Abstract

The present invention relates to a kind of production technology of the warming worsted fabric containing soybean fiber, the production technology of this warming worsted fabric containing soybean fiber carries out anti pilling process from phosphate ester antimony oxide mixture as anti pilling agent, further increase the anti-hairy effect of fiber and fabric, anti-hairy effect is up to 4-5 level.Carry out soft treatment from water-soluble organic silicon softening agent, woollen and cashmere fabric can be made to have more smooth, plentiful feel.Soybean fiber can make be made into fabric have the soft feel as cashmere further; sub-dued lustre as silkworm silk; the premium properties such as the warmth retention property of cotton and good skin-friendly; also has obvious bacteria resistance function simultaneously; thus preferably achieving mutual supplement with each other's advantages and the inferior position abatement of each fiber; so that the fabric intensity made with above-mentioned fiber more preferably, water suction heat-insulating property higher, and more well-pressed, also have preferable benefit to health and environmental conservation.

Description

The production technology of the warming worsted fabric containing soybean fiber

Technical field

The present invention relates to a kind of production technology of fabric, the production technology of more particularly, to a kind of warming worsted fabric containing soybean fiber, belong to garment material technical field.

Background technology

Weaving wool fibre is main to be sheep's wool, so-called Pilus Caprae seu Oviss, or claims wool fibre, or abbreviation hair.Its advantage is it is obvious that one is that dress is as snug as a bug in a rug with high-hydroscopicity.Two is with warmth retention property, natural crimp, can be formed between many immobilising air zone as barrier.Three is with ruggedness, has extraordinary draftability and elastic recovery.Wool worsted face fabric in the market is often due to employ inappropriate manufacture method so that the quality of fabric substantially reduces.For example, using mordant dyeing technique although uniform color, good color fastness, cost is relatively low, but dyeing temperature is high, and time-consuming, much to wool damage, and fabric resilience is poor.Again for example, using inappropriate postfinishing process, fabric cloth cover out-of-flatness can be made, edge-curl phenomenon is serious, washing shrinkage is big, easy pilling.

Content of the invention

It is an object of the invention to overcoming above-mentioned deficiency, a kind of production technology of the warming worsted fabric containing soybean fiber is provided, this technique productions wool fabric out can greatly reduce the damage of product of wool fiber, reduce balling-up, fabric feel is more soft, felting shrinkage factor is also greatly lowered, and fabric quality is more preferably.

The object of the present invention is achieved like this：

A kind of production technology of the warming worsted fabric containing soybean fiber, the comprising the following steps that of this production technology：

1）, yarn variety design：

From cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber, to cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber carry out anti pilling process, ferment treatment and soft treatment, anti pilling is processed from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2）, recombing technique：

Wool top is made in cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber recombing.

3）, spinning process：

Premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, and it is 81Nm that spun yarn its number is wherein obtained, twist 780Z twist/m；Its double strand yarn for number 80Nm of prepared yarn, twist 810S twist/m of pooling capital；Weight percent content in warp thread with weft yarn for the anti-transparent terylene is 30；

4）, postfinishing process：

Final finishing includes：Singe-mono- boil-braying-bis- boil-dry-photocatalyst working fluid pads-dries-TEFLON three-prevention finishing-bake-ripe-bristle-cropping-bristle-dewing-tank of repairing and steam, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, pick-up rate 75% 85%, keeps car 25m/min 30m/min, 120 DEG C 135 DEG C of temperature in the use of photocatalyst working fluid, the mangle 75-85% of TEFLON three-prevention finishing processing, speed keeps 18-22m/min, temperature 160-180 DEG C, and the fabric specification being finally obtained is：Yarn count 96/2-100/2Nm, total tightness degree 145-165, end count 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 grams m.

