CN106498706A - A kind of processing technique of water proof type silk fabrics - Google Patents

A kind of processing technique of water proof type silk fabrics Download PDF

Info

Publication number
CN106498706A
CN106498706A CN201610939974.5A CN201610939974A CN106498706A CN 106498706 A CN106498706 A CN 106498706A CN 201610939974 A CN201610939974 A CN 201610939974A CN 106498706 A CN106498706 A CN 106498706A
Authority
CN
China
Prior art keywords
parts
silk fabrics
waterproofing agent
proof type
processing technique
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610939974.5A
Other languages
Chinese (zh)
Inventor
王栋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU WINDOW SILK Co Ltd
Original Assignee
SUZHOU WINDOW SILK Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU WINDOW SILK Co Ltd filed Critical SUZHOU WINDOW SILK Co Ltd
Priority to CN201610939974.5A priority Critical patent/CN106498706A/en
Publication of CN106498706A publication Critical patent/CN106498706A/en
Pending legal-status Critical Current

Abstract

The invention provides a kind of processing technique of water proof type silk fabrics, it is characterised in that：Comprise the steps：（1）Silk fabrics is carried out surface cleaning in the sink；（2）Silk fabrics after by cleaning at the uniform velocity passes through waterproofing agent starching box；（3）Surface smear there is is the silk fabrics of waterproofing agent by baking oven, drying and processing is carried out to waterproofing agent；（4）Winding；Wherein, waterproofing agent is calculated in parts by weight, including following component：Sodium carbonate：9 11 parts；59 parts of acrylic resin；38 parts of Colophonium；12 15 parts of stearic acid；24 parts of lake essence；24 parts of calcium chloride；38 parts of paraffin；13 parts of sodium hydroxide；12 parts of fiberglass reinforcing polyester felt；0.5 1.5 parts of sodium benzoate；13 parts of aluminium potassium sulfate；36 parts of polyvinylpyrrolidone；250 300 parts of water.Silk fabrics can be made after the completion of processing and sorting, not only be there is preferable water proofing property, and breathability and flexibility are also more preferable.

Description

A kind of processing technique of water proof type silk fabrics
Technical field
The present invention relates to a kind of processing technique of water proof type silk fabrics, belongs to silk technical field of textile processing.
Background technology
Silk fabrics is a kind of weaving face fabric for being favored very much in people's life, and silk fabrics is in process of production Can water proofing property process be an important operation, weigh the quality of water proof type silk fabrics performance, make silk mostly in reference to which Silk fabric has good waterproof, the performance such as ventilative after arrangement.But the anti-water-reeled pongee species that sells in the market is various, and Relatively costly.
Content of the invention
The technical problem to be solved is to provide a kind of processing technique of water proof type silk fabrics, can make silk Fabric has preferable water proofing property after the completion of processing and sorting, not only, and breathability and flexibility are also more preferable.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is：
A kind of processing technique of water proof type silk fabrics, it is characterised in that：Comprise the steps：
（1）Silk fabrics is carried out surface cleaning in the sink；
（2）Silk fabrics after by cleaning at the uniform velocity passes through waterproofing agent starching box；
（3）Surface smear there is is the silk fabrics of waterproofing agent by baking oven, drying and processing is carried out to waterproofing agent；
（4）Winding；
Wherein, waterproofing agent is calculated in parts by weight, including following component：Sodium carbonate：9-11 parts；Acrylic resin 5-9 parts；Colophonium 3-8 parts；Stearic acid 12-15 parts；Lake essence 2-4 parts；Calcium chloride 2-4 parts；Paraffin 3-8 parts；Sodium hydroxide 1-3 parts；Fiberglass reinforced gathers Ester felt 1-2 parts；Sodium benzoate 0.5-1.5 parts；Aluminium potassium sulfate 1-3 parts；Polyvinylpyrrolidone 3-6 parts；Water 250-300 parts.
A kind of processing technique of aforesaid water proof type silk fabrics, it is characterised in that：The waterproofing agent is in parts by weight Calculate, also include following component：Polyvinylacetate 5-7 parts.
3rd, the processing technique of a kind of water proof type silk fabrics according to claim 1, it is characterised in that：The step （2）Silk fabrics after middle cleaning is 2m/s-4m/s by the speed of waterproofing agent starching box.
A kind of processing technique of aforesaid water proof type silk fabrics, it is characterised in that：The step（3）The drying of middle baking oven Temperature is 80 DEG C -95 DEG C.
A kind of processing technique of aforesaid water proof type silk fabrics, it is characterised in that：The step（2）Silk after middle cleaning Silk shell fabric is 3m/s by the speed of waterproofing agent starching box.
A kind of processing technique of aforesaid water proof type silk fabrics, it is characterised in that：The step（3）The drying of middle baking oven Temperature is 90 DEG C.
The invention has the beneficial effects as follows：By selecting the waterproofing agent of suitable component and proportioning, in conjunction with corresponding processing work Skill, can make the silk fabrics of addition waterproofing agent after the completion of processing and sorting, and not only there is preferable water proofing property, and breathability Also more preferable with flexibility.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
A kind of processing technique of water proof type silk fabrics, it is characterised in that：Comprise the steps：
（1）Silk fabrics is carried out surface cleaning in the sink；
（2）Silk fabrics after by cleaning at the uniform velocity passes through waterproofing agent starching box；
（3）Surface smear there is is the silk fabrics of waterproofing agent by baking oven, drying and processing is carried out to waterproofing agent；
（4）Winding；
Wherein, waterproofing agent is calculated in parts by weight, including following component：Sodium carbonate：9-11 parts；Acrylic resin 5-9 parts；Colophonium 3-8 parts；Stearic acid 12-15 parts；Lake essence 2-4 parts；Calcium chloride 2-4 parts；Paraffin 3-8 parts；Sodium hydroxide 1-3 parts；Fiberglass reinforced gathers Ester felt 1-2 parts；Sodium benzoate 0.5-1.5 parts；Aluminium potassium sulfate 1-3 parts；Polyvinylpyrrolidone 3-6 parts；Water 250-300 parts, institute State waterproofing agent to calculate in parts by weight, also include following component：Polyvinylacetate 5-7 parts.By select suitable component and The waterproofing agent of proportioning, in conjunction with corresponding processing technique, can make the silk fabrics of addition waterproofing agent after the completion of processing and sorting, no Only there is preferable water proofing property, and breathability and flexibility are also more preferable.
Through repetition test, the step（2）Silk fabrics after middle cleaning is 2m/ by the speed of waterproofing agent starching box S-4m/s, preferably 3m/s, the step（3）The drying temperature of middle baking oven is 80 DEG C -95 DEG C, preferably 90 DEG C.
In sum, the processing technique of a kind of water proof type silk fabrics that the present invention is provided, is adding can silk fabrics After the completion of carefully and neatly done reason, not only there is preferable water proofing property, and breathability and flexibility are also more preferable.
Ultimate principle, principal character and the advantage of the present invention has been shown and described above.The technical staff of the industry should Understand, the present invention is not restricted to the described embodiments, the original that the present invention is simply described described in above-described embodiment and description Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes and improvements Both fall within scope of the claimed invention.The claimed scope of the invention is by appending claims and its equivalent Boundary.

