CN106473516A - 一种活性床上用品及其制备方法 - Google Patents
一种活性床上用品及其制备方法 Download PDFInfo
- Publication number
- CN106473516A CN106473516A CN201610920776.4A CN201610920776A CN106473516A CN 106473516 A CN106473516 A CN 106473516A CN 201610920776 A CN201610920776 A CN 201610920776A CN 106473516 A CN106473516 A CN 106473516A
- Authority
- CN
- China
- Prior art keywords
- mixed
- powder
- parts
- bedding
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种活性床上用品及其制备方法，属于生活用品领域。包括枕头、被子和床垫，其特征在于：所述的枕头、被子和床垫上设有载有混合粉末的载体，其中混合粉末在多种矿物原料的搭配下添加一定量的葡萄糖酸钙、砭石、谷氨酸锌和龙骨组成的辅料。能够更好的激发各混合粉末的活性，使其能量场形成相协调统一的综合能量场。床上用品的制备方法的特征在于：床上用品的主体上以混编或者直接添加到纤维配方中的混合粉末的研磨过程中保持520℃~580℃这一特定温度，在这一温度下研磨能够使得各物料的能量场在特定的激发状态下被研磨混合，从而在最终的床上用品中表现出了更强的场效应。
Description
技术领域
一种活性床上用品及其制备方法，属于生活用品领域。
背景技术
现在已知诸多矿石中能够产生对生物的生理机能具有一定的作用和影响的能量场，这种能量场包括矿物自身发出的磁场、红外线等，其具体的作用机理尚不明确。但是对人体的积极影响又确确实实的客观存在着。这种物质能对生物的生理机能产生作用的效应本发明中统称为能量场效应或者简称为场效应。现在有较多的产品利用这种能量场效应制备医疗保健用品。
纤维材料作为传统的纺织材料被广泛的应用，而在纤维材料的工艺要求在熔融的聚合物中不能有大于20μm的颗粒，导致无法使用整块甚至保持功能的颗粒具有场效应的原料。矿物材料在粉碎到一定程度后导致场效应较弱甚至消失，这是因为粉末状态的各种具有场效应的原料粉粒的磁场或红外线各行其是，没有向整块原料那样形成统一的能量场，导致相互干扰，降低理疗效果，导致整体的疗效甚微。
发明内容
本发明要解决的技术问题是：克服现有技术的不足，提供一种效果相互促进、场效应较强的活性床上用品及其制备方法。
本发明解决其技术问题所采用的技术方案是：该活性床上用品，包括枕头、被子和床垫，其特征在于：所述的枕头、被子和床垫上设有载有混合粉末的载体，所述混合粉末的重量份组成为：金刚药石4~4.5份、碧玺4~4.5份、和田玉石0.2~0.23份、珊瑚石2~2.4份、黑曜石3~3.4份、黄水晶0.03~0.07份、麦饭石3~7份、葡萄糖酸钙3.8~4.1份、砭石0.3~0.6份、谷氨酸锌0.01~0.015份、龙骨0.2~0.3份。
本发明的床上用品上使用了一种能量活性混合粉末，这种混合粉末尤其适合于在纤维材料中添加使用，能够适应陶瓷釉料纤维材料的制备工艺。本发明添加的混合粉末中需要添加本发明的关键辅料组合，本发明的发明人发现添加所述的葡萄糖酸钙、砭石、谷氨酸锌、龙骨组成的辅料，能够更好的保留各混合粉末的活性，使混合粉末的各物料的能量场形成相协调统一的综合能量场，各添加组份的磁场或红外线处于相互激发状态，场效应增强，从而抵消部分材料因晶型结构破坏而造成的场效应损失。混合粉末中所述辅料以外的其它物料能够释放不同的能量场，在制成的床上用品上保持较高的场效应，保持各添加组份的磁场或红外线场处于相互激发状态。
所述龙骨，别名：陆虎遗生、那伽骨、生龙骨、煅龙骨、五花龙骨、青化龙骨、花龙骨、白龙骨。为古代哺乳动物如象类、犀牛类、三趾马等的骨胳的化石。
优选的，所述的葡萄糖酸钙和砭石的质量比为3.9~4.0：0.5。当上述辅料采用上述质量比时能够使混合粉末在陶瓷材料中表现出最高的场效应。
优选的，所述的黄水晶与麦饭石的质量比为0.01：1。发明人发现当黄水晶与麦饭石的质量比在此比例时能表现出更高的场效应。
