CN106496677A - Asphalt foaming agent and preparation method thereof - Google Patents
Asphalt foaming agent and preparation method thereof Download PDFInfo
- Publication number
- CN106496677A CN106496677A CN201611144716.4A CN201611144716A CN106496677A CN 106496677 A CN106496677 A CN 106496677A CN 201611144716 A CN201611144716 A CN 201611144716A CN 106496677 A CN106496677 A CN 106496677A
- Authority
- CN
- China
- Prior art keywords
- asphalt
- foaming agent
- colophonium
- asphalt foaming
- expansion rate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the foaming agent used in foamed asphalt production and the technology such as asphalt mixture warm-mixing construction, Bituminous Pavement Cold Regeneration, modified pitch for pavement engineering is manufactured, more particularly to a kind of for foamed asphalt and modified pitch in asphalt foaming agent and preparation method thereof.The constituent of the asphalt foaming agent is natural emulsion and industrial latex, and the mass ratio of two kinds of compositions is 100:0‑0:100;Its solid content mass percent is 1 80%, preferably 30 80%.The foaming agent of the present invention can not only improve expansion rate and the half-life of asphalt foaming, improve the stability of foamed asphalt, and Colophonium high temperature performance is significantly improved, improve the property of Colophonium.
Description
Technical field
The present invention relates to foamed asphalt production and asphalt mixture warm-mixing construction, Bituminous Pavement Cold for pavement engineering are again
Used in the technology such as life, modified pitch foaming agent manufacture, more particularly to a kind of for foamed asphalt and modified pitch in drip
Blue or green foaming agent and preparation method thereof.
Background technology
Foamed asphalt is that hard pitch is contacted with water, because of the Colophonium bubble that moisture vaporization in Colophonium forms steam bubble and formed
Foam system.As foamed asphalt can be rolled with aggregate blending, compound at relatively low temperatures at a lower temperature,
Well received in the construction of Colophonium warm mix, old asphalt pavement regeneration technique.
Two parameters for evaluating asphalt foaming effect are expansion rate and half-life.Expansion rate refers to that Colophonium is foamed with water mix
The maximum volume for reaching afterwards and the ratio of the unexpanded front volume of Colophonium;Half-life refers to the maximum volume of foaming to volume-diminished extremely
Half elapsed time, represented with the second (S).Expansion rate is bigger, and foamed asphalt is more abundant with the contact that gathers materials, the bubble of mixing
Foam quality of asphalt mixtures is better;Half-life is longer, foamed asphalt with gather materials to take the working time in longer, be conducive to carrying
The quality of high plate form rubber.At present, the key technology of production foamed asphalt is control using accurate water consumption and obtains
Obtain expansion rate most preferably.In actual production, typically require that more than 10 times of expansion rate, half-life typically require to be more than 8S.
Current technology, due to simply by adding water rate control expansion rate and half-life, regulating measure be limited, when
The viscosity of Colophonium is higher with when needing long period mix, and current foaming agent can not meet construction requirement.
Content of the invention
The purpose of the present invention is to propose to a kind of expansion rate that can improve asphalt foaming and half-life, improve foamed asphalt
Stability, the formula for improving the asphalt foaming agent of Colophonium high temperature performance are constituted and preparation method.
The asphalt foaming agent of the present invention, its constituent are that natural emulsion and industrial latex, the mass ratio of two kinds of compositions are
100:0-0:100;Its solid content mass percent is in 1-80%, preferably 30-80%.
The preparation method of the asphalt foaming agent of the present invention:It is by Heveatex and industrial latex in mass ratio 100:0-0:
100 scopes, at a temperature of 10-40 DEG C, in reactor, 30-50 turn/min speed is uniformly mixed prepared asphalt foaming agent.
Heveatex of the present invention, refers to a kind of milky white liquid from gained in the rubber tree of cultivation, is a kind of life
Thing sinteticses, in 20-50%, its filming performance is good for solid content, and wet gel strength is high, springiness.
Commercial latex of the present invention, refers to the butylbenzene class latex of commercial synthesis, NBR latex, polychloroprene latex, SBS glue
Breast, solid content is in 1-80%.
The using method of above-mentioned asphalt foaming agent is according to traditional asphalt foaming agent addition, is added in Colophonium and sends out
Bubble production foamed asphalt.
The foaming agent of the present invention can not only improve expansion rate and the half-life of asphalt foaming, improve stablizing for foamed asphalt
Property, and Colophonium high temperature performance is significantly improved, improve the property of Colophonium.
Specific embodiment
With reference to specific embodiment, the present invention is further elucidated with, it should be understood that these embodiments are merely to illustrate the present invention
Rather than the scope of the present invention is limited, and after the present invention has been read, various equivalences of the those skilled in the art to the present invention
The modification of form falls within the application claims limited range.
