CN106433302A - High-luster quick-drying non-skinning ink used for printing patterns on clothes - Google Patents
High-luster quick-drying non-skinning ink used for printing patterns on clothes Download PDFInfo
- Publication number
- CN106433302A CN106433302A CN201610876646.5A CN201610876646A CN106433302A CN 106433302 A CN106433302 A CN 106433302A CN 201610876646 A CN201610876646 A CN 201610876646A CN 106433302 A CN106433302 A CN 106433302A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- quick
- skinning
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-luster quick-drying non-skinning ink used for printing patterns on clothes. The high-luster quick-drying non-skinning ink comprises the following components in parts by weight: 30-40 parts of composite polymer resin, 10-20 parts of gummy oil, 10-20 parts of pigment, 6-12 parts of polysiloxane KH-550, 3-8 parts of a thickening agent, 2-5 parts of a plasticizing agent, 2-6 parts of a dispersing agent, 1-5 parts of an adhesion promoter, 1-2 parts of dibutyltin dilaurate, 1-2 parts of a 0.1%-0.9% surface active agent Walloxen TR50, and 25-45 parts of a mixed solvent. In addition, the high-luster quick-drying non-skinning ink has the advantages that the silicone-modified acrylic resin, vinyl-vinyl acetate copolymer resin and rosin resin are adopted to obtain the composite polymer resin, so that the pollution of phenolic substances to the environment is reduced, and the printing adaptability and the effect are better than those of single-component resin; and the bonding material adopts gummy oil as a film forming substance, so that the luster of the ink is greatly improved, the ink property and the viscoelasticity of the ink are greatly improved, and the balance between the high luster and the setting speed of the ink is realized.
Description
Technical field
The present invention relates to clothes manufacture field, particularly relate to a kind of high light carrying out pattern printing on ready-made clothes fast
Dry not skinning ink.
Background technology
In order to make the class of clothes improving product in appearance so that it is more eye-catching and attractive in appearance, in order to obtain consumer's
Favor and accreditation, reach to expand the purpose of production marketing, and ready-made clothes processing industry is provided with pattern at clothing surface.At present, exist
Clothing surface arranges pattern and comprises the following steps:1st, ready-made clothes processing industry provides AI shelves data and paper mold to manufacturer；2nd, manufacturer
Set up draft；3rd, ready-made clothes processing industry confirms sign-off draft；4th, manufacturer makes the web plate of basic code；5th, ready-made clothes processing industry
Confirm the web plate of sign-off basic code；6th, manufacturer sets up the draft of all-key；7th, ready-made clothes processing industry confirms the draft of sign-off all-key；
8th, manufacturer makes the web plate of all-key；9th, region, setting position；10th, position beaten by web plate；11. brush coatings/scrape gasoline water；12nd, material is joined
Double；13rd, material placement positioning；14th, core set half tone；15th, cleaning material；16th, print；17th, material is dried；18th, arrangement material is tidied up
Material；19th, web plate instrument is cleaned；20th, clothing surface arranges pattern and finishes.The above-mentioned step arranging pattern on ready-made clothes is many,
Complex procedures, processing cost is high, and its effect of the pattern of printing is undesirable.Owing to arranging the clothes price of pattern on ready-made clothes
Higher, ordinary consumer is beyond affordability, so, limit the development of ready-made clothes processing industry.Therefore, the highly desirable one of people
On ready-made clothes, the method for three-dimensional printing pattern is come out.
But, on clothes, print pattern is also more and more higher to the requirement of pad-ink, and traditional resistance to anti-boiling ink uses
Polyurethane, vinyl chloride-vinyl acetate resin and chlorinated polypropylene etc., as binder, use the butanone, dimethylbenzene etc. that toxicity is bigger as solvent,
Serious environment pollution, works the mischief to the health of printing worker simultaneously.In terms of environmental protection, presently the most urgent is environmental protection
The preparation of type high temperature steam endurance ink and use.In order to solve the pollution problem of traditional resistance to anti-boiling ink, water color ink meet the tendency and
Raw.But owing to water color ink is difficult to wetting and spreading on plastic basis material, rate of drying is slow, performance can't be fully achieved and beat
The use standard of printing ink.Alcohol-soluble printing ink uses the alcohols of the low toxicity such as ethanol, isopropanol as solvent, can solve the problem that traditional oils
Ink injury health and problem of solvent residual, can improve again wetting and spreading performance on plastic basis material for the ink simultaneously.In addition, it is existing
Market conventional printing ink is broadly divided into " high light quicksetting ink ", " high light not skinning ink " two classes, is used alone one type
Ink printing is all unable to reach, and it is undesirable with product quality to there is production operation difficulty, it is impossible to reach optimum efficiency.
Content of the invention
Present invention aim to provide a kind of a kind of High-gloss quick-drying skinning-free ink printing for clothing popularity, should
Ink reduces the pollution to environment for the aldehydes matter, makes the gloss of the ink that the present invention obtains be greatly improved, ink skinning
Slowly, it is also possible to avoid declining because little Mo belt carrys out printing quality in printing process, be properly arrived at properties of product and require.
