CN106498714A - A kind of silk waterproofing agent - Google Patents
A kind of silk waterproofing agent Download PDFInfo
- Publication number
- CN106498714A CN106498714A CN201610935283.8A CN201610935283A CN106498714A CN 106498714 A CN106498714 A CN 106498714A CN 201610935283 A CN201610935283 A CN 201610935283A CN 106498714 A CN106498714 A CN 106498714A
- Authority
- CN
- China
- Prior art keywords
- parts
- silk
- waterproofing agent
- sodium
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of silk waterproofing agent, is calculated in parts by weight, including following component:Sodium carbonate:9 11 parts;59 parts of acrylic resin;38 parts of Colophonium;58 parts of stearic acid;24 parts of lake essence;5 10 parts of calcium chloride;38 parts of paraffin;13 parts of sodium hydroxide;12 parts of fiberglass reinforcing polyester felt;0.5 1.5 parts of sodium benzoate;7 14 parts of aluminium potassium sulfate;36 parts of polyvinylpyrrolidone;150 200 parts of water.By selecting suitable component and proportioning, the silk fabrics of addition waterproofing agent can be made after the completion of processing and sorting, not only be there is preferable water proofing property, and breathability and flexibility are also more preferable.
Description
Technical field
The present invention relates to a kind of silk waterproofing agent, belongs to silk textile technology field.
Background technology
Silk fabrics is a kind of weaving face fabric for being favored very much in people's life, and silk fabrics is in process of production
Can water proofing property process be an important operation, weighs the quality of waterproofing agent performance, arranging mostly in reference to which silk
There is good waterproof, the performance such as ventilative afterwards.But the waterproofing agent species that sells in the market is various and relatively costly.
Content of the invention
The technical problem to be solved is to provide a kind of silk waterproofing agent, can make silk fabrics in processing and sorting
After the completion of, not only there is preferable water proofing property, and breathability and flexibility are also more preferable.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
A kind of silk waterproofing agent, is calculated in parts by weight, including following component:
Sodium carbonate:9-11 parts;Acrylic resin 5-9 parts;Colophonium 3-8 parts;Stearic acid 5-8 parts;Lake essence 2-4 parts;Calcium chloride 5-10
Part;Paraffin 3-8 parts;Sodium hydroxide 1-3 parts;Fiberglass reinforcing polyester felt 1-2 parts;Sodium benzoate 0.5-1.5 parts;Aluminium potassium sulfate 7-14
Part;Polyvinylpyrrolidone 3-6 parts;Water 150-200 parts.
A kind of aforesaid silk waterproofing agent, it is characterised in that:Calculate in parts by weight, also include following component:Polyethylene
Acetass 8-10 parts.
A kind of aforesaid silk waterproofing agent, it is characterised in that:Calculate in parts by weight, including following component:Sodium carbonate:9
Part;6 parts of acrylic resin;4 parts of Colophonium;5 parts of stearic acid;2 parts of lake essence;10 parts of calcium chloride;5 parts of paraffin;2 parts of sodium hydroxide;Glass
1 part of fiber reinforced polyester felt;0.5 part of sodium benzoate;8 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;200 parts of water;Polyethylene second
9 parts of acid esters.
A kind of aforesaid silk waterproofing agent, it is characterised in that:Calculate in parts by weight, including following component:
Sodium carbonate:10 parts;8 parts of acrylic resin;5 parts of Colophonium;7 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
1 part of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;8 parts of aluminium potassium sulfate;4 parts of polyvinylpyrrolidone;Water
150 parts;10 parts of polyvinylacetate.
A kind of aforesaid silk waterproofing agent, it is characterised in that:Calculate in parts by weight, including following component:
Sodium carbonate:11 parts;8 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;10 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
200 parts;10 parts of polyvinylacetate.
A kind of aforesaid silk waterproofing agent, it is characterised in that:Calculate in parts by weight, including following component:
Sodium carbonate:11 parts;9 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;2 parts of fiberglass reinforcing polyester felt;1.5 parts of sodium benzoate;12 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
160 parts;8 parts of polyvinylacetate.
