CN106495604A - A kind of building compound containing FS101 mortar waterproof agents - Google Patents
A kind of building compound containing FS101 mortar waterproof agents Download PDFInfo
- Publication number
- CN106495604A CN106495604A CN201610900929.9A CN201610900929A CN106495604A CN 106495604 A CN106495604 A CN 106495604A CN 201610900929 A CN201610900929 A CN 201610900929A CN 106495604 A CN106495604 A CN 106495604A
- Authority
- CN
- China
- Prior art keywords
- mortar
- mortar waterproof
- waterproof agents
- compound containing
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building compound containing FS101 mortar waterproof agents, is mixed by FS101 mortar waterproof agents, Portland cement, Sha Heshui；Wherein, FS101 mortar waterproof agents are mixed to form FS101 mortar waterproof agent dilutions with water according to 1 150～250 weight proportion；The process for preparation of the waterproof mortar is as follows：Cement bonded sand FS101 mortar waterproof agents dilution mixes according to 1 2～3 0.45～0.55 weight proportion.Building compound containing FS101 mortar waterproof agents of the invention can be combined together with main structure body concrete, solve the problems, such as the channeling water for being difficult to always solve in waterproofing work.
Description
Technical field
The present invention relates to a kind of building compound containing FS101 mortar waterproof agents.
Background technology
Buildings waterproof is prevents water from being taken the infiltration at some positions of building from construction material and on construction
Measure.Using in roofing, hypogee, the under ground portion of building and needing interior room and the water storage structures of waterproof more than waterproof
Deng.The measure that takes by which and the difference of means, are divided into two big class of material waterproofing and constructional waterproofing.Material waterproofing is by Building wood
The path of material blocking water, to reach the purpose of waterproof or the ability of increase anti-leakage, such as waterproof coiled material, coating waterproofing, concrete
And cement mortar rigid waterproofing and clay, grey great soil group waterproof etc..Constructional waterproofing is then to take suitable structural form, blocks water
Path, to reach the purpose of waterproof, such as waterstop and cavity construction etc..
Rigid waterproofing is referred to materials such as concrete, cement mortar or while mixes the rigid waterproof layer that waterproofing agent is constituted.
There are in the following manner, first engineering construction to adopt water-proof concrete in itself in practical engineering application（Concrete is made with grading of aggregates
Closely knit or mix additive, or both dual-purpose）.Which two is that structure layer surface adds and does thin layer reinforcing bar pea gravel concreten or mixed with waterproof
The cement screedn of agent.But existing mortar waterproof agent is difficult in adapt to meet《Architecture indoor waterproofing work technical regulation》In
The requirement of preferred material, i.e., " mix additive waterproof mortar using appropriate to the occasion selection response type, low alkali, low-dosage, easily scattered new
Section bar material ".In addition existing mortar waterproof agent improving mortar density while, there is no the feature for reducing Mortar shrinkage.
Content of the invention
It is an object of the invention to provide a kind of building compound containing FS101 mortar waterproof agents.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of building containing FS101 mortar waterproof agents is mixed
Material is closed, is mixed by FS101 mortar waterproof agents, Portland cement, Sha Heshui；Wherein, FS101 mortar waterproof agents and water
Weight proportion according to 1 150～250 is mixed to form FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar
As follows：Cement bonded sand FS101 mortar waterproof agents dilution mixes according to 1 2～3 0.45～0.55 weight proportion.
Another building compound for containing FS101 mortar waterproof agents that the present invention is provided, by FS101 mortar waterproofs
Agent, Portland cement, sand, synergist and water are mixed；Hydroxypropyl methyl cellulose of the synergist by 5 weight portions
Ether, 16 weight account polyethylene alcohol, 28 weight portion lithium nitrates are constituted；Wherein, FS101 mortar waterproof agents and water are according to 1 150～250
Weight proportion be mixed to form FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand increases
Effect agent FS101 mortar waterproof agents dilution mixes according to 1 2～3 0.15～0.20 0.45～0.55 weight proportion.
Building compound containing FS101 mortar waterproof agents as above of the invention, it is preferable that FS101 mortar waterproofs
Agent is mixed to form FS101 mortar waterproof agent dilutions with water according to 1 200 weight proportion；The preparation of the building compound
Journey is as follows：Cement bonded sand FS101 mortar waterproof agents dilution mixes according to 1 2.5 0.45～0.55 weight proportion.
Building compound containing FS101 mortar waterproof agents as above of the invention, it is preferable that the normal silicate
The strength grade of cement is more than or equal to 32.5Mpa.