优选的，所述载有混合粉末的载体为混编、粘贴在枕头、被子和床垫上或填充在枕头、被子和床垫内的陶瓷颗粒，陶瓷颗粒的釉料中包含有2%~3%的所述混合粉末。
优选的，所述的载有混合粉末的载体为枕头、被子和床垫的底布和/或面罩，底布和/或面罩所用的纤维材料中共混有质量分数占0.75%~1.25%的所述混合粉末。
混合粉末的载体可以有多种形式，目的在于将上述组成的混合粉末与床上用品的主体牢固结合。上述两种形式仅是本发明的优选形式，以此为目的的其他技术手段均可使用。
优选的，所述的纤维材料的纤维为涤纶。
优选的，所述的纤维材料中共混有质量分数占0.85%~1.0%的混合粉末。
一种上述的活性床上用品的制备方法，其特征在于，制备步骤为：
1）按混合粉末的重量份组成称取物料并进行充分混合；先用研磨机在520℃~580℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）2000目~6000目的混合粉末与釉料按重量份组成称取后共同在研磨机内研磨得活性釉料；在成型的颗粒底坯上施加活性釉料后烧制得陶瓷颗粒，陶瓷颗粒混编在枕头、被子和床垫上；
或者，
2000目~6000目的混合粉末中加入混合粉末总质量的12%~16%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体；熔体经纺丝工艺得到活性丝线；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
本发明床上用品的制备方法中，无论是混编还是与纤维中直接加入混合粉末，关键点均在于步骤1）中在混合粉末在研磨过程中保持520℃~580℃这一特定温度，发明人发现在这一温度下研磨能够使得各物料的能量场在特定的激发状态下被研磨混合，从而在最终的混合粉末中表现出了更强的场效应。在与其它釉料成分混合时只需共同研磨，即能保证在最后制成的陶瓷颗粒中保持各添加组份的磁场或红外线场处于相互激发状态。
步骤2）中包含混合粉末的载体的两种制备方式，目的在于将上述组成的混合粉末与床上用品的主体牢固结合。上述两种方式仅是本发明的优选形式，以此为目的的其他技术手段均可使用。如：对于天然纤维制成的布料可以采用高温蒸压的方式将本发明所用的混合粉末压入布料内，合适的布料同样可以制成具有较佳的场效应的床上用品。
优选的，所述的研磨机内的温度540℃~555℃。相同配比下能够得到场效应最强的最终陶瓷制品。
优选的，所述的混合粉末中加入混合粉末总质量的14%~14.5%的乙醇后再转入纳米研磨机内研磨。能够更好地激发混合粉末的活性，并保证纳米级混合粉末的颗粒均匀性。
优选的，步骤3）所述的纺丝工艺中包括集束上油工序，集束上油工序中所用的油料料中添加有质量分数占0.35%~0.55%的步骤2）制得的纳米级混合粉末。能够增加床上用品携载混合粉末的量，提高床上用品场效应。
本发明中采用的金刚药石中含有Zn,Fe,Mn,Cu,Co,A1,Se,Cr,Ag,Sr,Ga,Ge,Li,Ti,Mo,V等多种微量元素，金刚药石中的 Fe, Zn, Mn, Cu, Co 等微量元素促进有机体的成长和发育，并促进血液循环，Cu, Zn, Mo, I 等元素加强抵抗力和免疫能力的功能 金刚药石因结构上和化学上的特殊构造有着吸附作用和杀菌作用。通过实验得知金刚药石对元素的吸附力为Pb（铅）：63~95%,Cd（镉）：35~68%,As（砷）：37.2%,Hg（汞）：80%，F（氟）：64~69%。在大肠菌培养容器中放入金刚药石溶液，有97.55%被吸附死亡。吸附异味的能力比活性炭高好几倍，此外还有抗癌、防止辐射、调节物质代谢和血液循环、延长寿命、补充精力等作用，一般用于动脉硬化、高血压病、糖尿病、肾炎、静脉堵塞引起的腿部溃疡、火伤、脱毛、湿疹、脚癣、神经性皮肤炎、痱子、增高、抗癌、防止辐射等。
本发明中采用的珊瑚石可预防经痛等妇女生理病，保护骨骼成长的效果，对血液方面的疾病有探测功能，如果越戴颜色越淡的话，很可能有贫血，血液循环不良等问题，心脏病及神经系统疾病离患者也很适合佩带，基本上珊瑚石对皮肤、指甲、头发等生长都有帮助。
本发明中采用的黑曜石是所有晶石之中，吸纳性最强的一种晶石。可以很快便将附近的杂气或负性能量，吸进它内在的无形空间里。可将人体身体上过盛的能量引出，舒缓不适。
本发明中采用的黄水晶对于胰脏和内分泌神经系统也有疗效，对糖尿病者更不可或缺，也可治疗肿胀和胃抽筋，主肠胃功能，消化不良或饮食失衡者适宜使用。还有消解紧张情绪，帮助肠胃等消化系统的功能。