For achieving the above object, the present invention is achieved by the following scheme：
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 30～40 parts, colloid oil 10～20 parts, pigment 10～20 parts, polysiloxanes KH-5506～12 part, thickener
3～8 parts, 2～5 parts of plasticizer, dispersant 2～6 parts, adhesion promoter 1～5 part, dibutyl tin laurate 1～2 part,
Surfactant Walloxen TR501～2 part of 0.1%-0.9%, mixed solvent 25～45 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.2～0.4：0.5～0.8 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：
1：0.2～0.5 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, and before sand milling dispersion completes, 4-7 minute adds adhesion promoter；Dispersion adds thickening after completing
Agent, dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
Wherein, described pigment includes Huang, red, blue and black pigment, and wherein, yellow uitramarine is pigment Yellow 12, pigment yellow
13, the one of pigment yellow 17 or its mixture；Red pigment is fuchsin 4B, fuchsin 6B, the one of fuchsin 8B or its mixture；Blue
Look pigment is Phthalocyanine Blue BGS, the one of phthalocyanine blue b or its mixture；Its black pigment is colour carbon black.
Described thickener is polyvinyl alcohol, polyvinylpyrrolidone, the mixture of one or more in polyethylene glycol oxide.
Described adhesion promoter is vinyl chloride-vinyl acetate resin.
Described dispersant is water soluble amino alcohol.
Described plasticizer is the one in dioctyl phthalate, dibutyl phthalate or trioctyl trimellitate (TOTM)
Or several combinations.
The viscosity of described High-gloss quick-drying skinning-free ink is 3.3-7.5CP/25 DEG C, and conductance is 750-1790 μ S, surface
Tension force is 32-42dyn/cm, 20 DEG C.
The invention has the beneficial effects as follows：The present invention uses organosilicon modified crylic acid resin, ethene-vinyl acetate copolymerization tree
Fat and rosin resin compound and obtain the minimizing pollution to environment for the aldehydes matter of composite polymeric resin, and contrast prior art
One-component resin has preferably printing adaptability and effect, and its binder, using colloid oil as film forming matter, makes the present invention obtain
To the gloss of ink be greatly improved, the ink of ink and viscoplasticity have had very big improvement, it is achieved that the height of ink
Light and the balance of set speed, in addition, the environmental protection quick-dry type ink storage time that the present invention prepares is longer, stability is preferable,
Under 70-80 DEG C of environment, 3min can be completely dried, it is to avoid stock is due to the adverse consequences such as deformation, variable color after high-temperature baking；
In addition, it is also an advantage of the present invention that its feature of environmental protection, use alcohol, water as solvent low toxic and environment-friendly, do not contain benzene, ketones solvent, its
Its raw material is also nontoxic to human body and environment or low toxicity composition；Ink adhesion reaches 0.35-0.55N/mm2, in addition, this
Inventive technique scheme is as an entirety, the mutual coordinated of each component so that the ink of preparation has excellent wear-resisting, resistance to
Water, resistance to chemical attack and good adhesive force, its quick drying capacity, it can be avoided that ink print through, uses tin dilaurate
The combination of dibutyl tin and surfactant Walloxen TR50 greatly improves the quick-drying performance of ink, and polysiloxanes
The addition of KH-550 improves the toughness of ink, maintains the stability of ink, stores 9-15 month and never degenerates.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described enforcement
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
Embodiment 1
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 30 parts, colloid oil 10 parts, pigment Phthalocyanine Blue BGS 10 parts, polysiloxanes KH-5506 part, thickener polyethylene
Alcohol 3 parts, plasticizer phthalic acid dioctyl ester 2 parts, dispersant water soluble amino alcohol 2 parts, adhesion promoter vinyl chloride-vinyl acetate resin 1
Part, dibutyl tin laurate 1 part, surfactant Walloxen TR501 part of 0.1%, mixed solvent 25 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.2：0.5 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.2 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, within 4 minutes before sand milling dispersion completes, adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
Embodiment 2
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 40 parts, colloid oil 20 parts, pigment Yellow 12 20 parts, polysiloxanes KH-55012 part, thickener polyvinyl pyrrole
Alkanone 8 parts, plasticizer phthalic acid dibutyl ester 5 parts, dispersant water soluble amino alcohol 6 parts, adhesion promoter vinyl chloride-vinyl acetate resin 5
Part, dibutyl tin laurate 2 parts, surfactant Walloxen TR502 part of 0.9%, mixed solvent 45 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.4：0.8 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.5 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, within 7 minutes before sand milling dispersion completes, adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
Embodiment 3
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 35 parts, colloid oil 15 parts, pigment phthalocyanine blue b 15 parts, polysiloxanes KH-5509 part, thickener polyoxyethylene
5 parts of alkene, plasticizer trioctyl trimellitate (TOTM) 3 parts, dispersant water soluble amino alcohol 4 parts, adhesion promoter vinyl chloride-vinyl acetate resin 3 parts,