Building compound containing FS101 mortar waterproof agents as above of the invention, it is preferable that the sand is middle sand,
Clay content is less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.
Building compound containing FS101 mortar waterproof agents as above of the invention, it is preferable that the building compound
Strength grade be more than or equal to 20Mpa.
The invention has the beneficial effects as follows：
FS101 mortar waterproof agents in compound improving mortar density while, with the feature for reducing Mortar shrinkage, this is
With the maximum difference of conventional rigid waterproof material.FS101 mortar waterproof agents are inorganic liquid, and good dispersion is naturally fused with water, keeps away
Pulvis and emulsion material have been exempted from and uniform problem have been difficult in mortar mix, so as to improve the impermeability of mortar integral waterproofing layer
And stability.Building compound containing FS101 mortar waterproof agents of the invention can be combined together with main structure body concrete, be solved
The channeling water problem that solve is difficult in waterproofing work always.
Specific embodiment
The embodiment that here is recorded is the specific specific embodiment of the present invention, for the design of the present invention is described,
It is explanatory and exemplary, should not be construed as the restriction to embodiment of the present invention and the scope of the invention.Except here record
Implement exception, those skilled in the art can also be based on the application claims and specification disclosure of that using aobvious and
Other technical schemes being clear to, these technical schemes include any obvious using making for the embodiment recorded by here
The technical scheme of substitutions and modifications.
The manufacturer of FS101 mortar waterproof agents of the present invention be Beijing Long Yang great achievements Science and Technology Co., Ltd., type
Number be FS101.
Embodiment 1
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand and water are mixed；Wherein, FS101 mortar waterproof agents and water are mixed to form FS101 mortars and prevent according to 1 250 weight proportion
Aqua dilution；The process for preparation of the waterproof mortar is as follows：Cement bonded sand FS101 mortar waterproof agents dilution is according to 13
0.45 weight proportion mixing.In the present embodiment, the strength grade of Portland cement is 42.5.The sand is middle sand, containing mud
Amount is less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.The waterproof layer for being formed
The performance test results are shown in Table 1.Its performance meets the requirement of JC474-2008 standards as seen from Table 1.
Table 1
Embodiment 2
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand and water are mixed；Wherein, FS101 mortar waterproof agents and water are mixed to form FS101 mortars and prevent according to 1 250 weight proportion
Aqua dilution；The process for preparation of the waterproof mortar is as follows：Cement bonded sand FS101 mortar waterproof agents dilution is according to 12
0.55 weight proportion mixing.In the present embodiment, the strength grade of Portland cement is 42.5R.The sand is middle sand, contains
Mud amount is less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.The waterproof layer for being formed
The performance test results be shown in Table 2.Its performance meets the requirement of JC474-2008 standards as seen from Table 2.
Table 2
Embodiment 3
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand and water are mixed；Wherein, FS101 mortar waterproof agents and water are mixed to form FS101 mortars and prevent according to 1 200 weight proportion
Aqua dilution；The process for preparation of the waterproof mortar is as follows：Cement bonded sand FS101 mortar waterproof agents dilution is according to 13
0.50 weight proportion mixing.In the present embodiment, the strength grade of Portland cement is 52.5.The sand is middle sand, containing mud
Amount is less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.The waterproof layer for being formed
The performance test results are shown in Table 3.Its performance meets the requirement of JC474-2008 standards as seen from Table 3.
Table 3
Embodiment 4
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand, synergist and water are mixed；Hydroxypropyl methyl cellulose ether of the synergist by 5 weight portions, 16 weight account polyethylenes
Alcohol, 28 weight portion lithium nitrates are constituted；Wherein, FS101 mortar waterproof agents are mixed to form according to 1 250 weight proportion with water
FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand synergist FS101 mortar waterproofs
Dilution agent liquid mixes according to 12 0.15 0.45 weight proportion.In the present embodiment, the strength grade of Portland cement is
42.5.The sand be middle sand, clay content be less than or equal to 1wt%, sulfide content be less than or equal to 1wt%, sulphates content less than etc.
In 1wt%.The performance test results of the waterproof layer for being formed are shown in Table 4.Its performance meets JC474-2008 standards and wants as seen from Table 4
Ask.
Table 4
Embodiment 5
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand, synergist and water are mixed；Hydroxypropyl methyl cellulose ether of the synergist by 5 weight portions, 16 weight account polyethylenes
Alcohol, 28 weight portion lithium nitrates are constituted；Wherein, FS101 mortar waterproof agents are mixed to form according to 1 250 weight proportion with water
FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand synergist FS101 mortar waterproofs
Dilution agent liquid mixes according to 1 2.5 0.20 0.55 weight proportion.The strength grade of Portland cement in the present embodiment
For 42.5R.The sand is middle sand, and clay content is less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than
It is equal to 1wt%.The performance test results of the waterproof layer for being formed are shown in Table 5.Its performance meets JC474-2008 standards as seen from Table 5
Require.