The invention has the beneficial effects as follows:By selecting suitable component and proportioning, the silk face of addition waterproofing agent can be made
Material has preferable water proofing property after the completion of processing and sorting, not only, and breathability and flexibility are also more preferable.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of silk waterproofing agent, is calculated in parts by weight, including following component:Sodium carbonate:9 parts;6 parts of acrylic resin;Colophonium 4
Part;5 parts of stearic acid;2 parts of lake essence;10 parts of calcium chloride;5 parts of paraffin;2 parts of sodium hydroxide;1 part of fiberglass reinforcing polyester felt;Benzoic acid
0.5 part of sodium;8 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;200 parts of water;9 parts of polyvinylacetate.
Embodiment 2
A kind of silk waterproofing agent, is calculated in parts by weight, including following component:
Sodium carbonate:10 parts;8 parts of acrylic resin;5 parts of Colophonium;7 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
1 part of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;8 parts of aluminium potassium sulfate;4 parts of polyvinylpyrrolidone;Water
150 parts;10 parts of polyvinylacetate.
Embodiment 3
A kind of silk waterproofing agent, is calculated in parts by weight, including following component:
Sodium carbonate:11 parts;8 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;10 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
200 parts;10 parts of polyvinylacetate.
Embodiment 4
A kind of silk waterproofing agent, is calculated in parts by weight, including following component:
Sodium carbonate:11 parts;9 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;2 parts of fiberglass reinforcing polyester felt;1.5 parts of sodium benzoate;12 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
160 parts;8 parts of polyvinylacetate.
In sum, a kind of silk waterproofing agent that the present invention is provided, can make silk fabrics after the completion of processing and sorting, no
Only there is preferable water proofing property, and breathability and flexibility are also more preferable.
Ultimate principle, principal character and the advantage of the present invention has been shown and described above.The technical staff of the industry should
Understand, the present invention is not restricted to the described embodiments, the original that the present invention is simply described described in above-described embodiment and description
Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes and improvements
Both fall within scope of the claimed invention.The claimed scope of the invention is by appending claims and its equivalent
Boundary.
Claims (6)
1. a kind of silk waterproofing agent, it is characterised in that:Calculate in parts by weight, including following component:
Sodium carbonate:9-11 parts;Acrylic resin 5-9 parts;Colophonium 3-8 parts;Stearic acid 5-8 parts;Lake essence 2-4 parts;Calcium chloride 5-10
Part;Paraffin 3-8 parts;Sodium hydroxide 1-3 parts;Fiberglass reinforcing polyester felt 1-2 parts;Sodium benzoate 0.5-1.5 parts;Aluminium potassium sulfate 7-14
Part;Polyvinylpyrrolidone 3-6 parts;Water 150-200 parts.
2. a kind of silk waterproofing agent according to claim 1, it is characterised in that:Calculate in parts by weight, also include as follows
Component:Polyvinylacetate 8-10 parts.
3. a kind of silk waterproofing agent according to claim 2, it is characterised in that:Calculate in parts by weight, including such as the following group
Part:Sodium carbonate:9 parts;6 parts of acrylic resin;4 parts of Colophonium;5 parts of stearic acid;2 parts of lake essence;10 parts of calcium chloride;5 parts of paraffin;Hydrogen-oxygen
Change 2 parts of sodium;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;8 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water 200
Part;9 parts of polyvinylacetate.
4. a kind of silk waterproofing agent according to claim 2, it is characterised in that:Calculate in parts by weight, including such as the following group
Part:
Sodium carbonate:10 parts;8 parts of acrylic resin;5 parts of Colophonium;7 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
1 part of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;8 parts of aluminium potassium sulfate;4 parts of polyvinylpyrrolidone;Water
150 parts;10 parts of polyvinylacetate.
5. a kind of silk waterproofing agent according to claim 2, it is characterised in that:Calculate in parts by weight, including such as the following group
Part:
Sodium carbonate:11 parts;8 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;1 part of fiberglass reinforcing polyester felt;0.5 part of sodium benzoate;10 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
200 parts;10 parts of polyvinylacetate.
6. a kind of silk waterproofing agent according to claim 2, it is characterised in that:Calculate in parts by weight, including such as the following group
Part:
Sodium carbonate:11 parts;9 parts of acrylic resin;8 parts of Colophonium;6 parts of stearic acid;3 parts of lake essence;8 parts of calcium chloride;8 parts of paraffin;Hydrogen
2 parts of sodium oxide;2 parts of fiberglass reinforcing polyester felt;1.5 parts of sodium benzoate;12 parts of aluminium potassium sulfate;5 parts of polyvinylpyrrolidone;Water
160 parts;8 parts of polyvinylacetate.