CN106479149A - A kind of Composite Coatings aluminium film - Google Patents
A kind of Composite Coatings aluminium film Download PDFInfo
- Publication number
- CN106479149A CN106479149A CN201610895379.6A CN201610895379A CN106479149A CN 106479149 A CN106479149 A CN 106479149A CN 201610895379 A CN201610895379 A CN 201610895379A CN 106479149 A CN106479149 A CN 106479149A
- Authority
- CN
- China
- Prior art keywords
- parts
- poly
- acid
- diester
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Composite Coatings aluminium film, including:Film base layer and aluminium coated, described film base layer are made up of following components:Isopropyl myristate, β (3,4 dihydroxy phenyls) α hydracrylic acid isopropyl ester, dihexyl sebacate, poly- carbonic acid 1,2 propylene diesters, poly- butanedioic acid fourth diester and citric acid three (2 propyl group heptan) ester, the weight content of its each component is:34 ~ 48 parts of isopropyl myristate, β (3,4 dihydroxy phenyls) 16 ~ 33 parts of α hydracrylic acid isopropyl ester, 10 ~ 22 parts of dihexyl sebacate, 15 ~ 29 parts of 1,2 propylene diester of poly- carbonic acid, 9 ~ 21 parts of poly- butanedioic acid fourth diester and citric acid three (2 propyl group heptan) 38 ~ 50 parts of ester.By the way, the back side of inventive film base layer is difficult scratch, and tensile resistance is excellent.
Description
Technical field
The present invention relates to aluminizer field, more particularly to a kind of Composite Coatings aluminium film.
Background technology
Aluminizer is that the one kind formed in the very thin metallic aluminium of Plastic film surface plating last layer using special process is multiple
Flexible packing material is closed, the processing method of most common of which, when number vacuum evaporated aluminium method, is exactly to pass through high temperature under high vacuum state
By metallic aluminium fusing evaporation, the steam precipitation of aluminium is made to be stacked in Plastic film surface, so that Plastic film surface has gold
Category gloss.As it had both had the characteristic of plastic sheeting, and the characteristic with metal, it is a kind of inexpensive attractive in appearance, function admirable, reality
With the strong packaging material of property, therefore, aluminizer has been widely used in the packaging of the products such as food, medicine, chemical industry, such as
The packaging of fast food, tealeaves, coffee and cosmetics.
The application of aluminizer is more and more extensive, has had become as the very universal a kind of packing timber of application in Flexible-Packaging Industry
Material.The species of aluminizer is a lot, applies most aluminizers to be mainly polyester aluminizer at present(VMPET)With CPP aluminizer
(VMCPP), polyester aluminizer(VMPET)The intermediate layer of composite packaging is typically used as, as its outward appearance is beautiful, in high-grade packaging
Application is most, the such as packaging bag such as milk powder, tealeaves.CPP aluminizer(VMCPP)The hot sealing layer of composite packaging is typically used as, is usually used in
Common pot foods(Such as biscuit)Packaging.
However, the back side of the film base layer of the aluminizer for using at present easily abrades, and tensile resistance is poor.
Content of the invention
The present invention solves the technical problem of providing a kind of Composite Coatings aluminium film, the back side of film base layer is difficult scratch,
And tensile resistance is excellent.
For solving above-mentioned technical problem, one aspect of the present invention is:A kind of Composite Coatings aluminium film is provided, including:Film
Base layer and aluminium coated, described film base layer are made up of following components:Isopropyl myristate, β-(3,4- dihydroxy phenyl)-
α-hydracrylate isopropyl ester, dihexyl sebacate, poly-carbonic acid 1,2-propylene diester, poly- butanedioic acid fourth diester and three (2- of citric acid
Propyl group heptan) ester, the weight content of its each component is:34 ~ 48 parts of isopropyl myristate, β-(3,4- dihydroxy phenyl)-Alpha-hydroxy
16 ~ 33 parts of isopropyl propionate, 10 ~ 22 parts of dihexyl sebacate, 15 ~ 29 parts of poly-carbonic acid 1,2-propylene diester, poly- butanedioic acid fourth two
9 ~ 21 parts of ester and citric acid three (2- propyl group heptan) 38 ~ 50 parts of ester.