Compared with prior art, the invention has the beneficial effects as follows：

The production technology of this warming worsted fabric containing soybean fiber carries out anti pilling process from phosphate ester antimony oxide mixture as anti pilling agent, further increases the anti-hairy effect of fiber and fabric, anti-hairy effect is up to 4-5 level.Carry out soft treatment from water-soluble organic silicon softening agent, woollen and cashmere fabric can be made to have more smooth, plentiful feel.Finally more described fabric is carried out post processing with soluble polyurethane Wool Shrink-Resist Agent, woolen knitwear area felting shrinkage factor≤3% after process, it is far smaller than the 8% of International Wool international office defined, greatly improve the integrated quality of described fabric, soybean fiber can make be made into fabric have the soft feel as cashmere further, sub-dued lustre as silkworm silk, the premium properties such as the warmth retention property of cotton and good skin-friendly, also has obvious bacteria resistance function simultaneously, thus preferably achieving mutual supplement with each other's advantages and the inferior position abatement of each fiber, so that the fabric intensity made with above-mentioned fiber is more preferable, water suction heat-insulating property is higher, and it is more well-pressed, also there is preferable benefit to health and environmental conservation.

Specific embodiment

The present invention relates to a kind of production technology of the warming worsted fabric containing soybean fiber, pass sequentially through variety development, recombing, spinning, postfinishing process make fabric, comprise the following steps that：

1）, yarn variety design：

From cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber, to cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber carry out anti pilling process, ferment treatment and soft treatment, anti pilling is processed from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2）, recombing technique：

Wool top is made in cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber recombing.

3）, spinning process：

Premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, and it is 81Nm that spun yarn its number is wherein obtained, twist 780Z twist/m；Its double strand yarn for number 80Nm of prepared yarn, twist 810S twist/m of pooling capital；Weight percent content in warp thread with weft yarn for the anti-transparent terylene is 30；

4）, postfinishing process：

Final finishing includes：Singe-mono- boil-braying-bis- boil-dry-photocatalyst working fluid pads-dries-TEFLON three-prevention finishing-bake-ripe-bristle-cropping-bristle-dewing-tank of repairing and steam, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, pick-up rate 75% 85%, keeps car 25m/min 30m/min, 120 DEG C 135 DEG C of temperature in the use of photocatalyst working fluid, the mangle 75-85% of TEFLON three-prevention finishing processing, speed keeps 18-22m/min, temperature 160-180 DEG C, and the fabric specification being finally obtained is：Yarn count 96/2-100/2Nm, total tightness degree 145-165, end count 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 grams m.

Claims (1)

1. a kind of production technology of the warming worsted fabric containing soybean fiber it is characterised in that：The comprising the following steps that of this production technology：

1）, yarn variety design：

From cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber, to cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber carry out anti pilling process, ferment treatment and soft treatment, anti pilling is processed from phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system is processed using protease, albumen enzyme dosage is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；

2）, recombing technique：

Wool top is made in cashmere fiber, bamboo carbon dacron fiber, poly butylene succinate silk and soybean fiber recombing；

3）, spinning process：

Premenstrual spinning-spun yarn-winder-doubling-double twisting-yarn steaming makes yarn, and it is 81Nm that spun yarn its number is wherein obtained, twist 780Z twist/m；Its double strand yarn for number 80Nm of prepared yarn, twist 810S twist/m of pooling capital；Weight percent content in warp thread with weft yarn for the anti-transparent terylene is 30；

4）, postfinishing process：

Final finishing includes：Singe-mono- boil-braying-bis- boil-dry-photocatalyst working fluid pads-dries-TEFLON three-prevention finishing-bake-ripe-bristle-cropping-bristle-dewing-tank of repairing and steam, in addition, the consumption 30g/l 50g/l of photocatalyst working fluid, pick-up rate 75% 85%, keeps car 25m/min 30m/min, 120 DEG C 135 DEG C of temperature in the use of photocatalyst working fluid, the mangle 75-85% of TEFLON three-prevention finishing processing, speed keeps 18-22m/min, temperature 160-180 DEG C, and the fabric specification being finally obtained is：Yarn count 96/2-100/2Nm, total tightness degree 145-165, end count 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 grams m.