Claims (6)

1. a kind of processing technique of water proof type silk fabrics, it is characterised in that：Comprise the steps：
（1）Silk fabrics is carried out surface cleaning in the sink；
（2）Silk fabrics after by cleaning at the uniform velocity passes through waterproofing agent starching box；
（3）Surface smear there is is the silk fabrics of waterproofing agent by baking oven, drying and processing is carried out to waterproofing agent；
（4）Winding；
Wherein, waterproofing agent is calculated in parts by weight, including following component：Sodium carbonate：9-11 parts；Acrylic resin 5-9 parts；Colophonium 3-8 parts；Stearic acid 12-15 parts；Lake essence 2-4 parts；Calcium chloride 2-4 parts；Paraffin 3-8 parts；Sodium hydroxide 1-3 parts；Fiberglass reinforced gathers Ester felt 1-2 parts；Sodium benzoate 0.5-1.5 parts；Aluminium potassium sulfate 1-3 parts；Polyvinylpyrrolidone 3-6 parts；Water 250-300 parts.
2. the processing technique of a kind of water proof type silk fabrics according to claim 1, it is characterised in that：The waterproofing agent is pressed According to listed as parts by weight, also include following component：Polyvinylacetate 5-7 parts.
3. the processing technique of a kind of water proof type silk fabrics according to claim 1, it is characterised in that：The step（2） Silk fabrics after middle cleaning is 2m/s-4m/s by the speed of waterproofing agent starching box.
4. the processing technique of a kind of water proof type silk fabrics according to claim 1, it is characterised in that：The step（3） The drying temperature of middle baking oven is 80 DEG C -95 DEG C.
5. the processing technique of a kind of water proof type silk fabrics according to claim 3, it is characterised in that：The step（2） Silk fabrics after middle cleaning is 3m/s by the speed of waterproofing agent starching box.
6. the processing technique of a kind of water proof type silk fabrics according to claim 4, it is characterised in that：The step（3） The drying temperature of middle baking oven is 90 DEG C.
CN201610939974.5A 2016-10-25 2016-10-25 A kind of processing technique of water proof type silk fabrics Pending CN106498706A (en)