Embodiment 1
By Heveatex and industrial latex (styrene-butadiene latex) in mass ratio 100:0, solid content 35%, in 10-40 DEG C of temperature
Under, in reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 20-40 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition 2.86wt%
When, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 1 with reference, and Colophonium is shown in Table 1 with modified pitch leading indicator;
During addition 5.71wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 1, Colophonium and modified pitch
Leading indicator is shown in Table 1.
Table 1
Embodiment 2
By Heveatex and industrial latex (styrene-butadiene latex) in mass ratio 7:3, solid content 50%, at a temperature of 10-40 DEG C,
In reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 40-60 (25 DEG C, 100g, 5s) 0.1mm asphalt, during addition 2wt%,
The expansion rate of asphalt foaming and half-life result are relatively shown in Table 2 with reference, and Colophonium is shown in Table 2 with modified pitch leading indicator;Plus
When entering amount 4wt%, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 2 with reference, and Colophonium is main with modified pitch
Index is shown in Table 2.
Table 2
Embodiment 3
By Heveatex and industrial latex (NBR latex) in mass ratio 6:4, solid content 55%, at a temperature of 10-40 DEG C,
In reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 60-80 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition 2.22wt%
When, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 3 with reference, and Colophonium is shown in Table 3 with modified pitch leading indicator;
During addition 4.44wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 3, Colophonium and modified pitch
Leading indicator is shown in Table 3.
Table 3
Embodiment 4
By Heveatex and industrial latex (polychloroprene latex) in mass ratio 1:1, solid content 60%, at a temperature of 10-40 DEG C,
In reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 80-100 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition 2.5wt%
When, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 4 with reference, and Colophonium is shown in Table 4 with modified pitch leading indicator;
During addition 5.0wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 4, Colophonium and modified pitch
Leading indicator is shown in Table 4.
Table 4
Embodiment 5
By Heveatex and industrial latex (SBS latex) in mass ratio 4:6, solid content 65%, at a temperature of 10-40 DEG C,
In reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 100-120 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition
During 2.86wt%, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 5 with reference, and Colophonium is referred mainly to modified pitch
Mark is shown in Table 5;During addition 5.72wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 5, Colophonium with
Modified pitch leading indicator is shown in Table 5.
Table 5
Embodiment 6
By Heveatex and industrial latex (styrene-butadiene latex) in mass ratio 3:7, solid content 70%, at a temperature of 10-40 DEG C,
In reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 120-140 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition
During 3.33wt%, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 6 with reference, and Colophonium is referred mainly to modified pitch
Mark is shown in Table 6;During addition 6.66wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 6, Colophonium with
Modified pitch leading indicator is shown in Table 6.
Table 6
Embodiment 7
By Heveatex and industrial latex (styrene-butadiene latex) in mass ratio 0:100, solid content 80%, in 10-40 DEG C of temperature
Under, in reactor, 30-50 turns/and min speed stirs prepared asphalt foaming agent.
Foaming agent is added in needle penetration 140-200 (25 DEG C, 100g, 5s) 0.1mm asphalt, addition 5wt%
When, the expansion rate of asphalt foaming and half-life result are relatively shown in Table 7 with reference, and Colophonium is shown in Table 7 with modified pitch leading indicator;
During addition 10wt%, the expansion rate of asphalt foaming and half-life result and reference are relatively shown in Table 7, Colophonium and modified pitch master
Index is wanted to be shown in Table 7.
Table 7
By the contrast of embodiment 1-7 foaming effect as can be seen that the novel asphalt foaming agent of the present invention is sent out for raising Colophonium
The expansion rate of bubble and prolongation half-life have significant effect, substantially increase the stability of foamed asphalt quality.
By the contrast of embodiment 1-7 modified effect as can be seen that the novel asphalt foaming agent of the present invention is for the height of Colophonium
Warm nature can have and significantly improve, and modified foaming agent addition is more, and the modified effect to Colophonium is more obvious.
Claims (3)
1. a kind of asphalt foaming agent, is characterized in that:Its constituent is natural emulsion and industrial latex, the mass ratio of two kinds of compositions
For 100:0-0:100;Its solid content mass percent is in 1-80%.
2. asphalt foaming agent according to claim 1, is characterized in that:Its solid content is 30-80%.
3. a kind of preparation method of asphalt foaming agent:By Heveatex and industrial latex in mass ratio 100:0-0:100 scopes,
At a temperature of 10-40 DEG C, in reactor, 30-50 turn/min speed is uniformly mixed prepared asphalt foaming agent.