本发明中采用的麦饭石由25000多种成分组成，能释放多种矿物质。麦饭石还可以利用自身成分通过吸收、分解的方法电离有毒物质。释放矿物质并平衡矿物质数量，麦饭石能够在水中散发出人体必不可少的各种矿物质。通过吸收多余的矿物质或释放矿物质补充其不足，麦饭石可以平衡矿物质的数量。麦饭石释放的各种微量元素如：钾、磷、铁、磺、锰、镁等，这些物质对酶和荷尔蒙的合成起着重要作用。麦饭石还能治疗"皮肤病、肿胀、皮疥、皮外伤等"。而且麦饭石对清除各种化学毒素特别有效。还有本发明中最重视的，麦饭石能释放对人体有益的红外线。
本发明中采用的砭石可以发出许多对人体有益的远红外射线和超声波脉冲，促进血液微循环、调理新陈代谢，其功效相当于远红外治疗仪+超声波治疗仪的双重作用。砭石能靠其自身蕴涵的能量来激发人体的潜能，具有安神、调理气血、疏通经络、净化肝肾等脏器，排除多余的毒素，全面增强人的免疫能力的作用。
与现有技术相比，本发明所具有的有益效果是：本发明的上述活性床上用品，床上用品所携载的能量活性混合粉末能够适应床上用品的制备工艺环境和使用环境，保持较高的场效应，保持各添加组份的磁场或红外线场处于相互激发状态。同时本发明的上述技术方案所添加的能量活性混合粉末中需要使用本发明的关键辅料组合，本发明的发明人发现添加一定量的葡萄糖酸钙、砭石、谷氨酸锌、龙骨组成的辅料，能够更好的激发各混合粉末的活性，使其能量场形成相协调统一的综合能量场，各添加组份的磁场或红外线场处于相互激发状态，场效应更强。混合粉末中所述辅料以外的其它物料能够释放不同的能量场，本发明使用了上述适应床上用品制备工艺环境的混合粉末的手段。再经过本发明的特定研磨工艺制备后能够形成更佳的活性，本发明制备方法中添加的混合粉末在研磨过程中保持520℃~580℃这一特定温度，发明人发现在这一温度下研磨能够使得各物料的能量场在特定的激发状态下被研磨混合，从而在最终的床上用品中表现出了更强的场效应。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1
1）釉料原料按重量份组成：高岭土 400份，粘土 125份，滑石 65 份，长石 65份，白云石50份、氧化锌20份、色料10份称取物料后混合备用；
2）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.012份、龙骨0.25份称取物料并进行充分混合；然后用研磨机在550℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）26.9份2000目~6000目的混合粉末与745份的步骤1）制得的釉料原料按重量份称取后共同在研磨机内研磨即得釉料；
4）在成型颗粒底坯的表面上施加2mm厚的步骤3）制得的釉料，然后在1050℃~1130℃下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
实施例2
1）釉料原料的重量份组成包括高岭土 370份，粘土 170 份，滑石 60份，长石 80份，氧化锌30份、色料10份称取物料后混合备用；
2）混合粉末的重量份组成为：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.3份、黑曜石3.1份、黄水晶0.04份、麦饭石4份、葡萄糖酸钙4.0份、砭石0.5份、谷氨酸锌0.014份、龙骨0.28份称取物料并进行充分混合；然后用研磨机在545℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）27.0份2000目~6000目的混合粉末与760份的步骤1）制得的釉料原料按重量份称取后共同在研磨机内研磨即得釉料；
4）在成型颗粒底坯的表面上施加步骤3）制得的釉料，经1050℃~1130℃条件下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
实施例3
1）釉料原料的重量份组成包括高岭土 450 份，粘土 100份，滑石 80 份，长石 50份，白云石60份、氧化锌10份、色料10份称取物料后混合备用；
2）混合粉末的重量份组成为：金刚药石4.1份、碧玺4.1份、和田玉石0.22份、珊瑚石2.2份、黑曜石3.3份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.014份、龙骨0.23份称取物料并进行充分混合；然后用研磨机在540℃的温度下进行研磨得到2000目~6000目的混合粉末；3.9~4.0：0.5：0.12~0.13