Table 5
Embodiment 6
The present embodiment contains the building compound of FS101 mortar waterproof agents, by FS101 mortar waterproof agents, Portland cement,
Sand, synergist and water are mixed；Hydroxypropyl methyl cellulose ether of the synergist by 5 weight portions, 16 weight account polyethylenes
Alcohol, 28 weight portion lithium nitrates are constituted；Wherein, FS101 mortar waterproof agents are mixed to form according to 1 200 weight proportion with water
FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand synergist FS101 mortar waterproofs
Dilution agent liquid mixes according to 1 2.5 0.18 0.5 weight proportion.In the present embodiment, the strength grade of Portland cement is
52.5.The sand be middle sand, clay content be less than or equal to 1wt%, sulfide content be less than or equal to 1wt%, sulphates content less than etc.
In 1wt%.The performance test results of the waterproof layer for being formed are shown in Table 6.Its performance meets JC474-2008 standards and wants as seen from Table 6
Ask.
Table 6
Each technical characteristic of above-mentioned disclosure is not limited to disclosed combining with further feature, and those skilled in the art can also root
Other combinations between each technical characteristic are carried out according to the purpose of invention, to realize that the purpose of the present invention is defined.
Claims (10)
1. a kind of building compound containing FS101 mortar waterproof agents, it is characterised in that by FS101 mortar waterproof agents, ordinary silicon
Acid salt cement, Sha Heshui are mixed；Wherein, FS101 mortar waterproof agents are mixed according to 1 150～250 weight proportion with water
Form FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand FS101 mortar waterproof agents
Dilution mixes according to 1 2～3 0.45～0.55 weight proportion.
2. the building compound containing FS101 mortar waterproof agents according to claim 1, it is characterised in that FS101 mortars
Waterproofing agent is mixed to form FS101 mortar waterproof agent dilutions with water according to 1 200 weight proportion；The building compound is matched somebody with somebody
Process processed is as follows：Cement bonded sand FS101 mortar waterproof agents dilution mixes according to 1 2.5 0.45～0.55 weight proportion.
3. the building compound containing FS101 mortar waterproof agents according to claim 1 and 2, it is characterised in that described general
The strength grade of logical portland cement is more than or equal to 32.5Mpa.
4. the building compound containing FS101 mortar waterproof agents according to claim 3, it is characterised in that the sand is
Middle sand, clay content are less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.
5. the building compound containing FS101 mortar waterproof agents according to claim 1, it is characterised in that the building
The strength grade of compound is more than or equal to 20Mpa.
6. a kind of building compound containing FS101 mortar waterproof agents, it is characterised in that by FS101 mortar waterproof agents, ordinary silicon
Acid salt cement, sand, synergist and water are mixed；Hydroxypropyl methyl cellulose ether of the synergist by 5 weight portions, 16 weight
Part polyvinyl alcohol, 28 weight portion lithium nitrates are constituted；Wherein, FS101 mortar waterproof agents are matched somebody with somebody according to 1 150～250 weight with water
Than being mixed to form FS101 mortar waterproof agent dilutions；The process for preparation of the waterproof mortar is as follows：Cement bonded sand synergist
FS101 mortar waterproof agents dilution mixes according to 1 2～3 0.15～0.20 0.45～0.55 weight proportion.
7. the building compound containing FS101 mortar waterproof agents according to claim 6, it is characterised in that FS101 mortars
Waterproofing agent is mixed to form FS101 mortar waterproof agent dilutions with water according to 1 200 weight proportion；The building compound is matched somebody with somebody
Process processed is as follows：Cement bonded sand synergist FS101 mortar waterproof agents dilution according to 1 2～3 0.18 0.45～0.55 weight
Amount proportioning mixing.
8. the building compound containing FS101 mortar waterproof agents according to claim 6 or 7, it is characterised in that described general
The strength grade of logical portland cement is more than or equal to 32.5Mpa.
9. the building compound containing FS101 mortar waterproof agents according to claim 8, it is characterised in that the sand is
Middle sand, clay content are less than or equal to 1wt%, and sulfide content is less than or equal to 1wt%, and sulphates content is less than or equal to 1wt%.
10. the building compound containing FS101 mortar waterproof agents according to claim 6, it is characterised in that the building
The strength grade of compound is more than or equal to 20Mpa.