CN106436929A - Method for preventing seepage at seam crossings of prefabricated industrial external wallboards - Google Patents
Method for preventing seepage at seam crossings of prefabricated industrial external wallboards Download PDFInfo
- Publication number
- CN106436929A CN106436929A CN201610803173.6A CN201610803173A CN106436929A CN 106436929 A CN106436929 A CN 106436929A CN 201610803173 A CN201610803173 A CN 201610803173A CN 106436929 A CN106436929 A CN 106436929A
- Authority
- CN
- China
- Prior art keywords
- parts
- seam
- water
- antiseep
- groove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of building, and particularly relates to a method for preventing seepage at seam crossings of prefabricated industrial external wallboards. According to the method for preventing seepage at seam crossings of prefabricated industrial external wallboards, edge connection slots are formed in the edges of external wallboards; two edge connection slots are formed in seam crossings of two adjacent external wallboards to form a complete seam connection groove; and the seam connection groove is filled with joint mixture. According to the method for preventing seepage at seam crossings of prefabricated industrial external wallboards, the seam crossings approach the rainwater as little as possible, so that seepage channels are not formed; the seepage pressure of the water is cut off or lightened, and then the waterproof efficiency of the walls is ensured.
Description
Technical field
The invention belongs to building field, especially relate to the antiseep side of prefabricated assembled industrialization Side fascia seam crossing
Method.
Background technology
The Side fascia of building remove radiated by the sun, the changing of temperature and humidity, corrosive medium etc. affects in air
Outward, due also to the differential settlement of the horizontal curvature of building, ground, and joint filler performance change itself bring unfavorable because
Element, makes seam crossing become the weak link of wallboard waterproof it is therefore necessary to take measures it is ensured that the waterproof performance of body of wall.
Content of the invention
For above-mentioned technical problem, the present invention provides a kind of antiseep side of prefabricated assembled industrialization Side fascia seam crossing
Method is it is ensured that the waterproof performance of body of wall.
Specifically technical scheme is:
The Antiseep method of prefabricated assembled industrialization Side fascia seam crossing, arranges at the edge of Side fascia and connects side groove, described
The seam crossing of adjacent two blocks of Side fascias form two edge fit grooves and form complete seam grooves, filling in described seam groove
There is gap filler;
Described gap filler is by following raw material by weight:30~42 parts of portland cement, phthalic acid two are different
54~65 parts of the quartz sand of 1~2 part of last of the ten Heavenly stems ester, 1~2 part of triterpene saponin and 20 ~ 40 mesh, 1.0 ~ 2.0 parts of methyl silicon sodium alcoholate, three ethanol
0.1 ~ 0.3 part of amine, 0.3 ~ 1.5 part of high strength high modulus polyvinyl alcohol fiber, 3.0 ~ 6.5 parts of 108 glue, 3 ~ 7 parts of epoxy resin, water 10 ~
15 parts, after above raw material mix homogeneously, it is filled in seam groove.
After described seam groove filling gap filler, surface is also coated with antiseep coating, described antiseep coating, former below
Material is by weight:
13 ~ 17 parts of hydroxymethylacrylate methyl ester, 12 ~ 16 parts of glycidyl amine epoxy resin, 1 ~ 2 part of alkylnaphthalene sulfonate, fat
1 ~ 2.5 part of fat polyoxyethylenated alcohol, 0.1 ~ 0.2 part of 2,2'-Azobis(2,4-dimethylvaleronitrile), 0.1 ~ 0.3 part of Ammonium persulfate., 20 ~ 22 parts of water, heating
Carry out reaction and obtain A material;
30 ~ 42 parts of A material, 12 ~ 15 parts of vinyl ester resin, 30 ~ 35 parts of glycidyl methacrylate, fluorine silicon resin 2 ~ 7
Part, 1 ~ 4 part of inorganic zinc-rich resin, 1 ~ 2 part of dodecylbenzene sodium sulfonate, 0.1 ~ 0.5 part of azodiisobutyronitrile, 50 ~ 55 parts of water, plus
Heat carries out reaction and obtains B substance;
70 ~ 72 parts of B substance, 0.3 ~ 1 part of defoamer, 0.1 ~ 0.2 part of preservative, 0.1 ~ 0.5 part of antifungus agent, antifreezing agent 0.5 ~ 1
Part, 0.5 ~ 1 part of film former, 25 ~ 27 parts of mixing of water.
