CN106433322A - 一种无尘粉笔及其制备方法 - Google Patents
一种无尘粉笔及其制备方法 Download PDFInfo
- Publication number
- CN106433322A CN106433322A CN201611128119.2A CN201611128119A CN106433322A CN 106433322 A CN106433322 A CN 106433322A CN 201611128119 A CN201611128119 A CN 201611128119A CN 106433322 A CN106433322 A CN 106433322A
- Authority
- CN
- China
- Prior art keywords
- powder
- dust
- chalk
- polyvinyl alcohol
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无尘粉笔及其制备方法，所述无尘粉笔包括：石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水，总的，本发明的无尘粉笔书写和擦拭不会出现粉尘，书写流畅的优点。
Description
技术领域
本发明属于粉笔加工技术领域，具体涉及一种无尘粉笔及其制备方法。
背景技术
粉笔是教使用的一种重要的工具，传统的粉笔在黑板上进行书写和擦拭的时候会出现大量的粉尘，污染教室环境，对教师和学生造成不同程度的身体伤害，随着科技的发展，无尘粉笔的出现一定程度上解决了上述的问题，但现有的无尘粉笔在使用过程中的效果不理想，还是会出现粉尘并出现书写不清晰的现象，为解决上述问题，因此需要一种无尘粉笔。
发明内容
本发明的目的是为了弥补现有技术的不足，而提供一种书写和擦拭不会出现粉尘，书写流畅的优点。
本发明的目的是这样实现的：一种无尘粉笔，所述无尘粉笔包括 石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水。
所述无尘粉笔由一下重量份的原料组成：
石膏粉 30-60
钛白 10-50
硬脂酸 5-15
聚乙烯醇 20-40
超细碳酸钙 15-30
石蜡油 10-20
元明粉 5-10
氧化锌 5-15
水 36-49 。
无尘粉笔的制备方法的步骤为：
a.将石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水按照重量份进行称重，
b.用搅拌机将步骤a中称重好的石膏粉、钛白、超细碳酸钙、元明粉、氧化锌与水进行搅拌30-50分钟，制成粉料
c．将步骤a中称重好的硬脂酸、聚乙烯醇、石蜡油使用乳化机乳化45-60分钟，然后加入步骤b中的粉料中，继续搅拌30-50分钟，进行充分的混合，形成混合料
d.将步骤c中的混合料注入模具内，经过冷却，压制，脱模，剪切，烘干后既得到成品。
本发明的有益效果：本发明中含有多种大分子材料，使用乳化机进行充分的乳化，乳化之后的大分子材料在与无机分子材料进行搅拌的过程中将无机分子进行很好地包裹，在书写和擦拭过程中不会产生粉尘，同时本发明的大分子材料很容易降解，不污染环境；总的，本发明的无尘粉笔书写和擦拭不会出现粉尘，书写流畅的优点。
具体实施方式
实施例一
一种无尘粉笔，所述无尘粉笔包括 石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水。
所述无尘粉笔由一下重量份的原料组成：
石膏粉 30
钛白 15
硬脂酸 5
聚乙烯醇 18
超细碳酸钙 18
石蜡油 10
元明粉 5
氧化锌 5
水 37。
无尘粉笔的制备方法的步骤为：
a.将石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水按照重量份进行称重，
b.用搅拌机将步骤a中称重好的石膏粉、钛白、超细碳酸钙、元明粉、氧化锌与水进行搅拌30-50分钟，制成粉料
c．将步骤a中称重好的硬脂酸、聚乙烯醇、石蜡油使用乳化机乳化45-60分钟，然后加入步骤b中的粉料中，继续搅拌30-50分钟，进行充分的混合，形成混合料
d.将步骤c中的混合料注入模具内，经过冷却，压制，脱模，剪切，烘干后既得到成品。
实施例二
一种无尘粉笔，所述无尘粉笔包括 石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水。
所述无尘粉笔由一下重量份的原料组成：
石膏粉 35
钛白 27
硬脂酸 10
聚乙烯醇 27
超细碳酸钙 28
石蜡油 15
元明粉 8
氧化锌 10
水 40。
无尘粉笔的制备方法的步骤为：
a.将石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水按照重量份进行称重，
b.用搅拌机将步骤a中称重好的石膏粉、钛白、超细碳酸钙、元明粉、氧化锌与水进行搅拌30-50分钟，制成粉料
c．将步骤a中称重好的硬脂酸、聚乙烯醇、石蜡油使用乳化机乳化45-60分钟，然后加入步骤b中的粉料中，继续搅拌30-50分钟，进行充分的混合，形成混合料
d.将步骤c中的混合料注入模具内，经过冷却，压制，脱模，剪切，烘干后既得到成品。
实施例三
一种无尘粉笔，所述无尘粉笔包括 石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水。
所述无尘粉笔由一下重量份的原料组成：
石膏粉 55
钛白 36
硬脂酸 15
聚乙烯醇 35
超细碳酸钙 30
石蜡油 20
元明粉 10
氧化锌 15
水 45。
无尘粉笔的制备方法的步骤为：
a.将石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水按照重量份进行称重，
b.用搅拌机将步骤a中称重好的石膏粉、钛白、超细碳酸钙、元明粉、氧化锌与水进行搅拌30-50分钟，制成粉料
c．将步骤a中称重好的硬脂酸、聚乙烯醇、石蜡油使用乳化机乳化45-60分钟，然后加入步骤b中的粉料中，继续搅拌30-50分钟，进行充分的混合，形成混合料
d.将步骤c中的混合料注入模具内，经过冷却，压制，脱模，剪切，烘干后既得到成品；总的，本发明的无尘粉笔书写和擦拭不会出现粉尘，书写流畅的优点。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (3)
1.一种无尘粉笔，其特征在于：所述无尘粉笔包括 石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水。
2.根据权利要求1所述的一种无尘粉笔，其特征在于：所述无尘粉笔由一下重量份的原料组成：
石膏粉 30-60
钛白 10-50
硬脂酸 5-15
聚乙烯醇 20-40
超细碳酸钙 15-30
石蜡油 10-20
元明粉 5-10
氧化锌 5-15
水 36-49 37 。
3.一种无粉笔的制备方法，其特征在于：制备方法的步骤为：
a.将石膏粉、钛白、硬脂酸、聚乙烯醇、超细碳酸钙、石蜡油、元明粉、氧化锌、水按照重量份进行称重，
b.用搅拌机将步骤a中称重好的石膏粉、钛白、超细碳酸钙、元明粉、氧化锌与水进行搅拌30-50分钟，制成粉料
c．将步骤a中称重好的硬脂酸、聚乙烯醇、石蜡油使用乳化机乳化45-60分钟，然后加入步骤b中的粉料中，继续搅拌30-50分钟，进行充分的混合，形成混合料
d.将步骤c中的混合料注入模具内，经过冷却，压制，脱模，剪切，烘干后既得到成品。