Dibutyl tin laurate 1 part, surfactant Walloxen TR501 part of 0.5%, mixed solvent 35 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.3：0.6 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.4 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, within 6 minutes before sand milling dispersion completes, adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
Embodiment 4
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 32 parts, colloid oil 12 parts, pigment carmine 6B 12 parts, polysiloxanes KH-5508 part, thickener polyvinyl alcohol 4
Part, plasticizer phthalic acid dibutyl ester 3 parts, dispersant water soluble amino alcohol 3 parts, adhesion promoter vinyl chloride-vinyl acetate resin 2 parts, two
Dibutyl tin laurate 2 parts, surfactant Walloxen TR501.5 part of 0.4%, mixed solvent 30 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.2：0.6 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.3 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, within 5 minutes before sand milling dispersion completes, adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
Embodiment 5
A kind of High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, described ink is made up of following component：Multiple
Close fluoropolymer resin 37 parts, colloid oil 17 parts, pigment carmine 8B 17 parts, polysiloxanes KH-55010 part, thickener polyoxyethylene
6 parts of alkene, plasticizer trioctyl trimellitate (TOTM) 4 parts, dispersant water soluble amino alcohol 5 parts, adhesion promoter vinyl chloride-vinyl acetate resin 4 parts,
Dibutyl tin laurate 2 parts, surfactant Walloxen TR502 part of 0.7%, mixed solvent 32 parts；
Wherein, described composite polymeric resin by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and
Rosin resin is in mass ratio：1：0.4：0.6 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.4 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed
Uniformly, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by face
Material, polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min
Clock, sand milling disperses 50 minutes, within 6 minutes before sand milling dispersion completes, adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
The ink to embodiment 1-5 for the present invention has carried out the test of respective performances, the results are shown in Table 1：
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from the spirit or essential attributes of the present invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but not each embodiment only wraps
Containing an independent technical scheme, this narrating mode of specification is only that for clarity sake those skilled in the art should
Using specification as an entirety, the technical scheme in each embodiment also can form those skilled in the art through appropriately combined
May be appreciated other embodiments.
Claims (7)
1. the High-gloss quick-drying skinning-free ink that can be used for clothing popularity printing, it is characterised in that described ink is by following group
It is grouped into：Composite polymeric resin 30～40 parts, colloid oil 10～20 parts, pigment 10～20 parts, polysiloxanes KH-5506～12
Part, thickener 3～8 parts, 2～5 parts of plasticizer, dispersant 2～6 parts, adhesion promoter 1～5 part, dibutyl tin laurate
1～2 part, surfactant Walloxen TR501～2 part of 0.1%-0.9%, mixed solvent 25～45 parts；
Wherein, described composite polymeric resin is by organosilicon modified crylic acid resin, ethene-vinyl acetate copolymer resins and rosin
Resin is in mass ratio：1：0.2～0.4：0.5～0.8 composition；Described mixed solvent is by absolute ethyl alcohol and water in mass ratio：1：0.2
～0.5 composition；
The preparation method of described High-gloss quick-drying skinning-free ink comprises the steps：First dispersant and mixed solvent are mixed all
Even, after adding composite polymeric resin and colloid oil to mix under stirring, pour in sand milling container；Then by pigment,
Polysiloxanes KH-550 and plasticizer are separately added in sand milling container, after pre-dispersed, rotating speed bring up to 2500 revs/min,
Sand milling disperses 50 minutes, and before sand milling dispersion completes, 4-7 minute adds adhesion promoter；Dispersion complete after add thickener,
Dibutyl tin laurate and surfactant Walloxen TR50, after stirring, to obtain final product.
2. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described pigment includes Huang, red, blue
And black pigment, wherein, yellow uitramarine is pigment Yellow 12, pigment yellow 13, the one of pigment yellow 17 or its mixture；Red pigment
For fuchsin 4B, fuchsin 6B, the one of fuchsin 8B or its mixture；Blue pigment is Phthalocyanine Blue BGS, the one of phthalocyanine blue b or its
Mixture；Its black pigment is colour carbon black.
3. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described thickener be polyvinyl alcohol,
The mixture of one or more in polyvinylpyrrolidone, polyethylene glycol oxide.
4. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described adhesion promoter is chlorine vinegar
Resin.
5. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described dispersant is water soluble amino
Alcohol.
6. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described plasticizer is phthalic acid
The combination of one or more in dioctyl ester, dibutyl phthalate or trioctyl trimellitate (TOTM).
7. High-gloss quick-drying skinning-free ink according to claim 1, it is characterised in that described High-gloss quick-drying skinning-free ink
Viscosity be 3.3-7.5CP/25 DEG C, conductance is 750-1790 μ S, and surface tension is 32-42dyn/cm, 20 DEG C.