The Antiseep method of the prefabricated assembled industrialization Side fascia seam crossing that the present invention provides, makes seam crossing connect less as far as possible
Nearly rainwater, does not form seepage channel;Break off or mitigate the osmotic pressure of water it is ensured that the waterproof performance of body of wall.
Specific embodiment
It is described in conjunction with the embodiments the specific embodiment of the present invention.
Embodiment 1
The Antiseep method of prefabricated assembled industrialization Side fascia seam crossing, arranges at the edge of Side fascia and connects side groove, described
The seam crossing of adjacent two blocks of Side fascias form two edge fit grooves and form complete seam grooves, filling in described seam groove
There is gap filler;
Described gap filler is by following raw material by weight:35 parts of portland cement, diisooctyl phthalate 1
55 parts of the quartz sand of part, 2 parts of triterpene saponin and 20 ~ 40 mesh, 1.3 parts of methyl silicon sodium alcoholate, 0.1 part of triethanolamine, high-strength and high-modulus gather
1.5 parts of alcohol fibers, 5 parts of 108 glue, 5 parts of epoxy resin, 10 parts of water, after above raw material mix homogeneously, are filled in seam groove
Interior.
Embodiment 2
The Antiseep method of prefabricated assembled industrialization Side fascia seam crossing, arranges at the edge of Side fascia and connects side groove, described
The seam crossing of adjacent two blocks of Side fascias form two edge fit grooves and form complete seam grooves, filling in described seam groove
There is gap filler;
Described gap filler is by following raw material by weight:30 parts of portland cement, diisooctyl phthalate 2
54 parts of the quartz sand of part, 1.2 parts of triterpene saponin and 20 ~ 40 mesh, 1.0 parts of methyl silicon sodium alcoholate, 0.2 part of triethanolamine, high-strength and high-modulus
0.3 part of vinal, 3.0 parts of 108 glue, 7 parts of epoxy resin, 15 parts of water, after above raw material mix homogeneously, are filled in seam
In groove.
Embodiment 3
The Antiseep method of prefabricated assembled industrialization Side fascia seam crossing, arranges at the edge of Side fascia and connects side groove, described
The seam crossing of adjacent two blocks of Side fascias form two edge fit grooves and form complete seam grooves, filling in described seam groove
There is gap filler;
Described gap filler is by following raw material by weight:42 parts of portland cement, diisooctyl phthalate
65 parts of the quartz sand of 1.4 parts, 1 part of triterpene saponin and 20 ~ 40 mesh, 2.0 parts of methyl silicon sodium alcoholate, 0.3 part of triethanolamine, high-strength and high-modulus
1 part of vinal, 6.5 parts of 108 glue, 3 parts of epoxy resin, 12 parts of water, after above raw material mix homogeneously, are filled in seam groove
Interior.
Embodiment 4
After described seam groove filling gap filler, surface is also coated with antiseep coating, described antiseep coating, and following raw material is pressed
According to parts by weight composition:
13 parts of hydroxymethylacrylate methyl ester, 14 parts of glycidyl amine epoxy resin, 1 part of alkylnaphthalene sulfonate, fatty alcohol polyoxy
2.5 parts of vinyl Ether, 0.1 part of 2,2'-Azobis(2,4-dimethylvaleronitrile), 0.2 part of Ammonium persulfate., 20 parts of water, heating carries out reaction and obtains A material;
30 parts of A material, 12 parts of vinyl ester resin, 32 parts of glycidyl methacrylate, 2 parts of fluorine silicon resin, inorganic zinc-rich
3 parts of resin, 1 part of dodecylbenzene sodium sulfonate, 0.1 part of azodiisobutyronitrile, 50 parts of water, heating carries out reaction and obtains B substance;
70 parts of B substance, 1 part of defoamer, 0.2 part of preservative, 0.1 part of antifungus agent, 0.5 part of antifreezing agent, 0.7 part of film former, water 25
Part mixing.
