CN106497422A - A kind of fire-retardant paint compositionss and preparation method thereof - Google Patents
A kind of fire-retardant paint compositionss and preparation method thereof Download PDFInfo
- Publication number
- CN106497422A CN106497422A CN201610914182.2A CN201610914182A CN106497422A CN 106497422 A CN106497422 A CN 106497422A CN 201610914182 A CN201610914182 A CN 201610914182A CN 106497422 A CN106497422 A CN 106497422A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- agent
- retardant
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, specifically a kind of fire-retardant paint compositionss, the weight fraction of its each component is：25 ~ 30 parts of oil plant, 4 ~ 8 parts of epoxy resin, 3 ~ 5 parts of firming agent, 6 ~ 8 parts of anti-blushing agent, 5 ~ 10 parts of pigment, 3 ~ 5 parts of foaming agent, 1 ~ 2 part of Borax, 6 ~ 10 parts of ethyl acetate, 2 ~ 4 parts of fire retardant.The paint composite that the present invention is provided, using the interaction between related chemical constituents, influences each other, with the effect that adhesive force is good, bright in color is moistureproof, while also having flame retardant effect.
Description
Technical field
The present invention relates to technical field of coatings, specifically a kind of fire-retardant paint compositionss.
Background technology
Paint English name：paint or coating.Paint is that one kind firmly can be covered in body surface, plays protection, dress
The chemical mixture coating of decorations, mark and other specific uses.Chinese coating circle is more authoritative《Coating process》One book is this
Sample definition：" coating is a kind of material, and this material can be coated in object surface with different construction technologies, form adhesion
Firmly, there is some strength, continuous solid film.The film common name film for so being formed, also known as paint film or coating.”
Coating is typically by film forming matter, filler（Color stuffing）, solvent, four parts such as auxiliary agent composition.According to performance requirement sometimes into
Part can be slightly changed, such as do not have can be without solvent in color stuffing, powdery paints for varnish.
In various disasters, fire be most frequently, most threaten at large public security and social development major casualty it
One.And
Indispensable in building have the wood materials articles for use such as furniture, once there is fire, itself had is inflammable
Property fire will be promoted to spread rapidly, bring the harm of great lives and properties to the public.
Content of the invention
It is an object of the invention to provide a kind of fire-retardant paint compositionss.
For achieving the above object, following technical scheme present invention employs：
A kind of fire-retardant paint compositionss, the weight fraction of its each component is：
25 ~ 30 parts of oil plant
4 ~ 8 parts of epoxy resin
3 ~ 5 parts of firming agent
6 ~ 8 parts of anti-blushing agent
5 ~ 10 parts of pigment
3 ~ 5 parts of foaming agent
1 ~ 2 part of Borax
6 ~ 10 parts of ethyl acetate
2 ~ 4 parts of fire retardant
Additionally, the present invention also provides attached technical scheme as follows：
Preferably, the preferable weight of each component is：It is prepared from by the raw material of following weight portion：
25 ~ 28 parts of oil plant
5 ~ 7 parts of epoxy resin
3 ~ 5 parts of firming agent
6 ~ 7 parts of anti-blushing agent
5 ~ 8 parts of pigment
3 ~ 5 parts of foaming agent
1 ~ 2 part of Borax
6 ~ 8 parts of ethyl acetate
2 ~ 3 parts of fire retardant.
Preferably, the optimum weight of each component is：It is prepared from by the raw material of following weight portion：
27 parts of oil plant
7 parts of epoxy resin
5 parts of firming agent
6 parts of anti-blushing agent
8 parts of pigment
5 parts of foaming agent
2 parts of Borax
7 parts of ethyl acetate
3 parts of fire retardant.
Preferably, the firming agent be fatty amine, alicyclic ring reflect and polyamide in one or two kinds of mixture.
Preferably, the anti-blushing agent is the mixture of calcium chloride and Calcium Carbonate.
Preferably, the pigment is Ludox, calcium acetate ridge soil according to 3:5:6 ratio mixing composition.
