CN106436443A - Light and high-strength glass fiber filter paper and preparation method thereof - Google Patents
Light and high-strength glass fiber filter paper and preparation method thereof Download PDFInfo
- Publication number
- CN106436443A CN106436443A CN201610834464.1A CN201610834464A CN106436443A CN 106436443 A CN106436443 A CN 106436443A CN 201610834464 A CN201610834464 A CN 201610834464A CN 106436443 A CN106436443 A CN 106436443A
- Authority
- CN
- China
- Prior art keywords
- filter paper
- glass fibre
- component
- adhesive
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Light and high-strength glass fiber filter paper is prepared from double-component hollow glass fibers and an adhesive and is characterized in that the double-component hollow glass fibers have the hollow rate being 0.60-0.95, the average diameter being 0.8-7.2 mu m and the length-diameter ratio being 16-78, the section is one or a mixture of round and oval, the double-component hollow glass fibers are formed by melting two glass raw materials in two kilns to form a mixed liquid and performing blowing with high-temperature flames at 1,450-1,550 and drawing. The invention further discloses a preparation method of the light and high-strength glass fiber filter paper. The preparation method comprises steps as follows: (1) dispersion with a beater; (2) stirring and deslagging treatment; (3) papermaking, vacuum water removal and pressing to form ground paper; (4) adhesive spraying; (5) drying. The light and high-strength glass fiber filter paper has the benefits of (1) lightness and environment-friendliness; (2) high strength.
Description
Technical field
The invention belongs to field of air filtration, it is related to a kind of air filter paper, particularly to a kind of light-high-strength glass
Fiber filter paper and preparation method thereof.
Background technology
All-glass paper/felt has fabulous fire-retardant, sound-absorbing, heat-insulating property, be provided simultaneously with light weight, inexpensive the advantages of.Mesh
Before, all-glass paper is widely used in fields such as household decoration, building external wall energy-saving insulation, air cleanings.Glass
Fiber air filter paper is the key components of filtering element for air filter, and the performance such as its thickness, grammes per square metre, intensity, rigidity determines
The performance of air filter.Glass fibre air filter paper is mainly used in the air filtration under special environment, by the air
The oil molecule of diffusion stops or is trapped in outside by air filting material, and protection is polluted the space of environment by oil molecule.Due to
Filter be by glass fibre air filter paper through giving a discount, machine is converted into filter element, is fixed on housing through PUR is fixed-type
On, therefore the thickness of glass fibre air filter paper, intensity must are fulfilled for the requirement of filter applying working condition, so that filter is suitable for
In different wind speed, flow it is adaptable to different ambient temperatures requires.
A kind of high-strength glass fiber air filter paper is disclosed on the Chinese patent of Publication No. CN 103721477 A
And preparation method thereof, this high-strength glass fiber air filter paper is made up of with adhesive glass fibre, and glass fibre is at one
In plane, uniform random distribution, forms micron-sized gap between multiple glass fibre, and adhesive wraps between glass fibre
On intertwined point, form netted joint face.Glass fibre is made up of glass chopped silk and/or glass fibre cotton, adhesive by
Inorganic silica gel or colloidal alumina or combinations thereof, overcome existing all-glass paper low intensity, high temperature filtration effect bad etc.
Shortcoming, this kind of high-strength glass fiber air filter paper can be used as building, the heat insulating element in the field such as machinery, heat energy or heat-insulated fill out
Material is it is also possible to be used for air cleaner.But the filter paper unit weight of this method preparation is larger, and filter efficiency is poor.
A kind of high-strength glass fiber air filter paper is disclosed on the Chinese patent of Publication No. CN 102505554 A,
Add the organic fibers such as terylene, aramid fiber, acrylon, polypropylene, polyvinyl, fibre length preferably 3~15mm in organic fiber, fiber is straight
Footpath preferably 0.3~5dan.Not only increase the intensity under glass fibre air filter paper normality and deflection, be dispersed in simultaneously
Organic fiber in page is melted into binding agent in high temperature, compensate for because of forfeiture after acrylic adhesive pyrolytic
Intensity.The high resiliency of organic fiber is it is ensured that the breathability of air filter paper and filter efficiency are it is ensured that the efficient sky made simultaneously
Air filter continuously can work at a temperature of more than or equal to 250 DEG C.But it is larger still to there is filter paper unit weight in this design
Problem, causes equipment energy consumption higher during use.