Embodiment 5
After described seam groove filling gap filler, surface is also coated with antiseep coating, described antiseep coating, and following raw material is pressed
According to parts by weight composition:
17 parts of hydroxymethylacrylate methyl ester, 12 parts of glycidyl amine epoxy resin, 1 ~ 2 part of alkylnaphthalene sulfonate, poly alkyl alcohol
1 part of oxygen vinyl Ether, 0.2 part of 2,2'-Azobis(2,4-dimethylvaleronitrile), 0.3 part of Ammonium persulfate., 22 parts of water, heating carries out reaction and obtains A material;
42 parts of A material, 15 parts of vinyl ester resin, 35 parts of glycidyl methacrylate, 7 parts of fluorine silicon resin, inorganic zinc-rich
1 part of resin, 1 part of dodecylbenzene sodium sulfonate, 0.5 part of azodiisobutyronitrile, 55 parts of water, heating carries out reaction and obtains B substance;
71 parts of B substance, 0.3 part of defoamer, 0.2 part of preservative, 0.5 part of antifungus agent, 0.7 part of antifreezing agent, 1 part of film former, water 27
Part mixing.
Embodiment 6
After described seam groove filling gap filler, surface is also coated with antiseep coating, described antiseep coating, and following raw material is pressed
According to parts by weight composition:
15 parts of hydroxymethylacrylate methyl ester, 16 parts of glycidyl amine epoxy resin, 1 part of alkylnaphthalene sulfonate, fatty alcohol polyoxy
2.5 parts of vinyl Ether, 0.1 part of 2,2'-Azobis(2,4-dimethylvaleronitrile), 0.1 part of Ammonium persulfate., 20 ~ 22 parts of water, heating carries out reaction and obtains A material;
38 parts of A material, 13 parts of vinyl ester resin, 30 parts of glycidyl methacrylate, 5 parts of fluorine silicon resin, inorganic zinc-rich
4 parts of resin, 2 parts of dodecylbenzene sodium sulfonate, 0.1 part of azodiisobutyronitrile, 52 parts of water, heating carries out reaction and obtains B substance;
72 parts of B substance, 0.6 part of defoamer, 0.1 part of preservative, 0.3 part of antifungus agent, 1 part of antifreezing agent, 0.5 part of film former, water
26 parts of mixing.
Claims (3)
1. prefabricated assembled industrialization Side fascia seam crossing Antiseep method it is characterised in that:In the setting of the edge of Side fascia
Connect side groove, the seam crossing of described adjacent two blocks of Side fascias forms two edge fit grooves and forms a complete seam groove, described
Seam groove in be filled with gap filler.
2. prefabricated assembled industrialization Side fascia seam crossing according to claim 1 Antiseep method it is characterised in that:
Described gap filler is by following raw material by weight:30~42 parts of portland cement, diisooctyl phthalate 1
54~65 parts of the quartz sand of~2 parts, 1~2 part of triterpene saponin and 20 ~ 40 mesh, 1.0 ~ 2.0 parts of methyl silicon sodium alcoholate, triethanolamine 0.1
~ 0.3 part, 0.3 ~ 1.5 part of high strength high modulus polyvinyl alcohol fiber, 3.0 ~ 6.5 parts of 108 glue, 3 ~ 7 parts of epoxy resin, 10 ~ 15 parts of water,
After above raw material mix homogeneously, it is filled in seam groove.
3. the Antiseep method of prefabricated assembled industrialization Side fascia seam crossing according to claim 1 and 2, its feature exists
In:After described seam groove filling gap filler, surface is also coated with antiseep coating, described antiseep coating, and following raw material is pressed
According to parts by weight composition:
13 ~ 17 parts of hydroxymethylacrylate methyl ester, 12 ~ 16 parts of glycidyl amine epoxy resin, 1 ~ 2 part of alkylnaphthalene sulfonate, fat
1 ~ 2.5 part of fat polyoxyethylenated alcohol, 0.1 ~ 0.2 part of 2,2'-Azobis(2,4-dimethylvaleronitrile), 0.1 ~ 0.3 part of Ammonium persulfate., 20 ~ 22 parts of water, heating
Carry out reaction and obtain A material;
30 ~ 42 parts of A material, 12 ~ 15 parts of vinyl ester resin, 30 ~ 35 parts of glycidyl methacrylate, fluorine silicon resin 2 ~ 7
Part, 1 ~ 4 part of inorganic zinc-rich resin, 1 ~ 2 part of dodecylbenzene sodium sulfonate, 0.1 ~ 0.5 part of azodiisobutyronitrile, 50 ~ 55 parts of water, plus
Heat carries out reaction and obtains B substance;
70 ~ 72 parts of B substance, 0.3 ~ 1 part of defoamer, 0.1 ~ 0.2 part of preservative, 0.1 ~ 0.5 part of antifungus agent, antifreezing agent 0.5 ~ 1
Part, 0.5 ~ 1 part of film former, 25 ~ 27 parts of mixing of water.