CN106493370A - Without preparation method of the magnetic without nickel metal furnishings - Google Patents
Without preparation method of the magnetic without nickel metal furnishings Download PDFInfo
- Publication number
- CN106493370A CN106493370A CN201610921224.5A CN201610921224A CN106493370A CN 106493370 A CN106493370 A CN 106493370A CN 201610921224 A CN201610921224 A CN 201610921224A CN 106493370 A CN106493370 A CN 106493370A
- Authority
- CN
- China
- Prior art keywords
- furnishings
- magnetic
- parts
- nickel metal
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation method without magnetic without nickel metal furnishings, after the raw materials melt that group is divided into cobalt, chromium and molybdenum, chilling dusts and to form alloy powder, again through high-pressure molding, dumping degreasing and vacuum high-temperature sintering the step of, it is obtained without magnetic without nickel metal furnishings, processing procedure is simple, production efficiency is high, product yield is high, simultaneously because alloy powder is made up of cobalt, chromium and molybdenum, not comprising the nickel with sensitization, make obtained will not cause without nickel metal furnishings without magnetic allergic, with higher product quality.
Description
Technical field
A kind of the present invention relates to furnishings technical field, more particularly to making side without magnetic without nickel metal furnishings
Method.
Background technology
With growth in the living standard, requirement of the people to quality of the life and external image also more and more higher, and dress and use
Product not only act as the effect of decoration, also there is the effect for lifting image, be increasingly subject to the favor and attention of people, and this is to wearing
The development of articles for use industry brings opportunity.
The wide variety of traditional furnishings, not only includes the furnishings with specific function, such as wrist-watch etc., also wraps
Include pure ornamental furnishings, such as earrings, necklace, bracelet etc..As customer demand becomes more diverse, the kind of furnishings
Class is also being continuously increased.
Greatly made using metal alloy compositions in all kinds of furnishings in the market, due to metal alloy material
The cost of material is relatively low, and easily diversification of forms, makes that obtained furnishings are cheap, and pattern is various, can adapt to client's day
The esthetic requirement of benefit change, occupies the substantial amounts of market share.
However, the furnishings of majority can be with the direct skin contact of wearer when wearing, and existing metal alloy
Contain metallic nickel (Ni) in material mostly, nickel is a kind of sensitization metal, when the skin of wearer is closed with nickeliferous metal is adopted
During the furnishings directly contact that golden material makes, once contact position produces sweat, nickeliferous metal alloy compositions can discharge greatly
The nickel ion of amount, these nickel ions can be penetrated into inside the skin of wearer by pore and sebaceous glands, cause wearer's product
Life is allergic, redness, even itch, the phenomenon such as decortication occurs, and the duration of nickel allergy is long, the pressure suffered by allergy sufferers
The humidity of power, sweat, air and skin and friction can all increase the symptom of nickel allergy, and this can seriously threaten the body of wearer to be good for
Health, largely effects on the quality of furnishings, makes have larger limitation when making furnishings using existing metal alloy compositions
Property.
Content of the invention
It is an object of the invention to provide a kind of preparation method without magnetic without nickel metal furnishings, processing procedure is simple, production
Efficiency high, and yield is high, obtained will not cause without nickel metal furnishings without magnetic allergic.
For achieving the above object, the present invention provides a kind of preparation method without magnetic without nickel metal furnishings, including as follows
Step:
Step 1, provide raw material, raw material components and its weight portion as follows:Cobalt 30-35 parts, chromium 55-60 parts and molybdenum 5-10 parts;
Step 2, by each raw material components melt, then chilling dusts, formed alloy powder;
Step 3, high-pressure molding;
Step 4, dumping degreasing;
Step 5, vacuum high-temperature sintering.
The furnishings include wrist-watch and ornaments.
Parts by weight of raw materials in the step 1 is respectively 9 parts of 33 parts of cobalt, 58 parts of chromium and molybdenum.
The powder of the step 2 is filtered using 400 mesh half tones.
In the step 3, paraffin, microwax, stearin candle and plastic cement are added to alloy powder, and is well mixed, then adopted
With dry-pressing, hot pressing or isostatic pressing.
Each material content of the step 3 is distinguished as follows by weight:With alloy powder as 1000 parts, paraffin 11-17
Part, microwax 11-17 parts, stearin candle 1-3 parts, plastic cement 65-75 parts.
The plastic cement is therein a kind of from PE, PP, HIPS, PET or which combines.
In step 4, the temperature of dumping degreasing is less than or equal to 500 DEG C.
In the step 4, heating base substrate to 480 DEG C -500 DEG C, wherein base substrate degreasing before temperature reaches 100 DEG C,
Temperature reaches 200 DEG C of plastic removals afterwards.
In step 5, sintering temperature is 1350-1500 DEG C.
Beneficial effects of the present invention:The present invention the preparation method without magnetic without nickel metal furnishings, by group be divided into cobalt,
After the raw materials melt of chromium and molybdenum, chilling dusts to form alloy powder, then through high-pressure molding, dumping degreasing and vacuum high-temperature sintering
The step of, it is obtained without magnetic without nickel metal furnishings, processing procedure is simple, and production efficiency is high, and product yield is high, simultaneously because alloyed powder
End is made up of cobalt, chromium and molybdenum, not comprising the nickel with sensitization, makes obtained to draw without nickel metal furnishings without magnetic
Rise allergic, with higher product quality.