Content of the invention
The purpose of the present invention is intended to overcome the deficiencies in the prior art, provide a kind of light-high-strength glass fiber filter paper and its
Preparation method.By using double-component hollow glass fibre as the material making filter material, bicomponent fibers were both played natural
The characteristic of bending, mutually button solution, so that being difficult between fiber to slide, improves the stability of filter paper, viscous in conjunction with adhesive
Knot acts on, and the intensity maximum of filter paper improves, additionally, bicomponent fibers are made hollow form, has both alleviated the weight of filter material itself
Amount, also makes the specific surface area of filter material greatly increase, filter efficiency is greatly improved.
Employed technical scheme comprise that for realizing the purpose of the present invention:A kind of light-high-strength glass fiber filter paper, by double groups
Part hollow glass fibre with adhesive composition it is characterised in that described double-component hollow glass fibre hollow rate be 0.60~
0.95th, average diameter be 0.8~7.2 μm, draw ratio be 16~78, section is one of circular or oval or two
The mixing of person, described double-component glass fibre forms mixing respectively by the frit of two kinds of components after two furnace
Liquid, then be blown wire drawings through 1450~1550 DEG C of thermal-flames and formed, wherein the first component frit coefficient of expansion is 4.5 ×
10-6~6.0 × 10-6/ DEG C, composition is calculated by mass to be:45~76%SiO2, 6~22%Al2O3, 6~20%MgO, 0~3%
CaO, 0~2%FeO, 0~2%NaO+K2O;The second component frit coefficient of expansion is 8.0 × 10-6~10.0 × 10-6/
DEG C, composition is calculated by mass to be:45~76%SiO2, 6~22%Al2O3, 6~20%MgO, 0~3%CaO, 0~2%FeO, 8
~22%NaO+K2O.
In described double-component glass fibre the first component frit account for the frit of two kinds of components 30%~
60%wt, wherein preferably 45%~55%.
Described adhesive position is in phenolic resin adhesive or tripolycyanamide and urea-modified phenolic resin adhesive
One kind, wherein preferably tripolycyanamide and urea-modified phenolic resin adhesive.
The invention also discloses a kind of preparation method of light-high-strength glass fiber filter paper is it is characterised in that include following
Step:
(1) glass fibre is added in beater and is disperseed, with water as dispersant with solvent, glass fibre raw material
It is dissociated into cotton pulp;
(2) cotton pulp, aqueous solution are delivered in pond with slurry and stir and carry out slagging-off process, the solid content in slurry controls
0.25~0.6%wt, PH control 3~7, and air content controls 3~6%;
(3) mixed slurry stirring is delivered on the drainage screen of twin-wire press and is manufactured paper with pulp, THICKNESS CONTROL exists
Between 0.1~2mm, gains of manufacturing paper with pulp are obtained ground paper after carrying out vacuum draw eliminating water and squeezing;
(4) adhesive is diluted to 10~40 times, is equably sprayed on glass fibre ground paper, unnecessary adhesive is by taking out
Suction box aspirates, and separated tank comes back to after separating in circulation glue tank;
(5) the glass fibre ground paper after processing applying glue enters baking oven under the conditions of 260~300 DEG C, dries 1~5min,
Obtain light-high-strength glass fiber filter paper.
The present invention is had an advantageous effect in that:1. lightweight, due to employing the structure of hollow glass fibre, therefore filter paper
Under conditions of ensureing identical filter efficiency, lighter this of quality allows for filter paper and applies to when on removable facility oil consumption more
Few, energy-conservation, environmental protection;2. intensity is high, because fiber adopts double-component form, is mutually wound around between fiber, buckle and solve even closer, makes
Obtain the raising of the intensity maximum of filter paper, increased its service life.