3）26.3份2000目~6000目的混合粉末与760份的步骤1）制得的釉料原料按重量份称取后共同在研磨机内研磨即得面釉釉料；
4）在成型颗粒底坯的表面上施加1mm步骤3）制得的釉料，然后在1050℃~1130℃下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
实施例4
1）按将450份釉料熔块投入研磨机内研磨至2000目~6000目后，与200份高岭土、100份粘土、40份滑石、40份长石、25份白云石、5份氧化锌、10份色料组成生料釉混合得釉料原料；
2）混合粉末的重量份组成为：金刚药石4.1份、碧玺4.1份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.3份、黄水晶0.06份、麦饭石6份、葡萄糖酸钙4.0份、砭石0.5份、谷氨酸锌0.011份、龙骨0.22份称取物料并进行充分混合；先用研磨机在555℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）26.8份2000目~6000目的混合粉末与870份的步骤1）制得的釉料原料按重量份称取后共同在研磨机内研磨即得釉料；
4）在成型的颗粒底坯的表面淋2.5mm厚的步骤3）制得的釉料，在1050℃~1130℃下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
实施例5
1）将890份釉料熔块投入研磨机内研磨至2000目~6000目得熔块釉粉末作为釉料原料；
2）混合粉末的重量份组成为：金刚药石4份、碧玺4份、和田玉石0.23份、珊瑚石2份、黑曜石3.4份、黄水晶0.03份、麦饭石7份、葡萄糖酸钙3.8份、砭石0.6份、谷氨酸锌0.01份、龙骨0.3份称取物料并进行充分混合；先用研磨机在520℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）26.75份2000目~6000目的混合粉末与890份步骤1）制备的釉料原料按重量份称取后共同在研磨机内研磨即得面釉釉料；
4）在成型的颗粒底坯的表面上施加步骤3）制得的釉料，然后在1050℃~1130℃下进行烧制得陶瓷颗粒，在枕头的裁剪过程中将陶瓷颗粒缝制在枕头的主体内即得。
实施例6
1）将1126.5份釉料熔块投入研磨机内研磨至2000目~6000目得熔块釉粉末作为釉料原料；
2）混合粉末的重量份组成为：金刚药石4.5份、碧玺4.5份、和田玉石0.2份、珊瑚石2.4份、黑曜石3份、黄水晶0.07份、麦饭石3份、葡萄糖酸钙4.1份、砭石0.3份、谷氨酸锌0.015份、龙骨0.2份称取物料并进行充分混合；先用研磨机在580℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）27.03份2000目~6000目的混合粉末与1126.5份传统底釉原料的按重量份称取后共同在研磨机内研磨即得底釉釉料；
4）在成型的颗粒底坯的内外表面上施加步骤3）制得的釉料，经1050℃~1130℃条件下进行烧制得陶瓷颗粒，将陶瓷颗粒粘贴于枕头内即得。
对比例1
1）釉料原料按重量份组成：高岭土 400份，粘土 125份，滑石 65 份，长石 65份，白云石50份、氧化锌20份、色料10份称取物料后混合备用；
2）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份称取物料并进行充分混合；然后用研磨机在550℃的温度下进行研磨得到2000目~6000目的混合粉末；
3）19.17份2000目~6000目的混合粉末与745份的步骤1）制得的釉料原料按重量份称取后共同在研磨机内研磨即得面釉釉料；
4）在成型的颗粒底坯的内外表面上施加步骤3）制得的釉料，经1050℃~1130℃条件下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
对比例2
1）釉料原料按重量份组成：高岭土 400份，粘土 125份，滑石 65 份，长石 65份，白云石50份、氧化锌20份、色料10份称取物料后混合备用；
