtains final product described synthesis after disperseing at a high speed
Leather throws inorganic agent with skin sense wax.The performance indications that inorganic agent thrown by obtained use for synthetic leather skin sense wax are shown in Table 1.
The methods such as the dispersion employed in above-mentioned preparation process are customary way in the art.
Embodiment 2
Use for synthetic leather skin sense wax is thrown inorganic agent and is comprised 27.2 mass parts skin sense polyurethane resins, 5 mass parts gas phase titanium dioxide
Silicon flatting silica, 2 mass parts wax powders, 15 mass parts bcs, 15 mass parts isobutanol, 10 mass parts dmf, 25 mass parts ethyl acetates,
0.4 mass parts dispersant, the smooth hand feeling agent of 0.4 mass parts.
The preparation method that inorganic agent thrown by above-mentioned use for synthetic leather skin sense wax is: will comprise 27.2 mass parts skin sense polyurethane trees
Fat, 5 mass parts aerosil flatting silicas, 2 mass parts wax powders, 15 mass parts bcs, 15 mass parts isobutanol, 10 mass parts
Dmf, 25 mass parts ethyl acetates, 0.4 mass parts dispersant, the formula of the smooth hand feeling agent of 0.4 mass parts obtains final product after disperseing at a high speed
Inorganic agent thrown by described use for synthetic leather skin sense wax.The performance indications that inorganic agent thrown by obtained use for synthetic leather skin sense wax are shown in Table 1.
The methods such as the dispersion employed in above-mentioned preparation process are customary way in the art.
Embodiment 3
Use for synthetic leather skin sense wax is thrown inorganic agent and is comprised 23 mass parts skin sense polyurethane resins, 4.5 mass parts gas phase titanium dioxide
Silicon flatting silica, 2 mass parts wax powders, 17 mass parts bcs, 17 mass parts isobutanol, 8.5 mass parts dmf, 27 mass parts acetic acid second
Ester, 0.5 mass parts dispersant, the smooth hand feeling agent of 0.5 mass parts forms.
The preparation method that inorganic agent thrown by above-mentioned use for synthetic leather skin sense wax is: 23 mass parts skin sense polyurethane resins will be comprised,
4.5 mass parts aerosil flatting silicas, 2 mass parts wax powders, 17 mass parts bcs, 17 mass parts isobutanol, 8.5 mass parts
Dmf, 27 mass parts ethyl acetates, 0.5 mass parts dispersant, the formula of the smooth hand feeling agent of 0.5 mass parts obtains final product after disperseing at a high speed
Inorganic agent thrown by described use for synthetic leather skin sense wax.The performance indications that inorganic agent thrown by obtained use for synthetic leather skin sense wax are shown in Table 1.
The methods such as the dispersion employed in above-mentioned preparation process are customary way in the art.
Table 1
The foregoing is only presently preferred embodiments of the present invention, be not used for limiting the practical range of the present invention；If do not taken off
From the spirit and scope of the present invention, the present invention is modified or equivalent, all should cover in the claims in the present invention
In the middle of protection domain.
Claims (10)
1. a kind of use for synthetic leather skin sense wax throws inorganic agent it is characterised in that comprising following components: skin sense polyurethane resin, gas phase
Silicon dioxide flatting silica, wax powder, bcs, isobutanol, dmf, ethyl acetate, dispersant and smooth hand feeling agent.
2. use for synthetic leather skin sense wax according to claim 1 throw inorganic agent it is characterised in that the proportioning of described each component such as
Under: skin sense polyurethane resin 20～40 mass parts, aerosil flatting silica 4～5 mass parts, wax powder 2～5 mass parts, bcs
15～20 mass parts, isobutanol 15～20 mass parts, dmf 5～10 mass parts, ethyl acetate 25～30 mass parts, dispersant
0.4～1 mass parts, smooth hand feeling agent 0.4～1 mass parts.
3. use for synthetic leather skin sense wax according to claim 2 throw inorganic agent it is characterised in that the proportioning of described each component such as
Under: skin sense polyurethane resin 20 mass parts, aerosil flatting silica 4 mass parts, wax powder 5 mass parts, bcs 19 mass parts,
Isobutanol 15 mass parts, dmf 5 mass parts, ethyl acetate 30 mass parts, dispersant 1 mass parts, smooth hand feeling agent 1 mass parts.
4. use for synthetic leather skin sense wax according to claim 2 throw inorganic agent it is characterised in that the proportioning of described each component such as
Under: skin sense polyurethane resin 27.2 mass parts, aerosil flatting silica 5 mass parts, wax powder 2 mass parts, bcs 15 mass
Part, isobutanol 15 mass parts, dmf 10 mass parts, ethyl acetate 25 mass parts, dispersant 0.4 mass parts, smooth hand feeling agent 0.4
Mass parts.
5. use for synthetic leather skin sense wax according to claim 2 throw inorganic agent it is characterised in that the proportioning of described each component such as
Under: skin sense polyurethane resin 23 mass parts, wax powder 2 mass parts, dispersant 0.5 mass parts, smooth hand feeling agent 0.5 mass parts, gas
Aerosil flatting silica 4.5 mass parts, bcs17 mass parts, dmf 8.5 mass parts, isobutanol 17 mass parts, ethyl acetate 27
Mass parts.
6. the use for synthetic leather skin sense wax described in claim 1 throws the preparation method of inorganic agent it is characterised in that comprising following step
Rapid:
Skin sense polyurethane resin, aerosil flatting silica, wax powder, bcs, isobutanol, dmf, ethyl acetate, dispersion will be comprised
The formula of agent and smooth hand feeling agent disperses at a high speed.
7. use for synthetic leather skin sense wax according to claim 6 throws the preparation method of inorganic agent it is characterised in that each component
Proportioning is as follows: skin sense polyurethane resin 20～40 mass parts, aerosil flatting silica 4～5 mass parts, wax powder 2～5 mass
Part, bcs 15～20 mass parts, isobutanol 15～20 mass parts, dmf 5～10 mass parts, ethyl acetate 25～30 mass parts,
Dispersant 0.4～1 mass parts, smooth hand feeling agent 0.4～1 mass parts.
8. use for synthetic leather skin sense wax according to claim 7 throws the preparation method of inorganic agent it is characterised in that each component
Proportioning is as follows: skin sense polyurethane resin 20 mass parts, aerosil flatting silica 4 mass parts, wax powder 5 mass parts, bcs 19
Mass parts, isobutanol 15 mass parts, dmf5 mass parts, ethyl acetate 30 mass parts, dispersant 1 mass parts, smooth hand feeling agent 1 matter
Amount part.
9. use for synthetic leather skin sense wax according to claim 7 throws the preparation method of inorganic agent it is characterised in that each component
Proportioning is as follows: skin sense polyurethane resin 27.2 mass parts, aerosil flatting silica 5 mass parts, wax powder 2 mass parts, bcs
15 mass parts, isobutanol 15 mass parts, dmf10 mass parts, ethyl acetate 25 mass parts, dispersant 0.4 mass parts, smooth feel
Agent 0.4 mass parts.
10. use for synthetic leather skin sense wax according to claim 7 throws the preparation method of inorganic agent it is characterised in that each component
Proportioning as follows: skin sense polyurethane resin 23 mass parts, wax powder 2 mass parts, dispersant 0.5 mass parts, smooth hand feeling agent 0.5 matter
Amount part, aerosil flatting silica 4.5 mass parts, bcs17 mass parts, dmf 8.5 mass parts, isobutanol 17 mass parts, vinegar
Acetoacetic ester 27 mass parts.