CN106479415A - 木板用粘合剂 - Google Patents
木板用粘合剂 Download PDFInfo
- Publication number
- CN106479415A CN106479415A CN201510540127.7A CN201510540127A CN106479415A CN 106479415 A CN106479415 A CN 106479415A CN 201510540127 A CN201510540127 A CN 201510540127A CN 106479415 A CN106479415 A CN 106479415A
- Authority
- CN
- China
- Prior art keywords
- parts
- plank
- adhesive
- wax emulsion
- paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种木板用粘合剂，粘合剂原料按重量份包括下列组分：环氧树脂0‑500份、石蜡乳化液1‑200份、白乳胶1‑300份、固化剂1‑200份，超细纤维素粉50‑100份、纤维素酶0‑10份；粘合剂为上述原料溶于有机溶剂调成胶状物而成；利用环氧树脂与白乳剂的协同胶连作用，提高较强的粘接强度，可在较长时间使用过程中不易脱胶，而且，采用石蜡乳化液，因石蜡微粒径细，可自然渗透到木板内部，烘干即可达到防水的效果，使木板具有抗水性，另外，纤维素具有较好的吸收性，并在纤维素酶的作用下具有亲水性，达到防潮的目的。
Description
技术领域
本发明涉及粘合剂领域，特别涉及一种木板用粘合剂。
背景技术
目前木工用粘合剂多简单采用白乳胶，实际使用中存在强度不够，时间长以后，容易脱胶，粘接力不强，同时不耐水，易吸潮，家具等如果有水渗透与浸入后，即会脱胶，影响其使用效果。
因此，需要对木板用粘合剂进行改进，不但提高其粘接强度，防止脱胶，并使其具有较好的抗水性，达到防水效果。
发明内容
有鉴于此，本发明提供一种木板用粘合剂，提高其粘接强度，防止脱胶，并使其具有较好的抗水性，达到防水效果。
本发明的木板用粘合剂，粘合剂原料按重量份包括下列组分：环氧树脂0-500份、石蜡乳化液1-200份、白乳胶1-300份、固化剂1-200份，超细纤维素粉50-100份、纤维素酶0-10份；
所述粘合剂为上述原料溶于有机溶剂调成胶状物而成。
进一步，粘合剂原料按重量份包括下列组分：环氧树脂400份、石蜡乳化液200份、白乳胶300份、固化剂200份，超细纤维素粉80份、纤维素酶5份。
进一步，固化剂为甲基六氢苯酐、双氰胺、脂肪族多胺中的一种或两种以上混合物。
进一步，石蜡乳化液包括下列组分：石蜡2％～30％、石油树脂2％～30％、氧化蜡0.4％～12％、石蜡乳化剂0.6％～12％、水16％～95％。
进一步，超细纤维素粉由秸秆、稻草或木粉加工而成。
本发明的有益效果：本发明的木板用粘合剂，利用环氧树脂与白乳剂的协同胶连作用，提高较强的粘接强度，可在较长时间使用过程中不易脱胶，而且，采用石蜡乳化液，因石蜡微粒径细，可自然渗透到木板内部，烘干即可达到防水的效果，使木板具有抗水性，另外，纤维素具有较好的吸收性，有效降低了水分子对粘合剂的破坏，使的粘合剂的抗水性有很大的提高，具有较好的快干特性，同时粘接强度大大提高，耐水性明显提高，并在纤维素酶的作用下具有亲水性，达到防潮的目的。
具体实施方式
下面结合实施例对本发明作进一步的说明，但并不作为对本发明的限制的依据。
本实施例的木板用粘合剂，粘合剂原料按重量份包括下列组分：环氧树脂0-500份、石蜡乳化液1-200份、白乳胶1-300份、固化剂1-200份，超细纤维素粉50-100份、纤维素酶0-10份；
所述粘合剂为上述原料溶于有机溶剂调成胶状物而成。
优选的，粘合剂原料按重量份包括下列组分：环氧树脂400份、石蜡乳化液200份、白乳胶300份、固化剂200份，超细纤维素粉80份、纤维素酶5份。
本实施例中，固化剂为甲基六氢苯酐、双氰胺、脂肪族多胺中的一种或两种以上混合物。
本实施例中，石蜡乳化液包括下列组分：石蜡2％～30％、石油树脂2％～30％、氧化蜡0.4％～12％、石蜡乳化剂0.6％～12％、水16％～95％。
本实施例中，超细纤维素粉由秸秆、稻草或木粉加工而成。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (5)
1.一种木板用粘合剂，其特征在于：粘合剂原料按重量份包括下列组分：环氧树脂0-500份、石蜡乳化液1-200份、白乳胶1-300份、固化剂1-200份，超细纤维素粉50-100份、纤维素酶0-10份；
所述粘合剂为上述原料溶于有机溶剂调成胶状物而成。
2.根据权利要求1所述的木板用粘合剂，其特征在于：粘合剂原料按重量份包括下列组分：环氧树脂400份、石蜡乳化液200份、白乳胶300份、固化剂200份，超细纤维素粉80份、纤维素酶5份。
3.根据权利要求2所述的木板用粘合剂，其特征在于：固化剂为甲基六氢苯酐、双氰胺、脂肪族多胺中的一种或两种以上混合物。
4.根据权利要求3所述的木板用粘合剂，其特征在于：石蜡乳化液包括下列组分：石蜡2％～30％、石油树脂2％～30％、氧化蜡0.4％～12％、石蜡乳化剂0.6％～12％、水16％～95％。
5.根据权利要求4所述的木板用粘合剂，其特征在于：所述超细纤维素粉由秸秆、稻草或木粉加工而成。