2）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.012份、龙骨0.25份称取物料并进行充分混合；然后用研磨机在常温下进行研磨得到2000目~6000目的混合粉末；
3）26.9份2000目~6000目的混合粉末与745份步骤1）制备的釉料原料按重量份称取后共同在研磨机内研磨即得；
4）在成型的颗粒底坯的内外表面上施加步骤3）制得的釉料，经1050℃~1130℃条件下进行烧制得陶瓷颗粒，陶瓷颗粒打孔后在布料的织造过程中混编在布料内，布料裁剪为枕头、被子和床垫即得。
给100名老年人、100名亚健康、100名身体透支的中年人使用实施例1~6和对比例1、2制得的床上用品，在使用一周后进行实用测试，各实施例的使用者的身体状况明显好于对比例的使用者的身体状况。例如：（1）、负重能力测试中，实施例1的使用者的背负能力较对比例1的使用者平均高8.6%，较对比例2的使用者平均高4.3%；（2）平衡力（单腿站立伸直单臂）测试中，实施例1的使用者的平衡时间较对比例1的使用者平均高14.7%，较对比例2的使用者平均高8.2%；（3）柔韧性测试中（ 脚站立固定，直臂回转身体，用前转角Amax，用后转角A”max，则A” max〉Amax且（A” max—Amax）所对应弧长约10~30cm（身体越重效果越明显，意味着情况向好），实施例1的使用者的柔韧性较对比例1的使用者平均高12.8%，较对比例2的使用者平均高7.6%。实施例1与对比例1、2相较可以看出本发明此种形式下的床上用品中添加的辅料对各物料的活性具有激发作用，能够使各物料的能量场相统一，从而保持较高的综合场效应，抵消了部分材料因晶型结构破坏而造成的场效应损失，使用后激活人体细胞的活性，促进血液循环，对人体的健康具有更强的积极作用。
实施例7
1）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.012份、龙骨0.25份称取物料并进行充分混合；然后用研磨机在550℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）26.9份2000目~6000目的混合粉末中加入混合粉末总质量的14%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的0.9%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.45%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
实施例8
1）混合粉末的重量份组成为：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.3份、黑曜石3.1份、黄水晶0.04份、麦饭石4份、葡萄糖酸钙4.0份、砭石0.5份、谷氨酸锌0.014份、龙骨0.28份称取物料并进行充分混合；然后用研磨机在545℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）27.0份2000目~6000目的混合粉末中加入混合粉末总质量的14.5%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的1%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.40%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
实施例9
1）混合粉末的重量份组成为：金刚药石4.1份、碧玺4.1份、和田玉石0.22份、珊瑚石2.2份、黑曜石3.3份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.014份、龙骨0.23份称取物料并进行充分混合；然后用研磨机在540℃的温度下进行研磨得到2000目~6000目的混合粉末；3.9~4.0：0.5：0.12~0.13
2）26.3份2000目~6000目的混合粉末中加入混合粉末总质量的14%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的1.1%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.35%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