In a preferred embodiment of the present invention, described β-(3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester
Weight content is 18 ~ 30 parts.
In a preferred embodiment of the present invention, the weight content of described poly- carbonic acid 1,2- propylene diester is 17 ~ 29 parts.
In a preferred embodiment of the present invention, the weight content of described poly- butanedioic acid fourth diester is 11 ~ 21 parts.
The invention has the beneficial effects as follows:The back side of inventive film base layer is difficult scratch, and tensile resistance is excellent.
Specific embodiment
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described enforcement
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model of present invention protection
Enclose.
Embodiment 1
A kind of Composite Coatings aluminium film, including:Film base layer and aluminium coated, described film base layer are made up of following components:Tetradecylic acid
Isopropyl ester, β-(3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, dihexyl sebacate, poly-carbonic acid 1,2-propylene diester, poly-
Butanedioic acid fourth diester and citric acid three (2- propyl group heptan) ester, the weight content of its each component is:34 parts of isopropyl myristate, β-
18 parts of (3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, 10 parts of dihexyl sebacate, poly-carbonic acid 1,2-propylene diester 17
Part, 11 parts of poly- butanedioic acid fourth diester and citric acid three (2- propyl group heptan) 38 parts of ester.
Embodiment 2
A kind of Composite Coatings aluminium film, including:Film base layer and aluminium coated, described film base layer are made up of following components:Tetradecylic acid
Isopropyl ester, β-(3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, dihexyl sebacate, poly-carbonic acid 1,2-propylene diester, poly-
Butanedioic acid fourth diester and citric acid three (2- propyl group heptan) ester, the weight content of its each component is:48 parts of isopropyl myristate, β-
30 parts of (3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, 22 parts of dihexyl sebacate, poly-carbonic acid 1,2-propylene diester 29
Part, 21 parts of poly- butanedioic acid fourth diester and citric acid three (2- propyl group heptan) 50 parts of ester.
Embodiment 3
A kind of Composite Coatings aluminium film, including:Film base layer and aluminium coated, described film base layer are made up of following components:Tetradecylic acid
Isopropyl ester, β-(3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, dihexyl sebacate, poly-carbonic acid 1,2-propylene diester, poly-
Butanedioic acid fourth diester and citric acid three (2- propyl group heptan) ester, the weight content of its each component is:41 parts of isopropyl myristate, β-
24 parts of (3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, 16 parts of dihexyl sebacate, poly-carbonic acid 1,2-propylene diester 23
Part, 16 parts of poly- butanedioic acid fourth diester and citric acid three (2- propyl group heptan) 44 parts of ester.
The beneficial effect of Composite Coatings aluminium film of the present invention is:The back side of inventive film base layer is difficult scratch, and stretch-proof
Function admirable.
Embodiments of the invention are the foregoing is only, the scope of the claims of the present invention is not thereby limited, every using this
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (4)
1. a kind of Composite Coatings aluminium film, it is characterised in that include:Film base layer and aluminium coated, described film base layer is by with the following group
Divide and make:Isopropyl myristate, β-(3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, dihexyl sebacate, poly- carbonic acid
1,2- propylene diester, poly- butanedioic acid fourth diester and citric acid three (2- propyl group heptan) ester, the weight content of its each component is:Tetradecylic acid is different
34 ~ 48 parts of propyl ester, β -16 ~ 33 parts of (3,4- dihydroxy phenyl)-α-hydracrylate isopropyl ester, 10 ~ 22 parts of dihexyl sebacate,
15 ~ 29 parts of poly-carbonic acid 1,2-propylene diester, 9 ~ 21 parts of poly- butanedioic acid fourth diester and citric acid three (2- propyl group heptan) 38 ~ 50 parts of ester.
2. Composite Coatings aluminium film according to claim 1, it is characterised in that described β-(3,4- dihydroxy phenyl)-α-hydroxyl
The weight content of base isopropyl propionate is 18 ~ 30 parts.
3. Composite Coatings aluminium film according to claim 1, it is characterised in that the weight of described poly- carbonic acid 1,2- propylene diester contains
Measure as 17 ~ 29 parts.
4. Composite Coatings aluminium film according to claim 1, it is characterised in that the weight content of described poly- butanedioic acid fourth diester
For 11 ~ 21 parts.