Preferably, the fire retardant is the mixture of triphenyl phosphate and magnesium hydroxide, and its weight part ratio is 1:5.
A kind of preparation method of fire-retardant paint compositionss described above, including having the following steps：
1）, by epoxy resin, ethyl acetate add reactor in, warming while stirring, speed of agitator be 400 revs/min, the time
15 ~ 25 minutes；When temperature rises to 100 degrees Celsius, oil plant and pigment is added, is stirred, kept for 15 ~ 20 minutes；
2）, by step 1）Reactor be cooled to 45 degree, then add firming agent, anti-blushing agent, foaming agent Borax and fire-retardant wherein
Agent, then stirred 20 minutes with 450 revs/min of rotating speed, obtain final product.
Compared to prior art, advantage of the invention is that：
The paint composite that the present invention is provided, using the interaction between related chemical constituents, influences each other, with adhesive force
The moistureproof effect of good, bright in color, while also have flame retardant effect.
Specific embodiment
It is further non-limitingly described in detail below in conjunction with preferred embodiment and to technical solution of the present invention.
Embodiment 1
A kind of fire-retardant paint compositionss, the weight fraction of its each component is：
25 parts of oil plant
5 parts of epoxy resin
3 parts of firming agent
6 parts of anti-blushing agent
5 parts of pigment
3 parts of foaming agent
1 part of Borax
6 parts of ethyl acetate
2 parts of fire retardant.
In the present embodiment, above-mentioned firming agent is fatty amine.
Damp agent is the mixture of calcium chloride and Calcium Carbonate, and its weight part ratio is 2:3.
Pigment is Ludox, calcium acetate ridge is native according to 3:5:6 ratio mixing composition.
Fire retardant is the mixture of triphenyl phosphate and magnesium hydroxide, and its weight part ratio is 1:5.
A kind of preparation method of fire-retardant paint compositionss, including having the following steps：
1）, by epoxy resin, ethyl acetate add reactor in, warming while stirring, speed of agitator be 400 revs/min, the time
25 minutes；When temperature rises to 100 degrees Celsius, oil plant and pigment is added, is stirred, kept for 15 minutes；
2）, by step 1）Reactor be cooled to 45 degree, then add firming agent, anti-blushing agent, foaming agent Borax and fire-retardant wherein
Agent, then stirred 20 minutes with 450 revs/min of rotating speed, obtain final product.
Embodiment 2
A kind of fire-retardant paint compositionss, the preferable weight of each component are to be prepared from by the raw material of following weight portion：
28 parts of oil plant
8 parts of epoxy resin
5 parts of firming agent
7 parts of anti-blushing agent
8 parts of pigment
5 parts of foaming agent
2 parts of Borax
8 parts of ethyl acetate
4 parts of fire retardant.
In the present embodiment, above-mentioned firming agent is reflected for alicyclic ring.
Anti-blushing agent is the mixture of calcium chloride and Calcium Carbonate, and its weight part ratio is 2:3.
Pigment is Ludox, calcium acetate ridge is native according to 3:5:6 ratio mixing composition.
The fire retardant is the mixture of triphenyl phosphate and magnesium hydroxide, and its weight part ratio is 1:5.
A kind of preparation method of fire-retardant paint compositionss, it is characterised in that including having the following steps：
1）, by epoxy resin, ethyl acetate add reactor in, warming while stirring, speed of agitator be 400 revs/min, the time
20 minutes；When temperature rises to 100 degrees Celsius, oil plant and pigment is added, is stirred, kept for 18 minutes；
2）, by step 1）Reactor be cooled to 45 degree, then add firming agent, anti-blushing agent, foaming agent Borax and fire-retardant wherein
Agent, then stirred 20 minutes with 450 revs/min of rotating speed, obtain final product.