Specific embodiment
With reference to specific embodiment, it is further elucidated with the present invention it should be understood that these embodiments are merely to illustrate the present invention
Rather than restriction the scope of the present invention, after having read the present invention, the various equivalences to the present invention for the those skilled in the art
The modification of form all falls within the application claims and is limited.
Embodiment 1
A kind of light-high-strength glass fiber filter paper, is made up of double-component hollow glass fibre and adhesive, and its feature exists
In described double-component hollow glass fibre hollow rate be 0.60, average diameter be 0.8 μm, draw ratio be 16, section be circle,
Described double-component glass fibre forms mixed liquor respectively by the frit of two kinds of components after two furnace, then warp
1450 DEG C of thermal-flame injection wire drawings are formed, and wherein the first component frit coefficient of expansion is 4.5 × 10-6, composition is with matter
Amount is calculated as:76%SiO2, 11%Al2O3, 10%MgO, 3%CaO, 0%FeO, 0%NaO+K2O;Second component glass is former
The material coefficient of expansion is 8.0 × 10-6, composition is calculated by mass to be:70%SiO2, 8%Al2O3, 7%MgO, 6%CaO, 1%FeO,
8%NaO+K2O.
In described double-component glass fibre, the first component frit accounts for the 45%wt of the frit of two kinds of components.
Described adhesive position is phenolic resin adhesive.
The invention also discloses a kind of preparation method of light-high-strength glass fiber filter paper is it is characterised in that include following
Step:
(1) glass fibre is added in beater and is disperseed, with water as dispersant with solvent, glass fibre raw material
It is dissociated into cotton pulp;
(2) cotton pulp, aqueous solution are delivered in pond with slurry and stir and carry out slagging-off process, the solid content in slurry controls
0.25%wt, PH control 3, and air content controls 3%;
(3) mixed slurry stirring is delivered on the drainage screen of twin-wire press and is manufactured paper with pulp, THICKNESS CONTROL exists
0.1mm, gains of manufacturing paper with pulp are obtained ground paper after carrying out vacuum draw eliminating water and squeezing;
(4) adhesive is diluted to 40 times, is equably sprayed on glass fibre ground paper, unnecessary adhesive is by suction box
Suction, separated tank comes back to after separating in circulation glue tank;
(5) the glass fibre ground paper after processing applying glue enters baking oven under the conditions of 260 DEG C, dries 1min, that is, obtain light
Matter high strength glass fiber filter paper.
Embodiment 2
A kind of light-high-strength glass fiber filter paper, is made up of double-component hollow glass fibre and adhesive, and its feature exists
In described double-component hollow glass fibre hollow rate be 0.95, average diameter be 7.2 μm, draw ratio be 78, section be ellipse
Shape, described double-component glass fibre forms mixed liquor respectively by the frit of two kinds of components after two furnace, then
It is blown wire drawing through 1550 DEG C of thermal-flames to be formed, wherein the first component frit coefficient of expansion is 6.0 × 10-6/ DEG C, composition
Calculated by mass it is:45%SiO2, 20%Al2O3, 15%MgO, 12%CaO, 5%FeO, 3%NaO+K2O;Second component glass
The glass raw material coefficient of expansion is 10.0 × 10-6/ DEG C, composition is calculated by mass to be:45%SiO2, 17%Al2O3, 15%MgO, 1%
CaO, 0%FeO, 22%NaO+K2O.
In described double-component glass fibre, the first component frit accounts for the 60%wt of the frit of two kinds of components.
Described adhesive position is tripolycyanamide and urea-modified phenolic resin adhesive.