Specific embodiment
The present invention provides a kind of preparation method without magnetic without nickel metal furnishings, and the furnishings include wrist-watch and decorations
The all types of furnishings such as product, the preparation method without magnetic without nickel metal furnishings comprise the steps:
Step 1, provide raw material, raw material components and its weight portion as follows:Cobalt 30-35 parts, chromium 55-60 parts and molybdenum 5-10 parts.
Preferably, the parts by weight of raw materials in the step 1 is respectively 9 parts of 33 parts of cobalt, 58 parts of chromium and molybdenum.
Step 2, by each raw material components melt, then chilling dusts, formed alloy powder.
Specifically, the powder of the step 2 is filtered using 400 mesh half tones.
Step 3, high-pressure molding.
Specifically, in the step 3, paraffin, microwax, stearin candle and plastic cement are added to alloy powder, and are well mixed,
Then dry-pressing, hot pressing or isostatic pressing are adopted.
Further, each material content of the step 3 is distinguished as follows by weight:With alloy powder as 1000 parts,
Paraffin 11-17 parts, microwax 11-17 parts, stearin candle 1-3 parts, plastic cement 65-75 parts.
Specifically, the plastic cement is therein a kind of from PE, PP, HIPS, PET or which combines.
Step 4, dumping degreasing.
Specifically, in step 4, the temperature of dumping degreasing is less than or equal to 500 DEG C.
Specifically, in the step 4, base substrate to 480 DEG C -500 DEG C is heated, wherein base substrate is before temperature reaches 100 DEG C
Degreasing, reaches 200 DEG C of plastic removals afterwards in temperature.
Step 5, vacuum high-temperature sintering.
Specifically, in step 5, sintering temperature is 1350-1500 DEG C.
The preparation method without magnetic without nickel metal furnishings of the present invention, is entered by group to be divided into the raw material of cobalt, chromium and molybdenum
After row melting, chilling dusts to form alloy powder, then the step of through high-pressure molding, dumping degreasing and vacuum high-temperature sintering, is obtained
Without magnetic without nickel metal furnishings, processing procedure is simple, and production efficiency is high, and product yield is high, simultaneously because constituting without magnetic without nickel metal
The composition of the alloy powder of furnishings be cobalt, chromium and molybdenum, not comprising the nickel with sensitization, nickeliferous with of the prior art
Metal alloy compositions compare, can make obtained will not cause allergic without magnetic without nickel metal furnishings, greatly promote
Product quality.
In sum, group is divided into cobalt, chromium and molybdenum by the preparation method without magnetic without nickel metal furnishings of the invention
After raw materials melt, chilling dusts to form alloy powder, then the step of through high-pressure molding, dumping degreasing and vacuum high-temperature sintering, system
Without magnetic without nickel metal furnishings, processing procedure is simple, and production efficiency is high, and product yield is high, simultaneously because alloy powder be by cobalt,
Chromium and molybdenum composition, not comprising the nickel with sensitization, make obtained to cause skin mistake without magnetic without nickel metal furnishings
Quick, with higher product quality.
The above, for the person of ordinary skill of the art, can be with technology according to the present invention scheme and technology
Other various corresponding changes and deformation are made in design, and all these changes and deformation should all belong to appended right of the invention
The protection domain of requirement.
Claims (10)
1. a kind of preparation method without magnetic without nickel metal furnishings, it is characterised in that comprise the steps:
Step 1, provide raw material, raw material components and its weight portion as follows:Cobalt 30-35 parts, chromium 55-60 parts and molybdenum 5-10 parts;
Step 2, by each raw material components melt, then chilling dusts, formed alloy powder;
Step 3, high-pressure molding;
Step 4, dumping degreasing;
Step 5, vacuum high-temperature sintering.
2. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that the furnishings
Including wrist-watch and ornaments.
3. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that in the step 1
Parts by weight of raw materials be respectively 9 parts of 33 parts of cobalt, 58 parts of chromium and molybdenum.
4. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that the step 2
Powder is filtered using 400 mesh half tones.
5. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that in the step 3,
Paraffin, microwax, stearin candle and plastic cement are added to alloy powder, and is well mixed, then adopt dry-pressing, hot pressing or isostatic pressed
Shaping.
6. the preparation method without magnetic without nickel metal furnishings as claimed in claim 5, it is characterised in that the step 3
Each material content is distinguished as follows by weight:With alloy powder as 1000 parts, paraffin 11-17 parts, microwax 11-17 parts,
Stearin candle 1-3 parts, plastic cement 65-75 parts.
7. the preparation method without magnetic without nickel metal furnishings as claimed in claim 6, it is characterised in that the plastic cement is selected
PE, PP, HIPS, PET are therein a kind of or which combines.
8. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that in step 4, dumping
The temperature of degreasing is less than or equal to 500 DEG C.
9. the preparation method without magnetic without nickel metal furnishings as claimed in claim 8, it is characterised in that in the step 4,
Heating base substrate to 480 DEG C -500 DEG C, wherein base substrate degreasing before temperature reaches 100 DEG C, in the heel row that temperature reaches 200 DEG C
Modeling.
10. the preparation method without magnetic without nickel metal furnishings as claimed in claim 1, it is characterised in that in step 5, burn
Junction temperature is 1350-1500 DEG C.