Embodiment 3
A kind of fire-retardant paint compositionss, the optimum weight of each component are prepared from by the raw material of following weight portion：
27 parts of oil plant
7 parts of epoxy resin
5 parts of firming agent
6 parts of anti-blushing agent
8 parts of pigment
5 parts of foaming agent
1 part of Borax
7 parts of ethyl acetate
3 parts of fire retardant.
In the present embodiment, firming agent is the mixture of fatty amine and polyamide, and its weight part ratio is 1:3.
Anti-blushing agent is the mixture of calcium chloride and Calcium Carbonate, and its weight part ratio is 2:5.
Pigment is Ludox, calcium acetate ridge is native according to 3:5:6 ratio mixing composition.
Fire retardant is the mixture of triphenyl phosphate and magnesium hydroxide, and its weight part ratio is 1:5.
A kind of preparation method of fire-retardant paint compositionss, including having the following steps：
1）, by epoxy resin, ethyl acetate add reactor in, warming while stirring, speed of agitator be 400 revs/min, the time
15 minutes；When temperature rises to 100 degrees Celsius, oil plant and pigment is added, is stirred, kept for 20 minutes；
2）, by step 1）Reactor be cooled to 45 degree, then add firming agent, anti-blushing agent, foaming agent Borax and fire-retardant wherein
Agent, then stirred 20 minutes with 450 revs/min of rotating speed, obtain final product.
It is pointed out that above-mentioned preferred embodiment technology design only to illustrate the invention and feature, its object is to
Allow person skilled in the art will appreciate that present disclosure and implement according to this, protection of the invention can not be limited with this
Scope.All equivalence changes that is made according to spirit of the invention or modification, should all be included within the scope of the present invention.
Claims (7)
1. a kind of fire-retardant paint compositionss, it is characterised in that the weight fraction of its each component is：
25 ~ 30 parts of oil plant
4 ~ 8 parts of epoxy resin
3 ~ 5 parts of firming agent
6 ~ 8 parts of anti-blushing agent
5 ~ 10 parts of pigment
3 ~ 5 parts of foaming agent
1 ~ 2 part of Borax
6 ~ 10 parts of ethyl acetate
2 ~ 4 parts of fire retardant；
A kind of preparation method of above-mentioned fire-retardant paint compositionss, including having the following steps：
1）, by epoxy resin, ethyl acetate add reactor in, warming while stirring, speed of agitator be 400 revs/min, the time
15 ~ 25 minutes；When temperature rises to 100 degrees Celsius, oil plant and pigment is added, is stirred, kept for 15 ~ 20 minutes；
2）, by step 1）Reactor be cooled to 45 degree, then add firming agent, anti-blushing agent, foaming agent, Borax and fire-retardant wherein
Agent, then stirred 20 minutes with 450 revs/min of rotating speed, obtain final product.
2. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that prepared by the raw material of following weight portion
Form：
25 ~ 28 parts of oil plant
5 ~ 7 parts of epoxy resin
3 ~ 5 parts of firming agent
6 ~ 7 parts of anti-blushing agent
5 ~ 8 parts of pigment
3 ~ 5 parts of foaming agent
1 ~ 2 part of Borax
6 ~ 8 parts of ethyl acetate
2 ~ 3 parts of fire retardant.
3. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that prepared by the raw material of following weight portion
Form：
27 parts of oil plant
6 parts of epoxy resin
5 parts of firming agent
6 parts of anti-blushing agent
8 parts of pigment
5 parts of foaming agent
1 part of Borax
7 parts of ethyl acetate
3 parts of fire retardant.
4. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that the firming agent is fatty amine, fat
Ring reflect and polyamide in one or two kinds of mixture.
5. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that the anti-blushing agent is calcium chloride and carbon
The mixture of sour calcium.
6. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that the pigment is Ludox, acetic acid
Calcium ridge is native according to 3:5:6 ratio mixing composition.
7. a kind of fire-retardant paint compositionss according to claim 1, it is characterised in that the fire retardant is triphenyl phosphate
With the mixture of magnesium hydroxide, its weight part ratio is 1:5.