实施例10
1）混合粉末的重量份组成为：金刚药石4.1份、碧玺4.1份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.3份、黄水晶0.06份、麦饭石6份、葡萄糖酸钙4.0份、砭石0.5份、谷氨酸锌0.011份、龙骨0.22份称取物料并进行充分混合；先用研磨机在555℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）26.8份2000目~6000目的混合粉末中加入混合粉末总质量的13%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的0.85%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.55%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
实施例11
1）混合粉末的重量份组成为：金刚药石4份、碧玺4份、和田玉石0.23份、珊瑚石2份、黑曜石3.4份、黄水晶0.03份、麦饭石7份、葡萄糖酸钙3.8份、砭石0.6份、谷氨酸锌0.01份、龙骨0.3份称取物料并进行充分混合；先用研磨机在520℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）26.75份2000目~6000目的混合粉末中加入混合粉末总质量的12%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的0.75%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
实施例12
1）混合粉末的重量份组成为：金刚药石4.5份、碧玺4.5份、和田玉石0.2份、珊瑚石2.4份、黑曜石3份、黄水晶0.07份、麦饭石3份、葡萄糖酸钙4.1份、砭石0.3份、谷氨酸锌0.015份、龙骨0.2份称取物料并进行充分混合；先用研磨机在580℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）27.03份2000目~6000目的混合粉末中加入混合粉末总质量的16%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的1.25%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
对比例3
1）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份称取物料并进行充分混合；然后用研磨机在550℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）19.17份2000目~6000目的混合粉末中加入混合粉末总质量的14%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的0.9%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.45%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
对比例4
1）按混合粉末的重量份组成：金刚药石4.3份、碧玺4.3份、和田玉石0.22份、珊瑚石2.1份、黑曜石3.2份、黄水晶0.05份、麦饭石5份、葡萄糖酸钙3.9份、砭石0.5份、谷氨酸锌0.012份、龙骨0.25份称取物料并进行充分混合；然后用研磨机在常温下进行研磨得到2000目~6000目的混合粉末；
2）26.9份2000目~6000目的混合粉末中加入混合粉末总质量的14%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；
3）纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体，纳米级混合粉末占熔体质量分数的0.9%；熔体经挤出丝束、吹风冷却、集束上油等纺丝工序得到活性丝线，其中集束上油工序中所用的油料中添加有质量分数占0.45%的步骤2）制得的纳米级混合粉末；活性丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