The invention also discloses a kind of preparation method of light-high-strength glass fiber filter paper is it is characterised in that include following
Step:
(1) glass fibre is added in beater and is disperseed, with water as dispersant with solvent, glass fibre raw material
It is dissociated into cotton pulp;
(2) cotton pulp, aqueous solution are delivered in pond with slurry and stir and carry out slagging-off process, the solid content in slurry controls
0.6%wt, PH control 7, and air content controls 6%;
(3) mixed slurry stirring is delivered on the drainage screen of twin-wire press and is manufactured paper with pulp, THICKNESS CONTROL exists
2mm, gains of manufacturing paper with pulp are obtained ground paper after carrying out vacuum draw eliminating water and squeezing;
(4) adhesive is diluted to 40 times, is equably sprayed on glass fibre ground paper, unnecessary adhesive is by suction box
Suction, separated tank comes back to after separating in circulation glue tank;
(5) the glass fibre ground paper after processing applying glue enters baking oven under the conditions of 300 DEG C, dries 5min, that is, obtain light
Matter high strength glass fiber filter paper.
Above are only two specific embodiments of the present invention, but the design concept of the present invention is not limited thereto, all profits
With this design, the present invention is carried out with the change of unsubstantiality, the behavior invading the scope of protection of the invention all should be belonged to.In every case it is
Without departing from the content of technical solution of the present invention, any type of letter above example made according to the technical spirit of the present invention
Single modification, equivalent variations and remodeling, still fall within the protection domain of technical solution of the present invention.
Claims (4)
1. a kind of light-high-strength glass fiber filter paper, be made up of double-component hollow glass fibre and adhesive it is characterised in that
Described double-component hollow glass fibre hollow rate be 0.60~0.95, average diameter be 0.8~7.2 μm, draw ratio be 16~
78, section is one of circular or oval or both mixing, and described double-component glass fibre is by two kinds of groups
The frit dividing forms mixed liquor respectively after two furnace, then is blown wire drawing shapes through 1450~1550 DEG C of thermal-flames
Become, wherein the first component frit coefficient of expansion is 4.5 × 10-6~6.0 × 10-6/ DEG C, composition is calculated by mass to be:45
~76% SiO2, 6~22%Al2O3, 6~20% MgO, 0~3% CaO, 0~2% FeO, 0~2% NaO+K2O;Second
Planting the component frit coefficient of expansion is 8.0 × 10-6~10.0 × 10-6/ DEG C, composition is calculated by mass to be:45~76%
SiO2, 6~22% Al2O3, 6~20% MgO, 0~3%CaO, 0~2% FeO, 8~22% NaO+K2O.
2. filter paper according to claim 1 is it is characterised in that the first component glass in described double-component glass fibre
Raw material accounts for 30%~60%wt of the frit of two kinds of components, and wherein preferably 45%~55%.
3. filter paper according to claim 1 is it is characterised in that described adhesive position is phenolic resin adhesive or trimerization
One of cyanamide and urea-modified phenolic resin adhesive, wherein preferred tripolycyanamide and urea-modified phenolic resin glue
Glutinous agent.
4. the invention also discloses a kind of preparation method of light-high-strength glass fiber filter paper is it is characterised in that include following walking
Suddenly:
(1) glass fibre is added in beater and is disperseed, with water as dispersant with solvent, glass fibre raw material dissociation
Become cotton pulp;
(2) cotton pulp, aqueous solution are delivered in pond with slurry and stir and carry out slagging-off process, the solid content in slurry controls 0.25
~0.6%wt, PH control 3~7, and air content controls 3~6%;
(3) mixed slurry stirring is delivered on the drainage screen of twin-wire press and is manufactured paper with pulp, THICKNESS CONTROL 0.1~
Between 2mm, gains of manufacturing paper with pulp are obtained ground paper after carrying out vacuum draw eliminating water and squeezing;
(4) adhesive is diluted to 10~40 times, is equably sprayed on glass fibre ground paper, unnecessary adhesive is by suction box
Suction, separated tank comes back to after separating in circulation glue tank;
(5) the glass fibre ground paper after processing applying glue enters baking oven under the conditions of 260~300 DEG C, dries 1~5min, that is, obtains
Obtain light-high-strength glass fiber filter paper.