给100名老年人、100名亚健康、100名身体透支的中年人使用实施例7~12和对比例3、4制得的床上用品，在使用一周后进行实用测试，各实施例的使用者的身体状况明显好于对比例的使用者的身体状况。例如：（1）、负重能力测试中，实施例7的使用者的背负能力较对比例3的使用者平均高8.3%，较对比例4的使用者平均高4.0%；（2）平衡力（单腿站立伸直单臂）测试中，实施例7的使用者的平衡时间较对比例3的使用者平均高15.2%，较对比例4的使用者平均高7.2%；（3）柔韧性测试中（ 脚站立固定，直臂回转身体，用前转角Amax，用后转角A”max，则A” max〉Amax且（A” max—Amax）所对应弧长约10~30cm（身体越重效果越明显，意味着情况向好），实施例7的使用者的柔韧性较对比例3的使用者平均高11.4%，较对比例4的使用者平均高8.3%。实施例7与对比例3、4相较可以看出此种形式下本发明的床上用品中添加的辅料对各物料的活性具有激发作用，能够使各物料的能量场相统一，从而保持较高的综合场效应，抵消了部分材料因晶型结构破坏而造成的场效应损失，使用后激活人体细胞的活性，促进血液循环，对人体的健康具有更强的积极作用。
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。
Claims (10)
1.一种活性激发的床上用品，包括枕头、被子和床垫，其特征在于：所述的枕头、被子和床垫上设有载有混合粉末的载体，所述混合粉末的重量份组成为：金刚药石4~4.5份、碧玺4~4.5份、和田玉石0.2~0.23份、珊瑚石2~2.4份、黑曜石3~3.4份、黄水晶0.03~0.07份、麦饭石3~7份、葡萄糖酸钙3.8~4.1份、砭石0.3~0.6份、谷氨酸锌0.01~0.015份、龙骨0.2~0.3份。
2.根据权利要求1所述的一种活性激发的床上用品，其特征在于：所述的葡萄糖酸钙和砭石的质量比为3.9~4.0：0.5。
3.根据权利要求1所述的一种活性激发的床上用品，其特征在于：所述的黄水晶与麦饭石的质量比为0.01：1。
4.根据权利要求1所述的一种活性激发的床上用品，其特征在于：所述载有混合粉末的载体为混编、粘贴在枕头、被子和床垫上或填充在枕头、被子和床垫内的陶瓷颗粒，陶瓷颗粒的釉料中包含有2%~3%的所述混合粉末。
5.根据权利要求1所述的一种活性激发的床上用品，其特征在于：所述的载有混合粉末的载体为枕头、被子和床垫的底布和/或面罩，底布和/或面罩所用的纤维材料中共混有质量分数占0.75%~1.25%的所述混合粉末。
6.一种权利要求1~4任一项所述的活性激发的床上用品的制备方法，其特征在于，制备步骤为：
1）按混合粉末的重量份组成称取物料并进行充分混合；先用研磨机在520℃~580℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）2000目~6000目的混合粉末与釉料按重量份组成称取后，共同在研磨机内研磨得到活性釉料；
3）在成型的颗粒底坯上施加活性釉料后烧制成陶瓷颗粒，陶瓷颗粒混编在枕头、被子和床垫上。
7.根据权利要求6所述的一种活性激发的床上用品的制备方法，其特征在于：步骤1）中所述的研磨机内的温度为540℃~555℃。
8.根据权利要求6所述的一种活性激发的床上用品的制备方法，其特征在于：步骤2）中所述的混合粉末中加入混合粉末总质量的14%~14.5%的乙醇后再转入纳米研磨机内研磨。
9.一种权利要求1~3或5任一项所述的活性激发的床上用品的制备方法，其特征在于，制备步骤为：
1）按混合粉末的重量份组成称取物料并进行充分混合；先用研磨机在520℃~580℃的温度下进行研磨得到2000目~6000目的混合粉末；
2）2000目~6000目的混合粉末中加入混合粉末总质量的12%~16%的乙醇后再转入纳米研磨机内利用0.8mm~2.5mm的研磨介质进行研磨，干燥破碎后得到纳米级混合粉末；纳米级混合粉末与纤维树脂按配比称取后共同熔融混炼得到熔体；熔体经纺丝工艺得到活性激发的丝线；活性激发的丝线织成布料后作为底布和/或面罩制得枕头、被子和床垫。
10.根据权利要求9所述的一种活性激发的床上用品的制备方法，其特征在于：步骤3）所述的纺丝工艺中包括集束上油工序，集束上油工序中所用的油料中添加有质量分数占0.35%~0.55%的步骤2）制得的纳米级混合粉末。